CN105671579B - A kind of bearing in pump and bearing block cleaning agent - Google Patents
A kind of bearing in pump and bearing block cleaning agent Download PDFInfo
- Publication number
- CN105671579B CN105671579B CN201610073119.0A CN201610073119A CN105671579B CN 105671579 B CN105671579 B CN 105671579B CN 201610073119 A CN201610073119 A CN 201610073119A CN 105671579 B CN105671579 B CN 105671579B
- Authority
- CN
- China
- Prior art keywords
- parts
- bearing
- powder
- bearing block
- cleaning agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of bearing in pump and bearing block cleaning agents, are related to corrective maintenance technical field, are made of the raw material of following parts by weight：15 20 parts of ore deposit soil, 10 15 parts of hydrogenated rosin, 10 15 parts of asbestos wool, 8 11 parts of tea seed powder, 69 parts of soap powder, 69 parts of stearic acid, 48 parts of volcanic ash, 36 parts of poly-aspartate, 36 parts of sodium salicylate, 24 parts of soda ash, 12 parts of aluminium powder, 0.5 1 parts of borax, 0.2 0.3 parts of silane coupling agent, 200 250 parts of ethyl alcohol.Cleaning agent of the present invention is easy to use, a small amount of cleaning agent need to be only dipped during use with rag can to wipe bearing and bearing block, the dirt of its surface attachment can thoroughly be removed, and there is antirust function after wiping, bearing and bearing block is avoided to be acted on the moisture in environment or oxygen and corrosion phenomena occurs, extend its service life, so as to ensure the normal operation of pump.
Description
Technical field：
The present invention relates to corrective maintenance technical fields, and in particular to a kind of bearing in pump and bearing block cleaning agent.
Background technology：
Bearing is one of important component of pump, its major function is support pump shaft rotation, is reduced in its motion process
Coefficient of friction, and ensure its rotating accuracy.Sliding bearing is one of common bearing of pump, needs uniformly to apply on its surface when in use
One layer of lubricating grease is smeared, to protect bearing and pump shaft.It when carrying out pump care and maintenance, needs to get off bearing removal, through wiping
One layer of lubricating grease is smeared again afterwards, to protect bearing.But in use, the lubricating grease on bearing can become under long-term friction
Matter, viscosity increase, and a small amount of lubricating grease can it is extruded after adhere on bearing block.Therefore, using traditional rag wiping not
The lubricating grease that is adhered on bearing and bearing block and other dirts can be thoroughly removed, are washed also less than achieving the effect that thoroughly to remove,
The risk that bearing and bearing block get rusty can be increased instead.
Invention content：
The technical problems to be solved by the invention be to provide it is a kind of it is easy to use, cleaning performance is good and has anti-rust action
Bearing in pump and bearing block cleaning agent.
The technical problems to be solved by the invention are realized using following technical solution：
A kind of bearing in pump and bearing block cleaning agent, are made of the raw material of following parts by weight：
It is 15-20 parts of ore deposit soil, 10-15 parts of hydrogenated rosin, 10-15 parts of asbestos wool, 8-11 parts of tea seed powder, 6-9 parts of soap powder, hard
6-9 parts of resin acid, 4-8 parts of volcanic ash, 3-6 parts of poly-aspartate, 3-6 parts of sodium salicylate, 2-4 parts of soda ash, 1-2 parts of aluminium powder, boron
0.5-1 parts of sand, 0.2-0.3 parts of silane coupling agent, 200-250 parts of ethyl alcohol；
Preparation method is as follows：
(1) hydrogenated rosin is dissolved in ethyl alcohol, adds stearic acid and silane coupling agent, be uniformly mixed after Microwave Frequency
Microwave treatment 10min is to get material I under rate 2450MHz, power 800W；
(2) asbestos wool and volcanic ash are added in into ore deposit soil, 70-80 DEG C of heat preservation mixing 15min is first heated to, then adds in Soviet Union
Powder and aluminium powder are beaten, continues to be heated to 110-120 DEG C of heat preservation mixing 10min to get material II；
(3) material II, tea seed powder, soap powder, poly-aspartate, sodium salicylate and borax are added in into material I, mixing is equal
It is added in ball mill after even, is milled to fineness less than 50 μm.
