CN102732114B - Road marking paint - Google Patents

Road marking paint Download PDF

Info

Publication number
CN102732114B
CN102732114B CN 201210188044 CN201210188044A CN102732114B CN 102732114 B CN102732114 B CN 102732114B CN 201210188044 CN201210188044 CN 201210188044 CN 201210188044 A CN201210188044 A CN 201210188044A CN 102732114 B CN102732114 B CN 102732114B
Authority
CN
Grant status
Grant
Patent type
Prior art keywords
road
marking
paint
road marking
marking paint
Prior art date
Application number
CN 201210188044
Other languages
Chinese (zh)
Other versions
CN102732114A (en )
Inventor
章拥民
熊绍泊
Original Assignee
广州立邦涂料有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Grant date

Abstract

本发明公开了一种马路标线乳胶漆,其是由以下质量份的原料组成:30-70份的丙烯酸类乳液、0.5-5份的成膜助剂、0-15份的颜料、0-50份的填料、0.5-5份的助溶剂、0-3份的分散剂、0.1-1份的消泡剂、0-3份的增稠剂、0-1份的pH调节剂、0-1份的防霉剂、0-1份的防腐剂、10-25份的水。 The present invention discloses a road marking paint, which is composed of the following parts by mass of the raw material composition: 30 to 70 parts of acrylic emulsion, 0.5 to 5 parts coalescent, 0-15 parts of a pigment, 0 50 parts of a filler, 0.5-5 parts of a co-solvent, 0-3 parts of a dispersing agent, 0.1 parts of a defoaming agent, 0-3 parts thickener, 0-1 parts of a pH adjusting agent, 0- 1 parts of a fungicide, 0-1 parts of a preservative, 10 to 25 parts water. 本发明于提供的马路标线乳胶漆,能够很好的常温自干、无溶剂污染、固化迅速、耐磨性好、生产和施工成本低的特点,对安全环保、节能减排有卓越的贡献。 The present invention is to provide a road marking paint, can be a good dry at room temperature, solvent pollution, rapid curing, good wear resistance, low production cost and construction characteristics, outstanding contribution to the safety and environmental protection, energy conservation .

Description

一种马路标线乳胶漆 One kind of road marking paint

技术领域 FIELD

[0001] 本发明涉及一种马路标线乳胶漆。 [0001] The present invention relates to a road marking paint.

背景技术 Background technique

[0002] 当前的马路标示涂料主要有2种,加热型和溶融型,它们使用蒸发速快的酮类、酯类、脂肪族类、芳香族类溶剂等,由于溶剂的挥发而形成涂膜,从而存在安全隐患和大气污染等问题。 [0002] The current road marking paint there are two kinds of heat melting type and a type, which evaporator fast speed of ketones, esters, aliphatic, aromatic solvent or the like, since the volatilization of the solvent to form a coating film, thus a security risk and air pollution.

[0003] 水性马路标线乳胶漆,几乎不使用溶剂,响应了国家环保的要求,是非危险品,安全性高,无大气污染及贮存上的问题。 [0003] The aqueous road marking paint, virtually without using a solvent, in response to the state environmental requirements, non-hazardous, safe, no problems of air pollution and storage.

[0004] 然而,由于马路标线乳胶漆可能会经历气候、温度、阳光、雨雪等多重自然作用,因此,水性马路标线乳胶漆也必须具备良好的漆膜性能。 [0004] However, due to road marking paint may experience multiple role of natural climate, temperature, sunlight, rain, snow, etc. Therefore, water-based road marking paint must have good film properties.

发明内容 SUMMARY

[0005] 本发明的目的是提供一种马路标线乳胶漆。 [0005] The object of the present invention is to provide a road marking paint.

[0006] 本发明所采取的技术方案是: [0006] The technical solution by the present invention are:

[0007] -种马路标线乳胶漆,其是由以下质量份的原料组成:30_70份的丙烯酸类乳液、 〇. 5-5份的成膜助剂、0-15份的颜料、0-50份的填料、0. 5-5份的助溶剂、0-3份的分散剂、 〇. 1-1份的消泡剂、0-3份的增稠剂、0-1份的pH调节剂、0-1份的防霉剂、0-1份的防腐剂、 10-25份的水。 [0007] - Species road marking paint, which is composed of the following parts by mass of the raw material composition: 30_70 parts of acrylic emulsion, square coalescent 5-5 parts, 0-15 parts of a pigment, 0-50. parts of a filler, 0. 5-5 parts of the co-solvent, 0-3 parts of a dispersing agent, square. 1-1 parts of a defoaming agent, 0-3 parts thickener, 0-1 parts of a pH adjusting agent , 0-1 parts of a fungicide, 0-1 parts of a preservative, 10 to 25 parts water.

