CN103350059A - Manufacturing method of steel pipe - Google Patents
Manufacturing method of steel pipe Download PDFInfo
- Publication number
- CN103350059A CN103350059A CN2013103308791A CN201310330879A CN103350059A CN 103350059 A CN103350059 A CN 103350059A CN 2013103308791 A CN2013103308791 A CN 2013103308791A CN 201310330879 A CN201310330879 A CN 201310330879A CN 103350059 A CN103350059 A CN 103350059A
- Authority
- CN
- China
- Prior art keywords
- workpiece
- stage
- manufacturing
- steel pipe
- end product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of steel pipes, and particularly relates to a manufacturing method of a steel pipe. The manufacturing method comprises the following stages of: (1) a pretreatment stage, i.e., a workpiece is subjected to treatments through oil removing, rust cleaning, phosphorization and passivation processes; (2) an electrostatic coating stage, i.e., an electrostatic coating machine is utilized to spray a powder coating on the surface of the workpiece after pretreatment; (3) a high temperature solidifying stage, i.e., the sprayed workpiece is pushed into a curing oven, wherein the heating temperature is 170-190 DEG C, and the heat preservation time is 10-20 minutes; (4), an end product forming stage, i.e., the workpiece is taken out from the curing oven after high temperature solidification, and the end product is obtained after cooling. The manufacturing method provided by the invention has the advantages that the process is simple, the operation is convenient, the time and temperature are easy to control and master, the end product has the extremely high corrosion resistance, compression resistance and ageing-resistant performance, the service life is prolonged, and the actual use requirement is met.
Description
Technical field
The present invention relates to the technique of pipe field, be specifically related to the production method of steel pipe.
Background technology
At present, the steel pipe sold on the existing market is through after the simple surface treatment, and it is corrosion-resistant, compression resistance, ageing-resistant performance are lower, can not satisfy actual user demand.And existing steel tube surface complex treatment process, time, temperature are all wayward.
Summary of the invention
The purpose of this invention is to provide that a kind of technique is simple, easy to operate, time, temperature are easy to control and the production method of corrosion-resistant, compression resistance, steel pipe that ageing-resistant performance is high.
In order to solve the existing problem of background technology, the present invention is by the following technical solutions: the production method of steel pipe comprised with the next stage:
(1), pretreatment stage, workpiece is processed through oil removing, rust cleaning, phosphatization and passivation procedure;
(2), the electrostatic spraying stage, utilize electrostatic sprayer that powdery paints is sprayed on the surface of the described workpiece after the pre-treatment;
(3), the hot setting stage, the described workpiece that spraying is good is pushed in the curing oven 170～190 ℃ of heating-up temperatures, temperature retention time 10～20 minutes;
(4), finished product, the workpiece behind hot setting is taken out in blow-on, cooling namely obtains finished product.
The present invention has following beneficial effect: the production method of steel pipe of the present invention, mainly comprise pretreatment stage, electrostatic spraying stage and hot setting stage, and get at last finished product; Technique of the present invention is simple, easy to operate, time, temperature all are easy to control and grasp, and its finished product has high corrosion-resistant, compression resistance, ageing-resistant performance, has prolonged service life, satisfies actual user demand.
The specific embodiment
Below the present invention will be further described in detail.
Embodiment one:
The production method of steel pipe comprised with the next stage:
(1), pretreatment stage, workpiece is processed through oil removing, rust cleaning, phosphatization and passivation procedure; Wherein, workpiece after pre-treatment not only the surface do not have oil, rust, dirt but also the original even and coarse grey phosphating coat that is not easy to get rusty of silvery white glossiness Surface Creation one deck, can the antirust adhesive force that can increase again the plastic-blasting layer;
(2), the electrostatic spraying stage, utilize electrostatic sprayer that powdery paints is sprayed on the surface of the described workpiece after the pre-treatment; Workpiece after spraying has high corrosion-resistant, compression resistance, ageing-resistant performance, thereby can prolong its service life;
(3), the hot setting stage, the described workpiece that spraying is good is pushed in the curing oven 170 ℃ of heating-up temperatures, temperature retention time 10 minutes;
(4), finished product, the workpiece behind hot setting is taken out in blow-on, cooling namely obtains finished product.
Embodiment two:
The production method of steel pipe comprised with the next stage:
(1), pretreatment stage, workpiece is processed through oil removing, rust cleaning, phosphatization and passivation procedure;
(2), the electrostatic spraying stage, utilize electrostatic sprayer that powdery paints is sprayed on the surface of the described workpiece after the pre-treatment;
(3), the hot setting stage, the described workpiece that spraying is good is pushed in the curing oven 180 ℃ of heating-up temperatures, temperature retention time 15 minutes;
(4), finished product, the workpiece behind hot setting is taken out in blow-on, cooling namely obtains finished product.
Embodiment three:
The production method of steel pipe comprised with the next stage:
(1), pretreatment stage, workpiece is processed through oil removing, rust cleaning, phosphatization and passivation procedure;
(2), the electrostatic spraying stage, utilize electrostatic sprayer that powdery paints is sprayed on the surface of the described workpiece after the pre-treatment;
(3), the hot setting stage, the described workpiece that spraying is good is pushed in the curing oven 190 ℃ of heating-up temperatures, temperature retention time 20 minutes;
(4), finished product, the workpiece behind hot setting is taken out in blow-on, cooling namely obtains finished product.
Explanation is at last, above embodiment is only unrestricted in order to technical scheme of the present invention to be described, other modifications that those of ordinary skills make technical scheme of the present invention or be equal to replacement, only otherwise break away from the spirit and scope of technical solution of the present invention, all should be encompassed in the middle of the claim scope of the present invention.
Claims (1)
1. the production method of steel pipe is characterized in that, comprises with the next stage:
(1), pretreatment stage, workpiece is processed through oil removing, rust cleaning, phosphatization and passivation procedure;
(2), the electrostatic spraying stage, utilize electrostatic sprayer that powdery paints is sprayed on the surface of the described workpiece after the pre-treatment;
(3), the hot setting stage, the described workpiece that spraying is good is pushed in the curing oven 170～190 ℃ of heating-up temperatures, temperature retention time 10～20 minutes;
(4), finished product, the workpiece behind hot setting is taken out in blow-on, cooling namely obtains finished product.