The ore deposit soil is made of the raw material of following parts by weight：20-25 parts of atlapulgite, 10-15 parts of attapulgite, calcining
6-10 parts of kaolin, 5-8 parts of hydroxypropyl cellulose, 5-8 parts of rilanit special, 4-6 parts of ceramic, 3-5 parts of grease, nano oxygen
Change 2-3 parts of zinc, 2-3 parts of rice bran wax, preparation method is：Rilanit special and nano zine oxide are added in 5 times of w ethanols,
Stirring forms homogeneous solution, adds atlapulgite, attapulgite and calcined kaolin, is uniformly mixed after microwave frequency
Then microwave treatment 10min under 2450MHz, power 800W adds in ceramic and rice bran wax, continue microwave treatment 10min, mixes
Powder is made after conjunction object is spray-dried, is eventually adding hydroxypropyl cellulose and grease, is sufficiently mixed uniformly.
The grease is made of the raw material by following parts by weight：30-40 parts of acetone, 15-20 parts of machine oil, palm oil 10-
15 parts, 10-15 parts of tea-seed oil, 8-12 parts of polyoxyethylene carboxylate, 5-10 parts of cetanol, 4-8 parts of soybean lecithin, Sorbitan
4-8 parts of alcohol laurate, 3-5 parts of vaseline, 2-3 parts of glucoside.
The beneficial effects of the invention are as follows：The present invention, for raw material, makes full use of the absorption of ore deposit soil with ore deposit soil and hydrogenated rosin etc.
Bearing in pump and bearing block cleaning agent is made in cleaning action, and the cleaning agent is easy to use, and when use need to only be dipped on a small quantity with rag
Cleaning agent can wipe bearing and bearing block, can thoroughly remove the dirt of its surface attachment, and have after wiping
Antirust function avoids bearing and bearing block from being acted on the moisture in environment or oxygen and corrosion phenomena occurs, and extends it and uses the longevity
Life, so as to ensure the normal operation of pump.
Specific embodiment：
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below
Specific embodiment is closed, the present invention is further explained.
Embodiment 1
(1) 10 parts of hydrogenated rosins are dissolved in 200 parts of ethyl alcohol, add 6 parts of stearic acid and 0.2 part of silane coupling agent,
It is uniformly mixed after microwave treatment 10min under microwave frequency 2450MHz, power 800W to get material I；
(2) 12 parts of asbestos wools and 4 parts of volcanic ash are added in into 15 parts of ore deposit soil, are first heated to 70-80 DEG C of heat preservation mixing
Then 15min adds in 3 portions of soda ash and 1 part of aluminium powder, continue to be heated to 110-120 DEG C of heat preservation mixing 10min to get material II；
(3) material II, 8 parts of tea seed powder, 8 parts of soap powder, 3 parts of poly-aspartates, 3 parts of sodium salicylates are added in into material I
It with 1 part of borax, adds in ball mill after mixing, is milled to fineness less than 50 μm.
The preparation of ore deposit soil：6 parts of rilanit specials and 2 parts of nano zine oxides are added in 5 times of w ethanols, stirring forms equal
Even solution adds 20 parts of atlapulgites, 12 parts of attapulgites and 6 parts of calcined kaolins, is uniformly mixed after microwave frequency
Then microwave treatment 10min under 2450MHz, power 800W adds in 4 parts of ceramics and 2 parts of rice bran waxs, continue microwave treatment
Powder is made after mixture is spray-dried in 10min, is eventually adding 6 parts of hydroxypropyl celluloses and 5 parts of greases, is sufficiently mixed
It is even.
The preparation of grease：15 parts of machine oil, 13 parts of palm oils, 10 portions of tea-seed oils, 8 parts of fatty acid polyglycols are added in into 30 parts of acetone
Ethylene oxide ester, 5 parts of cetanols, 4 parts of soybean lecithins, 6 parts of anhydrous sorbitol laurates, 3 parts of vaseline and 2 portions of glucosides,
It is sufficiently mixed uniformly.
Embodiment 2
(1) 15 parts of hydrogenated rosins are dissolved in 250 parts of ethyl alcohol, add 8 parts of stearic acid and 0.3 part of silane coupling agent,
It is uniformly mixed after microwave treatment 10min under microwave frequency 2450MHz, power 800W to get material I；
(2) 10 parts of asbestos wools and 6 parts of volcanic ash are added in into 20 parts of ore deposit soil, are first heated to 70-80 DEG C of heat preservation mixing
Then 15min adds in 3 portions of soda ash and 1 part of aluminium powder, continue to be heated to 110-120 DEG C of heat preservation mixing 10min to get material II；
(3) material II, 10 parts of tea seed powder, 6 parts of soap powder, 5 parts of poly-aspartates, 4 parts of sodium salicylates are added in into material I
It with 0.5 part of borax, adds in ball mill after mixing, is milled to fineness less than 50 μm.