[0008]所述的成膜助剂包括Texanol酯醇、LusolvanFBH、Coasol、DBE_IB、DPNB、Dowanol pph〇 [0008] The film-forming aids include Texanol ester alcohol, LusolvanFBH, Coasol, DBE_IB, DPNB, Dowanol pph〇

[0009] 所述的颜料包括金红石型Ti02。 [0009] The pigments include rutile Ti02.

[0010] 所述的助溶剂包括1,2-丙二醇、乙醇。 [0010] The co-solvents include 1,2-propanediol, ethanol.

[0011] 所述填料包括碳酸钙、硅灰石、高岭土。 [0011] The fillers include calcium carbonate, wollastonite, kaolin.

[0012] 所述分散剂包括聚丙烯酰胺、聚羧酸盐。 [0012] The dispersing agents include polyacrylamides, polycarboxylates.

[0013] 所述消泡剂包括有机硅消泡剂、聚醚消泡剂。 [0013] The defoamers include silicone defoamers, polyether defoamers.

[0014] 所述增稠剂为纤维素醚及其衍生物与疏水改性的乙氧基聚氨酯水溶性聚合物的混合物。 [0014] The thickener is a cellulose ethers and their derivatives and hydrophobically modified ethoxylated polyurethane mixture of water soluble polymers.

[0015] 所述的pH调节剂包括2-氨基-2-甲基-1-丙醇、一乙醇胺、二乙醇胺、三乙醇胺、 羟乙基脲,四甲基氢氧化铵、氨水。 [0015] The pH adjusting agents include 2-amino-2-methyl-1-propanol, monoethanolamine, diethanolamine, triethanolamine, hydroxyethyl urea, tetramethylammonium hydroxide, aqueous ammonia.

[0016] 所述的防霉剂为苯并咪唑氨基甲酸甲酯、N' _(3,4_二氯苯基)-N,N-二甲基脲或其组合;所述的防腐剂包括1,2-苯并异噻唑-3-酮、甲基异噻唑啉酮、5-氯-2-甲基-4-异噻唑啉-3-酮。 [0016] the benzimidazole carbamate fungicide, N '_ (3,4_-dichlorophenyl) -N, N- dimethylurea or combinations thereof; said preservative comprises 1,2-benzisothiazol-3-one, methylisothiazolinone, 2-methyl-4-isothiazolin-3-one.

[0017]本发明的有益效果是:本发明提供的马路标线乳胶漆,能够很好的常温自干、无溶剂污染、固化迅速、耐磨性好、生产和施工成本低,对安全环保、节能减排有卓越的贡献。 [0017] Advantageous effects of the present invention are: road marking paint of the present invention provides, can be a good dry at room temperature, solvent pollution, rapid curing, good wear resistance, and low production cost construction, for safety and environmental protection, there are outstanding contributions to energy conservation.

具体实施方式 detailed description

[0018] 下面结合具体实施例对本发明做进一步的说明: [0018] Specific embodiments of the present invention in conjunction with the following further description:

[0019] 实施例1 : [0019] Example 1:

[0020] -种马路标线乳胶漆,其配方组成如下表: [0020] - Species road marking paint, which composition formula as follows:

Figure CN102732114BD00041

[0022] 实施例2 : [0022] Example 2:

[0023] -种马路标线乳胶漆,其配方组成如下表: [0023] - Species road marking paint, which composition formula as follows:

[0024] [0024]

Figure CN102732114BD00051

[0025] 实施例3 : [0025] Example 3:

[0026] -种马路标线乳胶漆,其配方组成如下表: [0026] - Species road marking paint, which composition formula as follows:

