CN106947290A - 彩色二氧化硅粉体材料的制备方法 - Google Patents

彩色二氧化硅粉体材料的制备方法 Download PDF

Info

Publication number
CN106947290A
CN106947290A CN201710209840.2A CN201710209840A CN106947290A CN 106947290 A CN106947290 A CN 106947290A CN 201710209840 A CN201710209840 A CN 201710209840A CN 106947290 A CN106947290 A CN 106947290A
Authority
CN
China
Prior art keywords
silicon
dioxide powdery
copper chloride
dioxide
powdery material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710209840.2A
Other languages
English (en)
Inventor
赵慧军
方春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEFEI YUELAN INFORMATION TECHNIQUE Co Ltd
Original Assignee
HEFEI YUELAN INFORMATION TECHNIQUE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEFEI YUELAN INFORMATION TECHNIQUE Co Ltd filed Critical HEFEI YUELAN INFORMATION TECHNIQUE Co Ltd
Priority to CN201710209840.2A priority Critical patent/CN106947290A/zh
Publication of CN106947290A publication Critical patent/CN106947290A/zh
Pending legal-status Critical Current

Abstract

一种彩色二氧化硅粉体材料的制备方法，涉及新材料领域，将氯化铜溶于乙醇中，得氯化铜的乙醇溶液，将二氧化硅粉体材料至于密闭容器中，密闭容器从底部向上产生高压氮气流使二氧化硅粉体材沸腾，然后将氯化铜的乙醇溶液雾化后喷入密闭容器中，与二氧化硅粉体结合，再经过火焰煅烧，即得彩色二氧化硅粉体材料。本发明彩色二氧化硅粉体材料的制备方法简单易行，制备出来的彩色二氧化硅同时具有不透光性和绝缘性，硬度低，非常容易进行穿孔、切削等机械加工，使二氧化硅粉体具有彩色的物质在二氧化硅颗粒内部，使二氧化硅颗粒本体由内而外的显现色彩，具有永不褪色的优点，可广泛应用于CCL、PP等需要满足不透光性能的电子基础材料。

