CN106746668B - 一种抗菌陶瓷釉液及其制备方法 - Google Patents
一种抗菌陶瓷釉液及其制备方法 Download PDFInfo
- Publication number
- CN106746668B CN106746668B CN201611154618.9A CN201611154618A CN106746668B CN 106746668 B CN106746668 B CN 106746668B CN 201611154618 A CN201611154618 A CN 201611154618A CN 106746668 B CN106746668 B CN 106746668B
- Authority
- CN
- China
- Prior art keywords
- parts
- liquid
- ceramic
- raw material
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种抗菌陶瓷釉液及其制备方法，抗菌陶瓷釉液的原料包括抗菌陶瓷底釉液、抗菌陶瓷面釉液；抗菌陶瓷底釉液的原料包括熔块、镁气石、纳米二氧化钛、高岭土、石英、六氟合锆酸铵、六偏磷酸钠、十二烷基苯磺酸钠、粘合剂和消泡剂；所述抗菌陶瓷面釉液的原料包括：硝酸镧、纳米氧化锌粉、氧化铝、硅酸锆、六氟硅酸锌、氟硼酸铵、硝酸银、粘合剂和消泡剂。本发明抗菌能力强、时间持久，对人体无害，组分中含氟离子的六氟合锆酸铵、氟硼酸铵可以和陶瓷的素坯中的硅酸盐溶为一体，使瓷釉光泽度好、化学性稳定；烧成的陶瓷砖负离子的释放能力符合国家健康建筑材料的健康要求标准。
Description
技术领域
本发明涉及陶瓷技术领域，具体是一种抗菌陶瓷釉液及其制备方法。
背景技术
细菌、霉菌（真菌）作为病原菌对人们的生活有很大危害，严重影响了人们的健康。人类很早就开始使用抗菌的东西了，从公元前埃及人使用的焦油、乳香、肉桂，到1828年韦勒合成尿素，进入20世纪，人们掌握了农药鱼、藤酮和除虫菊酯等的化学结构后，大量的有机抗菌剂诞生了。20世纪50年代，抗菌剂的开发和抗菌技术逐渐发展起来。进入80年代，人们开始注重生活质量，追求舒适卫生的生活环境，抗菌防臭纤维被制成。从此，抗菌陶瓷、抗菌涂料、抗菌薄膜、抗菌食品、抗菌化妆品等应运而生。90年代后，日本、美国等对抗菌陶瓷进行了广泛而深入的研究，无机抗菌剂及其制品以其安全、可靠、稳定和持久的抗菌性能成为大家主要研究的对象，并在市场上推出了抗菌卫生洁具和抗菌餐具等产品。
当今社会，健康是人们最关心的问题，空气中含有对人体有害的各种污染物，此外，建筑装饰材料中释放的各种有害物质也是危害人们健康的重要因素；然而，空气中也有对人体有益的物质，如空气中的负离子，能促进人体内合成和储存维生素，被誉为空气维生素。目前，人们多选用负离子发生器摆放在室内，达到净化空气的作用，但负离子发生器只能零散放置在室内，无法大面积使用，净化空气的效果有限，控制和消灭有害细菌的生长和繁殖日益成为科研领域的重要课题，并且不断受到越来越多人的关注，成为环保材料的重要组成部分。如何找到一种技术手段和方法将制成陶瓷砖能释放负离子，使室内环境更健康一直陶瓷砖从业者函待解决的问题。
发明内容
