CN106753705A - A kind of line cuts open grout additive and a kind of line cuts open method - Google Patents
A kind of line cuts open grout additive and a kind of line cuts open method Download PDFInfo
- Publication number
- CN106753705A CN106753705A CN201611032875.5A CN201611032875A CN106753705A CN 106753705 A CN106753705 A CN 106753705A CN 201611032875 A CN201611032875 A CN 201611032875A CN 106753705 A CN106753705 A CN 106753705A
- Authority
- CN
- China
- Prior art keywords
- cuts open
- mortar
- line
- grout additive
- additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Grout additive is cutd open this application discloses a kind of line and a kind of line cuts open method, wherein, the line cuts open grout additive to be included：Viscosity modifier, dispersant and defoamer.The above-mentioned line that the application is provided cuts open grout additive and a kind of line cuts open method, the viscosity of mortar can be reduced due to viscosity modifier therein, dispersant can reduce the sedimentation of mortar, maintain the cutting force of mortar, reduce deposition and lower ingot is carried, ensure cut quality, defoamer can eliminate the bubble of generation, therefore this line cuts open grout additive can reduce use cost and loss from spoilage, make cut surface stria even width, flatness is high, improve the performance of mortar, increase mortar service life, and the performance stabilization in Various Seasonal, foaminess is low, it is readily cleaned using rear silico briquette surface.
Description
Technical field
The invention belongs to field of photovoltaic technology, more particularly to a kind of line cuts open grout additive and a kind of line cuts open method.
Background technology
The method for maintaining mortar performance and service life in the market is all when mortar is prepared or in cutting liquid
In add dispersant, surfactant and metal corrosion inhibitor etc., it is polyethylene glycol and carbonization that line cuts open machine and uses mortar now
Silica flour carries out preparation and puts, and with the increase using knife number, mortar viscosity rises, and mobility is deteriorated, for the carbonization of effective cutting
Silica flour tails off；During the use of mortar, due to the entrance of the impurity such as material powder, moisture and copper and iron bits, the dispersiveness of mortar
Reduce, cause to produce and precipitate or be adsorbed in machine part surface, scattered carborundum is reduced in mortar, and cutting force declines.
The major defect of the above method includes：Relatively costly, dispersant has been added in the preparation of sand, prepares mortar again
Addition causes to waste；Using effect is poor, and performance when new mortar early stage is used remains fine, and the dispersant being added to and surface are lived
Property the role very little such as agent, and with the accumulation of use time, the additive of addition is because of chemical reaction and mechanical damage, quilt
Depleted, mortar performance declines and fails；In addition, the change of viscosity can not be adjusted.
The content of the invention
To solve the above problems, cut open grout additive the invention provides a kind of line and a kind of line cuts open method, can reduce
Use cost and loss from spoilage, make cut surface stria even width, and flatness is high, improve the performance of mortar, increase mortar
Performance stabilization in service life, and Various Seasonal, foaminess is low, is readily cleaned using rear silico briquette surface.
A kind of line that the present invention is provided cuts open grout additive, including：
Viscosity modifier, dispersant and defoamer.
Preferably, in above-mentioned line cuts open grout additive,
The viscosity modifier is glycerine and/or 1,3-PD；
The dispersant is triethanolamine oleate and/or sorbitan ester；
The defoamer is dimethyl polysiloxane and/or diethyl based polysiloxane and/or Methylethyl polysiloxanes.
Preferably, in above-mentioned line cuts open grout additive,
The proportion of the viscosity modifier is 95% to 96%；
The proportion of the dispersant is 2% to 3%；
The proportion of the defoamer is 1% to 2%.
Preferably, in above-mentioned line cuts open grout additive,
Also including metal corrosion inhibitor that proportion is 0.5% to 1%.
Preferably, in above-mentioned line cuts open grout additive,
The metal corrosion inhibitor is dodecenylsuccinic acid and/or cetyl monomethyl succinate and/or oxidation
Petrolatum derivative.
A kind of line that the present invention is provided cuts open method, during cuing open online, the line described in as above any one is cutd open into mortar addition
Agent is added in mortar.
Preferably, in above-mentioned line cuts open method, mortar is cutd open to account for the line that mortar proportion is 0.2% to 0.6%
Additive is added in mortar.
