CN108192443A - A kind of power equipment antirust paint - Google Patents
A kind of power equipment antirust paint Download PDFInfo
- Publication number
- CN108192443A CN108192443A CN201810066184.XA CN201810066184A CN108192443A CN 108192443 A CN108192443 A CN 108192443A CN 201810066184 A CN201810066184 A CN 201810066184A CN 108192443 A CN108192443 A CN 108192443A
- Authority
- CN
- China
- Prior art keywords
- parts
- antirust paint
- power equipment
- water
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to material of paint technical fields, and in particular to a kind of power equipment antirust paint.The antirust paint includes following component：Water-base resin, modified soluble Ludox, zinc oxide, talcum powder, sericite part, trbasic zinc phosphate, barium sulfate, thickener, levelling agent, pigment, antifoaming agent, deionized water.Wherein water-base resin is aqueous anionic acrylic resin lotion；Water silica sol is modified by adding nano-carbon powder and iron oxide by the way of Hybrid Heating.It after antirust paint each group lease making mixing dispersion, also needs to be ground refinement so that paint vehicle more uniform and smooth, generation protective layer is more stable and fine and close after spraying, improves the barrier propterty of paint vehicle.The antirust paint has the advantages of anti-oxidant, corrosion resistance is outstanding, nontoxic, and production cost is relatively low.
Description
Technical field
The invention belongs to material of paint technical fields, and in particular to a kind of power equipment antirust paint.
Background technology
Antirust paint is a kind of painting for the chemistry or electrochemical corrosion for protecting metal surfaces from air, seawater, salt fog etc.
Material；Main component is rust resisting pigment and film forming matter.Antirust paint currently on the market is broadly divided into two kinds of oil paint and water paint,
Wherein, oil paint has the advantages that cheap, easy to use, but the greasy easy attachment dirt in oil paint surface, cleans
It is next cumbersome, and the body of paint spraying operating personnel is good for containing noxious materials such as nitrite, chromate in ingredient
Health harm is larger, has been rarely employed at present.
Water paint has the advantages that Environmental Safety is healthy, and with the progress of material science and technology, the film forming of aqueous antirust paint
Effect, anticorrosion, anti-aging property are very outstanding, but the adhesive force of aqueous antirust paint, membranous layer stability etc. are comprehensive
Can be still to be improved, and the production cost of aqueous antirust paint is generally higher.
Invention content
In view of the above problems, the purpose of the present invention is to provide a kind of power equipment antirust paint, the antirust paint film layer is attached
Put forth effort that strong, stability is high, it is corrosion-resistant, anti-aging property is good, and production cost is relatively low.
A kind of power equipment antirust paint, it is characterised in that：According to mass fraction, the antirust paint contains following component：
30-45 parts of water-base resin, 7-12 parts of modified soluble Ludox, 10-15 parts of zinc oxide, 10-16 parts of talcum powder, sericite part 8-
10 parts, 5-8 parts of trbasic zinc phosphate, 5-7 parts of barium sulfate, 3-6 parts of thickener, 2-3 parts of levelling agent, 15-25 parts of pigment；Antifoaming agent 0.3-
0.5 part, 15-20 parts of deionized water.
Preferably, according to mass fraction, the antirust paint contains following component：35-40 parts of water-base resin, modified soluble
8-10 parts of Ludox, 12-13 parts of zinc oxide, 12-15 parts of talcum powder, 8-9 parts of sericite part, 6-7 parts of trbasic zinc phosphate, barium sulfate 5-6
Part, 4-5 parts of thickener, 2.5-3 parts of levelling agent, 20-22 parts of pigment；0.4-0.5 parts of antifoaming agent, 17-18 parts of deionized water.
Wherein, the preparation method of the modified soluble Ludox is：It is 6- that mass fraction is added in hydrotropism's Ludox
8% nano-carbon powder and the iron oxide of 4-6%, then heat the mixture to 45-50 DEG C, stir evenly postcooling to room temperature i.e.
It can.
Preferably, the water-base resin is aqueous anionic acrylic resin lotion；Using the resin emulsion as bonding
The progress of pigment, filler and various auxiliary agents can effectively be bonded, improves the compatibility of each paint components by agent.
Preferably, the thickener is polyacrylic acid and the mixture of silica；Antifoaming agent is polyether-modified poly- silica
Alkane；Thickener and antifoaming agent are used to improve the property of antirust paint, by the gas dissolution rate in its paint vehicle, improve the stability of enamelled coating
And compactness extent.
