CN104388954A - Antirust metal surface treatment agent - Google Patents
Antirust metal surface treatment agent Download PDFInfo
- Publication number
- CN104388954A CN104388954A CN201410597359.1A CN201410597359A CN104388954A CN 104388954 A CN104388954 A CN 104388954A CN 201410597359 A CN201410597359 A CN 201410597359A CN 104388954 A CN104388954 A CN 104388954A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal surface
- surface treatment
- treatment agent
- antirust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antirust metal surface treatment agent, which is prepared from the following raw materials in parts by weight: 7-11 parts of calcium nitrate, 5-9 parts of sodium hypochlorite, 4-10 parts of tartaric acid, 3-8 parts of nickel nitrate, 2-6 parts of formaldehyde, 3-8 parts of sodium carbonate, 1-5 parts of trisodium phosphate, 5-9 parts of sodium hydroxide, 8-14 parts of triethanolamine, 3-8 parts of a silane coupling agent, 2-5 parts of ethanol and 14 parts of deionized water. The antirust metal surface treatment agent disclosed by the invention has a good antirust cleaning effect, and simultaneously is capable of improving the metal surface quality and improving the quality of metal surface.
Description
Technical field
The present invention relates to a kind of anti-rust metal surface treatment agent.
Background technology
Clean-out system metal and goods thereof often can at the various dirt of surface contamination and impurity in the course of processing.Cleaning is an extremely important ring in metal finishing.The conventional clean-out system being major objective with degreasing of deoiling has petroleum clean-out system, chloro hydrocarbon system clean-out system, alkaline cleaner and the clean-out system etc. containing tensio-active agent.The treatment effect with the surface treatment agent of very good effect of the prior art is not ideal, and use cost is higher, therefore, limits the further genralrlization application of surface treatment agent.
Summary of the invention
For the deficiencies in the prior art, the technical problem to be solved in the present invention is, provides a kind of anti-rust metal surface treatment agent, has good antirust cleaning performance, can improve metallic surface quality simultaneously, improves the quality of metallic surface.
For solving the deficiencies in the prior art, the technical scheme that the present invention takes is: a kind of anti-rust metal surface treatment agent, is made up of the raw material of following parts by weight:
Nitrocalcite 7-11 part, clorox 5-9 part, tartrate 4-10 part, nickelous nitrate 3-8 part, formaldehyde 2-6 part, sodium carbonate 3-8 part, tertiary sodium phosphate 1-5 part, sodium hydroxide 5-9 part, trolamine 8-14 part, silane coupling agent 3-8 part, ethanol 2-5 part, deionized water 14 parts.
The technical scheme of optimization of the present invention is, a kind of anti-rust metal surface treatment agent, is made up of the raw material of following parts by weight:
9 parts, nitrocalcite, clorox 7 parts, 7 parts, tartrate, nickelous nitrate 5 parts, 4 parts, formaldehyde, 6 parts, sodium carbonate, tertiary sodium phosphate 3 parts, 7 parts, sodium hydroxide, trolamine 11 parts, silane coupling agent 5 parts, ethanol 4 parts, deionized water 14 parts.
The invention has the beneficial effects as follows that anti-rust metal surface treatment agent of the present invention has good antirust cleaning performance, metallic surface quality can be improved simultaneously, improve the quality of metallic surface.
Embodiment
embodiment 1
A kind of anti-rust metal surface treatment agent, be made up of the raw material of following parts by weight:
7 parts, nitrocalcite, clorox 5 parts, 4 parts, tartrate, nickelous nitrate 3 parts, 2 parts, formaldehyde, 3 parts, sodium carbonate, tertiary sodium phosphate 1 part, 5 parts, sodium hydroxide, trolamine 8 parts, silane coupling agent 3 parts, ethanol 2 parts, deionized water 14 parts.
embodiment 2
A kind of anti-rust metal surface treatment agent, be made up of the raw material of following parts by weight:
11 parts, nitrocalcite, clorox 9 parts, 10 parts, tartrate, nickelous nitrate 8 parts, 6 parts, formaldehyde, 8 parts, sodium carbonate, tertiary sodium phosphate 5 parts, 9 parts, sodium hydroxide, trolamine 14 parts, silane coupling agent 8 parts, ethanol 5 parts, deionized water 14 parts.
embodiment 3
A kind of anti-rust metal surface treatment agent, be made up of the raw material of following parts by weight:
9 parts, nitrocalcite, clorox 7 parts, 7 parts, tartrate, nickelous nitrate 5 parts, 4 parts, formaldehyde, 6 parts, sodium carbonate, tertiary sodium phosphate 3 parts, 7 parts, sodium hydroxide, trolamine 11 parts, silane coupling agent 5 parts, ethanol 4 parts, deionized water 14 parts.
Claims (2)
1. an anti-rust metal surface treatment agent, is characterized in that: be made up of the raw material of following parts by weight:
Nitrocalcite 7-11 part, clorox 5-9 part, tartrate 4-10 part, nickelous nitrate 3-8 part, formaldehyde 2-6 part, sodium carbonate 3-8 part, tertiary sodium phosphate 1-5 part, sodium hydroxide 5-9 part, trolamine 8-14 part, silane coupling agent 3-8 part, ethanol 2-5 part, deionized water 14 parts.
2. anti-rust metal surface treatment agent according to claim 1, is characterized in that: be made up of the raw material of following parts by weight:
9 parts, nitrocalcite, clorox 7 parts, 7 parts, tartrate, nickelous nitrate 5 parts, 4 parts, formaldehyde, 6 parts, sodium carbonate, tertiary sodium phosphate 3 parts, 7 parts, sodium hydroxide, trolamine 11 parts, silane coupling agent 5 parts, ethanol 4 parts, deionized water 14 parts.