CN106752239A - 一种外墙柔性耐水腻子及其制备方法 - Google Patents
一种外墙柔性耐水腻子及其制备方法 Download PDFInfo
- Publication number
- CN106752239A CN106752239A CN201611043442.XA CN201611043442A CN106752239A CN 106752239 A CN106752239 A CN 106752239A CN 201611043442 A CN201611043442 A CN 201611043442A CN 106752239 A CN106752239 A CN 106752239A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- water proof
- flexible water
- wall flexible
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种外墙柔性耐水腻子及其制备方法,由下列重量份原料制成:水泥30‑50份、累托石粉5‑7份、凹凸棒土5‑7份、电气石粉3‑6份、蛭石粉5‑7份、阳起石粉3‑6份、灰钙粉1‑3份、粉煤灰3‑6份、固体丙烯酸可再分散胶粉10‑12份、环氧乙烷2‑4份、缓凝剂1‑3份、羟丙基甲基纤维素0.1‑0.3份、憎水剂0.3‑0.5份、剑麻纤维0.3‑0.5份、淀粉醚0.1‑0.3份、柠檬酸0.5‑0.6份、有机硅粉末0.5‑0.7份、复合助剂2‑5份。本发明的外墙柔性耐水腻子,具有优异的耐水、耐酸碱性,不会出现粉化、脱落、起壳现象,对环境无污染,粘接强度高,能适应环境变化而不自裂。
Description
技术领域
本发明涉及建筑材料技术领域,尤其涉及一种外墙柔性耐水腻子及其制备方法。
背景技术
腻子是建筑装饰材料的一种,是用来墙面修补找平的一种基材,为下一步装饰打下良好的基础。腻子为内墙和外墙两种,外墙腻子要抵抗风吹日晒所以胶性大、强度高,环保指数稍低。内墙腻子综合指数较好,健康环保,所以内墙不外用,外墙不内用。建筑工程对外墙腻子的质量要求,主要体现在粘结强度、初期抗开裂性及动态抗开裂性等指标上,现有外墙腻子普遍存在龟裂、起壳、脱落,耐水性差的问题。
发明内容
本发明的目的是克服现有技术的不足,提供一种外墙柔性耐水腻子,具有优异的耐水、耐酸碱性,被水浸泡后不会出现粉化、脱落、起壳的现象,对环境无污染,粘接强度高,与基层结合牢固,施工性能好,良好的柔韧性和较小的收缩率,使腻子层能适应环境的变化而不自裂,与弹性乳胶漆结合力强。
为了实现上述目的,本发明采用如下技术方案:
一种外墙柔性耐水腻子,由下列重量份的原料制成:水泥30-50份、累托石粉5-7份、凹凸棒土5-7份、电气石粉3-6份、蛭石粉5-7份、阳起石粉3-6份、灰钙粉1-3份、粉煤灰3-6份、固体丙烯酸可再分散胶粉10-12份、环氧乙烷2-4份、缓凝剂1-3份、羟丙基甲基纤维素0.1-0.3份、憎水剂0.3-0.5份、剑麻纤维0.3-0.5份、淀粉醚0.1-0.3份、柠檬酸0.5-0.6份、有机硅粉末0.5-0.7份、复合助剂2-5份。
所述的复合助剂由以下方法制备:按重量份比例将松香3份、环氧大豆油5份、单硬脂酸甘油酯2份,在160℃熔融共混均匀,然后将温度调至100℃,加入丙烯酸5份、硅烷偶联剂KH-570 2份搅拌2小时,即得。
所述的外墙柔性耐水腻子的制备方法,包括以下制备步骤:
(1)将水泥、累托石粉、蛭石粉、阳起石粉按配比称量配料,依次放入混合机中,经充分搅拌,混合均匀后加入粉碎机粉碎至小于120目,得混合物A;
(2)将凹凸棒土、电气石粉、灰钙粉、粉煤灰按配比称量配料,依次放入混合机中,经充分搅拌,混合均匀后进行研磨5-10分钟;再按配比量加入羟丙基甲基纤维素和剑麻纤维,研磨5-10分钟,得混合物B;
(3)将固体丙烯酸可再分散胶粉按配比量放入高速分散机上充分分散,在600r/min转速下依次加入按配比称量的环氧乙烷、缓凝剂,在1000-1200r/min转速下依次加入剩余原料,将所得物料搅拌均匀,得混合物C;
(4)将混合物A、混合物B和混合物C搅拌均匀,过筛即可。
与已有技术相比,本发明的有益效果如下:
本发明的外墙柔性耐水腻子,通过调整各组份的含量配比,制备的腻子具有优异的耐水、耐酸碱性,被水浸泡后不会出现粉化、脱落、起壳的现象,对环境无污染,粘接强度高,与基层结合牢固,施工性能好,良好的柔韧性和较小的收缩率,使腻子层能适应环境的变化而不自裂,与弹性乳胶漆结合力强;添加电气石粉,电气石是一种价格低廉容易获取的天然矿物,电气石能显著提高粘合强度,同时按一定比例与柠檬酸结合,能大大提高耐酸碱性,同时具有吸附有害气体的作用;添加复合助剂,复合助剂是一种成膜物质,可以增强产品的柔韧性、耐水性;固体丙烯酸可再分散胶粉具有突出的粘结强度,可提高粘合剂的柔性,并赋予产品优良的耐碱性;有机硅粉末具有良好的防水性能。
