CN106626650B - 一种用于卫浴制品的高分子树脂环保板材 - Google Patents
一种用于卫浴制品的高分子树脂环保板材 Download PDFInfo
- Publication number
- CN106626650B CN106626650B CN201611050528.5A CN201611050528A CN106626650B CN 106626650 B CN106626650 B CN 106626650B CN 201611050528 A CN201611050528 A CN 201611050528A CN 106626650 B CN106626650 B CN 106626650B
- Authority
- CN
- China
- Prior art keywords
- plate
- panel
- resin
- macromolecule resin
- friendly sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种用于卫浴制品的高分子树脂环保板材,所述板材自上而下依次包括面板、衬板,所述面板为亚克力面板;所述衬板自上而下由面层和底层组成,所述面层为环氧树脂颗粒板,所述底层为泡沫层。所述环氧树脂颗粒板为再生环氧树脂复合玻璃纤维板。本发明提供的用于卫浴制品的高分子树脂环保板材,将风力发电的环氧树脂叶片进行再生利用,采用玻璃短纤维增强,提高了内衬板的强度,而且泡沫层吸音减震,与传统的亚克力板材相比具有更好消音效果。
Description
技术领域
本发明涉及一种用于卫浴制品的高分子树脂环保板材。
背景技术
现有的洁具产品可分为陶瓷和亚克力两大类。
亚克力,又叫PMMA或有机玻璃,源自英文acrylic(丙烯酸塑料),化学名称为聚甲基丙烯酸甲酯。是一种开发较早的重要可塑性高分子材料,具有较好的透明性、化学稳定性和耐候性、易染色、易加工、外观优美,在建筑业中有着广泛的应用。有机玻璃产品通常可以分为浇注板、挤出板和模塑料。
亚克力制造成的洁具相比金属和陶瓷洁具的原料成本会低许多,且性能非常好,因此具有价格优势和更强的市场竞争力。
亚克力洁具具有一定程度的自我复原特性,若是亚克力洁具的表面有划痕,洁具本身会有一定程度的自我修复功能。而且亚克力洁具的表面光滑洁白,清洗方便。
亚克力洁具的热传递很慢,因此保温效果良好,即使是在寒冷的冬天,皮肤接触亚克力洁具体表也不会感觉到“冰冷”的感觉。人体与亚克力洁具碰撞,一般不会碰痛躯体,是制造豪华洁具的必选材料。
亚克力洁具的结构大多为,亚克力面板、内衬板以及支撑架。
内衬板大多采用玻璃钢,或玻璃纤维板。这种内衬强度有限,如作为马桶或浴缸可能存在局部强度的不足。
我国风电行业的迅猛发展为叶片用环氧结构胶粘剂和环氧基体树脂的应用提供了巨大的市场空间。环氧基体树脂是生产叶片和叶片模具的主体材料之一,环氧树脂结构胶用于风电叶片上壳体和下壳体的粘接。
目前,国内风电机组绝大多数为1.5MW的机型,每个机组需要三个叶片,每个叶片环氧结构胶的用量约为0.35吨,环氧基体树脂的用量约为2吨。这种叶片的寿命为10-15年,而风力发电叶片的环氧树脂并不是纯净物,存在各种各样的组分和配方,环氧树脂很难降解,因此,如何利用废旧的叶片成为业界的难题。
发明内容
为解决上述现有技术存在的不足,本发明提供了一种用于卫浴制品的高分子树脂环保板材,将风力发电的环氧树脂叶片进行再生利用,提高了现有亚克力洁具的内衬强度。
本发明采用的技术方案是:
一种用于卫浴制品的高分子树脂环保板材,所述板材自上而下依次包括面板、衬板,所述面板为亚克力面板;所述衬板自上而下由面层和底层组成,所述面层为环氧树脂颗粒板,所述底层为泡沫层。
所述面板的厚度为1~50mm,衬板厚度为1~40mm,其中面层厚度为0.5~20mm,泡沫层厚度为0.5~20mm