Wherein, the pigment selects one kind in titanium dioxide, aluminium triphosphate, carbon black, iron oxide red, the mesh number of pigment
Higher than 800 mesh；The zinc oxide, talcum powder, sericite part, trbasic zinc phosphate and barium sulfate mesh number be 300-500 mesh；It is thin using this
The filler of degree grade can allow paint vehicle evenly, also allow for the later stage to paint vehicle progress further grinding and refinement.
Antirust paint provided by the invention, preparation method are：By water-base resin, modified silicasol, zinc oxide, talcum powder,
Sericite part, trbasic zinc phosphate, barium sulfate and antifoaming agent are uniformly mixed in batching kettle, then feed the mixture into high-speed dispersing kettle
In be stirred and disperse, thickener, levelling agent, pigment are put into before dispersion, and disperseed will gradually to go simultaneously from
Sub- water is added in high-speed dispersing kettle；The rotating speed of Scattered Kettle is 2800-3000r/min, and jitter time 40-50min has disperseed
Slurry is sent to progress wet type sand milling in sand mill, the fineness of slurry is ground to 15-20 μm, you can needed for obtaining by Cheng Hou
Antirust paint.
A kind of power equipment antirust paint provided by the invention, compared with prior art, has the following advantages：
The antirust paint is water paint, and by organic binder, filler, the components such as auxiliary agent and pigment are formed, and each component is pair
The nontoxic green material of human body；Therefore the antirust paint product also has the characteristics that green, safe, to antirust paint spraying application
The health of personnel will not damage, and the administrative staff of the equipment using the antirust paint will not be damaged.
The antirust paint degree of protection is high, and coating property is uniform, adhesive force is good, and film layer is fine and smooth and fine and close；With good anti-
Rust, corrosion-resistant, antioxygenic property, and the ageing-resistant performance of paint vehicle is also preferable, it is ensured that and coating is anti-in longer life
Protect effect.
In addition, the filler and other components of the antirust paint while ensureing paint vehicle performance, are produced into after preferably
This more conventional aqueous antirust paint is also reduced.
Specific embodiment
The specific embodiment of the present invention is described in detail below.It should be understood that specific implementation described herein
Mode is merely to illustrate and explain the present invention, and is not intended to restrict the invention.
Embodiment 1
The nano-carbon powder and 4% iron oxide that mass fraction is 6% are added in hydrotropism's Ludox, then heats the mixture to 45
DEG C, it stirs evenly postcooling to room temperature and obtains modified soluble Ludox.
According to mass fraction, prepare following raw material：30 parts of water-base resin, 7 parts of modified soluble Ludox, zinc oxide 10
Part, 10 parts of talcum powder, 8 parts of sericite part, 5 parts of trbasic zinc phosphate, 5 parts of barium sulfate, 3 parts of thickener, 2 parts of levelling agent, 15 parts of pigment；Disappear
0.3 part of infusion, 15 parts of deionized water.
Wherein, water-base resin is aqueous anionic acrylic resin lotion；Thickener is polyacrylic acid and silica
Mixture；Antifoaming agent is Siloxane-Oxyalkylene Copolymers；Pigment selects titanium dioxide, and the mesh number of pigment is 850 mesh；The oxidation
Zinc, talcum powder, sericite part, trbasic zinc phosphate and barium sulfate mesh number be 300 mesh.
Water-base resin, modified silicasol, zinc oxide, talcum powder, sericite part, trbasic zinc phosphate, barium sulfate and antifoaming agent are existed
In batching kettle be uniformly mixed, then feed the mixture into high-speed dispersing kettle and be stirred and disperse, dispersion before by thickener,
Levelling agent, pigment input, and disperseed gradually deionized water is added in high-speed dispersing kettle simultaneously；Scattered Kettle turns
Speed is 2800r/min, jitter time 40min, and after the completion of dispersion, slurry is sent to progress wet type sand milling in sand mill, will
The fineness of slurry is ground to 15 μm, you can obtains required antirust paint.
Embodiment 2
The nano-carbon powder and 6% iron oxide that mass fraction is 8% are added in hydrotropism's Ludox, then heats the mixture to 50
DEG C, it stirs evenly postcooling to room temperature and obtains modified soluble Ludox.
According to mass fraction, prepare following raw material：45 parts of water-base resin, 12 parts of modified soluble Ludox, zinc oxide 15
Part, 16 parts of talcum powder, 10 parts of sericite part, 8 parts of trbasic zinc phosphate, 7 parts of barium sulfate, 6 parts of thickener, 3 parts of levelling agent, 25 parts of pigment；
0.5 part of antifoaming agent, 20 parts of deionized water.
