CN106400261A - Production method of woven fabrics - Google Patents
Production method of woven fabrics Download PDFInfo
- Publication number
- CN106400261A CN106400261A CN201611173364.5A CN201611173364A CN106400261A CN 106400261 A CN106400261 A CN 106400261A CN 201611173364 A CN201611173364 A CN 201611173364A CN 106400261 A CN106400261 A CN 106400261A
- Authority
- CN
- China
- Prior art keywords
- yarn
- production method
- shuttle
- woven fabric
- mercerising
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method of woven fabrics. The production method comprises the following steps of: preparing mercerized natural-color yarns, and carrying out non-size weaving and aftertreatment on the yarns to obtain woven fabrics; the mercerized natural-color yarns are prepared by the following steps of: carrying out singeing and reeling on the yarns, and carrying out mercerizing treatment on the yarns in a mercerizing machine, wherein the alkaline concentration of treating fluid is 35 baume degrees and the temperature is 30 DEG C; and applying tension, wherein the drawing percent is 8%, the time is 10 minutes, the speed is 1000m/min and the twisting weight of reeling is 600g. The production method disclosed by the invention has the advantages of shortened process flow and saved production cost, and is especially beneficial to environmental protection.
Description
Technical field
A kind of a kind of the present invention relates to textile technology field, in particular it relates to production method of shuttle-woven fabric.
Background technology
During shuttle-woven fabric weaving, due to the friction of weaving process to be born, surface can produce filoplume to yarn, bear relatively simultaneously
Strong tensile force, thus need through sizing process before weaving, to improve yarn strength and surface smoothness, but current use
The most mixed slurry for starch and PVA type of slurry, be also easy to produce waste water after desizing, cause environmental pollution, in this situation
Under, I takes charge of through years of researches, develops the production technology of slurry-free shuttle-woven fabric（Obtain license at present）, in conjunction with existing
The zero-discharge production process that row mercerising produces, the present invention mainly applies for that the true qualities mercerizing thread that Sustainable use zero-emission produces is exempted from
Slurry is weaved, thus obtaining a kind of production method of the shuttle-woven fabric that complete zero-emission produces.
Content of the invention
The present invention mainly overcomes the pollution problem in existing shuttle-woven fabric weaving, there is provided a kind of shuttle-woven fabric of environmental protection
Production method.
In order to solve above-mentioned technical problem, the invention provides following technical scheme：
A kind of production method of shuttle-woven fabric, comprises the following steps, and prepares mercerising true qualities yarn, above-mentioned yarn is carried out no slurry
Weaving, post processing, obtain final product shuttle-woven fabric；Described mercerising true qualities yarn is obtained by the following method：Carry out yarn singeing, reeling,
By above-mentioned yarn in mercerizing range mercerization finish, the alkali concn for the treatment of fluid is 35 Baume degrees, and temperature is 30 DEG C, applies tension force：Draw
Stretch 8%, the time is 10min；Speed is 1000 m/min, and the strand of reeling is 600g again.Further, the most also wrap before weaving
Include the step also including mercerized yarn being placed in the warp beam of loom or beam of a loom by required size.Specifically, described post processing
For the water-washing step of fabric, its temperature is 80 DEG C, time 20 min, then washes 10min with cold water；After washing, fabric is dried.Tool
Body ground, the temperature of described drying is 140 DEG C, and speed is 15m/min, and the time is 5min.
The production method of shuttle-woven fabric proposed by the invention has the advantages that：
1st, procedure proposed by the invention is simple, each step is all optimized, and has fully demonstrated with simple process
Prepare the advantage of high quality of products.
2nd, adopt this method the shortcoming that the fabric of preparation can avoid the easy staining of yarn after arrangement.
3rd, adopt the method for sorting of the present invention, the mercerising true qualities yarn strength after mercerization finish and surface hairiness permissible
Reach requirements of weaving process, can be directly used for the production of slurry-free shuttle-woven fabric；Because being freeed using zero-emission in mercerizing thread production process
Product method, so avoiding discharge of wastewater, achieves the recovery of alkali lye and heat energy again；No in the production process of slurry shuttle-woven fabric
Avoid starching, desizing method, decrease discharge of wastewater it is achieved that environmental protection.
Specific embodiment
Embodiment 1
The production method of shuttle-woven fabric, comprises the following steps, and prepares mercerising true qualities yarn, above-mentioned yarn is carried out no slurry and knits
Make, post-process, obtain final product shuttle-woven fabric；Described mercerising true qualities yarn is obtained by the following method：Carry out yarn singeing, reeling, will
Above-mentioned yarn mercerization finish in mercerizing range, the alkali concn for the treatment of fluid is 35 Baume degrees, and temperature is 30 DEG C, applies tension force：Stretching
8%, the time is 10min；Speed is 1000 m/min, and the strand of reeling is 600g again.
