CN106830887A - It is placed in the manufacture craft of Nixing pottery heated under naked light - Google Patents
It is placed in the manufacture craft of Nixing pottery heated under naked light Download PDFInfo
- Publication number
- CN106830887A CN106830887A CN201710074168.0A CN201710074168A CN106830887A CN 106830887 A CN106830887 A CN 106830887A CN 201710074168 A CN201710074168 A CN 201710074168A CN 106830887 A CN106830887 A CN 106830887A
- Authority
- CN
- China
- Prior art keywords
- base substrate
- nixing pottery
- temperature
- blank
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of manufacture craft of the Nixing pottery for being placed in and being heated under naked light, including blank, blank forming, finishing base substrate, body drying, base substrate firing are prepared, the blank is made up of the raw material of following weight portion:6~4 parts of eastern mud, 4~6 parts of western mud, MnCl20.1~0.5 part;It is, by base substrate feeding kiln, in temperature-rise period, when temperature is warming up to 700 DEG C, 10~15MPa to be forced into base substrate that the base substrate is fired, and when temperature rises to 1100 DEG C, stops pressurized treatments.The Nixing pottery vessel that the present invention makes have excellent heat-resisting acute degeneration and preferable mechanical strength, and thermal coefficient of expansion can be down to 2 × 10‑6/ DEG C (Rt~800 DEG C) below, directly can use on various thermals source, prolonged without cracking, can meet QB/T2580 2002《Fine ceramics cooking device》Standard requirement.
Description
Technical field
The present invention relates to the manufacture craft of Nixing pottery, and in particular to a kind of making of the Nixing pottery for being placed in being heated under naked light
Technique.
Background technology
Qiezhou Nixing pottery and yixing purple sand pottery, Sichuan Rongchang County pottery and Yunnan Jian Shui potteries, and claim the big name of China four to make pottery.Nixing pottery
Manufacture craft include prepare blank, blank forming, finishing base substrate, body drying, base substrate decoration, base substrate fire and polishing grinding
Operation.Raw material used by Nixing pottery includes eastern mud and western mud, and eastern mud is the soil from the Jiang Yidong that admires for crossing Qiezhou urban district, is
Mild-clay, color is yellow-white, and containing micro quartz sand, plasticity is good, is easy to shaping, but refractoriness is quite low, individually fires and holds
It is yielding;Western mud is the soil of region to the west of river by the emperor himself, is a kind of iron-holder purple mudstone higher, and color is aubergine, superficial layer
There is a small amount of irony to contaminate, be hard paste, fire resistance is good, it is not easy to deform, but poor plasticity, it is difficult to separately formed, by east
Mud and western mud are matched with constant weight and mixed, and the series of process such as ground, dehydration is made plastic blank.The base of Nixing pottery
SiO in material2Content is up to 67.7%, Al2O3Content is 18.14%, a part of SiO2With Al2O3Reaction generation mullite, Mo Lai
The thermal coefficient of expansion of stone is higher;A part turns into Free quartz, and Free quartz can occur crystal transfer at high temperature, becomes from quartz
Into cristobalite, the coefficient of expansion of cristobalite is more much bigger than quartz, and quartz can produce larger volume swollen to cristobalite conversion
It is swollen, so as to cause the thermal coefficient of expansion of Nixing pottery vessel larger, typically 5 × 10-6/ DEG C more than.Therefore Nixing pottery vessel conduct
When being used under the conditions of naked light, heating temperature can reach 600 DEG C to cooking ware, still suffer from the change of frequent thermal fluctuation, very
Easily burst during boiling.Therefore, Nixing pottery vessel can only be used as ceramics ware for daily use, such as conventional cup, dish, tea
Kettle, vase, and cannot function as cooking ware and used under the conditions of naked light.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of manufacture craft of the Nixing pottery for being placed in and being heated under naked light,
The Nixing pottery vessel coefficient of expansion that the technique is made is low, can be used under the conditions of naked light as cooking ware and not ruptured.
The technical scheme that the present invention is provided is a kind of manufacture craft of the Nixing pottery for being placed in and being heated under naked light, including is prepared
Blank, blank forming, finishing base substrate, body drying, base substrate are fired, and the blank is made up of the raw material of following weight portion:Eastern mud 6
~4 parts, 4~6 parts of western mud, MnCl20.1~0.5 part;
It is during base substrate sent into kiln, in temperature-rise period, when temperature is warming up to 700 DEG C, to base that the base substrate is fired
Body is forced into 10~15MPa, and when temperature rises to 1100 DEG C, stops pressurized treatments.
