CN109370376A - Water-based high-temperature resistant anticorrosive coating and preparation method thereof - Google Patents
Water-based high-temperature resistant anticorrosive coating and preparation method thereof Download PDFInfo
- Publication number
- CN109370376A CN109370376A CN201811202184.4A CN201811202184A CN109370376A CN 109370376 A CN109370376 A CN 109370376A CN 201811202184 A CN201811202184 A CN 201811202184A CN 109370376 A CN109370376 A CN 109370376A
- Authority
- CN
- China
- Prior art keywords
- water
- agent
- based high
- temperature resistant
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water-based high-temperature resistant anticorrosive coatings and preparation method thereof, ingredient is as follows by mass percentage in water-based high-temperature resistant anticorrosive coating: fire resistant resin 35~55%, ionized water 12~13%, cellulose ether 1~2%, sodium hexametaphosphate dispersant 0.4~0.6%, wetting agent 0.2~0.4%, defoaming agent 0.1~0.3%, levelling agent 0.2~0.5%, anti- flash rusting agent 0.5~0.7%, silane coupling agent 1~5%, trbasic zinc phosphate 1~8%, zirconium dioxide 10~15%, silica 1 0~15%, rutile titanium white powder 10~15%, iron oxide red 5~7%, surplus is water, wherein fire resistant resin is epoxy resin.The present invention passes through the anticorrosive paint with fire resistant resin for basic solvent generation, hard layer can be formed in coating surface after coating consolidation, improve the wearability of coating, preparation method of the present invention is simple, it is handled by ultrasonic wave and dispersing agent, it can effectively make each component in coating be uniformly dispersed, improve fine and smooth degree when coating application, enhance the stability of coating.
Description
Technical field
The invention belongs to technical field of coatings, more specifically more particularly to a kind of water-based high-temperature resistant anticorrosive coating and its
Preparation method.
Background technique
Loss brought by corrosion, especially corrosion of metal is extremely serious.Industrially developed country is every year since corrosion is made
At loss account for 4% or so of its total value of production in national economy.It is wide now with the preservative treatment that anticorrosive paint carries out metallic facility
The method of general application.
Such as application No. is the patents of CN201510770866.5, and it discloses a kind of nano-attapulgite stone composite water soluble epoxies
Anticorrosive paint and preparation method thereof, to solve existing anticorrosive paint, there are coatings with for a long time by the influence of factor of natural environment
It is easy to appear field cracking, is blistered, is peeled off, phenomena such as getting rusty, the problem that causes the antiseptic property of anticorrosive paint bad.The coating by
Component A and B component composition, wherein component A is prepared by following ingredients by following mass parts: liquid-state epoxy resin 85-95
Part, 5-15 parts of epoxy active diluent;B component is prepared by following ingredients by following mass parts: aqueous epoxy resins solidification
25-35 parts of agent, 0.5-1.5 parts of dispersing agent, 0.2-0.5 part of levelling agent, 0.5-1.5 parts of scratching resistant, 4-6 parts of trbasic zinc phosphate,
4-6 parts of pigment, 3-6 parts of talcum powder, 5-10 parts of barium sulfate, 10-20 parts of attapulgite, 0.3-0.5 part of defoaming agent, water
25-35 parts.Prepared coating has preferable workability, can be used in a humidity environment, belongs to low VOC product,
Meet environmental protection concept.
But above scheme has following deficiency: coating can not be formed wear-resisting after body surface is dry in coating surface
Hard layer, in equipment use process, coating be easy is scratched and generates destructions so that coating locally lose protection work
With.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of aqueous high-temperature-resistant anti-corrosion proposed
Coating and preparation method thereof.
