CN106567510A - 一种马尾松叶隔音瓷砖 - Google Patents
一种马尾松叶隔音瓷砖 Download PDFInfo
- Publication number
- CN106567510A CN106567510A CN201510649162.2A CN201510649162A CN106567510A CN 106567510 A CN106567510 A CN 106567510A CN 201510649162 A CN201510649162 A CN 201510649162A CN 106567510 A CN106567510 A CN 106567510A
- Authority
- CN
- China
- Prior art keywords
- pinus massoniana
- ceramic tile
- sound insulation
- leaves
- granular
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种马尾松叶隔音瓷砖,包括马尾松叶填充物、天然瓷泥,其技术特征是:将颗粒状马尾松叶均匀混充于天然瓷泥中,通过焙烧将颗粒状马尾松叶炭化或气化而形成多孔砖材。所述马尾松叶颗粒、天然瓷泥的基本比例为1∶1,所述马尾松叶颗粒的长度为1-2mm。本发明的积极效果与优点:一是环保、质轻、省料、生产与使用成本低;二是拒水透气性强,自重轻,具有柔性,耐酸碱耐冻融,抗震,抗裂,与外墙外保温体系相容性很好;三是隔音性强,美观大方;四是易于施工,粘贴方便。
Description
技术领域
本发明涉及一种隔音材料,特别涉及到一种马尾松叶隔音瓷砖。
背景技术
马尾松分布极广,北自河南及山东南部,南至两广、湖南(慈利县)、台湾,东自沿海,西至四川中部及贵州,遍布于华中华南各地。一般在长江下游海拔600~700m以下,中游约1200m以上,上游约1500m以下均有分布。是中国南部主要材用树种。经济价值高。
马尾松不耐腐。心边材区别不明显,淡黄褐色,长纵裂,长片状剥落;木材纹理直,结构粗;含树脂,耐水湿。比重0.39~0.49,有弹性,富树脂,耐腐力弱。是重要的用材树种,也是荒山造林的先锋树种。其经济价值高,用途广,松木是工农业生产上的重要用材,主要供建筑、枕木、矿柱、制板、包装箱、家具及木纤维工业(人造丝浆及造纸)原料等用。树干可割取松脂,为医药、化工原料。根部树脂含量丰富;树干及根部可培养茯苓、蕈类,供中药及食用,树皮可提取栲胶。为长江流域以南重要的荒山造林树种。
马尾松为乔木,高达45米,胸径1.5米;树皮红褐色,下部灰褐色,裂成不规则的鳞状块片;枝平展或斜展,树冠宽塔形或伞形,枝条每年生长一轮,但在广东南部则通常生长两轮,淡黄褐色,无白粉,稀有白粉,无毛;冬芽卵状圆柱形或圆柱形,褐色,顶端尖,芽鳞边缘丝状,先端尖或成渐尖的长尖头,微反曲。
马尾松针叶2针一束,稀3针一束,长12-20厘米,细柔,微扭曲,两面有气孔线,边缘有细锯齿;横切面皮下层细胞单型,第一层连续排列,第二层由个别细胞断续排列而成,树脂道约4-8个,在背面边生,或腹面也有2个边生;叶鞘初呈褐色,后渐变成灰黑色,宿存。
马尾松在整个生长过程中,连年生长量最大值出现在10年,在20年时又出现接近最大值,平均生长量最大值出现在10~15年之间(11年左右),平均生长量曲线与连年生长量曲线相交于10~15年之间(12年左右),此后连年生长量小于平均生长量,此时应进行抚育间伐,以保证林木充足的营养空间,满足树冠生长发育的需要,所以在本立地和经营条件下,第一次间伐年龄应在12年左右,但实际生产上第一次间伐在18年,显得偏迟。
马尾松平均生长量与连年生长量在20年生左右,出现第2次相交,这是由于第一次间伐(18年)后改善了林分卫生状况,扩大林木树冠的营养空间,形成了一段高速生长期。整个生长过程与实际生产经营管理情况相吻合,5~10年生是幼林生长阶段,树高生长较快;从第10年~25年生,树高连年生长量都超0.6m,是马尾松树高生长的旺盛时期;20之后连年生长量又急剧下降,在25生时进行大强度抚育间伐,从而减缓高生长急剧下降。
