CN1066459A - A kind of process of coal pyrogenic decomposition of multi-stage rotary - Google Patents
A kind of process of coal pyrogenic decomposition of multi-stage rotary Download PDFInfo
- Publication number
- CN1066459A CN1066459A CN 92104624 CN92104624A CN1066459A CN 1066459 A CN1066459 A CN 1066459A CN 92104624 CN92104624 CN 92104624 CN 92104624 A CN92104624 A CN 92104624A CN 1066459 A CN1066459 A CN 1066459A
- Authority
- CN
- China
- Prior art keywords
- coal
- pyrolysis
- gas
- technology
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of comprehensive utilization complete processing of pyrolysis process technology, particularly low-disintegration coal of coal.By placed in-line multistage rotary kiln internal heat type drying, external-heat pyrolysis are carried out in the feed coal segmentation, internal heat type carburetting hot-work obtains shot coke, tar products and middle calorific value of gas that granularity is 3-20mm.Adopt the technology of the present invention can be, thereby obtain the granularity shot coke product different, the Chemicals of multiple preciousnesses such as recyclable phenols, oil fuel, heavy oil and pitch from tar with volatile matter according to the end-use adjusting process.The coal gas that is produced by pyrolysis removes and can be used for this technology in addition, also can be used as civilian or industrial coal gas and supplies outward.
Description
The present invention relates to a kind of pyrolytic process of coal, particularly the multi-stage rotary pyrolysis process technology of low-disintegration coal.
Low-disintegration coal refers to the coal that metamorphic grade is lower, comprise brown coal, long-flame coal, non-caking coal, weakly caking coal, bottle coal etc., account for the over half of coal in China reserves, its coal characteristics is that volatile matter is higher, the low temperature pyrogenation tar yield is higher, and chemical reactivity is good, if burn as steam coal, then Bao Gui coal resource just can not be used adequately reasonably, and economic benefit is also poor simultaneously.Therefore, in the energy-intensive world today, the processing of coal transforms and comprehensive utilization has become the focus that people pay close attention to.
At the pyrolytic process of coal, the U.S. has just developed ground scott (Disco) technology as far back as the 30-40 age, and this technology is divided into four parts: (1) gives drying: wet coal makes its moisture reduce to 2-3% with the flue gas drying of heat; (2) roasting: dry coal is sent in the feeding type stoving oven and is heated to 320 ℃ by hot flue gases (470 ℃); (3) carbonization: the coal after the roasting is sent in the rotary kiln of an external-heat and is carried out carbonization, and carbonization temperature is spherical semicoke when reaching 450 ℃ discharges, and the heated air temperature is 570 ℃; (4) cooling: spherical hot semicoke cools off through crushing and screening.The organic volatile that coal produces in the external-heating revolving stove is through condensation separation, and coal gas returns and adds the converter hot spots and make burning gas, and waste heat flue gas is gone into firing section and made coal charge roasting gas.
This technology is used for producing block smokeless fuel by caking coal, and final pyrolysis temperature is about 450 ℃, and the volatilization of semicoke is divided into 15-17%, and this product can not be as industrial Jiao such as iron alloy, calcium carbides.
France Ma Linuo thermolysis center (CPM) has developed the multistage pyrolytic process the eighties, and this technology is divided into three parts: (1) drying: wet coal is used the hot flue gases drying in a pair of spiral conveyer, temperature reaches 250 ℃; (2) pyrolysis: moisture-free coal is sent into pyrolysis in the internal-heated rotary furnace, and the highest pyrolysis temperature can be controlled in 800-1200 ℃, and the organic volatile that produces by pyrolysis of coal heats in the stove internal combustion; (3) cooling: particle Jiao after the pyrolysis enters spray cooling in another rotary kiln by pyrolysis oven, and discharge the burnt cooling of finished product back.Coke volatile component is 2-5%.
The pyrolysis section of this technology is an internal-heated rotary furnace, and the valuable compounds such as tar that coal produces in pyrolytic process all do not reclaim processing and utilization; In addition, the duplex conveyer of dryer section is close defeated mutually material, is unsuitable for the drying and dehydrating of high-moisture feed coal.
Main purpose of the present invention is to overcome the deficiencies in the prior art part and a kind of method of processing low-disintegration coal is provided, and particularly a kind of processing contains the method for the high brown coal of moisture or other low-disintegration coal such as long-flame coal, sticking or weakly caking coal and bottle coal etc.
Another object of the present invention is to reclaim valuable chemical products such as oil fuel, phenolic compound, heavy oil or the pitch etc. that produce in the pyrolysis of coal process.
A further object of the present invention be by the pyrolytic process production granularity of coal suitable, volatile matter is lower, be suitable for the shot coke that industry such as iron alloy and calcium carbide are used.