Eastern mud and western mud main component are SiO2And Al2O3, during high-temperature firing, SiO2And Al2O3Aluminium silicon can be generated
Spinelle, when more than 1000 DEG C, aluminium silicon spinel can be further converted to mullite.Mullite crystal structure can be regarded as
The structural evolution of sillimanite, its structure cell is made up of 4 sillimanite structure cells, and each sillimanite structure cell is by 4 Al2O3·SiO2
Composition.Therefore, mullite structure cell is equivalent to 16Al2O3·SiO2's.Mullite belongs to orthorhombic system, and containing axle is parallel to, it contains
It is parallel to axle AlO6Octahedron, these AlO6The octahedra SiO by transverse direction4Tetrahedron is connected.The application is added in blank
MnCl2, in 700~1100 DEG C of baking temperature range, the SiO in blank2And Al2O3Activated by bivalent manganese, promote SiO2With
Al2O3Mullite is converted into, due to 10~15MPa of condition of high voltage, SiO4Tetrahedron can combine to form N and save ring by bridging oxygen key,
AlO6It is octahedra to be connected to form the crystal structure with big cavity structure with N section rings.When crystal is heated, particle thermal vibration is shaken
Width increases, and big cavity makes crystal not have obvious expansion, thus shows the less coefficient of expansion.
Preferably, the weight portion of each raw material of blank is:6 parts of eastern mud, 4 parts of western mud, MnCl20.1~0.5 part.
It is further preferred that the weight portion of each raw material of blank is:6 parts of eastern mud, 4 parts of western mud, MnCl20.3~0.5
Part.MnCl2Addition when being eastern mud and western mud gross weight 3~5%, activation effect is best.
It is, by base substrate feeding kiln, when being warming up to 1150~1200 DEG C, to stop heating that the base substrate is fired, and is gone out after cooling
Kiln, completes to fire;When temperature is warming up to 700 DEG C, 10~15MPa is forced into base substrate, when temperature rises to 1100 DEG C, stopped
Pressurized treatments.
Preferably, it is that dried base substrate is put into kiln that the base substrate is fired, to heat up per hour 20~30 DEG C
Programming rate rise to 250~350 DEG C, then rise to 700 DEG C with 80~100 DEG C of the programming rate of heating up per hour, then with every
The programming rate of 40~60 DEG C of hour intensification rises to 1150~1200 DEG C, stops heating, kiln discharge after cooling.
Compared with prior art, the Nixing pottery vessel that the present invention makes have excellent heat-resisting acute degeneration and preferably machinery
Intensity, thermal coefficient of expansion can be down to 2 × 10-6/ DEG C (Rt~800 DEG C) below, can directly be used on various thermals source, it is prolonged without
Cracking, can meet QB/T2580-2002《Fine ceramics cooking device》Standard requirement.
Specific embodiment
The present invention is further elaborated for specific examples below, but not as a limitation of the invention.
Embodiment 1
1) blank is prepared:By eastern mud 600kg, western mud 400kg, MnCl210kg is well mixed, ground, press filtration, vacuum
After pugging, old operation, blank is obtained;
2) blank forming:Base substrate is made outer bore=250mm, the jar base substrate of capacity=3000ml 100;
3) body drying:Base substrate is dried;
4) base substrate is fired:Dried base substrate is put into kiln, to heat up per hour, 20 DEG C of programming rate rises to 250
DEG C, then rise to 700 DEG C with 80 DEG C of the programming rate of heating up per hour, then rise to 40 DEG C of the programming rate of heating up per hour
1150 DEG C, stop heating, kiln discharge after cooling;In temperature-rise period, when temperature is warming up to 700 DEG C, base substrate is forced into
10MPa, when temperature rises to 1100 DEG C, stops pressurized treatments.
Nixing pottery finished product is filled one by one and be directly introduced to after water heating on gas burner and have no cracking, and carry out 400 DEG C one by one
Do not split once to 20 DEG C of heat exchanges.One of finished product detection is selected, thermal coefficient of expansion is 1.88 × 10-6/ DEG C (Rt~800
℃)。
Embodiment 2
1) blank is prepared:By eastern mud 600kg, western mud 400kg, MnCl230kg is well mixed, ground, press filtration, vacuum
After pugging, old operation, blank is obtained;
2) blank forming:Base substrate is made outer bore=250mm, the jar base substrate of capacity=3000ml 100;
3) body drying:Base substrate is dried;
4) base substrate is fired:Dried base substrate is put into kiln, to heat up per hour, 30 DEG C of programming rate rises to 350
DEG C, then rise to 700 DEG C with 100 DEG C of the programming rate of heating up per hour, then rise to 60 DEG C of the programming rate of heating up per hour
1200 DEG C, stop heating, kiln discharge after cooling;In temperature-rise period, when temperature is warming up to 700 DEG C, base substrate is forced into
15MPa, when temperature rises to 1100 DEG C, stops pressurized treatments.
Nixing pottery finished product is filled one by one and be directly introduced to after water heating on gas burner and have no cracking, and carry out 400 DEG C one by one
Do not split once to 20 DEG C of heat exchanges.One of finished product detection is selected, thermal coefficient of expansion is 1.82 × 10-6/ DEG C (Rt~800
℃)。
Embodiment 3
1) blank is prepared:By eastern mud 600kg, western mud 400kg, MnCl250kg is well mixed, ground, press filtration, vacuum
After pugging, old operation, blank is obtained;
2) blank forming:Base substrate is made outer bore=250mm, the jar base substrate of capacity=3000ml 100;
3) body drying:Base substrate is dried;
4) base substrate is fired:Dried base substrate is put into kiln, to heat up per hour, 25 DEG C of programming rate rises to 300
DEG C, then rise to 700 DEG C with 90 DEG C of the programming rate of heating up per hour, then rise to 50 DEG C of the programming rate of heating up per hour
1180 DEG C, stop heating, kiln discharge after cooling;In temperature-rise period, when temperature is warming up to 700 DEG C, base substrate is forced into
12MPa, when temperature rises to 1100 DEG C, stops pressurized treatments.
