CN1069074A - 离心铸造复合轧辊球化处理方法 - Google Patents

离心铸造复合轧辊球化处理方法 Download PDF

Info

Publication number
CN1069074A
CN1069074A CN 92108792 CN92108792A CN1069074A CN 1069074 A CN1069074 A CN 1069074A CN 92108792 CN92108792 CN 92108792 CN 92108792 A CN92108792 A CN 92108792A CN 1069074 A CN1069074 A CN 1069074A
Authority
CN
China
Prior art keywords
spheroidizing
molten iron
alloy
roller
roll
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 92108792
Other languages
English (en)
Other versions
CN1023237C (zh
Inventor
俞哲达
邵素云
王刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Central Iron and Steel Research Institute
Original Assignee
Central Iron and Steel Research Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Central Iron and Steel Research Institute filed Critical Central Iron and Steel Research Institute
Priority to CN 92108792 priority Critical patent/CN1023237C/zh
Publication of CN1069074A publication Critical patent/CN1069074A/zh
Application granted granted Critical
Publication of CN1023237C publication Critical patent/CN1023237C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明提供了一种离心铸造复合轧辊的球化处 理方法。其主要特征是轧辊外层铁水球化处理采用 由镍镁合金和稀土硅铁镁合金组成的复合球化剂。 镍镁合金的化学成分(重量%)为Ni80~90%,Mg10 ~20%;稀土硅铁镁合金的化学成分(重量%)为: RE1~10%,Mg6~12%,Si35~45%,余为Fe。球化 处理采用包底冲入法,其浇包底部有一倾角为55° ~70°的堤坝。其球化效果稳定,镁收得率高,铁水 中夹杂少等特点。

