CN105624631A - Anti-corrosion treatment technology for bottom plate of automobile seat - Google Patents
Anti-corrosion treatment technology for bottom plate of automobile seat Download PDFInfo
- Publication number
- CN105624631A CN105624631A CN201511013712.8A CN201511013712A CN105624631A CN 105624631 A CN105624631 A CN 105624631A CN 201511013712 A CN201511013712 A CN 201511013712A CN 105624631 A CN105624631 A CN 105624631A
- Authority
- CN
- China
- Prior art keywords
- parts
- precursor composition
- minutes
- seat
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of die machining, in particular to an anti-corrosion treatment technology for a bottom plate of an automobile seat. An anti-corrosion precursor composition is prepared and is composed of 15 parts of acrylate emulsion, 20 parts of o-xylene, 5 parts of petroleum ether, 5 parts of citric acid, 0.5 part of glycyrrhizic acid and other components; the bottom plate of the seat is put into the anti-corrosion precursor composition to be soaked, and then the soaked anti-corrosion precursor composition is flushed to be clean through clean water; zirconium phosphate, silica, chromium chromate and sodium fluosilicate are injected into the surface of the bottom plate of the seat in an ion implantation manner, and an insoluble co-complexing layer with the thickness of 100 nm is formed; and the insoluble co-complexing layer on the bottom plate of the seat is coated with primer with the thickness of 200 nm. By means of the anti-corrosion treatment technology, the reasonable anti-corrosion precursor composition is added to be soaked and the formula of the anti-corrosion precursor composition and a preparing method of the anti-corrosion precursor composition are reasonably designed, so that the anti-corrosion performance of the bottom plate of the seat is obviously improved, and the service life of a pedal is greatly prolonged.
Description
Technical field
The present invention relates to mold machining technology field, specifically relate to a kind of automotive seat base plate anticorrosive treatment process.
Background technology
Seat plate is when machine-shaping, it is necessary to it is carried out anti-corrosive treatment. When carrying out rotproofing, there is not any pretreating scheme in prior art, directly carries out anti-corrosive treatment. This kind of cooked mode easily cause seat plate the big heavy discount in work-ing life of preservative coat, it may also be useful to will seem after for some time that rust mark is full of stains or spots.
Summary of the invention
For the technical problem existed in prior art, it is an object of the invention to provide a kind of automotive seat base plate anticorrosive treatment process, for achieving the above object, present invention employs following technical scheme:
A kind of automotive seat base plate anticorrosive treatment process, step is as follows:
Step 1., prepare anticorrosion precursor composition:
Anticorrosion precursor composition is made up of 15 parts of acrylic ester emulsions, 20 parts of o-Xylols, 5 parts of sherwood oils, 5 parts of citric acids, 0.5 part of Potenlini, 5 parts of glycerol and 40 parts of water;
First in container, add 15 parts of acrylic ester emulsions, 20 parts of o-Xylols and 15 parts of water, stir 5 minutes; Then 5 parts of citric acids are slowly added, stirring while adding, stir 10 minutes after interpolation; Then 5 parts of sherwood oils and 15 parts of water are slowly added, stirring while adding, stir 5 minutes after interpolation; Then 0.5 part of Potenlini is slowly added, stirring while adding, stir 5 minutes after interpolation; Finally add 5 parts of glycerol and 10 parts of water fast, stir 15 minutes;
Step 2., seat plate is put into be heated in advance 45 DEG C anticorrosion precursor composition soak 50 minutes, then rinse well with clear water;
3., in seat backplate surface employing ion implantation mode step injects the insoluble network layers altogether that zirconium phosphate, silicon-dioxide, chromic acid chromium and Sodium Silicofluoride formation thickness are 100nm;
4., in the insoluble network layers altogether of seat plate step is coated with the priming paint that thickness is 200nm.