Another object of the present invention is the civilian or industrial coal gas by calorific value in the pyrolysis process explained hereafter of coal.
The pyrolysis process technology of coal of the present invention comprises following steps:
(1) be that the feed coal of 3~30mm is sent in the dry rotary kiln and to be lower than 300 ℃ hot flue gases direct heat exchange dehydration with temperature with granularity, final drying temperature is 200~250 ℃;
(2) dried coal charge is sent into the pyrolysis rotary stove, coal charge is decomposed generation granular semicoke, tar steam and coal gas by the heat indirect heating that is provided by pyrolysis heater, and final pyrolysis temperature is 500~650 ℃;
(3) gas mixture of tar steam and coal gas is delivered in the condenser separated, obtain crude tar oil and coal gas;
(4) granular semicoke is sent in the carburetting rotary kiln, under 800~850 ℃ temperature, through the internal heat type heating, obtained shot coke and high-temperature gas mixture, gas mixture is imported into pyrolysis heater;
(5) will on vibratory screening apparatus, spray water by the shot coke that the carburetting rotary kiln is discharged and put out head, make product Jiao.
The coal that the pyrolysis process technology of coal of the present invention is suitable for processing is extensive, as brown coal, long-flame coal, not sticking or weakly caking coal or bottle coal, also can be used for processing rubbish such as wood chip, agriculture waste residue, organic waste materials.The moisture content of described brown coal is higher, is generally more than 15%, reaches as high as 30~40%.
The pyrolysis process process using plural serial stage rotary kiln of coal of the present invention, and employing zone heating mode, wherein dryer section is the gas internal heat type, with the hot flue gases of discharging by pyrolysis heater as drying medium and feed coal countercurrent flow, thereby slough most of moisture content in the coal and 1~2% volatile matter.Therefore to containing the high coal of moisture, can obtain to remove upgraded coal most of moisture content, that thermal value increases by dryer section.If be used for bunker coal, thereby then this upgraded coal has the advantages that to be convenient to transport owing to removed most of moisture content.Pyrolysis section is the gas external-heat, provides pyrolysis required heat by a pyrolysis heater, and this heat is by the generation of burning in process furnace of air, pyrolysis coal gas or other fuel.Because pyrolysis section adopts the indirect heating mode, semicoke quality, caloric power of gas, tar are reclaimed be effectively controlled and improve.The tar that pyrolysis section produces can obtain valuable phenol products, oil fuel and heavy oil or asphalt product after condensation separation.The carburetting section is the gas internal heat type, by semicoke inflammable gas that produces in the carburetting stove and the air mixed burning that enters in this stove, supplies with carburetting stove heat, and the hot waste gas of generation imports pyrolysis heater.Because dry rotary kiln and carburetting rotary kiln adopt the gas internal heat type, thereby can improve the mass-and heat-transfer efficient of process, alleviate requirement to equipment material.
Product Jiao's who is made by pyrolysis process technology of the present invention granularity is 3~20mm, and volatile matter is lower than 7%, or according to customer need, produces product Jiao of the volatilization score value of regulation.
The volatile matter of the semicoke of discharging when pyrolysis section does not need to reduce or reduces not for a long time, carburetting section and pyrolysis section can be merged into inside and outside and hot mode, with raising heat transfer rate and pyrolysis rate, thereby has simplified technology.
When need supply pyrolysis coal gas outside as civilian or industrial gas, then low-grade gas or other fuel are infeeded pyrolysis heater.
Because feed coal is in vertically in each section rotary kiln all the time and the state of radially continuous flow in, thereby make powdery coal or Paniculate coal all can adopt technology of the present invention to process.In addition, because the movement velocity and the residence time of coal grain can be controlled,,, also carry out pyrolysis serially as bottle coal, weakly caking coal even certain close-burning coal is arranged.
Seal with close blow-off valve mutually by the buffering bed of material between each section of the present invention.Dry and carburetting section is the micro-vacuum state operation, and pyrolysis section is micro-pressure operation.The final treatment temp of each section is decided according to ature of coal and end-use.
Therefore, the pyrolysis process technology of coal of the present invention has following advantage and positively effect:
1, it is wide to adapt to coal, both can be used for the brown coal of high water content, also can be used for long-flame coal, non-caking coal, weakly caking coal and bottle coal, also can be used for processing wood chip, agriculture waste residue, as the seed shell of plant, cane etc., and some organic waste materials or rubbish etc.
2, production controllable granularity built in 3~20mm, high chemical reactivity can (α
1100 ℃>80%), high specific resistance (>2 * 10
4Ω mm
2/ M) shot coke, this product Jiao be used for iron alloy, calcium carbide industry have enhance productivity, quality product, characteristics such as energy-saving effect is remarkable.In addition, can produce semicokes such as being used for blast furnace blowing, smokeless fuel, support of the catalyst, active adsorbing material as required.