Nixing pottery finished product is filled one by one and be directly introduced to after water heating on gas burner and have no cracking, and carry out 400 DEG C one by one
Do not split once to 20 DEG C of heat exchanges.One of finished product detection is selected, thermal coefficient of expansion is 1.76 × 10-6/ DEG C (Rt~800
℃)。
Embodiment 4
1) blank is prepared:By eastern mud 400kg, western mud 600kg, MnCl210kg is well mixed, ground, press filtration, vacuum
After pugging, old operation, blank is obtained;
2) blank forming:Base substrate is made outer bore=250mm, the jar base substrate of capacity=3000ml 100;
3) body drying:Base substrate is dried;
4) base substrate is fired:Dried base substrate is put into kiln, to heat up per hour, 20 DEG C of programming rate rises to 350
DEG C, then rise to 700 DEG C with 80 DEG C of the programming rate of heating up per hour, then rise to 60 DEG C of the programming rate of heating up per hour
1150 DEG C, stop heating, kiln discharge after cooling;In temperature-rise period, when temperature is warming up to 700 DEG C, base substrate is forced into
15MPa, when temperature rises to 1100 DEG C, stops pressurized treatments.
Nixing pottery finished product is filled one by one and be directly introduced to after water heating on gas burner and have no cracking, and carry out 400 DEG C one by one
Do not split once to 20 DEG C of heat exchanges.One of finished product detection is selected, thermal coefficient of expansion is 1.89 × 10-6/ DEG C (Rt~800
℃)。
Embodiment 5
1) blank is prepared:By eastern mud 500kg, western mud 500kg, MnCl250kg is well mixed, ground, press filtration, vacuum
After pugging, old operation, blank is obtained;
2) blank forming:Base substrate is made outer bore=250mm, the jar base substrate of capacity=3000ml 100;
3) body drying:Base substrate is dried;
4) base substrate is fired:Dried base substrate is put into kiln, to heat up per hour, 30 DEG C of programming rate rises to 250
DEG C, then rise to 700 DEG C with 100 DEG C of the programming rate of heating up per hour, then rise to 40 DEG C of the programming rate of heating up per hour
1200 DEG C, stop heating, kiln discharge after cooling;In temperature-rise period, when temperature is warming up to 700 DEG C, base substrate is forced into
10MPa, when temperature rises to 1100 DEG C, stops pressurized treatments.
Nixing pottery finished product is filled one by one and be directly introduced to after water heating on gas burner and have no cracking, and carry out 400 DEG C one by one
Do not split once to 20 DEG C of heat exchanges.One of finished product detection is selected, thermal coefficient of expansion is 1.90 × 10-6/ DEG C (Rt~800
℃)。
Claims (5)
1. the manufacture craft of Nixing pottery heated under naked light is placed in, including prepares blank, blank forming, finishing base substrate, base substrate
Dry, base substrate is fired, it is characterised in that:
The blank is made up of the raw material of following weight portion:6~4 parts of eastern mud, 4~6 parts of western mud, MnCl20.1~0.5 part;
The base substrate is fired and is during base substrate sent into kiln, in temperature-rise period, when temperature is warming up to 700 DEG C, to base substrate plus
10~15MPa is depressed into, and when temperature rises to 1100 DEG C, stops pressurized treatments.
2. the manufacture craft of the Nixing pottery for being placed in heating under naked light according to claim 1, it is characterised in that:The base
The weight portion for expecting each raw material is:6 parts of eastern mud, 4 parts of western mud, MnCl20.1~0.5 part.
3. the manufacture craft of the Nixing pottery for being placed in heating under naked light according to claim 1, it is characterised in that:The base
The weight portion for expecting each raw material is:6 parts of eastern mud, 4 parts of western mud, MnCl20.3~0.5 part.
4. the manufacture craft of the Nixing pottery for being placed in heating under naked light according to claim 1, it is characterised in that:The base
It is, by base substrate feeding kiln, when being warming up to 1150~1200 DEG C, to stop heating that body is fired, and kiln discharge after cooling completes to fire;When
When temperature is warming up to 700 DEG C, 10~15MPa is forced into base substrate, when temperature rises to 1100 DEG C, stops pressurized treatments.
5. the manufacture craft of the Nixing pottery for being placed in heating under naked light according to claim 1, it is characterised in that:The base
It is that dried base substrate is put into kiln that body is fired, and to heat up per hour, 20~30 DEG C of programming rate rises to 250~350
DEG C, then rise to 700 DEG C with 80~100 DEG C of the programming rate of heating up per hour, then with 40~60 DEG C of the intensification of heating up per hour
Speed rises to 1150~1200 DEG C, stops heating, kiln discharge after cooling.