CN106854396A - Aqueous mill base and color and manufacture method - Google Patents
Aqueous mill base and color and manufacture method Download PDFInfo
- Publication number
- CN106854396A CN106854396A CN201611268654.8A CN201611268654A CN106854396A CN 106854396 A CN106854396 A CN 106854396A CN 201611268654 A CN201611268654 A CN 201611268654A CN 106854396 A CN106854396 A CN 106854396A
- Authority
- CN
- China
- Prior art keywords
- aqueous
- parts
- color
- deionized water
- mill base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aqueous mill base and color and its manufacture method.Aqueous mill base and color of the invention, are made up of deionized water, aqueous coupling agent, aqueous dispersion, aqueous pigment.Aqueous color paste and aqueous color are obtained according to the different number of aqueous pigment, the maximal compatible with simplest proportioning to reach with water-base resin gives the factory formula of producer maximum flexibility.Aqueous mill base of the invention and color have environmental protection, using simple, applicability is splendid, low-cost advantage.
Description
Technical field
The present invention relates to a kind of aqueous mill base and color, the specifically related to production of water-based ink and water paint.
Background technology
Current China ink industry mostly uses solvent-based ink, poisonous and harmful VOC volatilizations high, water-based ink to be in greatly
Power development；With the strict demand of environmental protection, water-based ink factory, water paint factory directly produce water-based ink using pigment
Water paint some difficulty, environmental protection treatment is costly；Aqueous mill base of the invention and color are free of organic solvent, safety collar
Protect, easy to use, wide adaptability.
The content of the invention
The present invention solves the technical problem of offer a kind of aqueous mill base and color, aqueous mill base of the invention
Organic solvent is free of with color, safety and environmental protection is easy to use, wide adaptability.
Aqueous mill base and color of the invention, by deionized water, aqueous coupling agent, aqueous dispersion, aqueous pigment group
Into：
Described deionized water 30-70 parts；
Described aqueous coupling agent 3-20 parts；
Described aqueous dispersion 3-20 parts；
Described aqueous pigment 20-60 parts；
Described number is parts by weight.
Machine required for the preparation of aqueous mill base and color of the invention has：
High-speed stirred tank, sand mill, batch mixer, three-roll grinder, spraying machine.
Preferably one is：
62.5 parts of the deionized water；
3.125 parts of the aqueous coupling agent；
3.125 parts of the aqueous dispersion；
31.25 parts of the aqueous pigment；
Described number is parts by weight.
The preparation method of above-mentioned aqueous mill base, is carried out as steps described below：
First, deionized water, aqueous coupling agent, aqueous dispersion are sequentially added in high-speed stirred tank, is stirred 5 minutes；
2nd, to aqueous pigment is slowly added in the liquid of step one, stir 60 minutes, pulp；
3rd, aqueous slurry in step 2 is taken, adds sand mill to grind three times, into flowable pulpous state.
Preferably two are：
41.67 parts of the deionized water；
4.165 parts of the aqueous coupling agent；
4.165 parts of the aqueous dispersion；
50 parts of the aqueous pigment；
Described number is parts by weight.
The preparation method of above-mentioned aqueous color, is carried out as steps described below：
First, deionized water, aqueous coupling agent, aqueous dispersion are sequentially added in high-speed stirred tank, is stirred 5 minutes；
2nd, aqueous pigment is poured into batch mixer, by 30 revs/min of stirrings；
3rd, the liquid in step one is stirred 120 minutes, into viscous paste with spraying machine penetrating step 2；
4th, aqueous cream in step 3 is taken, input sand mill grinds three times, into even and fine paste.
The beneficial effects of the invention are as follows：Aqueous mill base of the invention and color are formed by plurality of raw materials rational proportion, root
Aqueous color paste and aqueous color is obtained according to the different numbers of aqueous pigment, is reached with water-base resin most with simplest proportioning
Big compatibility, gives the factory formula of producer maximum flexibility.Aqueous mill base of the invention and color have environmental protection, use letter
Single, applicability is splendid, low-cost advantage.
