CN102838340A - Novel fireproof thermal-insulating soundproof material and preparation method of novel fireproof thermal-insulating soundproof material - Google Patents
Novel fireproof thermal-insulating soundproof material and preparation method of novel fireproof thermal-insulating soundproof material Download PDFInfo
- Publication number
- CN102838340A CN102838340A CN2012103601256A CN201210360125A CN102838340A CN 102838340 A CN102838340 A CN 102838340A CN 2012103601256 A CN2012103601256 A CN 2012103601256A CN 201210360125 A CN201210360125 A CN 201210360125A CN 102838340 A CN102838340 A CN 102838340A
- Authority
- CN
- China
- Prior art keywords
- weight percent
- novel fireproof
- preparation
- heat insulating
- soundproof material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a novel fireproof thermal-insulating soundproof material and a preparation method of the novel fireproof thermal-insulating soundproof material, which are applicable to fireproof building materials. The novel fireproof thermal-insulating soundproof material is characterized by comprising raw materials in percentage by weight: 36-44% magnesium oxide, 36-44% of magnesium sulfate or magnesium chloride, 1-3% of aluminum oxide, 1-3% of silicon dioxide, 16-24% of sawdust or ceramiste, and 0.5-2.5% of waterproof agent. The fireproof thermal-insulating soundproof material is prepared by adding water in compositions according to the proportions and agitating and mixing with a foam material, and the fireproof grade of the fireproof insulating soundproof material can achieve grade A, the fireproof limit achieves over 1.5 hours, the purposes of being high in fireproof grade and high in insulating coefficient can be achieved, and the fireproof thermal-insulating soundproof material is not easy to crack after being burnt, and has good soundproof effect.
Description
Technical field
The present invention relates to a kind of novel fireproof heat insulating sound-proof material and preparation method thereof.
Background technology
The generation of a lot of in recent years building fire incidents; Impel fire-retardant material in architectural extensive application; Fire-retardant material can stop fire spreading when fire takes place, for firefighter's fire extinguishing provides valuable time, thereby reduced loss of life and personal injury and property damage.And to fire-retardant material itself, fire-protection rating is high more, the resistance to extreme temperature time is long more, and is just good more from the angle of safety, if a kind of material can prevent fires, again can heat preservation and soundproof, and then meet people's demand more.How normally used on the market at present fireproof heat insulating sound insulation building materials mix with foam beads with cement, form through compacting; This building materials are met fire and can not burnt, and can stop fire spreading, but the heatproof time are not long; Easy of crack after burning; When the intensity of a fire was bigger, its effect some deficiency that just seems can not reach the purpose of fireproof heat insulating.
Summary of the invention
The present invention aims to provide that a kind of fire-protection rating is high, heat insulating coefficient is high, be difficult for novel fireproof heat insulating sound-proof material of rimose and preparation method thereof.
A kind of novel fireproof heat insulating sound-proof material of the present invention contains the Natural manganese dioxide that weight percent is 36%-44%; Weight percent is sal epsom or the magnesium chloride of 36%-44%; Weight percent is the aluminum oxide of 1%-3%; Weight percent is the silicon-dioxide of 1%-3%, and weight percent is wooden chaff or the haydite of 16%-24%, and weight percent is the water-resisting agent of 0.5%-2.5%.
The preparation method of a kind of novel fireproof heat insulating sound-proof material of the present invention, it comprises following steps:
1) with weight percent is the Natural manganese dioxide of 36%-44%; Weight percent is sal epsom or the magnesium chloride of 36%-44%; Weight percent is the aluminum oxide of 1%-3%; Weight percent is the silicon-dioxide of 1%-3%, and weight percent is wooden chaff or the haydite of 16%-24%, and weight percent is that the water-resisting agent of 0.5%-2.5% mixes and stirs and obtains dissolving slurry;
2) perfusion prime cement: will dissolve slurry according to setting thickness and pour on the mould of composition board machine;
3) foam material is covered on the prime cement;
4) perfusion layer slurry: will dissolve slurry and cover foam material fully;
5) sheet material of accomplishing that will be in the milk leaves standstill more than one hour promptly plastic.
A kind of novel fireproof heat insulating sound-proof material of the present invention and preparation method can be used for construction timber, and component mixes the molten slurry good fluidity of back gained according to the above ratio; Be easy to form, time of repose is short, and prepared fireproof heat insulating sound-proof material fire-protection rating reaches the A level; Fire endurance reached more than 1.5 hours; Reached the purpose that fire-protection rating is high, heat insulating coefficient is high, and not easy to crack after burning, soundproof effect is also fine.
