CN106747338A - A kind of medical ceramic material and preparation method thereof - Google Patents

A kind of medical ceramic material and preparation method thereof Download PDF

Info

Publication number
CN106747338A
CN106747338A CN201611031315.8A CN201611031315A CN106747338A CN 106747338 A CN106747338 A CN 106747338A CN 201611031315 A CN201611031315 A CN 201611031315A CN 106747338 A CN106747338 A CN 106747338A
Authority
CN
China
Prior art keywords
powder
parts
ceramic material
mixture
melilite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201611031315.8A
Other languages
Chinese (zh)
Inventor
不公告发明人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhengzhou Renhong Pharmaceutical Technology Co Ltd
Original Assignee
Zhengzhou Renhong Pharmaceutical Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhengzhou Renhong Pharmaceutical Technology Co Ltd filed Critical Zhengzhou Renhong Pharmaceutical Technology Co Ltd
Priority to CN201611031315.8A priority Critical patent/CN106747338A/en
Publication of CN106747338A publication Critical patent/CN106747338A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of medical ceramic material, it is made up of according to weight portion following raw material：29 parts of modified 5 13 parts of melilite powder, 38 parts of calcium carbonate powder, 25 parts of Nano Silver powder, 16 parts of pearl powder, 5 11 parts of silica flour, 8 16 parts of vegetable oil, 26 parts of Zirconium oxide powder, 37 parts of alumina powder, 5 10 parts of dolomite powder, 3 11 parts of magnesium oxide powder and bone meal.The present invention also disclosed the preparation method of the ceramic material.Raw material sources of the present invention are extensive, preparation process is simple, it is adaptable to the large-scale production of industry；Not only hardness is big and good biocompatibility for ceramic material prepared by the present invention, and acid-proof alkaline and good anti-bacterial effect, it is adaptable to prepare artificial tooth or bone, wide market.