Description

彩色二氧化硅粉体材料的制备方法
技术领域：
本发明涉及新材料领域，尤其涉及一种彩色二氧化硅粉体材料的制备方法。
背景技术：
纳米二氧化硅粉体材料可广泛应用于机械、日用化工、生物医药、建筑业、航空航天业、农业等领域，在声、光、电、磁及热力学等方面也呈现出奇异的特性，亦可广泛用于微电子、信息材料、涂料、橡胶、塑料、农作物种子处理剂、抛光剂、LED光扩散剂、高级耐火材料及造纸等方面。
复合材料是由两种或两种以上不同性质的材料，通过物理或化学的方法，在宏观上组成具有新性能的材料。各种材料在性能上互相取长补短，产生协同效应，使复合材料的综合性能优于原组成材料而满足各种不同的要求。在很多领域都发挥了很大的作用，代替了很多传统的材料。
传统的纳米二氧化硅粉体材料是一种不具有导电性的二氧化硅粉体材料，虽有很广泛的应用领域，但若将其改性为具有导电性的无机粉体材料，应用领域和方向还具有很大的拓展空间。
发明内容：
本发明的目的在于，提供一种彩色二氧化硅粉体材料的制备方法，以拓展纳米二氧化硅材料新的应用领域和方向。
本发明所要解决的技术问题采用以下技术方案来实现。
一种彩色二氧化硅粉体材料的制备方法，其特征在于：将氯化铜溶于乙醇中，得氯化铜的乙醇溶液，将二氧化硅粉体材料至于密闭容器中，密闭容器从底部向上产生高压氮气流使二氧化硅粉体材沸腾，然后将氯化铜的乙醇溶液雾化后喷入密闭容器中，与二氧化硅粉体结合，氯化铜的乙醇溶液与二氧化硅粉体结合过程中，二氧化硅粉体的温度控制在45-50℃，氯化铜的乙醇溶液与二氧化硅粉体充分结合后，氯化铜的乙醇溶液吸附于二氧化硅粉体颗粒的孔洞内，再经过火焰煅烧，即得彩色二氧化硅粉体材料；
上述氯化铜、乙醇、二氧化硅粉体的质量比为3：17：45。
作为优选，所述纳米二氧化硅颗粒在使用前经过质量分数为2～3％的双氧水浸泡，浸泡时间为15min，然后用纯水漂洗干净后干燥、打散。
作为优选，所述纳米二氧化硅粒径分布在50～80纳米范围内。
利用纳米二氧化硅颗粒的多孔性，将氯化铜的乙醇溶液吸附在二氧化硅颗粒的孔洞内，再经过火焰煅烧，去除乙醇，将氯化铜留在二氧化硅颗粒的孔洞内，即得彩色二氧化硅粉体材料。
本发明彩色二氧化硅粉体材料的制备方法简单易行，制备出来的彩色二氧化硅同时具有不透光性和绝缘性，硬度低，非常容易进行穿孔、切削等机械加工，使二氧化硅粉体具有彩色的物质(氯化铜)在二氧化硅颗粒内部，使二氧化硅颗粒本体由内而外的显现色彩，具有永不褪色的优点，可广泛应用于CCL、PP等需要满足不透光性能的电子基础材料。
具体实施方式：
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例一
彩色二氧化硅粉体材料的制备方法，步骤为：将氯化铜溶于乙醇中，得氯化铜的乙醇溶液，将粒径分布在50～80纳米的二氧化硅粉体材料至于密闭容器中，密闭容器从底部向上产生高压氮气流使二氧化硅粉体材沸腾，然后将氯化铜的乙醇溶液雾化后喷入密闭容器中，与二氧化硅粉体结合，氯化铜的乙醇溶液与二氧化硅粉体结合过程中，二氧化硅粉体的温度控制在45-50℃，氯化铜的乙醇溶液与二氧化硅粉体充分结合后，氯化铜的乙醇溶液吸附于二氧化硅粉体颗粒的孔洞内，再经过火焰煅烧，即得彩色二氧化硅粉体材料；
上述氯化铜、乙醇、二氧化硅粉体的质量比为3：17：45。
实施例二
彩色二氧化硅粉体材料的制备方法，步骤为：将氯化铜溶于乙醇中，得氯化铜的乙醇溶液，将粒径分布在50～80纳米的二氧化硅粉体材料至于密闭容器中，密闭容器从底部向上产生高压氮气流使二氧化硅粉体材沸腾，然后将氯化铜的乙醇溶液雾化后喷入密闭容器中，与二氧化硅粉体结合，氯化铜的乙醇溶液与二氧化硅粉体结合过程中，二氧化硅粉体的温度控制在45-50℃，氯化铜的乙醇溶液与二氧化硅粉体充分结合后，氯化铜的乙醇溶液吸附于二氧化硅粉体颗粒的孔洞内，再经过火焰煅烧，即得彩色二氧化硅粉体材料；
上述氯化铜、乙醇、二氧化硅粉体的质量比为3：17：45；纳米二氧化硅颗粒在使用前经过质量分数为2～3％的双氧水浸泡，浸泡时间为15min，然后用纯水漂洗干净后干燥、打散。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (3)

1.一种彩色二氧化硅粉体材料的制备方法，其特征在于：将氯化铜溶于乙醇中，得氯化铜的乙醇溶液，将二氧化硅粉体材料至于密闭容器中，密闭容器从底部向上产生高压氮气流使二氧化硅粉体材沸腾，然后将氯化铜的乙醇溶液雾化后喷入密闭容器中，与二氧化硅粉体结合，氯化铜的乙醇溶液与二氧化硅粉体结合过程中，二氧化硅粉体的温度控制在45-50℃，氯化铜的乙醇溶液与二氧化硅粉体充分结合后，氯化铜的乙醇溶液吸附于二氧化硅粉体颗粒的孔洞内，再经过火焰煅烧，即得彩色二氧化硅粉体材料；
上述氯化铜、乙醇、二氧化硅粉体的质量比为3：17：45。
2.根据权利要求1所述的彩色二氧化硅粉体材料的制备方法，其特征在于：所述纳米二氧化硅颗粒在使用前经过质量分数为2～3％的双氧水浸泡，浸泡时间为15min，然后用纯水漂洗干净后干燥、打散。
3.根据权利要求1所述的彩色二氧化硅粉体材料的制备方法，其特征在于：所述纳米二氧化硅粒径分布在50～80纳米范围内。
CN201710209840.2A 2017-03-31 2017-03-31 彩色二氧化硅粉体材料的制备方法 Pending CN106947290A (zh)