CN106585014A - 一种耐热高强度复合塑料制品 - Google Patents
一种耐热高强度复合塑料制品 Download PDFInfo
- Publication number
- CN106585014A CN106585014A CN201611180432.0A CN201611180432A CN106585014A CN 106585014 A CN106585014 A CN 106585014A CN 201611180432 A CN201611180432 A CN 201611180432A CN 106585014 A CN106585014 A CN 106585014A
- Authority
- CN
- China
- Prior art keywords
- parts
- accounts
- heat
- tube layer
- vinyon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明揭示了一种耐热高强度复合塑料制品，包括外部的第一复合管层和内部的第二复合管层，所述第一复合管层由聚乙烯塑料、耐热剂、热稳定剂、填充剂以及分散剂组成，所述耐热剂为聚戊二酰亚胺，所述热稳定剂为水合三盐基硫酸铅，所述填充剂为石棉纤维，所述分散剂为三乙基己基磷酸，所述第二复合管层由聚乙烯塑料、光稳定剂、增韧剂、表面活性剂以及补强剂组成，所述光稳定剂为2，4‑二羟基二苯甲酮，所述增韧剂为丁腈橡胶，所述表面活性剂为十二烷基苯磺酸钠，所述补强剂为碳纤维。本发明采用复合结构设置，具有耐高温、热稳定性好、韧性好、强度高、耐老化性好及使用寿命长的特点。
Description
技术领域
本发明涉及一种耐热高强度复合塑料制品。
背景技术
聚乙烯是乙烯经聚合制得的一种热塑性树脂。在工业上，也包括乙烯与少量α-烯烃的共聚物。聚乙烯无臭，无毒，手感似蜡，具有优良的耐低温性能（最低使用温度可达-100~-70°C），化学稳定性好，能耐大多数酸碱的侵蚀（不耐具有氧化性质的酸）。常温下不溶于一般溶剂，吸水性小，电绝缘性优良，有优异的化学稳定性，但是聚乙烯制品同样存在随温度升高而软化的缺点。
发明内容
本发明的目的在于提供一种采用复合结构设置，具有耐高温、热稳定性好、韧性好、强度高、耐老化性好及使用寿命长的特点的耐热高强度复合塑料制品。
本发明的技术方案是，一种耐热高强度复合塑料制品，包括外部的第一复合管层和内部的第二复合管层，所述第一复合管层由聚乙烯塑料、耐热剂、热稳定剂、填充剂以及分散剂组成，所述耐热剂为聚戊二酰亚胺，所述热稳定剂为水合三盐基硫酸铅，所述填充剂为石棉纤维，所述分散剂为三乙基己基磷酸，所述第一复合管层各成分所占重量份数分别为：所述聚乙烯塑料占70-77份，所述聚戊二酰亚胺占5-9份，所述水合三盐基硫酸铅占3-7份，所述石棉纤维占28-33份，所述三乙基己基磷酸占1-5份，所述第二复合管层由聚乙烯塑料、光稳定剂、增韧剂、表面活性剂以及补强剂组成，所述光稳定剂为2，4-二羟基二苯甲酮，所述增韧剂为丁腈橡胶，所述表面活性剂为十二烷基苯磺酸钠，所述补强剂为碳纤维，所述第二复合管层各成分所占重量份数分别为：所述聚乙烯塑料占79-86份，所述2，4-二羟基二苯甲酮占4-8份，所述丁腈橡胶占15-20份，所述十二烷基苯磺酸钠占2-6份，所述碳纤维占36-42份。