By foregoing description, the above-mentioned line that the present invention is provided cuts open grout additive, because the line cuts open grout additive
Including：Viscosity modifier, dispersant and defoamer, viscosity modifier therein can reduce the viscosity of mortar, and dispersant can
The sedimentation of mortar is reduced, the cutting force of mortar is maintained, is reduced deposition and the carrying of lower ingot, it is ensured that cut quality, defoamer can disappear
Except the bubble for producing, therefore this line cut open grout additive and can reduce use cost and loss from spoilage, make cut surface stria wide
Degree is uniform, and flatness is high, improves the performance of mortar, increases mortar service life, and performance in Various Seasonal is steady
Fixed, foaminess is low, is readily cleaned using rear silico briquette surface.
Brief description of the drawings
In order to illustrate more clearly about the embodiment of the present invention or technical scheme of the prior art, below will be to embodiment or existing
The accompanying drawing to be used needed for having technology description is briefly described, it should be apparent that, drawings in the following description are only this
Inventive embodiment, for those of ordinary skill in the art, on the premise of not paying creative work, can also basis
The accompanying drawing of offer obtains other accompanying drawings.
Fig. 1 cuts open the schematic diagram of grout additive for the first line that the embodiment of the present application is provided.
Specific embodiment
Core concept of the invention is that a kind of line of offer cuts open grout additive and a kind of line cuts open method, can reduce and use
Cost and loss from spoilage, make cut surface stria even width, and flatness is high, improve the performance of mortar, increase mortar and use
Performance stabilization in life-span, and Various Seasonal, foaminess is low, is readily cleaned using rear silico briquette surface.
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation is described, it is clear that described embodiment is only a part of embodiment of the invention, rather than whole embodiments.It is based on
Embodiment in the present invention, it is every other that those of ordinary skill in the art are obtained under the premise of creative work is not made
Embodiment, belongs to the scope of protection of the invention.
The first line that the embodiment of the present application is provided cuts open grout additive as shown in figure 1, Fig. 1 is provided for the embodiment of the present application
The first line cut open the schematic diagram of grout additive, the line cuts open grout additive to be included：Viscosity modifier 1, dispersant 2 and froth breaking
Agent 3.
It should be noted that above-mentioned various composition is added in the container that can be stirred, addition sequence can be, but not limited to
Size is sequentially added in proportion, and the residing environment temperature of operation can be 25 DEG C of room temperature, can just be applied after fully stirring evenly.Tool
Body, the range of speeds of whipping process can be set for 40r/min to 80r/min, the time range of stirring is 20 minutes to 30
Minute.These different types of liquid are sufficiently mixed uniformly using whipping process, so that each composition therein can fill
Respective effect is waved in distribution.
By foregoing description, above-mentioned the first line that the embodiment of the present application is provided cuts open grout additive, due to including：
By viscosity modifier, dispersant and defoamer, viscosity modifier therein can reduce the viscosity of mortar, and dispersant can be reduced
The sedimentation of mortar, maintains the cutting force of mortar, reduces deposition and the carrying of lower ingot, it is ensured that cut quality, defoamer can eliminate product
Raw bubble, therefore, it is possible to reduce use cost and loss from spoilage, makes cut surface stria even width, and flatness is high, improves sand
The performance of slurry, increases mortar service life, and the performance stabilization in Various Seasonal, and foaminess is low, uses rear silico briquette
Surface is readily cleaned.
Second line that the embodiment of the present application is provided cuts open grout additive, is to cut open grout additive in above-mentioned the first line
On the basis of, also including following technical characteristic：
The viscosity modifier is glycerine and/or 1,3-PD, that is to say, that can be one kind therein or two
Kind, it is not intended to limit herein, furthermore, it is also possible to be the other kinds of polyalcohol with viscosity regulatory function；
The dispersant is triethanolamine oleate and/or sorbitan ester, that is to say, that can be it is therein a kind of or
Two kinds, it is not intended to limit herein, moreover, it is also possible to be other kinds of non-ionic dispersing agent that can be miscible with mortar, can
The sedimentation of mortar is reduced, the cutting force of mortar is maintained, is reduced deposition and the carrying of lower ingot, it is ensured that cut quality；
The defoamer be dimethyl polysiloxane and/or diethyl based polysiloxane and/or Methylethyl polysiloxanes,
That is, it is possible to be it is therein it is a kind of, two kinds or three kinds, be not intended to limit herein, can also be it is other kinds of can be with sand
Any miscible and stable existence material of slurry, can reduce during mortar use or eliminate foam, eliminate viscosity regulation
Agent and the negative effect of dispersant, improve permeability and mobility of the mortar in cutting seam.