Wherein, water-base resin is aqueous anionic acrylic resin lotion；Thickener is polyacrylic acid and silica
Mixture；Antifoaming agent is Siloxane-Oxyalkylene Copolymers；Pigment selects aluminium triphosphate, and the mesh number of pigment is 900 mesh；The oxidation
Zinc, talcum powder, sericite part, trbasic zinc phosphate and barium sulfate mesh number be 500 mesh.
Water-base resin, modified silicasol, zinc oxide, talcum powder, sericite part, trbasic zinc phosphate, barium sulfate and antifoaming agent are existed
In batching kettle be uniformly mixed, then feed the mixture into high-speed dispersing kettle and be stirred and disperse, dispersion before by thickener,
Levelling agent, pigment input, and disperseed gradually deionized water is added in high-speed dispersing kettle simultaneously；Scattered Kettle turns
Speed is 3000r/min, jitter time 50min, and after the completion of dispersion, slurry is sent to progress wet type sand milling in sand mill, will
The fineness of slurry is ground to 20 μm, you can obtains required antirust paint.
Embodiment 3
The nano-carbon powder and 5% iron oxide that mass fraction is 7% are added in hydrotropism's Ludox, then heats the mixture to 48
DEG C, it stirs evenly postcooling to room temperature and obtains modified soluble Ludox.
According to mass fraction, prepare following raw material：40 parts of water-base resin, 10 parts of modified soluble Ludox, zinc oxide 13
Part, 14 parts of talcum powder, 9 parts of sericite part, 7 parts of trbasic zinc phosphate, 6 parts of barium sulfate, 5 parts of thickener, 2.5 parts of levelling agent, 20 parts of pigment；
0.4 part of antifoaming agent, 17 parts of deionized water.
Wherein, water-base resin is aqueous anionic acrylic resin lotion；Thickener is polyacrylic acid and silica
Mixture；Antifoaming agent is Siloxane-Oxyalkylene Copolymers；Pigment selects carbon black, and the mesh number of pigment is 850 mesh；The zinc oxide, cunning
Mountain flour, sericite part, trbasic zinc phosphate and barium sulfate mesh number be 400 mesh.
Water-base resin, modified silicasol, zinc oxide, talcum powder, sericite part, trbasic zinc phosphate, barium sulfate and antifoaming agent are existed
In batching kettle be uniformly mixed, then feed the mixture into high-speed dispersing kettle and be stirred and disperse, dispersion before by thickener,
Levelling agent, pigment input, and disperseed gradually deionized water is added in high-speed dispersing kettle simultaneously；Scattered Kettle turns
Speed is 2900r/min, jitter time 45min, and after the completion of dispersion, slurry is sent to progress wet type sand milling in sand mill, will
The fineness of slurry is ground to 18 μm, you can obtains required antirust paint.
Embodiment 4
The nano-carbon powder and 4% iron oxide that mass fraction is 8% are added in hydrotropism's Ludox, then heats the mixture to 45
DEG C, it stirs evenly postcooling to room temperature and obtains modified soluble Ludox.
According to mass fraction, prepare following raw material：45 parts of water-base resin, 7 parts of modified soluble Ludox, zinc oxide 15
Part, 16 parts of talcum powder, 8 parts of sericite part, 8 parts of trbasic zinc phosphate, 5 parts of barium sulfate, 6 parts of thickener, 2 parts of levelling agent, 20 parts of pigment；Disappear
0.3 part of infusion, 20 parts of deionized water.
Wherein, water-base resin is aqueous anionic acrylic resin lotion；Thickener is polyacrylic acid and silica
Mixture；Antifoaming agent is Siloxane-Oxyalkylene Copolymers；Pigment selects iron oxide red, and the mesh number of pigment is 900 mesh；The oxidation
Zinc, talcum powder, sericite part, trbasic zinc phosphate and barium sulfate mesh number be 500 mesh.
Water-base resin, modified silicasol, zinc oxide, talcum powder, sericite part, trbasic zinc phosphate, barium sulfate and antifoaming agent are existed
In batching kettle be uniformly mixed, then feed the mixture into high-speed dispersing kettle and be stirred and disperse, dispersion before by thickener,
Levelling agent, pigment input, and disperseed gradually deionized water is added in high-speed dispersing kettle simultaneously；Scattered Kettle turns
Speed is 3000r/min, jitter time 40min, and after the completion of dispersion, slurry is sent to progress wet type sand milling in sand mill, will
The fineness of slurry is ground to 15 μm, you can obtains required antirust paint.
