CN106671237A - 一种林木炭化处理工艺 - Google Patents
一种林木炭化处理工艺 Download PDFInfo
- Publication number
- CN106671237A CN106671237A CN201611131527.3A CN201611131527A CN106671237A CN 106671237 A CN106671237 A CN 106671237A CN 201611131527 A CN201611131527 A CN 201611131527A CN 106671237 A CN106671237 A CN 106671237A
- Authority
- CN
- China
- Prior art keywords
- forest
- wood
- temperature
- warmed
- stage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种林木炭化处理工艺,包括以下步骤:(1)高温干燥,(2)炭化处理,(3)降温处理。本发明分别采用干燥和炭化过程,与现有技术相比,减少处理时间,提高生产效率。另外,用经硫酸铝中和后稀甲基硅酸钠溶液对木材进行表面处理,可以提高木材的疏水性能、防腐性能和力学强度,从而拓宽了木材的应用范围。
Description
技术领域
本发明涉及炭化工艺技术领域,特别是一种林木炭化处理工艺。
背景技术
炭化木是在不含任何化学剂条件下应用高温对木材进行炭化处理,使其组分中羟基浓度减小,从而增加其的尺寸稳定性;同时还改变了其的某些营养成分,从而具有较好的防虫功能。炭化木又可以分为表层炭化木和深度炭化木。表层炭化木,也称为工艺炭化木、炭烧木,主要是指用氧焊枪烧烤,使木材表面具有一层很薄的炭化层,对木材性能的改变可以类比木材的油漆,但可以突显表面凹凸的木纹,产生立体效果,但是,炭化木也存在一些不足之处,如经高温炭化后的木材变脆,密度、力学强度下降,在生产或使用过程中可能断裂。
发明内容
为了克服现有的技术不足的问题,本发明提供一种林木炭化处理工艺。
本发明的技术方案是这样实现的:一种林木炭化处理工艺,包括以下步骤:
(1)高温干燥,将林木放置在干燥炉中进行脱水干燥,在所述干燥炉的出口处连接排风扇,将排出的水分及时排除;
(2)炭化处理,将处理好的林木,放入炭化设备中的炭化室内,并关闭炭化室的大门;然后将炭化室内温度以升温到90~110℃,并保温1 .2~1 .8h;然后升温到110~125℃,并保温2 .2~2 .6h,使林木内部的含水率为0;最后升温到200~215℃,并保温2~5h,在此升温阶段采用间歇式喷蒸汽法喷入蒸汽作为保护气体;
(3)降温处理,分阶段降温,直至达到室温。
优选地,在林木高温干燥之前先进行表面处理,具体为经硫酸铝中和后稀甲基硅酸钠溶液对林木进行表面处理。
本发明有益效果是:本发明分别采用干燥和炭化过程,与现有技术相比,减少处理时间,提高生产效率。另外,用经硫酸铝中和后稀甲基硅酸钠溶液对木材进行表面处理,可以提高木材的疏水性能、防腐性能和力学强度,从而拓宽了木材的应用范围。
具体实施方式
结合实施例对本发明做进一步的说明。
一种林木炭化处理工艺,包括以下步骤:
(1)高温干燥,将林木放置在干燥炉中进行脱水干燥,在所述干燥炉的出口处连接排风扇,将排出的水分及时排除;
(2)炭化处理,将处理好的林木,放入炭化设备中的炭化室内,并关闭炭化室的大门;然后将炭化室内温度以升温到90~110℃,并保温1 .2~1 .8h;然后升温到110~125℃,并保温2 .2~2 .6h,使林木内部的含水率为0;最后升温到200~215℃,并保温2~5h,在此升温阶段采用间歇式喷蒸汽法喷入蒸汽作为保护气体;
(3)降温处理,分阶段降温,直至达到室温。
优选地,在林木高温干燥之前先进行表面处理,具体为经硫酸铝中和后稀甲基硅酸钠溶液对林木进行表面处理。
实施例1:
一种林木炭化处理工艺,包括以下步骤:
(1)表面处理,将经硫酸铝中和后稀甲基硅酸钠溶液对林木进行表面处理;
(2)高温干燥,将林木放置在干燥炉中进行脱水干燥,在所述干燥炉的出口处连接排风扇,将排出的水分及时排除;
(3)炭化处理,将处理好的林木,放入炭化设备中的炭化室内,并关闭炭化室的大门;然后将炭化室内温度以升温到100℃,并保温1 6h;然后升温到120℃,并保温2.5h,使林木内部的含水率为0;最后升温到210℃,并保温2h,在此升温阶段采用间歇式喷蒸汽法喷入蒸汽作为保护气体;
(4)降温处理,分阶段降温,第一阶段为降温到118℃,第二阶段降温到95℃,并保温0.8h;最后,自然降温至室温,取出林木。
本发明分别采用干燥和炭化过程,与现有技术相比,减少处理时间,提高生产效率。另外,用经硫酸铝中和后稀甲基硅酸钠溶液对木材进行表面处理,可以提高木材的疏水性能、防腐性能和力学强度,从而拓宽了木材的应用范围。
在此说明书中,本发明已参照其特定的实施例作了描述。但是,很显然仍可以做出各种修改和变换而不背离本发明的精神和范围。因此,说明书应被认为是说明性的而非限制性的。
Claims (2)
1.一种林木炭化处理工艺,其特征在于,包括以下步骤:
(1)高温干燥,将林木放置在干燥炉中进行脱水干燥,在所述干燥炉的出口处连接排风扇,将排出的水分及时排除;
(2)炭化处理,将处理好的林木,放入炭化设备中的炭化室内,并关闭炭化室的大门;然后将炭化室内温度以升温到90~110℃,并保温1 .2~1 .8h;然后升温到110~125℃,并保温2 .2~2 .6h,使林木内部的含水率为0;最后升温到200~215℃,并保温2~5h,在此升温阶段采用间歇式喷蒸汽法喷入蒸汽作为保护气体;
(3)降温处理,分阶段降温,直至达到室温。
2.根据权利要求1所述的林木炭化处理工艺,其特征在于,在林木高温干燥之前先进行表面处理,具体为经硫酸铝中和后稀甲基硅酸钠溶液对林木进行表面处理。