Description

A kind of medical ceramic material and preparation method thereof
Technical field
The present invention relates to a kind of ceramic material, specifically a kind of medical ceramic material.
Background technology
With the development of science and technology, various new materials emerge in large numbers like the mushrooms after rain, ceramic material is exactly one of which.Ceramic material Material is the class Inorganic Non-metallic Materials being made through overmolding or high-temperature calcination with natural or synthetic compound, and the species of ceramics is very Many, purposes is different.With the development of modern science technology, many new ceramic kinds are occurred in that again in the last hundred years.They are no longer Using or be rarely employed the traditional ceramics raw material such as clay, feldspar, quartz, but use other special materials, or even be expanded to non- The scope of silicate and non-oxidized substance, medical ceramic material is exactly one of which, and medical ceramic material is usually as artificial bone The materials such as bone, artificial tooth.Although existing medical ceramic material is harmless to people and use intensity, biocompatibility, dielectricity Can be good with thermal stability, but existing medical ceramic material does not reach people's also in acid and alkali-resistance effect and antibacterial effect Expected, this is accomplished by people and continues to study.
The content of the invention
It is an object of the invention to provide a kind of medical ceramic material, to solve the problems, such as to be proposed in above-mentioned background technology.
To achieve the above object, the present invention provides following technical scheme：
A kind of medical ceramic material, is made up of following raw material according to weight portion：Modified 5-13 parts of melilite powder, calcium carbonate Powder 3-8 parts, 2-5 parts of Nano Silver powder, pearl powder 1-6 parts, silica flour 5-11 parts, vegetable oil 8-16 parts, Zirconium oxide powder 2-6 Part, alumina powder 3-7 parts, 5-10 parts, magnesium oxide powder 3-11 parts and bone meal 2-9 parts of dolomite powder.
As further scheme of the invention：Modified melilite powder is calcined using melilite under 350-460 degrees Celsius 30-60 minutes, the product after roasting soaked 10-25 minutes in being put into ethanol, then dries and grind into powder is obtained.
As further scheme of the invention：Bone meal using fishbone dust, bovine bone powder, lamb bone meal and Os Sus domestica powder one kind or Various mixtures, vegetable oil is using one or more the mixture in soybean oil, rapeseed oil and olive oil.
The preparation method of the medical ceramic material, comprises the following steps that：
Step one, ball milling is put into by alumina powder, Zirconium oxide powder, calcium carbonate powder, Nano Silver powder and pearl powder Ground 30-90 minutes in machine, obtain the first mixture；
Step 2, modified melilite powder, silica flour, vegetable oil and dolomite powder is dispersed in absolute ethyl alcohol and forms mixed Slurry is closed, is then dried and be can obtain sintering aid；
Step 3, the second mixed solution is mixed to get by the first mixture, magnesium oxide powder and bone meal, then mixed to second Solution is closed to be slowly added dropwise ammoniacal liquor and be slowly stirred, until the pH value of the second mixed solution is 7.8-8.9, then by second Mixed solution is put into reactor and is incubated 15-40 minutes under 1580-1750 degrees Celsius, obtains the 3rd mixture；
Step 4, the 3rd mixture and sintering aid is put into compacting is sintered in hot pressing die, then cooling down Can obtain finished product.
Compared with prior art, the beneficial effects of the invention are as follows：Raw material sources of the present invention extensively, fit by preparation process is simple For the large-scale production of industry；Not only hardness is big and good biocompatibility for ceramic material prepared by the present invention, and acid and alkali-resistance Performance and good anti-bacterial effect, it is adaptable to prepare artificial tooth or bone, wide market.
Specific embodiment
The technical scheme of this patent is described in more detail with reference to specific embodiment.
Embodiment 1
A kind of medical ceramic material, is made up of following raw material according to weight portion：Modified 5 parts of melilite powder, Paris white End 3 parts, 2 parts of Nano Silver powder, 1 part of pearl powder, 5 parts of silica flour, 8 parts of vegetable oil, 2 parts of Zirconium oxide powder, 3 parts of alumina powder, 2 parts of 5 parts of dolomite powder, 3 parts of magnesium oxide powder and bone meal.Modified melilite powder is roasted using melilite under 350 degrees Celsius Burn 30 minutes, the product after roasting soaks 10 minutes in being put into ethanol, then dries and grind into powder is obtained.
The preparation method of the medical ceramic material, comprises the following steps that：
Step one, ball milling is put into by alumina powder, Zirconium oxide powder, calcium carbonate powder, Nano Silver powder and pearl powder Ground 45 minutes in machine, obtain the first mixture；
Step 2, modified melilite powder, silica flour, vegetable oil and dolomite powder is dispersed in absolute ethyl alcohol and forms mixed Slurry is closed, is then dried and be can obtain sintering aid；
Step 3, the second mixed solution is mixed to get by the first mixture, magnesium oxide powder and bone meal, then mixed to second Solution is closed to be slowly added dropwise ammoniacal liquor and be slowly stirred, until the pH value of the second mixed solution is 7.8, then by the second mixing Solution is put into reactor and is incubated 15 minutes under 1580 degrees Celsius, obtains the 3rd mixture；
Step 4, the 3rd mixture and sintering aid is put into compacting is sintered in hot pressing die, then cooling down Can obtain finished product.
Embodiment 2
A kind of medical ceramic material, is made up of following raw material according to weight portion：Modified 8 parts of melilite powder, Paris white End 5 parts, 3 parts of Nano Silver powder, 4 parts of pearl powder, 7 parts of silica flour, 11 parts of vegetable oil, 4 parts of Zirconium oxide powder, 5 parts of alumina powder, 7 parts of 8 parts of dolomite powder, 6 parts of magnesium oxide powder and bone meal.Bone meal is planted using the mixture of fishbone dust, lamb bone meal and Os Sus domestica powder Thing oil uses soybean oil.
The preparation method of the medical ceramic material, comprises the following steps that：
Step one, ball milling is put into by alumina powder, Zirconium oxide powder, calcium carbonate powder, Nano Silver powder and pearl powder Ground 65 minutes in machine, obtain the first mixture；
Step 2, modified melilite powder, silica flour, soybean oil and dolomite powder is dispersed in absolute ethyl alcohol and forms mixed Slurry is closed, is then dried and be can obtain sintering aid；
Step 3, the second mixed solution is mixed to get by the first mixture, magnesium oxide powder and bone meal, then mixed to second Solution is closed to be slowly added dropwise ammoniacal liquor and be slowly stirred, until the pH value of the second mixed solution is 8.2, then by the second mixing Solution is put into reactor and is incubated 21 minutes under 1640 degrees Celsius, obtains the 3rd mixture；
Step 4, the 3rd mixture and sintering aid is put into compacting is sintered in hot pressing die, then cooling down Can obtain finished product.
Embodiment 3
A kind of medical ceramic material, is made up of following raw material according to weight portion：Modified 11 parts of melilite powder, Paris white 7 parts of end, 4 parts of Nano Silver powder, 5 parts of pearl powder, 10 parts of silica flour, 15 parts of vegetable oil, 6 parts of Zirconium oxide powder, alumina powder 6 Part, 9 parts of dolomite powder, 11 parts of magnesium oxide powder and 8 parts of bone meal.Modified melilite powder is taken the photograph using melilite in 350-460 It is calcined 30-60 minutes under family name's degree, the product after roasting soaks 10-25 minutes in being put into ethanol, then dries and pulverizes End obtains.Bone meal using fishbone dust, bovine bone powder, lamb bone meal and Os Sus domestica powder mixture, vegetable oil using soybean oil, rapeseed oil and Mixture in olive oil.
The preparation method of the medical ceramic material, comprises the following steps that：
Step one, ball milling is put into by alumina powder, Zirconium oxide powder, calcium carbonate powder, Nano Silver powder and pearl powder Ground 75 minutes in machine, obtain the first mixture；
Step 2, modified melilite powder, silica flour, vegetable oil and dolomite powder is dispersed in absolute ethyl alcohol and forms mixed Slurry is closed, is then dried and be can obtain sintering aid；
Step 3, the second mixed solution is mixed to get by the first mixture, magnesium oxide powder and bone meal, then mixed to second Solution is closed to be slowly added dropwise ammoniacal liquor and be slowly stirred, until the pH value of the second mixed solution is 8.6, then by the second mixing Solution is put into reactor and is incubated 36 minutes under 1720 degrees Celsius, obtains the 3rd mixture；
Step 4, the 3rd mixture and sintering aid is put into compacting is sintered in hot pressing die, then cooling down Can obtain finished product.
Comparative example
Except bone meal is not contained, remaining component of comparative example 1 and preparation method are with embodiment 1.
The product of embodiment 1-3, the product of comparative example 1 and existing product are carried out into acid and alkali-resistance and antibacterial test, test knot Fruit is shown in Table 1.
Table 1
It is acidproof It is alkaline-resisting Bacteriostasis rate (%)
Embodiment 1 By force By force 95
Embodiment 2 By force By force 98
Embodiment 3 By force By force 92
Comparative example 1 It is weak It is weak 64
Existing product Typically Typically 79
As it can be seen from table 1 the acid-proof alkaline and antibacterial effect of the product of embodiment 1-3 prepared by the present invention are much excellent In the product and existing product of comparative example 1, ceramic material prepared by the present invention is more suitable as medical ceramic material.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be in other specific forms realized.Therefore, no matter From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power Profit requires to be limited rather than described above, it is intended that all in the implication and scope of the equivalency of claim by falling Change is included in the present invention.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each implementation method is only wrapped Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should Specification an as entirety, the technical scheme in each embodiment can also be formed into those skilled in the art through appropriately combined May be appreciated other embodiment.