在本发明一个较佳实施例中，所述第一复合管层各成分所占重量份数具体为：所述聚乙烯塑料占76份，所述聚戊二酰亚胺占8份，所述水合三盐基硫酸铅占6份，所述石棉纤维占32份，所述三乙基己基磷酸占4份。
在本发明一个较佳实施例中，所述第一复合管层各成分所占重量份数具体为：所述聚乙烯塑料占71份，所述聚戊二酰亚胺占6份，所述水合三盐基硫酸铅占4份，所述石棉纤维占29份，所述三乙基己基磷酸占2份。
在本发明一个较佳实施例中，所述第一复合管层各成分所占重量份数具体为：所述聚乙烯塑料占73份，所述聚戊二酰亚胺占7份，所述水合三盐基硫酸铅占5份，所述石棉纤维占30份，所述三乙基己基磷酸占3份。
在本发明一个较佳实施例中，所述第二复合管层各成分所占重量份数具体为：所述聚乙烯塑料占85份，所述2，4-二羟基二苯甲酮占7份，所述丁腈橡胶占19份，所述十二烷基苯磺酸钠占5份，所述碳纤维占41份。
在本发明一个较佳实施例中，所述第二复合管层各成分所占重量份数具体为：所述聚乙烯塑料占80份，所述2，4-二羟基二苯甲酮占5份，所述丁腈橡胶占16份，所述十二烷基苯磺酸钠占3份，所述碳纤维占37份。
在本发明一个较佳实施例中，所述第二复合管层各成分所占重量份数具体为：所述聚乙烯塑料占82份，所述2，4-二羟基二苯甲酮占6份，所述丁腈橡胶占18份，所述十二烷基苯磺酸钠占4份，所述碳纤维占39份。
本发明所述为一种耐热高强度复合塑料制品，采用复合结构设置，具有耐高温、热稳定性好、韧性好、强度高、耐老化性好及使用寿命长的特点。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
本发明所述为一种耐热高强度复合塑料制品，包括外部的第一复合管层和内部的第二复合管层，所述第一复合管层由聚乙烯塑料、耐热剂、热稳定剂、填充剂以及分散剂组成，所述耐热剂为聚戊二酰亚胺，所述热稳定剂为水合三盐基硫酸铅，所述填充剂为石棉纤维，所述分散剂为三乙基己基磷酸，所述第一复合管层各成分所占重量份数分别为：所述聚乙烯塑料占70-77份，所述聚戊二酰亚胺占5-9份，所述水合三盐基硫酸铅占3-7份，所述石棉纤维占28-33份，所述三乙基己基磷酸占1-5份，所述第二复合管层由聚乙烯塑料、光稳定剂、增韧剂、表面活性剂以及补强剂组成，所述光稳定剂为2，4-二羟基二苯甲酮，所述增韧剂为丁腈橡胶，所述表面活性剂为十二烷基苯磺酸钠，所述补强剂为碳纤维，所述第二复合管层各成分所占重量份数分别为：所述聚乙烯塑料占79-86份，所述2，4-二羟基二苯甲酮占4-8份，所述丁腈橡胶占15-20份，所述十二烷基苯磺酸钠占2-6份，所述碳纤维占36-42份。
进一步地，所述第一复合管层各成分所占重量份数具体为：所述聚乙烯塑料占76份，所述聚戊二酰亚胺占8份，所述水合三盐基硫酸铅占6份，所述石棉纤维占32份，所述三乙基己基磷酸占4份。
进一步地，所述第一复合管层各成分所占重量份数具体为：所述聚乙烯塑料占71份，所述聚戊二酰亚胺占6份，所述水合三盐基硫酸铅占4份，所述石棉纤维占29份，所述三乙基己基磷酸占2份。
进一步地，所述第一复合管层各成分所占重量份数具体为：所述聚乙烯塑料占73份，所述聚戊二酰亚胺占7份，所述水合三盐基硫酸铅占5份，所述石棉纤维占30份，所述三乙基己基磷酸占3份。
进一步地，所述第二复合管层各成分所占重量份数具体为：所述聚乙烯塑料占85份，所述2，4-二羟基二苯甲酮占7份，所述丁腈橡胶占19份，所述十二烷基苯磺酸钠占5份，所述碳纤维占41份。
进一步地，所述第二复合管层各成分所占重量份数具体为：所述聚乙烯塑料占80份，所述2，4-二羟基二苯甲酮占5份，所述丁腈橡胶占16份，所述十二烷基苯磺酸钠占3份，所述碳纤维占37份。