To achieve the above object, the invention provides the following technical scheme:
A kind of water-based high-temperature resistant anticorrosive coating, the water-based high-temperature resistant anticorrosive coating, ingredient are as follows by mass percentage:
Fire resistant resin 35~55%
Ionized water 12~13%
Cellulose ether 1~2%
Sodium hexametaphosphate dispersant 0.4~0.6%
Wetting agent 0.2~0.4%
Defoaming agent 0.1~0.3%
Levelling agent 0.2~0.5%
Anti- flash rusting agent 0.5~0.7%
Silane coupling agent 1~5%
Trbasic zinc phosphate 1~8%
Zirconium dioxide 10~15%
Silica 1 0~15%
Rutile titanium white powder 10~15%
Iron oxide red 5~7%
Surplus is water, and wherein fire resistant resin is epoxy resin.
Preferably, the wetting agent is ethyl alcohol, propylene glycol, glycerol, any one in dimethyl sulfoxide.
Preferably, the defoaming agent is silicone emulsion, the fatty acid ester compounded object of higher alcohols, polyoxyethylene polyoxypropylene season penta
Any one in four alcohol ethers.
Preferably, the levelling agent is polyacrylic acid, any one in carboxymethyl cellulose.
Preferably, the anti-flash rusting agent is benzotriazole, sodium phytate, any one in strontium chromate.
A kind of preparation method of water-based high-temperature resistant anticorrosive coating, the preparation method of the water-based high-temperature resistant anticorrosive coating is such as
Under:
S1: fire resistant resin, zirconium dioxide, silica, rutile titanium white powder, wetting agent, silane coupling agent are sequentially added
It is heated to 55-63 DEG C into blend tank, and by blend tank, is constantly mixed, while ionized water is added and is diluted, is stirred
Basestocks are obtained after mixing uniformly, it is spare;
S2: cellulose ether, sodium hexametaphosphate dispersant, defoaming agent, levelling agent are added in basestocks, are mixed evenly, later
It is mixed by ultrasonic mixer, the ultrasonic frequency of ultrasonic mixer is 10-15MHz, and mixing duration 10-20 divides
Clock obtains mixed liquor after mixing, spare;
S3: anti-flash rusting agent, trbasic zinc phosphate, iron oxide red and water are added separately in the mixed liquor in S2, are stirring evenly and then adding into
Decentralized processing is carried out in dispersion machine, is dispersed duration 1-3 hours.
Technical effect and advantage of the invention:
The present invention is by being that the anticorrosive paint that basic solvent generates utilizes titanium dioxide with high temperature resistance with fire resistant resin
Silicon can form hard layer in coating surface after coating consolidation, improve the wearability of coating, preparation method letter of the present invention
It is single, it passes sequentially through ultrasonic wave and dispersing agent is handled, can effectively make each component in coating be uniformly dispersed, improve coating and apply
Fine and smooth degree when brush, enhances the stability of coating.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.Based on the embodiments of the present invention, those of ordinary skill in the art are not before making creative work
Every other embodiment obtained is put, shall fall within the protection scope of the present invention.
Embodiment 1
A kind of water-based high-temperature resistant anticorrosive coating, the water-based high-temperature resistant anticorrosive coating, ingredient are as follows by mass percentage:
Fire resistant resin 35%
Ionized water 12%
Cellulose ether 1%
Sodium hexametaphosphate dispersant 0.4%
Wetting agent 0.2%
Defoaming agent 0.1%
Levelling agent 0.2%
Anti- flash rusting agent 0.5%
Silane coupling agent 1%
Trbasic zinc phosphate 1%
Zirconium dioxide 10%
Silica 1 0%
Rutile titanium white powder 10%
Iron oxide red 5%
Surplus is water, and wherein fire resistant resin is epoxy resin.
The wetting agent is ethyl alcohol.
The defoaming agent is silicone emulsion.
The levelling agent is polyacrylic acid.
The anti-flash rusting agent is benzotriazole.
