CN104004416A - Water-based colour paste for printing ink - Google Patents
Water-based colour paste for printing ink Download PDFInfo
- Publication number
- CN104004416A CN104004416A CN201410243734.2A CN201410243734A CN104004416A CN 104004416 A CN104004416 A CN 104004416A CN 201410243734 A CN201410243734 A CN 201410243734A CN 104004416 A CN104004416 A CN 104004416A
- Authority
- CN
- China
- Prior art keywords
- parts
- printing ink
- mill base
- aqueous printing
- base according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of water-based colour paste and provides water-based colour paste which is environmentally friendly, non-toxic, good in dispersing performance, strong in tinting strength and resistant to light, does not become thick, has anti-ultraviolet ray property, good weatherability and resistance to chemical attack and does not get mildew. The water-based colour paste is prepared from the following raw materials in parts by weight: 50-60 parts of pigment, 4-6 parts of wetting agent, 9-12 parts of dispersing agent, 6-10 parts of antioxidant, 0.3-0.45 part of antiseptic, 0.3-0.5 part of mildew preventive, 0.5-0.7 part of water-based defoaming agent, 6-8 parts of thickening and anti-settling agnet, 6-10 parts of ultraviolet light absorber and 30-60 parts of deionized water.
Description
Technical field
The present invention relates to aqueous color paste technical field, relate in particular to a kind of aqueous printing ink mill base.
Background technology
Ink is mainly made up of mill base and binder two portions, and traditional mill base all contains organic solvent, and the consumption of the organic solvent that bring because of ink every year in the whole world, up to more than 1,000,000 tons, causes the huge wasting of resources.The organic solvents such as the ethanol that wherein often uses, butylacetate, toluene, dimethylbenzene.After dry, the overwhelming majority all can be eliminated, but lingering section still can work the mischief to human body, and Long Term Contact can make chapped skin, coarse, if infiltrate skin or blood vessel, can, with blood crisis people's blood cell and hematopoietic function, even may cause human body chronic poisoning.The volatilization of solvent causes topsoil, larger to the growth effect of each kind of plant, destroys the eubiosis.And heavy metal is absorbed by plants sometimes, will cause sizable harm if be absorbed by the body.
Along with scientific and technical development, requirement to mill base is more and more higher, there is on the market at present aqueous color paste, it is using water as solvent with thinner, environment-protecting asepsis, deeply be subject to consumers in general's welcome, but the organic solvent conventional compared with ink due to the surface tension of water is high, very large to the stability influence of aqueous color paste, easily cause that agglomeration appears in pigment particles, i.e. alleged " returning thick " phenomenon of factory, greatly affect the quality product of printing, the layering of even luming, scraps ink product, causes larger financial loss.
China Patent No. 201110104463.9 discloses a kind of high fineness aqueous color paste and preparation method, obtained through dispersion, grinding, high pressure homogenization, process of surface treatment process by pigment, aqueous dispersant, water-based defoamer, water-based coupling agent, synthetic wax emulsion, nanometer grade calcium carbonate, nano-kaoline, antisettling agent and deionized water, the aqueous color paste stability that relies on the method to make is stronger, but weather-resistant property is poor, light fugitive, not resistance to chemical attack, easily mouldy, and there is no anti-ultraviolet property.
Summary of the invention
Therefore,, for above content, the invention provides that a kind of environment-protecting asepsis, dispersing property are good, strong coloring force, do not return thick, fast light, there is anti-ultraviolet property, weathering resistance, be difficult for aqueous printing ink mill base mouldy, resistance to chemical attack.
For achieving the above object, the present invention is achieved by the following technical solutions: a kind of aqueous printing ink mill base, comprises each raw material of following weight part:
50～60 parts of pigment
4～6 parts of wetting agents
9～12 parts of dispersion agents
6～10 parts of antioxidants
Sanitas 0.3～0.45
0.3～0.5 part of mould inhibitor
0.5～0.7 part of water-based defoamer
6～8 parts of thickening anti-settling agents
6～10 parts of UV light absorber
30～60 parts of deionized waters.