Embodiment
Embodiment one,
The first step; With weight percent 36% Natural manganese dioxide; Weight percent is 36% sal epsom or magnesium chloride, and weight percent is 1% aluminum oxide, and weight percent is 1% silicon-dioxide; Weight percent is 24% wooden chaff or haydite, weight percent be 2% water-resisting agent mix and add suitable quantity of water stir molten slurry; Second step is for increasing sheet material hardness, the upper glass cloth on the mould upper berth of composition board machine; The 3rd step, perfusion prime cement: will dissolve slurry according to setting thickness and pour on the mould of composition board machine; In the 4th step, the XPE foam material is covered on the prime cement; The 5th step, perfusion layer slurry: will dissolve slurry and cover foam material fully; The 6th step, the sheet material of the slurry of having irritated is released, be placed on the ground and left standstill 1.5 hours, plate is fully solidified, then according to using size to cut; In the 7th step, edge sealing: through the whole sheet material of cutting, can expose the material of foaming all around, spread upon exposed region dissolving slurry, make it to reach the fp effect, packing is entered the storehouse then.
Embodiment two,
Weight percent is 40% Natural manganese dioxide, and weight percent is 40% sal epsom or magnesium chloride, and weight percent is 1% aluminum oxide, and weight percent is 1% silicon-dioxide, and weight percent is 16% wooden chaff or haydite, and weight percent is 2% water-resisting agent; Foam material is PE; The sheet material time of repose is 1.2 hours; All the other are identical with embodiment one.
Embodiment three,
Weight percent is 44% Natural manganese dioxide, and weight percent is 36% sal epsom or magnesium chloride, and weight percent is 1% aluminum oxide, and weight percent is 1% silicon-dioxide, and weight percent is 16% wooden chaff or haydite, and weight percent is 2% water-resisting agent; Foam material is a urethane; The sheet material time of repose is 1 hour; All the other are identical with embodiment one.
Embodiment four,
Weight percent is 36% Natural manganese dioxide, and weight percent is 44% sal epsom or magnesium chloride, and weight percent is 1% aluminum oxide, and weight percent is 1% silicon-dioxide, and weight percent is 16% wooden chaff or haydite, and weight percent is 2% water-resisting agent; The sheet material time of repose is 2 hours; All the other are identical with embodiment one.
Embodiment five,
Weight percent is 36% Natural manganese dioxide; Weight percent is 36% sal epsom or magnesium chloride, and weight percent is 3% aluminum oxide, and weight percent is 3% silicon-dioxide; Weight percent is 19.5% wooden chaff or haydite, and weight percent is 2.5% water-resisting agent; The sheet material time of repose is 2.2 hours; All the other are identical with embodiment one.
Embodiment six,
Weight percent is 36% Natural manganese dioxide; Weight percent is 39.5% sal epsom or magnesium chloride, and weight percent is 2% aluminum oxide, and weight percent is 2% silicon-dioxide; Weight percent is 20% wooden chaff or haydite, and weight percent is 0.5% water-resisting agent; The sheet material time of repose is 1.8 hours; All the other are identical with embodiment one.
Embodiment seven,
Weight percent is 38% Natural manganese dioxide; Weight percent is 41% sal epsom or magnesium chloride, and weight percent is 1.5% aluminum oxide, and weight percent is 1.5% silicon-dioxide; Weight percent is 17% wooden chaff or haydite, and weight percent is 1% water-resisting agent; The sheet material time of repose is 1.7 hours; All the other are identical with embodiment one.
Claims (5)
1. novel fireproof heat insulating sound-proof material; It is characterized in that: contain the Natural manganese dioxide that weight percent is 36%-44%; Weight percent is sal epsom or the magnesium chloride of 36%-44%, and weight percent is the aluminum oxide of 1%-3%, and weight percent is the silicon-dioxide of 1%-3%; Weight percent is wooden chaff or the haydite of 16%-24%, and weight percent is the water-resisting agent of 0.5%-2.5%.
2. the preparation method of a novel fireproof heat insulating sound-proof material, it is characterized in that: it comprises following steps:
1) with weight percent is the Natural manganese dioxide of 36%-44%; Weight percent is sal epsom or the magnesium chloride of 36%-44%; Weight percent is the aluminum oxide of 1%-3%, and weight percent is the silicon-dioxide of 1%-3%, and weight percent is wooden chaff or the haydite of 16%-24%; Weight percent is the water-resisting agent of 0.5%-2.5%, and the adding suitable quantity of water stirs and obtains dissolving slurry;
2) perfusion prime cement: will dissolve slurry according to setting thickness and pour into mould;
3) foam material is covered on the prime cement;
4) perfusion layer slurry: will dissolve slurry and cover foam material fully;
5) sheet material of accomplishing that will be in the milk leaves standstill more than one hour promptly plastic.
3. the preparation method of a kind of novel fireproof heat insulating sound-proof material according to claim 2 is characterized in that: described foam material is XPE, perhaps is PE, perhaps is urethane.
4. the preparation method of a kind of novel fireproof heat insulating sound-proof material according to claim 2 is characterized in that: before the described perfusion prime cement, on the mould of composition board machine, spread glasscloth earlier.
5. the preparation method of a kind of novel fireproof heat insulating sound-proof material according to claim 2 is characterized in that: the sheet material after described grouting is accomplished cuts the exposed part that is produced and smears with the molten slurry that makes after moulding.