A kind of preparation method of water-based high-temperature resistant anticorrosive coating, the preparation method of the water-based high-temperature resistant anticorrosive coating is such as
Under:
S1: fire resistant resin, zirconium dioxide, silica, rutile titanium white powder, wetting agent, silane coupling agent are sequentially added
55 DEG C are heated into blend tank, and by blend tank, is constantly mixed, while ionized water is added and is diluted, is stirred
Basestocks are obtained after uniformly, it is spare;
S2: cellulose ether, sodium hexametaphosphate dispersant, defoaming agent, levelling agent are added in basestocks, are mixed evenly, later
It is mixed by ultrasonic mixer, the ultrasonic frequency of ultrasonic mixer is 10MHz, is mixed duration 10 minutes, mixing
After mixed liquor, it is spare;
S3: anti-flash rusting agent, trbasic zinc phosphate, iron oxide red and water are added separately in the mixed liquor in S2, are stirring evenly and then adding into
Decentralized processing is carried out in dispersion machine, is dispersed duration 1 hour.
Embodiment 2
A kind of water-based high-temperature resistant anticorrosive coating, the water-based high-temperature resistant anticorrosive coating, ingredient are as follows by mass percentage:
Fire resistant resin 40%
Ionized water 12%
Cellulose ether 1.5%
Sodium hexametaphosphate dispersant 0.5%
Wetting agent 0.3%
Defoaming agent 0.2%
Levelling agent 0.3%
Anti- flash rusting agent 0.6%
Silane coupling agent 3%
Trbasic zinc phosphate 4%
Zirconium dioxide 10%
Silica 1 0%
Rutile titanium white powder 10%
Iron oxide red 5%
Surplus is water, and wherein fire resistant resin is epoxy resin.
The wetting agent is propylene glycol.
The defoaming agent is the fatty acid ester compounded object of higher alcohols.
The levelling agent is carboxymethyl cellulose.
The anti-flash rusting agent is sodium phytate.
A kind of preparation method of water-based high-temperature resistant anticorrosive coating, the preparation method of the water-based high-temperature resistant anticorrosive coating is such as
Under:
S1: fire resistant resin, zirconium dioxide, silica, rutile titanium white powder, wetting agent, silane coupling agent are sequentially added
60 DEG C are heated into blend tank, and by blend tank, is constantly mixed, while ionized water is added and is diluted, is stirred
Basestocks are obtained after uniformly, it is spare;
S2: cellulose ether, sodium hexametaphosphate dispersant, defoaming agent, levelling agent are added in basestocks, are mixed evenly, later
It is mixed by ultrasonic mixer, the ultrasonic frequency of ultrasonic mixer is 12MHz, is mixed duration 15 minutes, mixing
After mixed liquor, it is spare;
S3: anti-flash rusting agent, trbasic zinc phosphate, iron oxide red and water are added separately in the mixed liquor in S2, are stirring evenly and then adding into
Decentralized processing is carried out in dispersion machine, is dispersed duration 2 hours.
Embodiment 3
A kind of water-based high-temperature resistant anticorrosive coating, the water-based high-temperature resistant anticorrosive coating, ingredient are as follows by mass percentage:
Fire resistant resin 38%
Ionized water 13%
Cellulose ether 2%
Sodium hexametaphosphate dispersant 0.6%
Wetting agent 0.4%
Defoaming agent 0.3%
Levelling agent 0.5%
Anti- flash rusting agent 0.7%
Silane coupling agent 2%
Trbasic zinc phosphate 2%
Zirconium dioxide 11%
Silica 1 2%
Rutile titanium white powder 11%
Iron oxide red 6%
Surplus is water, and wherein fire resistant resin is epoxy resin.
The wetting agent is dimethyl sulfoxide.
The defoaming agent is polyoxyethylene polyoxypropylene pentaerythrite ether.
The levelling agent is carboxymethyl cellulose.
The anti-flash rusting agent is strontium chromate.