Embodiment 2
The production method of shuttle-woven fabric, comprises the following steps, and prepares mercerising true qualities yarn, above-mentioned yarn is carried out no slurry and knits
Make, post-process, obtain final product shuttle-woven fabric；Before weaving, mercerized yarn is placed on warp beam or the beam of a loom of loom by required size；Institute
State mercerising true qualities yarn to be obtained by the following method：Carry out yarn singeing, reeling, at above-mentioned yarn mercerising in mercerizing range
Reason, the alkali concn for the treatment of fluid is 35 Baume degrees, and temperature is 30 DEG C, applies tension force：Stretching 8%, the time is 10min；Speed is
1000 m/min, the strand of reeling is 600g again.
Embodiment 3
The production method of shuttle-woven fabric, comprises the following steps, and prepares mercerising true qualities yarn, above-mentioned yarn is carried out no slurry and knits
Make, post-process, obtain final product shuttle-woven fabric；Described mercerising true qualities yarn is obtained by the following method：Carry out yarn singeing, reeling, will
Above-mentioned yarn mercerization finish in mercerizing range, the alkali concn for the treatment of fluid is 35 Baume degrees, and temperature is 30 DEG C, applies tension force：Stretching
8%, the time is 10min；Speed is 1000 m/min, and the strand of reeling is 600g again.Described post processing is the washing step of fabric
Suddenly, its temperature is 80 DEG C, time 20 min, then washes 10min with cold water；After washing, fabric is dried.
Embodiment 4
The production method of shuttle-woven fabric, comprises the following steps, and prepares mercerising true qualities yarn, above-mentioned yarn is carried out no slurry and knits
Make, post-process, obtain final product shuttle-woven fabric；Described mercerising true qualities yarn is obtained by the following method：Carry out yarn singeing, reeling, will
Above-mentioned yarn mercerization finish in mercerizing range, the alkali concn for the treatment of fluid is 35 Baume degrees, and temperature is 30 DEG C, applies tension force：Stretching
8%, the time is 10min；Speed is 1000 m/min, and the strand of reeling is 600g again.Further, the most also include before weaving
Also include step mercerized yarn being placed in the warp beam of loom or beam of a loom by required size.Specifically, described post processing is
The water-washing step of fabric, its temperature is 80 DEG C, time 20 min, then washes 10min with cold water；After washing, fabric is dried.Specifically
Ground, the temperature of described drying is 140 DEG C, and speed is 15m/min, and the time is 5min.
The procedure of the present embodiment is simple, each step is all optimized, and has fully demonstrated with simple process system
The advantage of standby high quality of products.Adopt this method the shortcoming that the fabric of preparation can avoid the easy staining of yarn after arrangement.Using this
The method for sorting of invention, the mercerising true qualities yarn strength after mercerization finish and surface hairiness can reach requirements of weaving process, can
It is directly used in the production of slurry-free shuttle-woven fabric；Because adopting zero-emission production method in mercerizing thread production process, avoid
Discharge of wastewater, achieves the recovery of alkali lye and heat energy again；No avoid starching, desizing in the production process of slurry shuttle-woven fabric
Process, decreases discharge of wastewater it is achieved that environmental protection.
Finally it should be noted that：The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention,
Although being described in detail to the present invention with reference to the foregoing embodiments, for a person skilled in the art, it still may be used
To modify to the technical scheme described in foregoing embodiments, or equivalent is carried out to wherein some technical characteristics.
All any modification, equivalent substitution and improvement within the spirit and principles in the present invention, made etc., should be included in the present invention's
Within protection domain.
Claims (4)
1. a kind of production method of shuttle-woven fabric, it is characterised in that comprising the following steps, prepares mercerising true qualities yarn, will be above-mentioned
Yarn carries out no slurry weaving, post processing, obtains final product shuttle-woven fabric；Described mercerising true qualities yarn is obtained by the following method：Carry out
Yarn singeing, reeling, by above-mentioned yarn in mercerizing range mercerization finish, the alkali concn for the treatment of fluid is 35 Baume degrees, and temperature is 30
DEG C, apply tension force：Stretching 8%, the time is 10min；Speed is 1000m/min, and the strand of reeling is 600g again.
2. the production method of shuttle-woven fabric according to claim 1 is it is characterised in that also include mercerising yarn before weaving
Line is placed in the step in the warp beam of loom or beam of a loom by required size.
3. the production method of shuttle-woven fabric according to claim 1 is it is characterised in that described post processing is the water of fabric
Wash step, its temperature is 80 DEG C, time 20min, then washes 10min with cold water；After washing, fabric is dried.
4. shuttle-woven fabric according to claim 3 production method it is characterised in that described drying temperature be 140 DEG C,
Speed is 15m/min, and the time is 5min.