本发明的目的在于提供一种抗菌能力强、时间持久的抗菌陶瓷釉液及其制备方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种抗菌陶瓷釉液，按照重量份的原料包括：抗菌陶瓷底釉液25-45份、抗菌陶瓷面釉液20-35份；所述抗菌陶瓷底釉液按照重量份的原料包括：熔块10-20份、镁气石2-3份、纳米二氧化钛3-4份、高岭土5-7份、石英1-2份、六氟合锆酸铵1-3份、六偏磷酸钠1-2份、十二烷基苯磺酸钠2-4份、粘合剂0.1-0.2份、消泡剂0.15-0.25份；所述抗菌陶瓷面釉液按照重量份的原料包括：硝酸镧2-4份、纳米氧化锌粉3-5份、氧化铝1-2份、硅酸锆4-6份、六氟硅酸锌2-4份、氟硼酸铵2-6份、硝酸银6-8份、粘合剂0.1-0.2份、消泡剂0.15-0.25份。
作为本发明进一步的方案：所述抗菌陶瓷釉液，按照重量份的原料包括：抗菌陶瓷底釉液份29.3-40.7份、抗菌陶瓷面釉液23.7-31.3份；所述抗菌陶瓷底釉液按照重量份的原料包括：熔块12-18份、镁气石2.2-2.8份、纳米二氧化钛3.2-3.8份、高岭土5.5-6.5份、石英1.2-1.8份、六氟合锆酸铵1.5-2.5份、六偏磷酸钠1.2-1.8份、十二烷基苯磺酸钠2.5-3.5份、粘合剂0.125-0.175份、消泡剂0.175-0.225份；所述抗菌陶瓷面釉液按照重量份的原料包括：硝酸镧2.5-3.5份、纳米氧化锌粉3.5-4.5份、氧化铝1.2-1.8份、硅酸锆4.5-5.5份、六氟硅酸锌2.5-3.5份、氟硼酸铵3-5份、硝酸银6.5-7.5份、粘合剂0.125-0.175份、消泡剂0.175-0.225份。
作为本发明进一步的方案：所述抗菌陶瓷釉液，按照重量份的原料包括：抗菌陶瓷底釉液35份、抗菌陶瓷面釉液27.5份；所述抗菌陶瓷底釉液按照重量份的原料包括：熔块15份、镁气石2.5份、纳米二氧化钛3.5份、高岭土6份、石英1.5份、六氟合锆酸铵2份、六偏磷酸钠1.5份、十二烷基苯磺酸钠3份、粘合剂0.15份、消泡剂0.2份；所述抗菌陶瓷面釉液按照重量份的原料包括：硝酸镧3份、纳米氧化锌粉4份、氧化铝1.5份、硅酸锆5份、六氟硅酸锌3份、氟硼酸铵4份、硝酸银7份、粘合剂0.15份、消泡剂0.2份。
作为本发明进一步的方案：所述粘合剂为甲基纤维素、三聚磷酸钠、水溶性丙烯酸树脂、聚乙烯醇、阿拉伯胶中的一种或两种以上。
作为本发明进一步的方案：所述的分散剂为丙烯醇单体分散剂。
作为本发明再进一步的方案：所述的消泡剂为辛醇或有机硅乳液。
所述抗菌陶瓷釉液的制备方法，具体步骤如下：
（1）将熔块、镁气石、纳米二氧化钛、高岭土、石英、六氟合锆酸铵、六偏磷酸钠、十二烷基苯磺酸钠混合后放入球磨机中湿法球磨3-5h，过300-400目筛后制成浆状，再加入0.1-0.2份粘合剂和0.15-0.25份消泡剂后，再次放入球磨机中湿法球磨1-2h得到所述抗菌陶瓷底釉液；
（2）将硝酸镧、纳米氧化锌粉、氧化铝、硅酸锆、六氟硅酸锌、氟硼酸铵、硝酸银混入球磨机中湿法球磨2-4h，过300-400目筛后制成浆状，再加入0.1-0.2份粘合剂和0.15-0.25份消泡剂后，再次放入球磨机中湿法球磨40-60min后得到所述抗菌陶瓷面釉。
与现有技术相比，本发明的有益效果是：
