CN106747156A - A kind of novel high-performance glass magnesium fireproof board - Google Patents

A kind of novel high-performance glass magnesium fireproof board Download PDF

Info

Publication number
CN106747156A
CN106747156A CN201611051843.XA CN201611051843A CN106747156A CN 106747156 A CN106747156 A CN 106747156A CN 201611051843 A CN201611051843 A CN 201611051843A CN 106747156 A CN106747156 A CN 106747156A
Authority
CN
China
Prior art keywords
novel high
wooden chaff
fireproof board
performance glass
magnesia
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611051843.XA
Other languages
Chinese (zh)
Inventor
姚志英
梁永全
文彧
吴晖晖
梁丽君
梁丽明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUILIN YONGFU LONGGANG GREEN ENVIRONMENTAL PROTECTION BUILDING MATERIAL CO Ltd
Original Assignee
GUILIN YONGFU LONGGANG GREEN ENVIRONMENTAL PROTECTION BUILDING MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUILIN YONGFU LONGGANG GREEN ENVIRONMENTAL PROTECTION BUILDING MATERIAL CO Ltd filed Critical GUILIN YONGFU LONGGANG GREEN ENVIRONMENTAL PROTECTION BUILDING MATERIAL CO Ltd
Priority to CN201611051843.XA priority Critical patent/CN106747156A/en
Publication of CN106747156A publication Critical patent/CN106747156A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of novel high-performance glass magnesium fireproof board, including following mass percent component：Magnesia 30% 35%, magnesium chloride 45% 50%, wooden chaff 15% 25%, the PLASTIC LAMINATED have water-fast, sound-insulating and heat-insulating of preventing fires, energy-conserving and environment-protective, it is nonpoisonous and tasteless, can saw can follow closely can paste, long service life the characteristics of, improve the intensity and durability in Building Fire Protection region.

