CN106757671A - A kind of production method of shuttle-woven fabric - Google Patents
A kind of production method of shuttle-woven fabric Download PDFInfo
- Publication number
- CN106757671A CN106757671A CN201611191333.2A CN201611191333A CN106757671A CN 106757671 A CN106757671 A CN 106757671A CN 201611191333 A CN201611191333 A CN 201611191333A CN 106757671 A CN106757671 A CN 106757671A
- Authority
- CN
- China
- Prior art keywords
- yarn
- shuttle
- woven fabric
- production method
- mercerising
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production method of shuttle-woven fabric, comprise the following steps, prepare mercerising true qualities yarn, above-mentioned yarn is carried out, without slurry weaving, post processing, to obtain final product shuttle-woven fabric；The mercerising true qualities yarn is obtained by the following method：Carry out yarn singeing, reeling, by above-mentioned yarn in mercerizing machine mercerization finish, the alkali concn for the treatment of fluid is 35 Baume degrees, and temperature is 30 DEG C, applies tension force：Stretching 8%, the time is 10min；Speed is 1000m/min, and the strand weight of reeling is 600g.The production method of shuttle-woven fabric proposed by the invention has the advantages that to shorten technological process and saves production cost, and is especially beneficial environmental protection.
Description
Technical field
The present invention relates to a kind of textile technology field, in particular it relates to a kind of production method of shuttle-woven fabric.
Background technology
Shuttle-woven fabric weave when yarn due to the friction of weaving process to be born, surface can produce filoplume, at the same bear compared with
Needed by sizing process before strong tensile force, thus weaving, to improve yarn strength and surface smoothness, but used at present
Slurry it is most for starch and the mixed slurry of PVA types, waste water is also easy to produce after desizing, environmental pollution is caused, in such case
Under, I is taken charge of by years of researches, develops the production technology of slurry-free shuttle-woven fabric（License is obtained at present）, with reference to existing
The zero-discharge production process of row mercerising production, the true qualities mercerizing thread of the main application Sustainable use zero-emission production of the present invention is exempted from
Slurry is weaved, so as to obtain a kind of production method of the shuttle-woven fabric of complete zero-emission production.
The content of the invention
The present invention mainly overcomes the pollution problem in existing shuttle-woven fabric weaving, there is provided a kind of shuttle-woven fabric of environmental protection
Production method.
In order to solve the above-mentioned technical problem, the invention provides following technical scheme：
A kind of production method of shuttle-woven fabric, is comprised the following steps, and prepares mercerising true qualities yarn, and above-mentioned yarn is carried out without slurry
Weaving, post processing, obtain final product shuttle-woven fabric；The mercerising true qualities yarn is obtained by the following method：Yarn singeing, reeling are carried out,
By above-mentioned yarn in mercerizing machine mercerization finish, the alkali concn for the treatment of fluid is 35 Baume degrees, and temperature is 30 DEG C, applies tension force：Draw
8% is stretched, the time is 10min；Speed is 1000 m/min, and the strand weight of reeling is 600g.Further, most also wrapped before weaving
Including also includes the step that mercerized yarn is placed in the warp beam of loom or beam of a loom by required size.Specifically, described post processing
It is the water-washing step of fabric, its temperature is 80 DEG C, the min of time 20, then washes 10min with cold water；After washing, fabric is dried.Tool
Body ground, the temperature of the drying is 140 DEG C, and speed is 15m/min, and the time is 5min.
The production method of shuttle-woven fabric proposed by the invention has the advantages that：
1st, procedure proposed by the invention is simple, each step is all optimized, and has fully demonstrated with simple process
Prepare the advantage of high quality of products.
2nd, adopting this method the fabric of preparation can avoid the shortcoming of the easy staining of yarn after arrangement.
3rd, using method for sorting of the invention, can be with by the mercerising true qualities yarn strength and surface hairiness after mercerization finish
Requirements of weaving process is reached, the production of slurry-free shuttle-woven fabric is can be directly used for；Because being freeed using zero-emission in mercerizing thread production process
Product method, so avoiding discharge of wastewater, realizes the recovery of alkali lye and heat energy again；In production process without slurry shuttle-woven fabric
Starching, desizing method are avoided, discharge of wastewater is reduced, environmental protection is realized.
Specific embodiment
Embodiment 1
The production method of shuttle-woven fabric, is comprised the following steps, and prepares mercerising true qualities yarn, and above-mentioned yarn is carried out to be knitted without slurry
Make, post-process, obtain final product shuttle-woven fabric；The mercerising true qualities yarn is obtained by the following method：Yarn singeing, reeling are carried out, will
Above-mentioned yarn mercerization finish in mercerizing machine, the alkali concn for the treatment of fluid is 35 Baume degrees, and temperature is 30 DEG C, applies tension force：Stretching
8%, the time is 10min；Speed is 1000 m/min, and the strand weight of reeling is 600g.