本发明抗菌能力强、时间持久，对人体无害，组分中含氟离子的六氟合锆酸铵、氟硼酸铵可以和陶瓷的素坯中的硅酸盐溶为一体，使瓷釉光泽度好、化学性稳定；使用时将抗菌陶瓷底釉液和抗菌陶瓷面釉液分别采用淋釉或喷涂方式先后施于陶瓷砖坯上，然后烧成陶瓷砖，烧成的陶瓷砖负离子的释放能力符合国家健康建筑材料的健康要求标准。
具体实施方式
下面结合具体实施方式对本专利的技术方案作进一步详细地说明。
实施例1
一种抗菌陶瓷釉液，按照重量份的原料包括：抗菌陶瓷底釉液25份、抗菌陶瓷面釉液20份；所述抗菌陶瓷底釉液按照重量份的原料包括：熔块10份、镁气石2份、纳米二氧化钛3份、高岭土5份、石英1份、六氟合锆酸铵1份、六偏磷酸钠1份、十二烷基苯磺酸钠2份、粘合剂0.1份、消泡剂0.15份；所述抗菌陶瓷面釉液按照重量份的原料包括：硝酸镧2份、纳米氧化锌粉3份、氧化铝1份、硅酸锆4份、六氟硅酸锌2份、氟硼酸铵2份、硝酸银6份、粘合剂0.1份、消泡剂0.15份。
所述抗菌陶瓷釉液的制备方法，具体步骤如下：
（1）将熔块、镁气石、纳米二氧化钛、高岭土、石英、六氟合锆酸铵、六偏磷酸钠、十二烷基苯磺酸钠混合后放入球磨机中湿法球磨3h，过300目筛后制成浆状，再加入0.1份粘合剂和0.15份消泡剂后，再次放入球磨机中湿法球磨1h得到所述抗菌陶瓷底釉液；
（2）将硝酸镧、纳米氧化锌粉、氧化铝、硅酸锆、六氟硅酸锌、氟硼酸铵、硝酸银混入球磨机中湿法球磨2h，过300目筛后制成浆状，再加入0.1份粘合剂和0.15份消泡剂后，再次放入球磨机中湿法球磨40min后得到所述抗菌陶瓷面釉。
实施例2
一种抗菌陶瓷釉液，按照重量份的原料包括：抗菌陶瓷底釉液份29.3份、抗菌陶瓷面釉液23.7份；所述抗菌陶瓷底釉液按照重量份的原料包括：熔块12份、镁气石2.2份、纳米二氧化钛3.2份、高岭土5.5份、石英1.2份、六氟合锆酸铵1.5份、六偏磷酸钠1.2份、十二烷基苯磺酸钠2.5份、粘合剂0.125份、消泡剂0.175份；所述抗菌陶瓷面釉液按照重量份的原料包括：硝酸镧2.5份、纳米氧化锌粉3.5份、氧化铝1.2份、硅酸锆4.5份、六氟硅酸锌2.5份、氟硼酸铵3份、硝酸银6.5份、粘合剂0.125份、消泡剂0.175份。
所述抗菌陶瓷釉液的制备方法，具体步骤如下：
（1）将熔块、镁气石、纳米二氧化钛、高岭土、石英、六氟合锆酸铵、六偏磷酸钠、十二烷基苯磺酸钠混合后放入球磨机中湿法球磨3.5h，过320目筛后制成浆状，再加入0.12份粘合剂和0.18份消泡剂后，再次放入球磨机中湿法球磨1.2h得到所述抗菌陶瓷底釉液；
（2）将硝酸镧、纳米氧化锌粉、氧化铝、硅酸锆、六氟硅酸锌、氟硼酸铵、硝酸银混入球磨机中湿法球磨2.5h，过320目筛后制成浆状，再加入0.12份粘合剂和0.18份消泡剂后，再次放入球磨机中湿法球磨45min后得到所述抗菌陶瓷面釉。
实施例3
一种抗菌陶瓷釉液，按照重量份的原料包括：抗菌陶瓷底釉液35份、抗菌陶瓷面釉液27.5份；所述抗菌陶瓷底釉液按照重量份的原料包括：熔块15份、镁气石2.5份、纳米二氧化钛3.5份、高岭土6份、石英1.5份、六氟合锆酸铵2份、六偏磷酸钠1.5份、十二烷基苯磺酸钠3份、粘合剂0.15份、消泡剂0.2份；所述抗菌陶瓷面釉液按照重量份的原料包括：硝酸镧3份、纳米氧化锌粉4份、氧化铝1.5份、硅酸锆5份、六氟硅酸锌3份、氟硼酸铵4份、硝酸银7份、粘合剂0.15份、消泡剂0.2份。
所述抗菌陶瓷釉液的制备方法，具体步骤如下：