The third line that the embodiment of the present application is provided cuts open grout additive, is to cut open grout additive in above-mentioned second line
On the basis of, also including following technical characteristic：
The proportion of the viscosity modifier is 95% to 96%；
The proportion of the dispersant is 2% to 3%；
The proportion of the defoamer is 1% to 2%.
It should be noted that viscosity modifier is the material for playing main effect, therefore accounting is maximum, and a small amount of point
Powder can just give full play to peptizaiton, in addition, defoamer also only needs to the bubble that less ratio is just enough to eliminate generation.
The 4th kind of line that the embodiment of the present application is provided cuts open grout additive, is to cut open grout additive in above-mentioned the third line
On the basis of, also including following technical characteristic：
Also including metal corrosion inhibitor that proportion is 0.5% to 1%.
The 5th kind of line that the embodiment of the present application is provided cuts open grout additive, is to cut open grout additive in above-mentioned 4th kind of line
On the basis of, also including following technical characteristic：
The metal corrosion inhibitor is dodecenylsuccinic acid and/or cetyl monomethyl succinate and/or oxidation
Petrolatum derivative.
That is, can be it is therein it is a kind of, two kinds or three kinds, be not intended to limit herein.
The first line that the embodiment of the present application is provided cuts open method, is during cuing open online, by the line described in as above any one
Grout additive is cutd open to be added in mortar.Specifically, during the line that may apply to silica-based solar cell is cutd open, according to mortar
Actually used situation (viscosity, precipitation capacity) adds above-mentioned additive, ensure that the optimization of mortar performance, steady using proterties
Fixed, foaminess is low, is readily cleaned using rear silico briquette surface, and mortar ensure that product are cut on the surface of silico briquette in service life latter stage
Matter, cut surface stria is thinner, and flatness is higher, and stabilization is used under Various Seasonal, it is seen that prior relative to of the prior art
The scheme added additives in mortar is more advantageous.
Second line that the embodiment of the present application is provided cuts open method, is on the basis of above-mentioned the first line cuts open method, also to wrap
Include following technical characteristic：
Grout additive is cutd open accounting for the line that mortar proportion is 0.2% to 0.6% to be added in mortar.
The present embodiment can be added with the change of real-time detection viscosity when viscosity is excessive, and actual interpolation amount can basis
Use requirement is carried out, can be by viscosity number reduction by 200 to 500dPas.In this case, it is possible to increase the use of mortar 50%
In the life-span, reduce the workload when mortar is prepared.
The foregoing description of the disclosed embodiments, enables professional and technical personnel in the field to realize or uses the present invention.
Various modifications to these embodiments will be apparent for those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, the present invention
The embodiments shown herein is not intended to be limited to, and is to fit to and principles disclosed herein and features of novelty phase one
The scope most wide for causing.
Claims (7)
1. a kind of line cuts open grout additive, it is characterised in that including：Viscosity modifier, dispersant and defoamer.
2. line according to claim 1 cuts open grout additive, it is characterised in that
The viscosity modifier is glycerine and/or 1,3-PD；
The dispersant is triethanolamine oleate and/or sorbitan ester；
The defoamer is dimethyl polysiloxane and/or diethyl based polysiloxane and/or Methylethyl polysiloxanes.
3. line according to claim 2 cuts open grout additive, it is characterised in that
The proportion of the viscosity modifier is 95% to 96%；
The proportion of the dispersant is 2% to 3%；
The proportion of the defoamer is 1% to 2%.
4. line according to claim 3 cuts open grout additive, it is characterised in that
Also including metal corrosion inhibitor that proportion is 0.5% to 1%.
5. line according to claim 4 cuts open grout additive, it is characterised in that
The metal corrosion inhibitor is dodecenylsuccinic acid and/or cetyl monomethyl succinate and/or petroleum oxidate
Fat derivative.
6. a kind of line cuts open method, it is characterised in that during cuing open online, the line as described in claim any one of 1-5 is cutd open into sand
Slurry additive is added in mortar.
7. a kind of line according to claim 6 cuts open method, it is characterised in that with account for mortar proportion as 0.2% to
0.6% line cuts open grout additive and is added in mortar.