Performance test
According to GB/T1731-1993《Paint film flexibility measuring method》, GB/T 1732-1993《Paint film impact resistance mensuration》,
GB/T 1771-2007《The resistance to neutral salt spray performance measurement of paint and varnish》Etc. technical standards, it is flexibility to the present embodiment, resistance to
Impact, salt spray resistance and artificial weathering ageing resistance can wait and be tested, and obtain following test result：
Table 1：The performance test results of this implementation antirust paint
| Project | Index | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 |
| Flexibility | Without reticulate pattern, crackle, peeling | It is qualified | It is qualified | It is qualified | It is qualified |
| Impact resistance | Flawless, wrinkle, peeling | It is qualified | It is qualified | It is qualified | It is qualified |
| Salt spray resistance | ≥200h | 320 | 310 | 320 | 300 |
| Artificial weathering ageing resistance's energy | ≥1000h | It is qualified | It is qualified | It is qualified | It is qualified |
| Adhesive force grade | \ | 1 grade | 1 grade | 1 grade | 1 grade |
Data above surface, the present invention provide a kind of power equipment antirust paint, and properties are all very outstanding；In addition, this hair
For the antirust paint of bright offer by statistics, production cost declines 4-6% compared with common product also has higher economic value.
Specific embodiments of the present invention are described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (8)
1. a kind of power equipment antirust paint, it is characterised in that：According to mass fraction, the antirust paint contains following component：Water
30-45 parts of resin of property, 7-12 parts of modified soluble Ludox, 10-15 parts of zinc oxide, 10-16 parts of talcum powder, sericite part 8-10
Part, 5-8 parts of trbasic zinc phosphate, 5-7 parts of barium sulfate, 3-6 parts of thickener, 2-3 parts of levelling agent, 15-25 parts of pigment；Antifoaming agent 0.3-0.5
Part, 15-20 parts of deionized water.
2. a kind of power equipment antirust paint according to claim 1, it is characterised in that：According to mass fraction, the antirust
Paint contains following component：35-40 parts of water-base resin, 8-10 parts of modified soluble Ludox, 12-13 parts of zinc oxide, talcum powder 12-
15 parts, 8-9 parts of sericite part, 6-7 parts of trbasic zinc phosphate, 5-6 parts of barium sulfate, 4-5 parts of thickener, 2.5-3 parts of levelling agent, pigment 20-
22 parts；0.4-0.5 parts of antifoaming agent, 17-18 parts of deionized water.
3. a kind of power equipment antirust paint according to claim 1, it is characterised in that：The modified soluble Ludox
Preparation method is：Mass fraction is added in hydrotropism's Ludox as the nano-carbon powder of 6-8% and the iron oxide of 4-6%, it then will be mixed
Close object be heated to 45-50 DEG C, stir evenly postcooling to room temperature is sufficient.
4. a kind of power equipment antirust paint according to claim 1, it is characterised in that：The water-base resin for it is aqueous it is cloudy from
Sub- emulsion acrylic resin.
5. a kind of power equipment antirust paint according to claim 1, it is characterised in that：The thickener for polyacrylic acid and
The mixture of silica；Antifoaming agent is Siloxane-Oxyalkylene Copolymers.
6. a kind of power equipment antirust paint according to claim 1, it is characterised in that：The pigment selection titanium dioxide,
One kind in aluminium triphosphate, carbon black, iron oxide red, the mesh number of pigment are higher than 800 mesh.
7. a kind of power equipment antirust paint according to claim 1, it is characterised in that：The zinc oxide, talcum powder, thin,tough silk cloud
The mesh number of female part, trbasic zinc phosphate and barium sulfate is 300-500 mesh.
8. a kind of power equipment antirust paint according to claim 1, it is characterised in that：The preparation method of the antirust paint
For：By water-base resin, modified silicasol, zinc oxide, talcum powder, sericite part, trbasic zinc phosphate, barium sulfate and antifoaming agent in batching kettle
In be uniformly mixed, then feed the mixture into high-speed dispersing kettle and be stirred and disperse, by thickener, levelling before dispersion
Agent, pigment input, and disperseed gradually deionized water is added in high-speed dispersing kettle simultaneously；The rotating speed of Scattered Kettle is
Slurry after the completion of dispersion, is sent to progress wet type sand in sand mill by 2800-3000r/min, jitter time 40-50min
Mill, is ground to 15-20 μm, you can obtain required antirust paint by the fineness of slurry.