CN106826108A - A kind of preparation method of high temp.-resistant valve connector - Google Patents

A kind of preparation method of high temp.-resistant valve connector Download PDF

Info

Publication number
CN106826108A
CN106826108A CN201611213312.6A CN201611213312A CN106826108A CN 106826108 A CN106826108 A CN 106826108A CN 201611213312 A CN201611213312 A CN 201611213312A CN 106826108 A CN106826108 A CN 106826108A
Authority
CN
China
Prior art keywords
valve
valve connections
weight portion
blank
resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611213312.6A
Other languages
Chinese (zh)
Inventor
朱建惠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU HUIYI MECHANICAL AND ELECTRICAL Co Ltd
Original Assignee
CHANGSHU HUIYI MECHANICAL AND ELECTRICAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU HUIYI MECHANICAL AND ELECTRICAL Co Ltd filed Critical CHANGSHU HUIYI MECHANICAL AND ELECTRICAL Co Ltd
Priority to CN201611213312.6A priority Critical patent/CN106826108A/en
Priority to PCT/CN2016/112287 priority patent/WO2018119629A1/en
Publication of CN106826108A publication Critical patent/CN106826108A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of preparation method of high temp.-resistant valve connector, it is characterised in that comprise the following steps：1）Selection, the selection trade mark is the hard alloy wolfram steel of YL10 series as the turned blank of valve connections；2）Blank process, the blank to choosing carry out peripheral milling, drilling, inner circle grind, mill out internal thread, obtain rough valve connections；3）Rough valve connections surface be ground, polished, be cleaned by ultrasonic, dried, obtaining valve connections；4）High-temperaure coating is sprayed into valve connections surface, high temp.-resistant valve connector is obtained.The valve connections that a kind of preparation method of high temp.-resistant valve connector of the present invention is manufactured have preferable high temperature resistant property, can be very good to adapt to the use under hot conditions.