Claims (4)

1. a kind of medical ceramic material, it is characterised in that be made up of according to weight portion following raw material：Modified melilite powder 5-13 Part, calcium carbonate powder 3-8 parts, 2-5 parts of Nano Silver powder, pearl powder 1-6 parts, silica flour 5-11 parts, vegetable oil 8-16 parts, zirconium oxide Powder 2-6 parts, alumina powder 3-7 parts, 5-10 parts, magnesium oxide powder 3-11 parts and bone meal 2-9 parts of dolomite powder.
2. medical ceramic material according to claim 1, it is characterised in that the modified melilite powder uses melilite It is calcined 30-60 minutes under 350-460 degrees Celsius, the product after roasting soaks 10-25 minutes in being put into ethanol, then dries simultaneously And grind into powder is obtained.
3. medical ceramic material according to claim 1 and 2, it is characterised in that the bone meal uses fishbone dust, ox bone One or more mixture of powder, lamb bone meal and Os Sus domestica powder, vegetable oil is using in soybean oil, rapeseed oil and olive oil Plant or various mixtures.
4. the preparation method of a kind of medical ceramic material as described in claim 1-3 is any, it is characterised in that specific steps are such as Under：
Step one, by alumina powder, Zirconium oxide powder, calcium carbonate powder, Nano Silver powder and pearl powder input ball mill Grinding 30-90 minutes, obtains the first mixture；
Step 2, modified melilite powder, silica flour, vegetable oil and dolomite powder is dispersed in absolute ethyl alcohol and forms mixing slurry Material, is then dried and can obtain sintering aid；
Step 3, the second mixed solution is mixed to get by the first mixture, magnesium oxide powder and bone meal, then molten to the second mixing Liquid is slowly added dropwise ammoniacal liquor and is slowly stirred, until the pH value of the second mixed solution is 7.8-8.9, then by the second mixing Solution is put into reactor and is incubated 15-40 minutes under 1580-1750 degrees Celsius, obtains the 3rd mixture；
Step 4, the 3rd mixture and sintering aid is put into compacting is sintered in hot pressing die, then cooling down Obtain finished product.
CN201611031315.8A 2016-11-22 2016-11-22 A kind of medical ceramic material and preparation method thereof Withdrawn CN106747338A (en)