Description

本发明属于离心铸造轧辊技术。主要适用于离心铸造复合珠墨铸铁轧辊的球化处理。
离心铸造复合球墨铸铁轧辊是80年代发展起来的一种新型轧辊。它具有辊身硬度高,耐磨性好,辊颈强度高,韧性好等优点。
离心铸造复合球墨铸铁轧辊制造方法的关键之一是球化处理方法。众所周之,在球墨铸铁生产中,镁是最有效的球化元素。铁水中需保持一定含量的残镁量,才能保证铸件球化效果良好。离心铸造复合球墨铸铁轧辊时,球化处理后的铁水中含镁量随时间的延长而逐渐降低。同时,外层铁水浇入高速旋转的金属铸模时,铁水迅速展开,并与大气接触,加速了镁的氧化烧损。因此,选择合适的球化剂、孕育剂及球化处理工艺就成为保证铁水球化效果和轧辊质量的关键。
现有球墨铸铁轧辊的球化处理方法主要有两种:(1)采用纯镁球化剂,压力包球化处理;(2)稀土镁合金球化剂,冲入法球化处理(《铸铁轧辊生产》,王殿刚、杨和林编著,冶金工业出版社,1988·1,P170)。压力包纯镁球化处理,设备复杂,要求高,处理时间长,铁水降温快。而离心铸造复合球墨铸铁轧辊等,轧辊外层及芯部铁水需要分别进行球化处理,外层球化铁水量较少,采用压力包球化处理方法较为困难。稀土镁合金球化剂冲入法球化处理方法,通常采用堤垻式浇包(见附图1)。该浇包底部堤垻呈垂直状,并带有较大斜度,因而,放入堤垻内的球化、孕育剂无法被固定,加入稀土镁合金和硅铁合金比重较轻,铁水冲入时,球化剂和孕育剂很容易上浮,造成镁和稀土元素严重氧化烧损,使球化效果不稳定;同时,稀土镁合金处理铁水时所形成的大量稀土氧化物夹杂,因其比重较大,很难从铁水中去除,以致影响轧辊性能和质量。
本发明的目的在于提供一种离心铸造复合球墨铸铁轧辊的球化处理方法,包括球化剂及球化处理工艺。该球化处理方法不仅设备简单,操作灵活,而且球化效果稳定,铁水中夹杂物少,所铸造的轧辊性能好,质量高。
为达到上述目的,本发明所采用的主要技术方案是:(1)离心铸造复合球墨铸铁轧辊外层铁水采用镍镁合金、稀土硅铁镁合金复合球化剂;(2)轧辊外层、芯部铁水采用改进型浇包(见附图2)包底冲入法进行球化处理,浇包底部有一倾斜角为55°~70°的堤垻,在包底形成一个底大、口小的半园形球化处理反应室。
离心铸造复合球墨铸铁轧辊的铸造工艺流程为:
外层铁水熔炼→球化孕育处理→离心铸造
                                                            ↓
芯部铁水熔炼→球化孕育处理→填芯→冷却
现将离心铸造复合球墨铁铁轧辊外层及芯部的球化处理方法分述如下:
1.轧辊外层铁水球化处理方法
球化采用由镍镁合金和稀土硅铁镁合金组成的复合球化剂。镍镁合金的化学成分(重量%)为:Ni80~90%,Mg10~20%;稀土硅铁镁合金的化学成分(重量%)为:RE1~10%,Mg6~12%,Si35~45%,余为Fe。
镍镁合金的加入量:0.6~1.2%(占处理铁水总量之比)
稀土硅铁镁合金加入量0.3~0.8%(占处理铁水总量之比)
孕育剂采用硅铁合金(含Si60~75%),其加入量为0.3~0.8%(占处理铁水总量)。
镍镁合金、稀土硅铁镁合金和硅铁合金依次放入浇包反应室内,用木棒夯实,上面复盖铁板或铁屑,温度1380~1460℃的铁水冲入包底进行球化处理。
2    轧辊芯部铁水球化处理方法
球化剂采用稀土硅铁镁合金。稀土硅铁镁合金的化学成分(重量%)为RE5~10%,Mg6~10%,Si35~45%,余为Fe。
稀土硅铁镁合金的加入量为1.3~2.0%(占处理铁水总量的百分比)。
孕育剂采用硅铁合金(含Si量60~75%),其加入量为0.4~1.2%(占处理铁水总量的百分比)。
稀土硅铁镁合金、硅铁合金依次放入浇包反应室内,用木棒夯实,上面复盖铁板或铁屑,温度1380~1460℃的铁水冲入包底进行球化处理。
与现有技术相比,本发明具有如下优点:
(1)采用镍镁合金、稀土硅铁镁合金作为复合球化剂,具有铁水球化反应较平稳,球化效果稳定,减少污染等优点。复合球化剂中的稀土元素有脱氧、脱硫,中和干扰元素的作用,并能提高铁水的纯净度,降低铁水氧化膜形成温度,促进球化;另外,镍镁合金夹杂少,比重大,铁水冲入时,镍镁合金不易上浮,镁的收得率高,带入铁水中的夹杂物少。
(2)本发明的改进型堤垻浇包,由于反应室的口较小,铁水冲入时,球化剂、孕育剂不易上浮,球化过程主要在反应室中进行,致使镁与稀土元素氧化烧损小,球化效果稳定。
(3)本发明适用于立式、卧式和斜式离心铸造机铸造复合球墨铸铁轧辊。
附图说明
附图1为现有技术球化处理浇包的结构示意图
附图2为本发明球化处理改进型浇包结构示意图。
附图1、2中,1为包体,2为堤垻,2为堤垻的倾斜角,角度为55°~70°,3为反应室。
实施例
根据本发明所述的球化剂、孕育剂及加入量,和改进型堤垻浇包冲入法的球化处理方法,对5种规格的离心铸造复合球墨铸铁轧辊进行了球化处理。所采用的球化孕育剂的化学成分和加入量以及轧辊外层和芯部的铁水量如表1所示。离心铸造轧辊的尺寸,球化处理方法及轧辊中残存的Mg、RE含量如表2所示。
Figure 921087926_IMG2
Figure 921087926_IMG3

Claims (2)

1、一种离心铸造复合轧辊球化处理方法,其特征在于:
A、轧辊外层铁水球化处理采用由镍镁合金和稀土硅铁镁合金组成的复合球化剂;镍镁合金的化学成分(重量%)为:Ni80~90%,Mg10~20%;稀土硅铁镁合金的化学成分(重量%)为:RE1~10%,Mg6~12%,Si35~45%,余为Fe;镍镁合金的加入量为0.6~1.2%(占处理铁水总量之比),稀土硅铁镁合金的加入量为0.3~0.8%(占处理铁水总量之比);
B、采用包底冲入法进行球化处理的浇包的底部有一倾斜角为55°~70°的堤垻。
2、根据权利要求1所述的球化处理方法,其特征在于球化处理所用的浇包的反应室为底大、口小的半园形。
CN 92108792 1992-07-30 1992-07-30 离心铸造复合轧辊球化处理方法 Expired - Fee Related CN1023237C (zh)