Embodiment 2
The production method of shuttle-woven fabric, is comprised the following steps, and prepares mercerising true qualities yarn, and above-mentioned yarn is carried out to be knitted without slurry
Make, post-process, obtain final product shuttle-woven fabric；Before weaving, mercerized yarn is placed in the warp beam of loom or beam of a loom by required size；Institute
Mercerising true qualities yarn is stated to be obtained by the following method：Yarn singeing, reeling are carried out, by above-mentioned yarn at mercerising in mercerizing machine
Reason, the alkali concn for the treatment of fluid is 35 Baume degrees, and temperature is 30 DEG C, applies tension force：Stretching 8%, the time is 10min；Speed is
1000 m/min, the strand weight of reeling is 600g.
Embodiment 3
The production method of shuttle-woven fabric, is comprised the following steps, and prepares mercerising true qualities yarn, and above-mentioned yarn is carried out to be knitted without slurry
Make, post-process, obtain final product shuttle-woven fabric；The mercerising true qualities yarn is obtained by the following method：Yarn singeing, reeling are carried out, will
Above-mentioned yarn mercerization finish in mercerizing machine, the alkali concn for the treatment of fluid is 35 Baume degrees, and temperature is 30 DEG C, applies tension force：Stretching
8%, the time is 10min；Speed is 1000 m/min, and the strand weight of reeling is 600g.Described post processing is walked for the washing of fabric
Suddenly, its temperature is 80 DEG C, the min of time 20, then washes 10min with cold water；After washing, fabric is dried.
Embodiment 4
The production method of shuttle-woven fabric, is comprised the following steps, and prepares mercerising true qualities yarn, and above-mentioned yarn is carried out to be knitted without slurry
Make, post-process, obtain final product shuttle-woven fabric；The mercerising true qualities yarn is obtained by the following method：Yarn singeing, reeling are carried out, will
Above-mentioned yarn mercerization finish in mercerizing machine, the alkali concn for the treatment of fluid is 35 Baume degrees, and temperature is 30 DEG C, applies tension force：Stretching
8%, the time is 10min；Speed is 1000 m/min, and the strand weight of reeling is 600g.Further, most also include before weaving
Also include the step that mercerized yarn is placed in the warp beam of loom or beam of a loom by required size.Specifically, described post processing is
The water-washing step of fabric, its temperature is 80 DEG C, the min of time 20, then washes 10min with cold water；After washing, fabric is dried.Specifically
Ground, the temperature of the drying is 140 DEG C, and speed is 15m/min, and the time is 5min.
The procedure of the present embodiment is simple, each step is all optimized, and has fully demonstrated with simple process system
The advantage of standby high quality of products.Adopting this method the fabric of preparation can avoid the shortcoming of the easy staining of yarn after arrangement.Using this
The method for sorting of invention, requirements of weaving process can be reached by mercerising true qualities yarn strength and surface hairiness after mercerization finish, can
It is directly used in the production of slurry-free shuttle-woven fabric；Because using zero-emission production method in mercerizing thread production process, avoid
Discharge of wastewater, realizes the recovery of alkali lye and heat energy again；Starching, desizing are avoided in production process without slurry shuttle-woven fabric
Process, reduces discharge of wastewater, realizes environmental protection.
Finally it should be noted that：The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention,
Although being described in detail to the present invention with reference to the foregoing embodiments, for a person skilled in the art, it still may be used
Modified with to the technical scheme described in foregoing embodiments, or equivalent is carried out to which part technical characteristic.
All any modification, equivalent substitution and improvements within the spirit and principles in the present invention, made etc., should be included in of the invention
Within protection domain.
Claims (4)
1. a kind of production method of shuttle-woven fabric, it is characterised in that comprise the following steps, prepare mercerising true qualities yarn, will be above-mentioned
Yarn carries out, without slurry weaving, post processing, obtaining final product shuttle-woven fabric；The mercerising true qualities yarn is obtained by the following method：Carry out
Yarn singeing, reeling, by above-mentioned yarn in mercerizing machine mercerization finish, the alkali concn for the treatment of fluid is 35 Baume degrees, and temperature is 30
DEG C, apply tension force：Stretching 8%, the time is 10min；Speed is 1000 m/min, and the strand weight of reeling is 600g.
2. the production method of shuttle-woven fabric according to claim 1, it is characterised in that also include mercerising yarn before weaving
The step that line is placed in the warp beam of loom or beam of a loom by required size.
3. the production method of shuttle-woven fabric according to claim 1, it is characterised in that described post processing is the water of fabric
Step is washed, its temperature is 80 DEG C, time 20min, then washes 10min with cold water；After washing, fabric is dried.
4. the production method of shuttle-woven fabric according to claim 3, it is characterised in that the temperature of the drying is 140 DEG C,
Speed is 15m/min, and the time is 5min.