Especially the brown coal shot coke has good stability, characteristics such as high chemical reactivity, high specific resistance, its thermal value (27MJ/kg) is 1.4 times of former brown coal (19MJ/kg), both can be used for calcium carbide, iron alloy production, can be used as other industry again, as cement, agglomerating fuel.
3, reclaim the tar series products account for raw coal 5~10%, wherein 20~25% be phenol products, and 25~30% is the lightweight oil that can be processed into oil fuel, and all the other 40~45% are heavy oil or asphalt product.When this process using low-grade gas or other fuel, can outer heat supply value be 17~30MJ/NM
3Middle calorific value of gas, productive rate can reach dry coal 120~200NM per ton
3
4, owing to take the hot worked process of segmentation, moisture content a large amount of in the coal are discharged with stack gas, and the harmful waste water amount that pyrolytic process is produced significantly reduces, thereby helps the processing of waste water and prevent contaminate environment.
Brief Description Of Drawings:
Fig. 1: be the general flow chart of the pyrolysis process technology of coal of the present invention.
Wherein:
1, dry rotary kiln
2, blow-off valve
3, pyrolysis rotary stove
4, pyrolysis heater
5, blow-off valve
6, carburetting rotary kiln
7, vibratory screening apparatus
8, induced draft fan
Below in conjunction with accompanying drawing, with embodiment technology of the present invention is described further, but does not limit the present invention.
1 ton of God blessings coal is sent in the dry rotary kiln (1) continuously, and drying temperature is 200 ℃; The dry waste gas that produces of coal is through induced draft fan (8), and a part is returned dry rotary kiln (1), is used to adjust the temperature of the gas that enters this stove, a part of emptying.Dry coal enters pyrolysis rotary stove (3) through blow-off valve (2), and pyrolysis temperature is controlled at 650 ℃, and pyrolysis product is semicoke 616kg, and tar 101kg, calorific value are 30.43MJ/NM
3About 200 cubic metres of coal gas.Tar obtains the about 22kg of crude phenols, oil fuel 30kg, the about 40kg of heavy oil+pitch after condensation separation processing.
Because the God blessings coal is a bottle coal, 650 ℃ of pyrolysis obtain semicoke volatile matter (8.29%) near index 7% of the present invention, so embodiment 1 takes the simplification technology with pyrolysis carburetting associating.
The analytical data of God blessings coal sees Table 1.The productive rate of pyrolysis product and main proterties see Table 2.
Embodiment 2-3
Embodiment 4
With the Bao Rixile coal is that raw material (is the higher brown coal of water content, the analytical data of coal sees Table 1), take the final technology of carburetting (800 ℃) after the pyrolysis, product productive rate and main proterties see Table 2, reaction conditions sees Table 3, other condition is with embodiment 1, obtains volatile matter (6.44%) less than 7% shot coke product.
Claims (5)
1, a kind of process of coal pyrogenic decomposition of multi-stage rotary is characterized in that this technology comprises following steps:
(1) be that the feed coal of 3~30mm is sent in the dry rotary kiln and to be lower than 300 ℃ hot flue gases direct heat exchange dehydration with temperature with granularity, final drying temperature is 200~250 ℃;
(2) dried coal charge is sent into the pyrolysis rotary stove, coal charge is decomposed generation granular semicoke, tar steam and coal gas by the heat indirect heating that is provided by pyrolysis heater, and final pyrolysis temperature is 500~650 ℃;
(3) gas mixture of tar steam and coal gas is delivered in the condenser separated, obtain crude tar oil and coal gas;
(4) granular semicoke is sent in the carburetting rotary kiln, under 800~850 ℃ temperature, through the internal heat type heating, obtained shot coke and high-temperature gas mixture, gas mixture is imported into pyrolysis heater;
(5) will on vibratory screening apparatus, spray water by the shot coke that the carburetting rotary kiln is discharged and put out head, make product Jiao.
2, pyrolysis process technology as claimed in claim 1 is characterized in that described feed coal comprises brown coal, long-flame coal, non-caking coal, weakly caking coal, bottle coal or agriculture waste residue, wood chip and organic class rubbish.
3, pyrolysis process technology as claimed in claim 2 is characterized in that the moisture content of described brown coal is higher than 15%.
4, pyrolysis process technology as claimed in claim 1 is characterized in that obtaining raw gasline, gas oil, crude phenols, heavy oil and pitch by pyrogenous origin tar steam through condensation separation.
5, pyrolysis process technology as claimed in claim 1 is characterized in that described product Jiao's granularity is 3~20mm, and volatile matter is lower than 7%, or burnt as requested volatilization score value is regulated.