所述环氧树脂颗粒板为再生环氧树脂复合玻璃纤维板,由环氧树脂叶片再生制成,具体的,所述环氧树脂颗粒板包括再生环氧树脂颗粒、高分子树脂、玻璃短纤维、填充剂、改良剂。
所述环氧树脂颗粒板中,再生环氧树脂颗粒、高分子树脂、玻璃短纤维、填充剂、改良剂的质量份数各自为30~60份、20~50份、10~40份、5~20份、1~10份。
进一步,所述再生环氧树脂颗粒是将风力发电的环氧树脂叶片切割、粉碎成粒径为1~5mm的颗粒得到;
所述高分子树脂为不饱和聚酯树脂,进一步,所述不饱和聚酯树脂优选为邻苯型不饱和聚酯树脂,更优选为196树脂和191树脂,质量比为1:0.5~3。
所述191树脂可采用再生191树脂,是将191树脂边角料粉碎成粒径1~10mm的颗粒得到。
所述玻璃短纤维是指纤维长度0.1~10mm的玻璃纤维,优选0.2~5mm。
所述填充剂为石英粉、氢氧化铝粉、二氧化硅粉、大理石粉、碳酸钙粉中的一种或两种以上的混合。
所述改良剂为增韧剂、抗老剂、阻燃剂、增容剂中的一种或两种以上的混合。
所述面板与衬板中间可以垫有图案纸;使板材呈现不同图案色彩。
所述增韧剂可以为邻苯二甲酸二辛酯、邻苯二甲酸二丁脂、聚醋酸乙烯或者氯化石蜡等。
所述环氧树脂颗粒板是将各原料混合后,直接浇筑或用热压机热压制成。
所述底层为泡沫层,起到吸音减震的作用。所述泡沫层可以为聚氨酯泡沫和/或不饱和聚酯泡沫。
所述高分子树脂环保板材还可以包括底板,所述底板设于衬板之下,可以为支撑板或支撑架,所述支撑板可以为木板、塑料板、亚克力板等,所述支撑架可以为木支架、钢管架等。
所述高分子树脂环保板材的面板、衬板之间或面层、底层可通过胶合和/或热压复合。
本发明提供的用于卫浴制品的高分子树脂环保板材,将风力发电的环氧树脂叶片进行再生利用,采用玻璃短纤维增强,提高了内衬板的强度,而且泡沫层吸音减震,与传统的亚克力板材相比具有更好消音效果,而且特别适用于台盆、马桶等卫浴产品;节能环保,解决了环氧树脂的回收利用难题。
附图说明
图1实施例1的用于卫浴制品的高分子树脂环保板材的剖面结构图。
图2实施例2的用于卫浴制品的高分子树脂环保板材的剖面结构图。
图3实施例3的用于卫浴制品的高分子树脂环保板材的剖面结构图。
图中,1为面板,2为衬板,3为底板,2-1为面层,2-2为底层,4为图案纸。
具体实施方式
下面以具体实施例来对本发明的技术方案做进一步说明,但本发明的保护范围不限于此。
实施例1
一种用于卫浴制品的高分子树脂环保板材,一个实施方式如图1所示,所述板材自上而下依次包括面板1、衬板2,所述面板1为亚克力面板;所述衬板自上而下由面层2-1和底层2-2组成,所述面层2-1为环氧树脂颗粒板,所述底层2-2为泡沫层。面板、面层和底层之间通过胶合和/或热压复合。
所述环氧树脂颗粒板为再生环氧树脂复合玻璃纤维板,由环氧树脂叶片再生制成,具体的,所述环氧树脂颗粒板由再生环氧树脂颗粒、高分子树脂、玻璃短纤维、填充剂、改良剂组成。
在本实施例中,环氧树脂颗粒板中,再生环氧树脂颗粒、高分子树脂、玻璃短纤维、填充剂、改良剂的质量份数各自为60份、50份、20份、10份、5份。
所述再生环氧树脂颗粒是将风力发电的环氧树脂叶片切割、粉碎成棒材,然后切割、粉碎成粒径为1~5mm的颗粒;
所述高分子树脂为质量比1:2的196树脂和191树脂,所述191树脂可采用再生191树脂,将191树脂边角料粉碎成粒径1~5mm的颗粒得到。
所述玻璃短纤维是指纤维长度1~3mm的玻璃纤维。
所述填充剂为碳酸钙粉。
所述改良剂为增韧剂。
所述环氧树脂颗粒板是将各原料混合后,经热压机热压制成。
所述底层为泡沫层,起到吸音减震的作用。所述泡沫层为聚氨酯吸音泡沫。
在一个优选的实施方式中,所述面板1厚度为1mm;面层2-1厚度为2mm,底层2-2厚度为1mm。即衬板厚度为3mm。压缩强度260MPa。