Description

A kind of novel high-performance glass magnesium fireproof board
Technical field
The invention belongs to Building Fire Protection field, and in particular to a kind of novel high-performance glass magnesium fireproof board.
Background technology
PLASTIC LAMINATED also known as refractory slab, scientific name are thermosetting resin-impregnated paper high-pressure laminated board, and english abbreviation is HPL （Decorative High-pressure Laminate）It is incrustation refractory building material, there is abundant surface color and polish, lines And special physical property, it is widely used in the fields such as interior decoration, furniture, kitchen cabinet, laboratory table top, exterior wall.
Green building PLASTIC LAMINATED, with prevent fires water-fast, sound-insulating and heat-insulating, energy-conserving and environment-protective, it is nonpoisonous and tasteless, can saw can follow closely can paste, The characteristics of long service life, also have the advantages that construction is fast, effect is good, low-carbon (LC) design.Rupture strength dry state state is 15Mpa, It is 22Mpa under sucting wet state, that is, intensity is higher under washing wet condition.Good thermal and insulating performance, anti-folding shock resistance is good, is Instead of the renewal product of the sheet materials such as various glued boards, density board, particieboard, plasterboard,
But present PLASTIC LAMINATED body paper is processed by melmac with phenolic resin, and Main physical property is by resin Characteristic shows, glossy good, excellent transparency, case hardness be high, wear-resisting after melmac thermoset forming, high temperature resistant, The performances such as impact resistance, surface capillary hole be small to be difficult to be contaminated, resistance to chemical reagents, water resistance, solvent resistance, flame-proofness are excellent, and machinery is strong Degree, electrical insulating property, arc resistance are good and non-aging.
The content of the invention
It is an object of the invention to provide a kind of novel high-performance glass magnesium fireproof board, the PLASTIC LAMINATED have fire prevention it is water-fast, every Sound is heat-insulated, energy-conserving and environment-protective, it is nonpoisonous and tasteless, can saw can follow closely can paste, long service life the characteristics of, improve the intensity in Building Fire Protection region And durability.
To achieve these goals, the present invention is adopted the technical scheme that：
A kind of novel high-performance glass magnesium fireproof board, including following mass percent component：
Magnesia 30%-35%, magnesium chloride 45%-50%, wooden chaff 15%-25%
Content of magnesium >=85 of described magnesia, the mesh of granularity 200,
Described magnesium chloride is block, content 95%,
Described wooden chaff is Chinese fir wood chaff, and wooden chaff does not have impurity into sawdust shape, and the rate of wooden chaff is moisture content 10%-15%
Magnesium chloride glass magnesium degree is 21 DEG C -24 DEG C（22℃）This is ignorant of any meaning really
Beneficial effect：
The invention provides a kind of novel high-performance glass magnesium fireproof board, the PLASTIC LAMINATED has prevent fires water-fast, sound-insulating and heat-insulating, energy-saving ring Protect, it is nonpoisonous and tasteless, can saw can follow closely can paste, long service life the characteristics of, improve the intensity and durability in Building Fire Protection region.
Specific embodiment
The present invention is further elaborated with reference to embodiments, but is not limitation of the invention.
A kind of novel high-performance glass magnesium fireproof board, including following mass percent component：
Magnesia 30%-35%, magnesium chloride 45%-50%, wooden chaff 15%-25%
Content of magnesium >=85 of described magnesia, the mesh of granularity 200,
Described magnesium chloride is block, content 95%,
Described wooden chaff is Chinese fir wood chaff, and wooden chaff does not have impurity into sawdust shape, and the rate of wooden chaff is moisture content 10%-15%
The optimal ratio of described magnesia is（33%）,
The optimal ratio of described magnesium chloride is（47%）,
The optimal ratio of described wooden chaff is（20%）.
Embodiment 1：
Magnesia 30%, magnesium chloride 45%, wooden chaff 25%
Content of magnesium >=85 of magnesia, the mesh of granularity 200, described magnesium chloride is block, content 95%,
Wooden chaff is Chinese fir wood chaff, and wooden chaff does not have impurity into sawdust shape, and the rate of wooden chaff is moisture content 10%-15%
Raw material is mixed according to the above ratio：Magnesia, wooden chaff will be quantified by numerical control machine and add mixer, by quantitative high purity magnesium Solution adds mixer, and stir about 3-5 minutes, the material that will be accomplished fluently was put into laminator, cuts plate by after 1 rolling of laminator Break, then the thickness of needs is reached by 2 rolling of laminator, maintained 6 hours on the plate feeding brandreth that will be molded, sheet material reaches first Phase maintenance intensity just can be with the demoulding, and sheet material is transported to warehouse natural air drying and conserved 5-7 days, and the PLASTIC LAMINATED for obtaining meets fire-protection rating will Ask.
Embodiment 2：
Magnesia 30%, magnesium chloride 50%, wooden chaff 20%,
Content of magnesium >=85 of magnesia, the mesh of granularity 200, described magnesium chloride is block, content 95%,
Wooden chaff is Chinese fir wood chaff, and wooden chaff does not have impurity into sawdust shape, and the rate of wooden chaff is moisture content 10%-15%,
Raw material is mixed according to the above ratio：Magnesia, wooden chaff will be quantified by numerical control machine and add mixer, by quantitative high purity magnesium Solution adds mixer, and stir about 3-5 minutes, the material that will be accomplished fluently was put into laminator, cuts plate by after 1 rolling of laminator Break, then the thickness of needs is reached by 2 rolling of laminator, maintained 6 hours on the plate feeding brandreth that will be molded, sheet material reaches first Phase maintenance intensity just can be with the demoulding, and sheet material is transported to warehouse natural air drying and conserved 5-7 days, and the PLASTIC LAMINATED for obtaining meets fire-protection rating will Ask.
Embodiment 3：
Magnesia 35%, magnesium chloride 50%, wooden chaff 15%,
Content of magnesium >=85 of magnesia, the mesh of granularity 200, described magnesium chloride is block, content 95%,
Wooden chaff is Chinese fir wood chaff, and wooden chaff does not have impurity into sawdust shape, and the rate of wooden chaff is moisture content 10%-15%,
Raw material is mixed according to the above ratio：Magnesia, wooden chaff will be quantified by numerical control machine and add mixer, by quantitative high purity magnesium Solution adds mixer, and stir about 3-5 minutes, the material that will be accomplished fluently was put into laminator, cuts plate by after 1 rolling of laminator Break, then the thickness of needs is reached by 2 rolling of laminator, maintained 6 hours on the plate feeding brandreth that will be molded, sheet material reaches first Phase maintenance intensity just can be with the demoulding, and sheet material is transported to warehouse natural air drying and conserved 5-7 days, and the PLASTIC LAMINATED for obtaining meets fire-protection rating will Ask.

Claims (4)

1. a kind of novel high-performance glass magnesium fireproof board, it is characterised in that：Including following mass percent component：
Magnesia 30%-35%, magnesium chloride 45%-50%, wooden chaff 15%-25%,
Content of magnesium >=85 of described magnesia, the mesh of granularity 200,
Described magnesium chloride is block, content 95%,
Described wooden chaff is Chinese fir wood chaff, and wooden chaff does not have impurity into sawdust shape, and the rate of wooden chaff is moisture content 10%-15%.
2. novel high-performance glass magnesium fireproof board according to claim 1, it is characterised in that the optimal ratio of described magnesia Example be（33%）.
3. novel high-performance glass magnesium fireproof board according to claim 1, it is characterised in that the optimal ratio of described magnesium chloride Example be（47%）.
4. novel high-performance glass magnesium fireproof board according to claim 1, it is characterised in that the optimal ratio of described wooden chaff For（20%）.
CN201611051843.XA 2016-11-25 2016-11-25 A kind of novel high-performance glass magnesium fireproof board Pending CN106747156A (en)