CN103668201A - Anticorrosive treatment method of metal aluminum - Google Patents
Anticorrosive treatment method of metal aluminum Download PDFInfo
- Publication number
- CN103668201A CN103668201A CN201310653787.7A CN201310653787A CN103668201A CN 103668201 A CN103668201 A CN 103668201A CN 201310653787 A CN201310653787 A CN 201310653787A CN 103668201 A CN103668201 A CN 103668201A
- Authority
- CN
- China
- Prior art keywords
- treatment method
- metallic aluminium
- oxide layer
- metal aluminum
- metal oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anticorrosive treatment method of metal aluminum, and the anticorrosive treatment method comprises the following steps: 1) injecting zirconium phosphate, silicon dioxide, chromic chromate and sodium fluosilicate into the metal aluminum surface in an ion injection mode to form a insoluble co network layer with a thickness of 60-70 nm; 2) forming a metal oxide layer on the metal aluminum surface; 3) coating the metal oxide layer with a primer with a thickness of 230-250nm. The anticorrosive treatment method of the metal aluminum improves the anticorrosive effect.
Description
Technical field
The present invention relates to metallic aluminium anti-corrosive treatment method.
Background technology
The anticorrosion ability of metal current aluminium anti-corrosive treatment method is not very desirable.
Summary of the invention
The object of the present invention is to provide a kind of metallic aluminium anti-corrosive treatment method, improve anticorrosion ability.
For achieving the above object, technical scheme of the present invention is a kind of metallic aluminium anti-corrosive treatment method of design, comprises the steps:
1) on metallic aluminium surface, adopt ion implantation mode to inject the insoluble network layer altogether that zirconium phosphate, silicon-dioxide, chromic acid chromium and Sodium Silicofluoride formation thickness are 60-70nm;
2) on metallic aluminium surface, form metal oxide layer again;
3) on metal oxide layer, be coated with again the priming paint that thickness is 230-250nm.
Advantage of the present invention and beneficial effect are: a kind of metallic aluminium anti-corrosive treatment method is provided, improves anticorrosion ability.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples are only for technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.
The concrete technical scheme of implementing of the present invention is:
Embodiment 1
A metallic aluminium anti-corrosive treatment method, comprises the steps:
1) on metallic aluminium surface, adopt ion implantation mode to inject the insoluble network layer altogether that zirconium phosphate, silicon-dioxide, chromic acid chromium and Sodium Silicofluoride formation thickness are 60nm;
2) on metallic aluminium surface, form metal oxide layer again;
3) on metal oxide layer, be coated with again the priming paint that thickness is 230nm.
Embodiment 2
A metallic aluminium anti-corrosive treatment method, comprises the steps:
1) on metallic aluminium surface, adopt ion implantation mode to inject the insoluble network layer altogether that zirconium phosphate, silicon-dioxide, chromic acid chromium and Sodium Silicofluoride formation thickness are 70nm;
2) on metallic aluminium surface, form metal oxide layer again;
3) on metal oxide layer, be coated with again the priming paint that thickness is 250nm.
Embodiment 3
A metallic aluminium anti-corrosive treatment method, comprises the steps:
1) on metallic aluminium surface, adopt ion implantation mode to inject the insoluble network layer altogether that zirconium phosphate, silicon-dioxide, chromic acid chromium and Sodium Silicofluoride formation thickness are 65nm;
2) on metallic aluminium surface, form metal oxide layer again;
3) on metal oxide layer, be coated with again the priming paint that thickness is 240nm.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. metallic aluminium anti-corrosive treatment method, is characterized in that, comprises the steps:
1) on metallic aluminium surface, adopt ion implantation mode to inject the insoluble network layer altogether that zirconium phosphate, silicon-dioxide, chromic acid chromium and Sodium Silicofluoride formation thickness are 60-70nm;
2) on metallic aluminium surface, form metal oxide layer again;
3) on metal oxide layer, be coated with again the priming paint that thickness is 230-250nm.