广东雷州半岛沿海、广西北海及钦州湾沿海等均种植有大量的马尾松作为海岸防护(风)林,马尾松的生长周期快,每天的落叶很是可观,在过去,村子里的一般人家基本上都是靠(每天)耙落叶做饭烧菜。显然,一片海滩或树林中的落叶量是惊人的,收集不仅方便,而且廉价。另外,树木砍阀时,数量颇多的树叶若是废弃则是浪费,若是焚烧则是污染环境。
瓷砖是以耐火的金属氧化物及半金属氧化物,经由研磨、混合、压制、施釉、烧结之过程,而形成的一种耐酸碱的瓷质或石质等,建筑或装饰材料,称之为瓷砖。其原材料多由粘土、石英砂等等混合而成。瓷砖优势:
1、性能优势:拒水透气性强,自重轻,具有柔性,耐酸碱耐冻融,抗震,抗裂,与外墙外保温体系相容性很好。
2、安全优势。软瓷技术产品完全克服了陶瓷砖、马赛克等易脱落伤人的安全隐患,尤其适合作为高层建筑和外墙外保温系统的外墙饰面材料。
3、表现力优势。软瓷材料可随意赋形,突破了传统陶瓷砖的造型局限,软瓷技术产品具有古今中外所有建筑材料的集成能力,各种天然石材、土窖烧制劈开砖、各种天然木板、建筑清水、陶瓷砖、铝塑板、各种现代艺术精品、各种历代皇朝奢侈品——软瓷技术,均可快速克隆!同时,可逼真表现天然装饰材料,如木、皮、石、砖、布、金属等的纹理和颜色,也可按设计师的构想制造具有鲜明个性色彩的装饰纹理和颜色。
4、施工优势。尤其是在旧墙改造或空间翻新时,不需敲掉原有旧瓷砖和马赛克,可直接将MCM材料粘贴其上。
5、节能减排优势。软瓷技术产品的生产线燃料摒弃煤炭、重油等高污染原料,选用电能和太阳能,力求干净,来源有保障;生产过程中无废水、废气、粉尘排放,且所有废料可回收再利用。
6、环保优势。检测结果表明,MCM材料的放射性和可溶性铅镉含量远远低于环境标志产品陶瓷砖的要求;不含TVOC,并且当MCM材料使用到一定的 年限,或其款式、色彩需要更新时,可完全将其回收再加工成新品或重新还原成泥土用于耕种。
瓷砖通常是不隔音的,但是,如果通过马尾松叶颗粒作为填充物混入瓷泥丕中烧制瓷砖,利用瓷砖的优势将其改变成多孔材料无疑可以获得一种与众不同的隔音材料。
发明内容
本发明的目的是提出一种以马尾松叶颗粒作为填充物的隔音瓷砖,以实现上述目的。
本发明提供的一种马尾松叶隔音瓷砖,包括马尾松叶填充物、天然瓷泥,其技术特征是:将颗粒状马尾松叶均匀混充于天然瓷泥中,通过焙烧将颗粒状马尾松叶炭化或气化而形成多孔砖材。所述马尾松叶颗粒、天然瓷泥的基本比例为1∶1,所述马尾松叶颗粒的长度为1-2mm。
所述马尾松叶颗粒通过机械切割获取。
所述马尾松叶颗粒通过人工切割获取。通过人工切割获取的马尾松叶颗粒为收购所得。
由于马尾松的叶呈针状,2针一束或稀3针一束,长12-20厘米且细柔。因此,这是制作微孔不可多得的现成的精细与均匀原料(加上切割)。
本发明的积极效果与优点:一是环保、质轻、省料、生产与使用成本低;二是拒水透气性强,自重轻,具有柔性,耐酸碱耐冻融,抗震,抗裂,与外墙外保温体系相容性很好;三是隔音性强,美观大方;四是易于施工,粘贴方便。
实施方式
一种马尾松叶隔音瓷砖,包括马尾松叶填充物、天然瓷泥,其技术特征 是:将颗粒状马尾松叶均匀混充于天然瓷泥中,通过焙烧将颗粒状马尾松叶炭化或气化而形成多孔砖材。所述马尾松叶颗粒、天然瓷泥的基本比例为1.1∶0.9,所述马尾松叶颗粒的长度为1.5mm。所述马尾松叶颗粒通过机械切割获取。
所述马尾松叶为自然干燥原料。
本实施方式的生产工艺流程为:马尾松叶原料→切割→按比例与天然瓷泥丕浆拌搅→成形并凉干凝结→焙烧→成品。
Claims (1)
1.一种马尾松叶隔音瓷砖,包括马尾松叶填充物、天然瓷泥,其技术特征是:将颗粒状马尾松叶均匀混充于天然瓷泥中,通过焙烧将颗粒状马尾松叶炭化或气化而形成多孔砖材。所述马尾松叶颗粒、天然瓷泥的基本比例为1∶1,所述马尾松叶颗粒的长度为1-2mm。