The preparation of ore deposit soil：8 parts of rilanit specials and 3 parts of nano zine oxides are added in 5 times of w ethanols, stirring forms equal
Even solution adds 25 parts of atlapulgites, 10 parts of attapulgites and 8 parts of calcined kaolins, is uniformly mixed after microwave frequency
Then microwave treatment 10min under 2450MHz, power 800W adds in 6 parts of ceramics and 3 parts of rice bran waxs, continue microwave treatment
Powder is made after mixture is spray-dried in 10min, is eventually adding 8 parts of hydroxypropyl celluloses and 4 parts of greases, is sufficiently mixed
It is even.
The preparation of grease：20 parts of machine oil, 10 parts of palm oils, 12 portions of tea-seed oils, 10 parts of aliphatic acid are added in into 40 parts of acetone
Polyoxyethylene ester, 8 parts of cetanols, 6 parts of soybean lecithins, 4 parts of anhydrous sorbitol laurates, 5 parts of vaseline and 3 parts of glucose
Glycosides is sufficiently mixed uniformly.
The basic principles, main features and the advantages of the invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (3)
1. a kind of bearing in pump and bearing block cleaning agent, which is characterized in that be made of the raw material of following parts by weight：
15-20 parts of ore deposit soil, 10-15 parts of hydrogenated rosin, 10-15 parts of asbestos wool, 8-11 parts of tea seed powder, 6-9 parts of soap powder, stearic acid
6-9 parts, 4-8 parts of volcanic ash, 3-6 parts of poly-aspartate, 3-6 parts of sodium salicylate, 2-4 parts of soda ash, 1-2 parts of aluminium powder, borax
0.5-1 parts, 0.2-0.3 parts of silane coupling agent, 200-250 parts of ethyl alcohol；
Preparation method is as follows：
(1) hydrogenated rosin is dissolved in ethyl alcohol, adds stearic acid and silane coupling agent, be uniformly mixed after microwave frequency
Microwave treatment 10min is to get material I under 2450MHz, power 800W；
(2) asbestos wool and volcanic ash are added in into ore deposit soil, 70-80 DEG C of heat preservation mixing 15min is first heated to, then adds in soda ash
And aluminium powder, continue to be heated to 110-120 DEG C of heat preservation mixing 10min to get material II；
(3) material II, tea seed powder, soap powder, poly-aspartate, sodium salicylate and borax are added in into material I, after mixing
It adds in ball mill, is milled to fineness less than 50 μm.
2. bearing in pump according to claim 1 and bearing block cleaning agent, which is characterized in that the ore deposit soil is by following weight
The raw material of number is made：20-25 parts of atlapulgite, 10-15 parts of attapulgite, 6-10 parts of calcined kaolin, hydroxypropyl cellulose
5-8 parts, 5-8 parts of rilanit special, 4-6 parts of ceramic, 3-5 parts of grease, 2-3 parts of nano zine oxide, 2-3 parts of rice bran wax,
Preparation method is：Rilanit special and nano zine oxide are added in 5 times of w ethanols, stirring forms homogeneous solution, adds
Atlapulgite, attapulgite and calcined kaolin are uniformly mixed after microwave treatment under microwave frequency 2450MHz, power 800W
Then 10min adds in ceramic and rice bran wax, continue microwave treatment 10min, powder is made after mixture is spray-dried,
Hydroxypropyl cellulose and grease are eventually adding, is sufficiently mixed uniformly.
3. bearing in pump according to claim 2 and bearing block cleaning agent, which is characterized in that the grease by by weighing as follows
The raw material of amount number is made：30-40 parts of acetone, 15-20 parts of machine oil, 10-15 parts of palm oil, 10-15 parts of tea-seed oil, fatty acid polyglycol
8-12 parts of ethylene oxide ester, 5-10 parts of cetanol, 4-8 parts of soybean lecithin, 4-8 parts of anhydrous sorbitol laurate, vaseline 3-5
Part, 2-3 parts of glucoside.