实施例2
一种用于卫浴制品的高分子树脂环保板材,一个实施方式如图2所示,所述板材自上而下依次包括面板1、衬板、底板3,所述面板1为亚克力面板;所述衬板自上而下由面层2-1和底层2-2组成,所述面层2-1为环氧树脂颗粒板,所述底层2-2为泡沫层。所述底板3为亚克力板,面板、面层、底层、底板之间通过胶合和/或热压复合。
所述环氧树脂颗粒板由环氧树脂叶片再生制成,具体的,所述环氧树脂颗粒板由再生环氧树脂颗粒、高分子树脂、玻璃短纤维、填充剂、改良剂组成。
在本实施例中,环氧树脂颗粒板中,再生环氧树脂颗粒、高分子树脂、玻璃短纤维、填充剂、改良剂的质量份数各自为30份、40份、20份、10份、3份。
所述高分子树脂为质量比1:1的196树脂和191树脂。
所述玻璃短纤维是指纤维长度0.2~1mm的玻璃纤维。
所述填充剂为碳酸钙粉。
所述改良剂为增韧剂。
所述环氧树脂颗粒板是将各原料混合后,经热压机热压制成。
所述底层为泡沫层,起到吸音减震的作用。所述泡沫层为聚氨酯吸音泡沫。
在一个优选的实施方式中,所述面板1厚度为3mm;面层2-1厚度为5mm,底层2-2厚度为3mm,底板3厚度为3mm。压缩强度270MPa。
实施例3
一种用于卫浴制品的高分子树脂环保板材,一个实施方式如图3所示,所述板材自上而下依次包括面板1、图案纸4,衬板,所述面板1为亚克力面板;所述衬板自上而下由面层2-1和底层2-2组成,所述面层2-1为环氧树脂颗粒板,所述底层2-2为泡沫层。图案纸设于面板与衬板中间。面板、图案纸、面层、底层之间通过胶合和/或热压复合。
所述环氧树脂颗粒板由环氧树脂叶片再生制成,具体的,所述环氧树脂颗粒板由再生环氧树脂颗粒、高分子树脂、玻璃短纤维、填充剂、改良剂组成。
在本实施例中,环氧树脂颗粒板中,再生环氧树脂颗粒、高分子树脂、玻璃短纤维、填充剂、改良剂的质量份数各自为40份、20份、10份、5份、1份。
所述高分子树脂为质量比1:0.5的196树脂和191树脂。
所述玻璃短纤维是指纤维长度1~5mm的玻璃纤维。
所述填充剂为二氧化硅粉。
所述改良剂为增韧剂。
所述环氧树脂颗粒板是将各原料混合后,经浇筑制成。
所述底层为泡沫层,起到吸音减震的作用。所述泡沫层为聚氨酯吸音泡沫。
在一个优选的实施方式中,所述面板1厚度为3mm;图案纸4厚度为0.1mm,面层2-1厚度为4mm,底层2-2厚度为3mm。压缩强度265MPa。
Claims (5)
1.一种用于卫浴制品的高分子树脂环保板材,其特征在于所述板材自上而下依次包括面板、衬板,所述面板为亚克力面板;所述衬板自上而下由面层和底层组成,所述面层为环氧树脂颗粒板,所述底层为泡沫层;所述环氧树脂颗粒板包括再生环氧树脂颗粒、高分子树脂、玻璃短纤维、填充剂、改良剂;所述环氧树脂颗粒板中,再生环氧树脂颗粒、高分子树脂、玻璃短纤维、填充剂、改良剂的质量份数各自为30~60份、20~50份、10~40份、5~20份、1~10份;所述再生环氧树脂颗粒是将风力发电的环氧树脂叶片切割、粉碎成粒径为1~5mm的颗粒得到;所述高分子树脂为不饱和聚酯树脂,所述不饱和聚酯树脂为196树脂和191树脂,质量比为1:0.5~3。
2.如权利要求1所述的用于卫浴制品的高分子树脂环保板材,其特征在于所述面板的厚度为1~50mm,衬板厚度为1~40mm,其中面层厚度为0.5~20mm,泡沫层厚度为0.5~20mm。
3.如权利要求1所述的用于卫浴制品的高分子树脂环保板材,其特征在于所述面板与衬板中间垫有图案纸。
4.如权利要求1所述的用于卫浴制品的高分子树脂环保板材,其特征在于所述底层为泡沫层,所述泡沫层为聚氨酯泡沫和/或不饱和聚酯泡沫。
5.如权利要求1所述的用于卫浴制品的高分子树脂环保板材,其特征在于所述高分子树脂环保板材还包括底板,所述底板设于衬板之下。