A kind of preparation method of water-based high-temperature resistant anticorrosive coating, the preparation method of the water-based high-temperature resistant anticorrosive coating is such as
Under:
S1: fire resistant resin, zirconium dioxide, silica, rutile titanium white powder, wetting agent, silane coupling agent are sequentially added
63 DEG C are heated into blend tank, and by blend tank, is constantly mixed, while ionized water is added and is diluted, is stirred
Basestocks are obtained after uniformly, it is spare;
S2: cellulose ether, sodium hexametaphosphate dispersant, defoaming agent, levelling agent are added in basestocks, are mixed evenly, later
It is mixed by ultrasonic mixer, the ultrasonic frequency of ultrasonic mixer is 15MHz, is mixed duration 20 minutes, mixing
After mixed liquor, it is spare;
S3: anti-flash rusting agent, trbasic zinc phosphate, iron oxide red and water are added separately in the mixed liquor in S2, are stirring evenly and then adding into
Decentralized processing is carried out in dispersion machine, is dispersed duration 3 hours.
The present invention is by being that the anticorrosive paint that basic solvent generates utilizes two with high temperature resistance with fire resistant resin
Silica can form hard layer in coating surface after coating consolidation, improve the wearability of coating, preparation method of the present invention
Simply, it passes sequentially through ultrasonic wave and dispersing agent is handled, can effectively make each component in coating be uniformly dispersed, improve coating
Fine and smooth degree when brushing, enhances the stability of coating.
Finally, it should be noted that the foregoing is only a preferred embodiment of the present invention, it is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features,
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention
Within protection scope.
Claims (6)
1. a kind of water-based high-temperature resistant anticorrosive coating, it is characterised in that: the water-based high-temperature resistant anticorrosive coating, ingredient press quality percentage
It is as follows than counting:
Fire resistant resin 35~55%
Ionized water 12~13%
Cellulose ether 1~2%
Sodium hexametaphosphate dispersant 0.4~0.6%
Wetting agent 0.2~0.4%
Defoaming agent 0.1~0.3%
Levelling agent 0.2~0.5%
Anti- flash rusting agent 0.5~0.7%
Silane coupling agent 1~5%
Trbasic zinc phosphate 1~8%
Zirconium dioxide 10~15%
Silica 1 0~15%
Rutile titanium white powder 10~15%
Iron oxide red 5~7%
Surplus is water, and wherein fire resistant resin is epoxy resin.
2. a kind of water-based high-temperature resistant anticorrosive coating according to claim 1, it is characterised in that: the wetting agent be ethyl alcohol,
Propylene glycol, glycerol, any one in dimethyl sulfoxide.
3. a kind of water-based high-temperature resistant anticorrosive coating according to claim 1, it is characterised in that: the defoaming agent is emulsification silicon
Any one in oil, the fatty acid ester compounded object of higher alcohols, polyoxyethylene polyoxypropylene pentaerythrite ether.
4. a kind of water-based high-temperature resistant anticorrosive coating according to claim 1, it is characterised in that: the levelling agent is polypropylene
Any one in acid, carboxymethyl cellulose.
5. a kind of water-based high-temperature resistant anticorrosive coating according to claim 1, it is characterised in that: the anti-flash rusting agent is benzene a pair of horses going side by side
Triazole, sodium phytate, any one in strontium chromate.
6. a kind of preparation method of water-based high-temperature resistant anticorrosive coating described in -5 any one according to claim 1, feature exist
In: the water-based high-temperature resistant anticorrosive coating the preparation method is as follows:
S1: fire resistant resin, zirconium dioxide, silica, rutile titanium white powder, wetting agent, silane coupling agent are sequentially added
It is heated to 55-63 DEG C into blend tank, and by blend tank, is constantly mixed, while ionized water is added and is diluted, is stirred
Basestocks are obtained after mixing uniformly, it is spare;
S2: cellulose ether, sodium hexametaphosphate dispersant, defoaming agent, levelling agent are added in basestocks, are mixed evenly, later
It is mixed by ultrasonic mixer, the ultrasonic frequency of ultrasonic mixer is 10-15MHz, and mixing duration 10-20 divides
Clock obtains mixed liquor after mixing, spare;
S3: anti-flash rusting agent, trbasic zinc phosphate, iron oxide red and water are added separately in the mixed liquor in S2, are stirring evenly and then adding into
Decentralized processing is carried out in dispersion machine, is dispersed duration 1-3 hours.