进一步地，所述第二复合管层各成分所占重量份数具体为：所述聚乙烯塑料占82份，所述2，4-二羟基二苯甲酮占6份，所述丁腈橡胶占18份，所述十二烷基苯磺酸钠占4份，所述碳纤维占39份。
另外，可通过调节产品各成分的不同重量份数，使得得到的产品性能高低不一。
本发明所述为一种耐热高强度复合塑料制品，采用复合结构设置，具有耐高温、热稳定性好、韧性好、强度高、耐老化性好及使用寿命长的特点。
以上所述仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本领域的技术人员在本发明所揭露的技术范围内，可不经过创造性劳动想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (7)
1.一种耐热高强度复合塑料制品，其特征在于：包括外部的第一复合管层和内部的第二复合管层，所述第一复合管层由聚乙烯塑料、耐热剂、热稳定剂、填充剂以及分散剂组成，所述耐热剂为聚戊二酰亚胺，所述热稳定剂为水合三盐基硫酸铅，所述填充剂为石棉纤维，所述分散剂为三乙基己基磷酸，所述第一复合管层各成分所占重量份数分别为：所述聚乙烯塑料占70-77份，所述聚戊二酰亚胺占5-9份，所述水合三盐基硫酸铅占3-7份，所述石棉纤维占28-33份，所述三乙基己基磷酸占1-5份，所述第二复合管层由聚乙烯塑料、光稳定剂、增韧剂、表面活性剂以及补强剂组成，所述光稳定剂为2，4-二羟基二苯甲酮，所述增韧剂为丁腈橡胶，所述表面活性剂为十二烷基苯磺酸钠，所述补强剂为碳纤维，所述第二复合管层各成分所占重量份数分别为：所述聚乙烯塑料占79-86份，所述2，4-二羟基二苯甲酮占4-8份，所述丁腈橡胶占15-20份，所述十二烷基苯磺酸钠占2-6份，所述碳纤维占36-42份。
2.根据权利要求1所述的耐热高强度复合塑料制品，其特征在于：所述第一复合管层各成分所占重量份数具体为：所述聚乙烯塑料占76份，所述聚戊二酰亚胺占8份，所述水合三盐基硫酸铅占6份，所述石棉纤维占32份，所述三乙基己基磷酸占4份。
3.根据权利要求1所述的耐热高强度复合塑料制品，其特征在于：所述第一复合管层各成分所占重量份数具体为：所述聚乙烯塑料占71份，所述聚戊二酰亚胺占6份，所述水合三盐基硫酸铅占4份，所述石棉纤维占29份，所述三乙基己基磷酸占2份。
4.根据权利要求1所述的耐热高强度复合塑料制品，其特征在于：所述第一复合管层各成分所占重量份数具体为：所述聚乙烯塑料占73份，所述聚戊二酰亚胺占7份，所述水合三盐基硫酸铅占5份，所述石棉纤维占30份，所述三乙基己基磷酸占3份。
5.根据权利要求1所述的耐热高强度复合塑料制品，其特征在于：所述第二复合管层各成分所占重量份数具体为：所述聚乙烯塑料占85份，所述2，4-二羟基二苯甲酮占7份，所述丁腈橡胶占19份，所述十二烷基苯磺酸钠占5份，所述碳纤维占41份。
6.根据权利要求1所述的耐热高强度复合塑料制品，其特征在于：所述第二复合管层各成分所占重量份数具体为：所述聚乙烯塑料占80份，所述2，4-二羟基二苯甲酮占5份，所述丁腈橡胶占16份，所述十二烷基苯磺酸钠占3份，所述碳纤维占37份。
7.根据权利要求1所述的耐热高强度复合塑料制品，其特征在于：所述第二复合管层各成分所占重量份数具体为：所述聚乙烯塑料占82份，所述2，4-二羟基二苯甲酮占6份，所述丁腈橡胶占18份，所述十二烷基苯磺酸钠占4份，所述碳纤维占39份。