Figure CN102732114BD00052

[0028] 以实施例1的原料配方制备成品乳胶漆为例,说明本发明的乳胶漆的制备方法: 先将30质量份FASTRACK 3427乳液置于分散罐内,转速控制在500-700转/分钟;将0. 4 质量份聚羧酸铵盐分散剂5027、0. 4质量份有机硅消泡剂BYK-141依次加入配料罐,搅拌均匀后;再加入1. 5质量份羟乙基纤维素,搅拌5分钟;将45质量份1000目重钙粉、12质量份金红石型Ti02按顺序加入,再加入0. 8质量份水,高速(转速控制在1300转/分钟)研磨l(T20min ;然后加入1质量份无水乙醇和1质量份醇酯十二,搅拌5分钟;然后依次加入〇. 1质量份N'-(3,4-二氯苯基)-N,N-二甲基脲和0. 1质量份1,2-苯并异噻唑-3-酮,搅拌3分钟;然后加入0. 3质量份有机硅消泡剂BYK-141,分散3分钟;然后再加入0. 2质量份25wt%氨水,分散5分钟;最后加入10质量份水,搅拌均匀后即制成成品。 [0028] In embodiments of the finished latex paint formulation Example 1 preparation of starting materials, illustrate the preparation of the latex of the present invention: 30 parts by mass FASTRACK 3427 first emulsion was placed in a dispersion tank, speed control 500-700 rev / min ;. the parts 0.4 parts by mass of ammonium polycarboxylate dispersant 5027,0 4 mass silicone defoamer BYK-141 were added a mixing tank, stirring evenly; adding 1.5 parts by mass of hydroxyethylcellulose, stirred for 5 minutes; and 45 parts by mass of heavy calcium entry 1000, 12 parts by mass of rutile Ti02 added sequentially, and then added 0.8 parts by mass of water, high speed (speed at 1300 rev / min) polishing l (T20min; was then added 1 parts by mass of anhydrous ethanol and 1 part by mass ester XII, stirred for 5 minutes; followed by addition of 1 billion parts by mass of N '- (3,4- dichlorophenyl) -N, N- dimethylurea and. 0.1 parts by mass of 1,2-benzisothiazol-3-one, stirred for 3 minutes; followed by addition of 0.3 parts by mass of a silicone defoamer BYK-141, dispersion for 3 min; then added 0.2 parts by mass 25wt% ammonia water, dispersed for 5 minutes; finally adding 10 mass parts of water, stir after finished products.

[0029] 本发明的乳胶漆的制备方法简单,为本领域公知技术。 [0029] Preparation of latex of the present invention is simple techniques known in the art.

[0030] 使用本发明的马路标线乳胶漆,其方法如下: [0030] Using the present invention, road marking paint, which method is as follows:

[0031] 首先在施工前要清扫地面,除净灰尘杂物、油污等杂质以免影响漆膜路面之间的附着力,将马路标线乳胶漆用水稀释至浓度为10-15VO1%,搅匀,直接在道路上涂刷一道, 30-40分钟后再涂刷第两道即可。 [0031] First, before the construction of the floor to be cleaned, dust and other debris net, oil and other impurities so as not to affect the adhesion between the film surface, the road marking paint is diluted with water to a concentration of 10-15VO1%, stir, brushing a straight on the road, 30-40 minutes before brushing Di two can be.

[0032] 对实施例1制备的乳胶漆进行性能测试(测试标准JT/T 280-2004),其结果如下表: [0032] Example 1 Preparation of paint performance testing (test standard JT / T 280-2004), which results in the following table:

[0033] [0033]

Figure CN102732114BD00071

Claims (1)

  1. 1. 一种马路标线乳胶漆,其特征在于:其是由以下质量份的原料组成:30份的FASTRACK 3427乳液、1份的醇酯十二、12份的金红石型Ti02、45份的1000目重钙粉、1份的无水乙醇、0. 4份的聚羧酸铵盐分散剂5027、0. 7份的有机硅消泡剂BYK-141U. 5份的羟乙基纤维素、〇. 2份的25wt%氨水、0. 1份的N' -(3, 4-二氯苯基)-N,N-二甲基脲、0. 1份的1,2-苯并异噻唑-3-酮、10. 8份的水。 A road marking paint, characterized in that: it is composed of the following parts by mass of the raw material composition: 30 parts of the emulsion FASTRACK 3427, 1 part of alcohol ester XII 12 parts of rutile Ti02,45 1000 parts head heavy calcium, 1 part of ethanol, 5027,0. 7 parts of 0.4 parts of ammonium salt of a polycarboxylic acid dispersant silicone defoamer BYK-141U. 5 parts of hydroxyethyl cellulose, square. 2 parts of a 25wt% aqueous ammonia, 01 parts of N '- (3, 4- dichlorophenyl) -N, N- dimethylurea, 01 parts of a 1,2-benzisothiazol-3. - ketone, 108 parts of water.
CN 201210188044 2012-06-08 2012-06-08 Road marking paint CN102732114B (en)