具体实施方式
以下结合实施例对本发明作进一步的说明,但本发明不仅限于这些实施例,在未脱离本发明宗旨的前提下,所作的任何改进均落在本发明的保护范围之内。
实施例1:
一种外墙柔性耐水腻子,由下列重量份的原料制成:水泥50份、累托石粉5份、凹凸棒土5份、电气石粉3份、蛭石粉5份、阳起石粉5份、灰钙粉2份、粉煤灰5份、固体丙烯酸可再分散胶粉10份、环氧乙烷2份、缓凝剂1份、羟丙基甲基纤维素0.1份、憎水剂0.3份、剑麻纤维0.3份、淀粉醚0.1份、柠檬酸0.5份、有机硅粉末0.5份、复合助剂2份。
所述的复合助剂由以下方法制备:按重量份比例将松香3份、环氧大豆油5份、单硬脂酸甘油酯2份,在160℃熔融共混均匀,然后将温度调至100℃,加入丙烯酸5份、硅烷偶联剂KH-570 2份搅拌2小时,即得。
所述的外墙柔性耐水腻子的制备方法,包括以下制备步骤:
(1)将水泥、累托石粉、蛭石粉、阳起石粉按配比称量配料,依次放入混合机中,经充分搅拌,混合均匀后加入粉碎机粉碎至小于120目,得混合物A;
(2)将凹凸棒土、电气石粉、灰钙粉、粉煤灰按配比称量配料,依次放入混合机中,经充分搅拌,混合均匀后进行研磨5分钟;再按配比量加入羟丙基甲基纤维素和剑麻纤维,研磨10分钟,得混合物B;
(3)将固体丙烯酸可再分散胶粉按配比量放入高速分散机上充分分散,在600r/min转速下依次加入按配比称量的环氧乙烷、缓凝剂,在1000r/min转速下依次加入剩余原料,将所得物料搅拌均匀,得混合物C;
(4)将混合物A、混合物B和混合物C搅拌均匀,过筛即可。
实施例2:
一种外墙柔性耐水腻子,由下列重量份的原料制成:水泥40份、累托石粉6份、凹凸棒土6份、电气石粉5份、蛭石粉6份、阳起石粉5份、灰钙粉2份、粉煤灰5份、固体丙烯酸可再分散胶粉11份、环氧乙烷3份、缓凝剂2份、羟丙基甲基纤维素0.2份、憎水剂0.4份、剑麻纤维0.4份、淀粉醚0.2份、柠檬酸0.6份、有机硅粉末0.7份、复合助剂5份。
所述的复合助剂由以下方法制备:按重量份比例将松香3份、环氧大豆油5份、单硬脂酸甘油酯2份,在160℃熔融共混均匀,然后将温度调至100℃,加入丙烯酸5份、硅烷偶联剂KH-570 2份搅拌2小时,即得。
所述的外墙柔性耐水腻子的制备方法,包括以下制备步骤:
(1)将水泥、累托石粉、蛭石粉、阳起石粉按配比称量配料,依次放入混合机中,经充分搅拌,混合均匀后加入粉碎机粉碎至小于120目,得混合物A;
(2)将凹凸棒土、电气石粉、灰钙粉、粉煤灰按配比称量配料,依次放入混合机中,经充分搅拌,混合均匀后进行研磨5-10分钟;再按配比量加入羟丙基甲基纤维素和剑麻纤维,研磨5-10分钟,得混合物B;
(3)将固体丙烯酸可再分散胶粉按配比量放入高速分散机上充分分散,在600r/min转速下依次加入按配比称量的环氧乙烷、缓凝剂,在1200r/min转速下依次加入剩余原料,将所得物料搅拌均匀,得混合物C;
(4)将混合物A、混合物B和混合物C搅拌均匀,过筛即可。
Claims (3)
1.一种外墙柔性耐水腻子,其特征在于:由下列重量份的原料制成:水泥30-50份、累托石粉5-7份、凹凸棒土5-7份、电气石粉3-6份、蛭石粉5-7份、阳起石粉3-6份、灰钙粉1-3份、粉煤灰3-6份、固体丙烯酸可再分散胶粉10-12份、环氧乙烷2-4份、缓凝剂1-3份、羟丙基甲基纤维素0.1-0.3份、憎水剂0.3-0.5份、剑麻纤维0.3-0.5份、淀粉醚0.1-0.3份、柠檬酸0.5-0.6份、有机硅粉末0.5-0.7份、复合助剂2-5份。
2.根据权利要求1所述的外墙柔性耐水腻子,其特征在于:所述的复合助剂由以下方法制备:按重量份比例将松香3份、环氧大豆油5份、单硬脂酸甘油酯2份,在160℃熔融共混均匀,然后将温度调至100℃,加入丙烯酸5份、硅烷偶联剂KH-5702份搅拌2小时,即得。
3.根据权利要求1或2所述的外墙柔性耐水腻子的制备方法,其特征在于:包括以下制备步骤:
(1)将水泥、累托石粉、蛭石粉、阳起石粉按配比称量配料,依次放入混合机中,经充分搅拌,混合均匀后加入粉碎机粉碎至小于120目,得混合物A;
(2)将凹凸棒土、电气石粉、灰钙粉、粉煤灰按配比称量配料,依次放入混合机中,经充分搅拌,混合均匀后进行研磨5-10分钟;再按配比量加入羟丙基甲基纤维素和剑麻纤维,研磨5-10分钟,得混合物B;
(3)将固体丙烯酸可再分散胶粉按配比量放入高速分散机上充分分散,在600r/min转速下依次加入按配比称量的环氧乙烷、缓凝剂,在1000-1200r/min转速下依次加入剩余原料,将所得物料搅拌均匀,得混合物C;
(4)将混合物A、混合物B和混合物C搅拌均匀,过筛即可。