Described above is only the general introduction of technical solution of the present invention, in order to better understand technological means of the invention,
And can be practiced according to the content of specification, described in detail as after with presently preferred embodiments of the present invention below.
Embodiment 1：Aqueous mill base and color of the invention, by deionized water, aqueous coupling agent, aqueous dispersion, water
Property pigment composition：62.5 parts of the deionized water；3.125 parts of the aqueous coupling agent；3.125 parts of the aqueous dispersion；Institute
State 31.25 parts of aqueous pigment；Described number is parts by weight.
The preparation method of aqueous mill base is stated, is carried out as steps described below：
First, deionized water, aqueous coupling agent, aqueous dispersion are sequentially added in high-speed stirred tank, is stirred 5 minutes；
2nd, to aqueous pigment is slowly added in the liquid of step one, stir 60 minutes, pulp；
3rd, aqueous slurry in step 2 is taken, adds sand mill to grind three times, into flowable pulpous state.
Embodiment 2：Aqueous mill base and color of the invention, by deionized water, aqueous coupling agent, aqueous dispersion, water
Property pigment composition：41.67 parts of the deionized water；4.165 parts of the aqueous coupling agent；4.165 parts of the aqueous dispersion；Institute
State 50 parts of aqueous pigment；Described number is parts by weight.
The preparation method of above-mentioned aqueous color, is carried out as steps described below：
First, deionized water, aqueous coupling agent, aqueous dispersion are sequentially added in high-speed stirred tank, is stirred 5 minutes；
2nd, aqueous pigment is poured into batch mixer, by 30 revs/min of stirrings；
3rd, a kind of liquid of step is stirred 120 minutes, into viscous paste with spraying machine penetrating step 2；
4th, in the viscous cream addition three-roll grinder in step 3, grind twice, into uniform paste；
5th, uniform cream in step 4 is taken, input sand mill grinds twice, into fine and smooth paste.
Embodiments of the invention are the foregoing is only, the scope of the claims of the invention is not thereby limited, it is every to utilize this hair
Equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, is included within the scope of the present invention.
Claims (5)
1. a kind of aqueous mill base and color, it is characterised in that：Aqueous mill base and color of the invention, by deionized water, water
Property coupling agent, aqueous dispersion, aqueous pigment composition；Described deionized water 30-70 parts；Described aqueous coupling agent 3-20 parts；Institute
State aqueous dispersion 3-20 parts；Described aqueous pigment 20-60 parts；Described number is parts by weight.
2. aqueous mill base according to claim 1, it is characterised in that：62.5 parts of the deionized water；The aqueous idol
3.125 parts of agent of connection；3.125 parts of the aqueous dispersion；31.25 parts of the aqueous pigment；Described number is parts by weight.
3. the preparation method of mill base according to claim 2, is carried out as steps described below：
First, deionized water, aqueous coupling agent, aqueous dispersion are sequentially added in high-speed stirred tank, is stirred 5 minutes；
2nd, to aqueous pigment is slowly added in the liquid of step one, stir 60 minutes, pulp；
3rd, aqueous slurry in step 2 is taken, adds sand mill to grind three times, into flowable pulpous state.
4. aqueous color according to claim 1, it is characterised in that：41.67 parts of the deionized water；The aqueous idol
4.165 parts of agent of connection；4.165 parts of the aqueous dispersion；50 parts of the aqueous pigment；Described number is parts by weight.
5. the preparation method of aqueous color according to claim 4, is carried out as steps described below：
First, deionized water, aqueous coupling agent, aqueous dispersion are sequentially added in high-speed stirred tank, is stirred 5 minutes；
2nd, aqueous pigment is poured into batch mixer, by 30 revs/min of stirrings；
3rd, a kind of liquid of step is stirred 120 minutes, into viscous paste with spraying machine penetrating step 2；
4th, in the viscous cream addition three-roll grinder in step 3, grind twice, into uniform paste；
5th, uniform cream in step 4 is taken, input sand mill grinds twice, into fine and smooth paste.