Description

A kind of preparation method of high temp.-resistant valve connector
Technical field
The present invention relates to a kind of preparation method of high temp.-resistant valve connector.
Background technology
Valve connections can be applied in some hot environments often, for the valve connections processed without high temperature resistant It is susceptible to damage under the influence of hot conditions are subject to for a long time.
The content of the invention
It is an object of the invention to provide a kind of preparation method of high temp.-resistant valve connector, it is intended to solve the above problems.
To achieve these goals, the technical scheme is that designing a kind of preparation side of high temp.-resistant valve connector Method, comprises the following steps：
1）Selection, the selection trade mark is the hard alloy wolfram steel of YL10 series as the turned blank of valve connections；
2）Blank is processed, and the blank to choosing carries out peripheral milling, drilling, inner circle mill, mills out internal thread, obtains rough valve and connect Part；
3）Rough valve connections surface be ground, polished, be cleaned by ultrasonic, dried, obtaining valve connections；
4）High-temperaure coating is sprayed into valve connections surface；High-temperaure coating is formulated：The weight of thermoplastic phenolic resin 150 ~ 200 Amount part, the weight portion of zirconium oxide 30 ~ 50, the weight portion of gallium oxide 3 ~ 5, the weight portion of silica 3 ~ 5, the weight portion of cobalt oxide 3 ~ 5, methyl alcohol 70 ~ 90 weight portions, the weight portion of silane coupler 30 ~ 50；Spraying method：By above-mentioned high-temperaure coating be configured to viscosity 1cP ~ 10cP it Between, then it is sprayed on valve connections surface, high temperature prebake conditions 1min, 50 ~ 90 DEG C of temperature, low temperature prebake conditions 5min, temperature 30 ~ 50 DEG C, high temperature drying 15min, 100 ~ 200 DEG C of temperature obtains high temp.-resistant valve connector.
Preferably, the hard alloy wolfram steel trade mark is YL10.1.
The advantages of the present invention are：A kind of preparation method of high temp.-resistant valve connector of the present invention is produced The valve connections for coming have preferable high temperature resistant property, can be very good to adapt to the use under hot conditions.
With reference to embodiment, specific embodiment of the invention is further described.Following examples are only used for more Plus technical scheme is clearly demonstrated, and can not be limited the scope of the invention with this.
Embodiment 1：
A kind of preparation method of high temp.-resistant valve connector, comprises the following steps：
1）Selection, the selection trade mark is the hard alloy wolfram steel of YL10.1 as the turned blank of valve connections；
2）Blank is processed, and the blank to choosing carries out peripheral milling, drilling, inner circle mill, mills out internal thread, obtains rough valve and connect Part；
3）Rough valve connections surface be ground, polished, be cleaned by ultrasonic, dried, obtaining valve connections；
4）High-temperaure coating is sprayed into valve connections surface；High-temperaure coating is formulated：The weight of thermoplastic phenolic resin 150 Part, the weight portion of zirconium oxide 30, the weight portion of gallium oxide 3, the weight portion of silica 3, the weight portion of cobalt oxide 3, the weight portion of methyl alcohol 70, silane The weight portion of coupling agent 30；Spraying method：Above-mentioned high-temperaure coating is configured between viscosity 1cPcP, valve company is then sprayed on Fitting surface, high temperature prebake conditions 1min, temperature 70 C, low temperature prebake conditions 5min, 30 DEG C of temperature, high temperature drying 15min, temperature 100 DEG C, obtain high temp.-resistant valve connector.
Embodiment 2：
A kind of preparation method of high temp.-resistant valve connector, comprises the following steps：
1）Selection, the selection trade mark is the hard alloy wolfram steel of YL10.1 as the turned blank of valve connections；
2）Blank is processed, and the blank to choosing carries out peripheral milling, drilling, inner circle mill, mills out internal thread, obtains rough valve and connect Part；
3）Rough valve connections surface be ground, polished, be cleaned by ultrasonic, dried, obtaining valve connections；
4）High-temperaure coating is sprayed into valve connections surface；High-temperaure coating is formulated：The weight portion of thermoplastic phenolic resin 00, The weight portion of zirconium oxide 50, the weight portion of gallium oxide 5, the weight portion of silica 5, the weight portion of cobalt oxide 5, the weight portion of methyl alcohol 90, silane idol The connection weight portion of agent 50；Spraying method：Above-mentioned high-temperaure coating is configured between viscosity 7cP, valve connections are then sprayed on Surface, high temperature prebake conditions 1min, 80 DEG C of temperature, low temperature prebake conditions 5min, temperature 50 C, high temperature drying 15min, 150 DEG C of temperature, Obtain high temp.-resistant valve connector.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art For member, on the premise of the technology of the present invention principle is not departed from, some improvements and modifications can also be made, these improvements and modifications Also should be regarded as protection scope of the present invention.

Claims (2)

1. a kind of preparation method of high temp.-resistant valve connector, it is characterised in that comprise the following steps：
1）Selection, the selection trade mark is the hard alloy wolfram steel of YL10 series as the turned blank of valve connections；
2）Blank is processed, and the blank to choosing carries out peripheral milling, drilling, inner circle mill, mills out internal thread, obtains rough valve and connect Part；
3）Rough valve connections surface be ground, polished, be cleaned by ultrasonic, dried, obtaining valve connections；
4）High-temperaure coating is sprayed into valve connections surface；High-temperaure coating is formulated：The weight of thermoplastic phenolic resin 150 ~ 200 Amount part, the weight portion of zirconium oxide 30 ~ 50, the weight portion of gallium oxide 3 ~ 5, the weight portion of silica 3 ~ 5, the weight portion of cobalt oxide 3 ~ 5, methyl alcohol 70 ~ 90 weight portions, the weight portion of silane coupler 30 ~ 50；Spraying method：By above-mentioned high-temperaure coating be configured to viscosity 1cP ~ 10cP it Between, then it is sprayed on valve connections surface, high temperature prebake conditions 1min, 50 ~ 90 DEG C of temperature, low temperature prebake conditions 5min, temperature 30 ~ 50 DEG C, high temperature drying 15min, 100 ~ 200 DEG C of temperature obtains high temp.-resistant valve connector.
2. the preparation method of a kind of high temp.-resistant valve connector according to claim 1, it is characterised in that：The hard is closed The golden wolfram steel trade mark is YL10.1.
CN201611213312.6A 2016-12-26 2016-12-26 A kind of preparation method of high temp.-resistant valve connector Pending CN106826108A (en)