Further improve and be: described aqueous printing ink mill base comprises each raw material of following weight part:
Pigment yellow 155～60 part
5～6 parts of wetting agents
10～12 parts of dispersion agents
8～10 parts of antioxidants
Sanitas 0.4～0.45
0.4～0.5 part of mould inhibitor
0.6～0.7 part of water-based defoamer
7～8 parts of thickening anti-settling agents
8～10 parts of UV light absorber
45～60 parts of deionized waters.
Further improve and be: described pigment be in titanium dioxide, iron oxide red, middle Huang, lemon yellow, bright red, permanent bordeaux, carbon black, permanent violet, phthalocyanine blue or phthalocyanine green any one or two or more with arbitrarily than the mixture mixing.
Further improve and be: described wetting agent is alkyl polyoxyethylene ether solution.
Further improve and be: described dispersion agent is Zelan 338 solution.
Further improve and be: described antioxidant is aromatic amine, Hinered phenols or phosphorous acid esters antioxidant.
Further improve and be: described sanitas is 5-chloro-2 methyl-3-isothiazolones, and described mould inhibitor is any one in Sodium dehydroacetate, sodium sorbate, Sodium Benzoate or sodium pentachlorophenol.
Further improve and be: described water-based defoamer is silicone based defoamer.
Further improve and be: described thickening anti-settling agent is any one or the two or more mixture with any combination in modified alta-mud, aerosil or Natvosol.
Further improve and be: described UV light absorber is any one in salicylate class, benzophenone class, hindered amines, triazines or Benzotriazole Ultraviolet Stabilizer.
By adopting aforementioned techniques scheme, the invention has the beneficial effects as follows: a kind of aqueous printing ink mill base of the present invention, comprises each raw material of following weight part: 50～60 parts of pigment, 4～6 parts of wetting agents, 9～12 parts of dispersion agents, 6～10 parts of antioxidants, sanitas 0.3～0.45,0.3～0.5 part of mould inhibitor, 0.5～0.7 part of water-based defoamer, 6～8 parts of thickening anti-settling agents, 6～10 parts of UV light absorber, 30～60 parts of deionized waters.Adopt above integral formula to make the present invention have anti-ultraviolet property, weathering resistance, is difficult for mouldy, resistance to chemical attack, meanwhile, strong coloring force, good stability, does not return slightly, and dispersing property is good, environment-protecting asepsis, can be widely used in ink industry, and human body is not injured, compared with traditional organic mill base, Long Term Contact there will not be chapped skin, the phenomenon such as coarse, and solvent is not volatile, can not exert an influence to the growth of each kind of plant, can not destroy the eubiosis.
Embodiment
Describe embodiments of the present invention in detail below with reference to specific embodiment, to the present invention, how utilisation technology means solve technical problem whereby, and the implementation procedure of reaching technique effect can fully understand and implement according to this.
If do not specialize, the conventional means that the technique means adopting in embodiment is well known to those skilled in the art, the reagent adopting and product are also and can business obtain.Source, the trade(brand)name of agents useful for same and be necessary to list its moiety person all indicated in the time occurring first.
Embodiment mono-
A kind of aqueous printing ink mill base, comprises each raw material of following weight part:
50 parts of titanium dioxides
4 parts of alkyl polyoxyethylene ether solution
9 parts of Zelan 338 solution
6 parts of tri-grades of butyl-4-methylphenols of 2,6-
0.3 part of 5-chloro-2 methyl-3-isothiazolones
0.5 part of Sodium Benzoate
0.7 part of silicone based defoamer
8 parts of Natvosols
10 parts of salols
60 parts of deionized waters.
Embodiment bis-
A kind of aqueous printing ink mill base, comprises each raw material of following weight part:
55 parts of phthalocyanine blues
5 parts of alkyl polyoxyethylene ether solution
10 parts of Zelan 338 solution
Three 8 parts of monooctyl esters
0.4 part of 5-chloro-2 methyl-3-isothiazolones
0.4 part of sodium sorbate
0.6 part of silicone based defoamer
7 parts of aerosils
2-(2 ' hydroxyl-3 ', 5 '-bis-tertiary phenyl) 8 parts of-5-chlorination benzotriazoles
45 parts of deionized waters.