（1）将熔块、镁气石、纳米二氧化钛、高岭土、石英、六氟合锆酸铵、六偏磷酸钠、十二烷基苯磺酸钠混合后放入球磨机中湿法球磨4h，过350目筛后制成浆状，再加入0.15份粘合剂和0.2份消泡剂后，再次放入球磨机中湿法球磨1.5h得到所述抗菌陶瓷底釉液；
（2）将硝酸镧、纳米氧化锌粉、氧化铝、硅酸锆、六氟硅酸锌、氟硼酸铵、硝酸银混入球磨机中湿法球磨3h，过350目筛后制成浆状，再加入0.15份粘合剂和0.2份消泡剂后，再次放入球磨机中湿法球磨50min后得到所述抗菌陶瓷面釉。
实施例4
一种抗菌陶瓷釉液，按照重量份的原料包括：抗菌陶瓷底釉液份40.7份、抗菌陶瓷面釉液31.3份；所述抗菌陶瓷底釉液按照重量份的原料包括：熔块18份、镁气石2.8份、纳米二氧化钛3.8份、高岭土6.5份、石英1.8份、六氟合锆酸铵2.5份、六偏磷酸钠1.8份、十二烷基苯磺酸钠3.5份、粘合剂0.175份、消泡剂0.225份；所述抗菌陶瓷面釉液按照重量份的原料包括：硝酸镧3.5份、纳米氧化锌粉4.5份、氧化铝1.8份、硅酸锆5.5份、六氟硅酸锌3.5份、氟硼酸铵5份、硝酸银7.5份、粘合剂0.175份、消泡剂0.225份。
所述抗菌陶瓷釉液的制备方法，具体步骤如下：
（1）将熔块、镁气石、纳米二氧化钛、高岭土、石英、六氟合锆酸铵、六偏磷酸钠、十二烷基苯磺酸钠混合后放入球磨机中湿法球磨4.5h，过380目筛后制成浆状，再加入0.18份粘合剂和0.22份消泡剂后，再次放入球磨机中湿法球磨1.8h得到所述抗菌陶瓷底釉液；
（2）将硝酸镧、纳米氧化锌粉、氧化铝、硅酸锆、六氟硅酸锌、氟硼酸铵、硝酸银混入球磨机中湿法球磨3.5h，过380目筛后制成浆状，再加入0.18份粘合剂和0.22份消泡剂后，再次放入球磨机中湿法球磨55min后得到所述抗菌陶瓷面釉。
实施例5
一种抗菌陶瓷釉液，按照重量份的原料包括：抗菌陶瓷底釉液45份、抗菌陶瓷面釉液35份；所述抗菌陶瓷底釉液按照重量份的原料包括：熔块20份、镁气石3份、纳米二氧化钛4份、高岭土7份、石英2份、六氟合锆酸铵3份、六偏磷酸钠2份、十二烷基苯磺酸钠4份、粘合剂0.2份、消泡剂0.25份；所述抗菌陶瓷面釉液按照重量份的原料包括：硝酸镧4份、纳米氧化锌粉5份、氧化铝2份、硅酸锆6份、六氟硅酸锌4份、氟硼酸铵6份、硝酸银8份、粘合剂0.2份、消泡剂0.25份。
所述抗菌陶瓷釉液的制备方法，具体步骤如下：
（1）将熔块、镁气石、纳米二氧化钛、高岭土、石英、六氟合锆酸铵、六偏磷酸钠、十二烷基苯磺酸钠混合后放入球磨机中湿法球磨5h，过3400目筛后制成浆状，再加入0.2份粘合剂和0.25份消泡剂后，再次放入球磨机中湿法球磨2h得到所述抗菌陶瓷底釉液；
（2）将硝酸镧、纳米氧化锌粉、氧化铝、硅酸锆、六氟硅酸锌、氟硼酸铵、硝酸银混入球磨机中湿法球磨4h，过3400目筛后制成浆状，再加入0.2份粘合剂和0.25份消泡剂后，再次放入球磨机中湿法球磨60min后得到所述抗菌陶瓷面釉。
本发明抗菌能力强、时间持久，对人体无害，组分中含氟离子的六氟合锆酸铵、氟硼酸铵可以和陶瓷的素坯中的硅酸盐溶为一体，使瓷釉光泽度好、化学性稳定；使用时将抗菌陶瓷底釉液和抗菌陶瓷面釉液分别采用淋釉或喷涂方式先后施于陶瓷砖坯上，然后烧成陶瓷砖，烧成的陶瓷砖负离子的释放能力符合国家健康建筑材料的健康要求标准。