The useful effect of the present invention shows:
1) the anticorrosion precursor composition, used in anticorrosive treatment process, its formulating of recipe is reasonable, novel, particularly with the addition of a small amount of Potenlini, the efficiency of follow-up rotproofing can be significantly improved, the antiseptic property of seat plate is significantly improved, and the work-ing life of greatly prolonged pedal.
2), the preparation method of anticorrosion precursor composition, by the method progressively added, by appropriate design order of addition(of ingredients), it is not only possible to improve the solubility property between each material, the possibility of particle agglomeration can also be avoided, and the rotproofing efficiency making anticorrosion precursor composition is significantly improved.
3), anticorrosive treatment process, operating procedure is simple, soak by adding rational anticorrosion precursor composition, and the preparation method of the formula of the anticorrosion precursor composition of appropriate design and anticorrosion precursor composition, the antiseptic property of seat plate is significantly improved, and the work-ing life of greatly prolonged pedal.
Embodiment
Below with reference to embodiment, the present invention is described in detail. But; embodiment content is only citing made for the present invention and explanation; described specific embodiment is made various amendment or supplements or adopt similar mode to substitute by affiliated those skilled in the art; as long as not deviateing the design of invention or surmounting this scope as defined in the claims, protection scope of the present invention all should be belonged to.
One, the composition of anticorrosion precursor composition
15 parts of acrylic ester emulsions, 20 parts of o-Xylols, 5 parts of sherwood oils, 5 parts of citric acids, 0.5 part of Potenlini, 5 parts of glycerol and 40 parts of water.
Two, the preparation method of anticorrosion precursor composition is:
First in container, add 15 parts of acrylic ester emulsions, 20 parts of o-Xylols and 15 parts of water, stir 5 minutes; Then 5 parts of citric acids are slowly added, stirring while adding, stir 10 minutes after interpolation; Then 5 parts of sherwood oils and 15 parts of water are slowly added, stirring while adding, stir 5 minutes after interpolation; Then 0.5 part of Potenlini is slowly added, stirring while adding, stir 5 minutes after interpolation; Finally add 5 parts of glycerol and 10 parts of water fast, stir 15 minutes.
Three, automotive seat base plate anticorrosive treatment process
Step 1., seat plate is put into be heated in advance 45 DEG C anticorrosion precursor composition soak 50 minutes, then rinse well with clear water;
2., in seat backplate surface employing ion implantation mode step injects the insoluble network layers altogether that zirconium phosphate, silicon-dioxide, chromic acid chromium and Sodium Silicofluoride formation thickness are 100nm;
3., in the insoluble network layers altogether of seat plate step is coated with the priming paint that thickness is 200nm.
Claims (1)
1. an automotive seat base plate anticorrosive treatment process, it is characterised in that step is as follows:
Step 1., prepare anticorrosion precursor composition:
Anticorrosion precursor composition is made up of 15 parts of acrylic ester emulsions, 20 parts of o-Xylols, 5 parts of sherwood oils, 5 parts of citric acids, 0.5 part of Potenlini, 5 parts of glycerol and 40 parts of water;
First in container, add 15 parts of acrylic ester emulsions, 20 parts of o-Xylols and 15 parts of water, stir 5 minutes; Then 5 parts of citric acids are slowly added, stirring while adding, stir 10 minutes after interpolation; Then 5 parts of sherwood oils and 15 parts of water are slowly added, stirring while adding, stir 5 minutes after interpolation; Then 0.5 part of Potenlini is slowly added, stirring while adding, stir 5 minutes after interpolation; Finally add 5 parts of glycerol and 10 parts of water fast, stir 15 minutes;
Step 2., seat plate is put into be heated in advance 45 DEG C anticorrosion precursor composition soak 50 minutes, then rinse well with clear water;
3., in seat backplate surface employing ion implantation mode step injects the insoluble network layers altogether that zirconium phosphate, silicon-dioxide, chromic acid chromium and Sodium Silicofluoride formation thickness are 100nm;
4., in the insoluble network layers altogether of seat plate step is coated with the priming paint that thickness is 200nm.