Embodiment tri-
A kind of aqueous printing ink mill base, comprises each raw material of following weight part:
60 parts of carbon blacks
6 parts of alkyl polyoxyethylene ether solution
12 parts of Zelan 338 solution
10 parts of aniline
0.45 part of 5-chloro-2 methyl-3-isothiazolones
0.5 part of Sodium dehydroacetate
0.5 part of silicone based defoamer
6 parts of modified alta-muds
6 parts of ESCALOL 567s
30 parts of deionized waters.
A kind of aqueous printing ink mill base of the present invention, comprise each raw material of following weight part: 50～60 parts of pigment, 4～6 parts of wetting agents, 9～12 parts of dispersion agents, 6～10 parts of antioxidants, sanitas 0.3～0.45,0.3～0.5 part of mould inhibitor, 0.5～0.7 part of water-based defoamer, 6～8 parts of thickening anti-settling agents, 6～10 parts of UV light absorber, 30～60 parts of deionized waters.Adopt above integral formula to make the present invention have anti-ultraviolet property, weathering resistance, is difficult for mouldy, resistance to chemical attack, meanwhile, strong coloring force, good stability, does not return slightly, and dispersing property is good, environment-protecting asepsis, can be widely used in ink industry, and human body is not injured, compared with traditional organic mill base, Long Term Contact there will not be chapped skin, the phenomenon such as coarse, and solvent is not volatile, can not exert an influence to the growth of each kind of plant, can not destroy the eubiosis.
Above record, only, for utilizing the embodiment of this origination techniques content, modification, variation that any those skilled in the art use this creation to do, all belong to the scope of the claims that this creation is advocated, and be not limited to those disclosed embodiments.
Claims (10)
1. an aqueous printing ink mill base, is characterized in that, comprises each raw material of following weight part:
50～60 parts of pigment
4～6 parts of wetting agents
9～12 parts of dispersion agents
6～10 parts of antioxidants
Sanitas 0.3～0.45
0.3～0.5 part of mould inhibitor
0.5～0.7 part of water-based defoamer
6～8 parts of thickening anti-settling agents
6～10 parts of UV light absorber
30～60 parts of deionized waters.
2. aqueous printing ink mill base according to claim 1, is characterized in that, comprises each raw material of following weight part:
Pigment yellow 155～60 part
5～6 parts of wetting agents
10～12 parts of dispersion agents
8～10 parts of antioxidants
Sanitas 0.4～0.45
0.4～0.5 part of mould inhibitor
0.6～0.7 part of water-based defoamer
7～8 parts of thickening anti-settling agents
8～10 parts of UV light absorber
45～60 parts of deionized waters.
3. aqueous printing ink mill base according to claim 1 and 2, is characterized in that: described pigment be in titanium dioxide, iron oxide red, middle Huang, lemon yellow, bright red, permanent bordeaux, carbon black, permanent violet, phthalocyanine blue or phthalocyanine green any one or two or more with arbitrarily than the mixture mixing.
4. aqueous printing ink mill base according to claim 1 and 2, is characterized in that: described wetting agent is alkyl polyoxyethylene ether solution.
5. aqueous printing ink mill base according to claim 1 and 2, is characterized in that: described dispersion agent is Zelan 338 solution.
6. aqueous printing ink mill base according to claim 1 and 2, is characterized in that: described antioxidant is aromatic amine, Hinered phenols or phosphorous acid esters antioxidant.
7. aqueous printing ink mill base according to claim 1 and 2, is characterized in that: described sanitas is 5-chloro-2 methyl-3-isothiazolones, and described mould inhibitor is any one in Sodium dehydroacetate, sodium sorbate, Sodium Benzoate or sodium pentachlorophenol.
8. aqueous printing ink mill base according to claim 1 and 2, is characterized in that: described water-based defoamer is silicone based defoamer.
9. aqueous printing ink mill base according to claim 1 and 2, is characterized in that: described thickening anti-settling agent is any one or the two or more mixture with any combination in modified alta-mud, aerosil or Natvosol.
10. aqueous printing ink mill base according to claim 1 and 2, is characterized in that: described UV light absorber is any one in salicylate class, benzophenone class, hindered amines, triazines or Benzotriazole Ultraviolet Stabilizer.