上面对本专利的较佳实施方式作了详细说明，但是本专利并不限于上述实施方式，在本领域的普通技术人员所具备的知识范围内，还可以在不脱离本专利宗旨的前提下作出各种变化。
Claims (6)
1.一种抗菌陶瓷釉液，其特征在于，按照重量份的原料包括：抗菌陶瓷底釉液25-45份、抗菌陶瓷面釉液20-35份；所述抗菌陶瓷底釉液按照重量份的原料包括：熔块10-20份、镁气石2-3份、纳米二氧化钛3-4份、高岭土5-7份、石英1-2份、六氟合锆酸铵1-3份、六偏磷酸钠1-2份、十二烷基苯磺酸钠2-4份、粘合剂0.1-0.2份、消泡剂0.15-0.25份；所述抗菌陶瓷面釉液按照重量份的原料包括：硝酸镧2-4份、纳米氧化锌粉3-5份、氧化铝1-2份、硅酸锆4-6份、六氟硅酸锌2-4份、氟硼酸铵2-6份、硝酸银6-8份、粘合剂0.1-0.2份、消泡剂0.15-0.25份。
2.根据权利要求1所述的抗菌陶瓷釉液，其特征在于，按照重量份的原料包括：抗菌陶瓷底釉液份29.3-40.7份、抗菌陶瓷面釉液23.7-31.3份；所述抗菌陶瓷底釉液按照重量份的原料包括：熔块12-18份、镁气石2.2-2.8份、纳米二氧化钛3.2-3.8份、高岭土5.5-6.5份、石英1.2-1.8份、六氟合锆酸铵1.5-2.5份、六偏磷酸钠1.2-1.8份、十二烷基苯磺酸钠2.5-3.5份、粘合剂0.125-0.175份、消泡剂0.175-0.225份；所述抗菌陶瓷面釉液按照重量份的原料包括：硝酸镧2.5-3.5份、纳米氧化锌粉3.5-4.5份、氧化铝1.2-1.8份、硅酸锆4.5-5.5份、六氟硅酸锌2.5-3.5份、氟硼酸铵3-5份、硝酸银6.5-7.5份、粘合剂0.125-0.175份、消泡剂0.175-0.225份。
3.根据权利要求1所述的抗菌陶瓷釉液，其特征在于，按照重量份的原料包括：抗菌陶瓷底釉液35份、抗菌陶瓷面釉液27.5份；所述抗菌陶瓷底釉液按照重量份的原料包括：熔块15份、镁气石2.5份、纳米二氧化钛3.5份、高岭土6份、石英1.5份、六氟合锆酸铵2份、六偏磷酸钠1.5份、十二烷基苯磺酸钠3份、粘合剂0.15份、消泡剂0.2份；所述抗菌陶瓷面釉液按照重量份的原料包括：硝酸镧3份、纳米氧化锌粉4份、氧化铝1.5份、硅酸锆5份、六氟硅酸锌3份、氟硼酸铵4份、硝酸银7份、粘合剂0.15份、消泡剂0.2份。
4.根据权利要求1-3任一所述的抗菌陶瓷釉液，其特征在于，所述粘合剂为甲基纤维素、三聚磷酸钠、水溶性丙烯酸树脂、聚乙烯醇、阿拉伯胶中的一种或两种以上。
5.根据权利要求1-3任一所述的抗菌陶瓷釉液，其特征在于，所述的消泡剂为辛醇或有机硅乳液。
6.一种如权利要求1-3任一所述的抗菌陶瓷釉液的制备方法，其特征在于，具体步骤如下：
（1）将熔块、镁气石、纳米二氧化钛、高岭土、石英、六氟合锆酸铵、六偏磷酸钠、十二烷基苯磺酸钠混合后放入球磨机中湿法球磨3-5h，过300-400目筛后制成浆状，再加入0.1-0.2份粘合剂和0.15-0.25份消泡剂后，再次放入球磨机中湿法球磨1-2h得到所述抗菌陶瓷底釉液；
（2）将硝酸镧、纳米氧化锌粉、氧化铝、硅酸锆、六氟硅酸锌、氟硼酸铵、硝酸银混入球磨机中湿法球磨2-4h，过300-400目筛后制成浆状，再加入0.1-0.2份粘合剂和0.15-0.25份消泡剂后，再次放入球磨机中湿法球磨40-60min后得到所述抗菌陶瓷面釉液。