CN106554617A - 一种高强度的聚酰胺材料 - Google Patents

一种高强度的聚酰胺材料 Download PDF

Info

Publication number
CN106554617A
CN106554617A CN201611090363.4A CN201611090363A CN106554617A CN 106554617 A CN106554617 A CN 106554617A CN 201611090363 A CN201611090363 A CN 201611090363A CN 106554617 A CN106554617 A CN 106554617A
Authority
CN
China
Prior art keywords
parts
high intensity
polyamide
polyamide material
graphene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611090363.4A
Other languages
English (en)
Inventor
朱世昌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu New Material Co Ltd
Original Assignee
Jiangsu New Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu New Material Co Ltd filed Critical Jiangsu New Material Co Ltd
Priority to CN201611090363.4A priority Critical patent/CN106554617A/zh
Publication of CN106554617A publication Critical patent/CN106554617A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高强度的聚酰胺材料，由下述重量份的原料制备而成：石墨烯2‑10份，PA40‑100份，氢氧化镁4‑6份，KH270 1‑7份，有机蒙脱土10‑30份，玻纤0‑45份，纳米氢氧化铝2‑18份，EVA 15‑35份，磷酸三苯酯10‑20份，硬脂酸0.5‑2.5份。本发明提供的高强度的聚酰胺材料解决了常规聚酰胺材料拉伸强度差的缺点,提升了材料的性能，扩大了材料的应用范围。

Description

一种高强度的聚酰胺材料
技术领域
本申请属于聚氨酯材料技术领域，特别是涉及一种高强度的聚酰胺材料
背景技术
聚酰胺是一种应用广泛的工程塑料，由其特殊的分子结构，使其具有优良的物理机械性能。然而由于聚酰胺含酰胺极性基团，因此吸水率高，热变型温度低，模量和强度不高限制了更广泛的应用。于是对聚酰胺材料进行改性，提高其强度和模量具有积极意义。中国专利CN1510084A公开了一种制备超强尼龙的方法，使用带活性反应基团的增容剂提高强度，但是，由于该专利方案推荐的原料来源困难，因此难以适应大规模的工业化放大生产。鉴此有必要加以改进。
发明内容
本发明的目的在于提供一种高强度的聚酰胺材料，以克服现有技术中的不足。
为实现上述目的，本发明提供如下技术方案：
本申请实施例公开一种高强度的聚酰胺材料，由下述重量份的原料制备而成：石墨烯2-10份，PA40-100份，氢氧化镁4-6份，KH270 1-7份，有机蒙脱土10-30份，玻纤0-45份，纳米氢氧化铝2-18份，EVA 15-35份，磷酸三苯酯10-20份，硬脂酸0.5-2.5份。
此外，本发明还提供如下附属技术方案：
由下述重量份的原料制备而成：石墨烯10份，尼龙100份，氢氧化镁4份，KH270 7份，有机蒙脱土10份，玻纤45份，纳米氢氧化铝8份，EVA 35份，磷酸三苯酯10份，硬脂酸2.5份。
与现有技术相比，本发明的聚酰胺材料解决了常规聚酰胺材料拉伸强度差的缺点,提升了材料的性能，扩大了材料的应用范围。
具体实施方式
下面对本发明实施例中的技术方案进行详细的描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动的前提下所获得的所有其他实施例，都属于本发明保护的范围。
聚酰胺(俗称尼龙)材料，具有良好的综合性能，包括力学性能、耐热性、耐磨损性、耐化学药品性和自润滑性，且摩擦系数低，有一定的阻燃性，易于加工，适于用玻璃纤维和其它填料填充增强改性，提高性能和扩大应用范围。尽管尼龙加玻璃纤维可以增强产品的拉伸强度，但有些场合还是无法满足要求，如混凝土的链接，金属材料的替代等。
石墨烯是由碳原子构成的只有一层原子厚度的二维晶体。自2004年被发现以来，由于其高导电性、高强度、超轻薄等特性，世界各国都对其进行积极的研究和深入的应用。随着批量化生产以及大尺寸等难题的逐步突破，石墨烯的产业化应用步伐正在加快，基于已有的研究成果，最先实现商业化应用的领域包括移动设备、航空航天、新能源电池领域。另外，在塑料里掺入百分之一的石墨烯，就能使塑料具备良好的导电性；加入千分之一的石墨烯，能使塑料的抗热性能提高30摄氏度。在此基础上可以研制出薄、轻、拉伸性好和超强韧新型材料，用于制造汽车、飞机、卫星等等。
实施例1
一种高强度的聚酰胺材料的制备，按重量份计，由以下组分制备而成：石墨烯10份，尼龙100份，氢氧化镁4份，KH270 7份，有机蒙脱土10份，玻纤45份，纳米氢氧化铝8份，EVA 35份，磷酸三苯酯10份，硬脂酸2.5份。
实施例2
一种高强度的聚酰胺材料的制备，按重量份计，由以下组分制备而成：石墨烯5份，尼龙80份，氢氧化镁6份，KH270 4份，有机蒙脱土20份，玻纤25份，纳米氢氧化铝6份，EVA 18份，磷酸三苯酯10份，硬脂酸1.5份。
实施例3
一种高强度的聚酰胺材料的制备，按重量份计，由以下组分制备而成：石墨烯2份，尼龙40份，氢氧化镁4份，KH270 1份，有机蒙脱土10份，玻纤15份，纳米氢氧化铝2份，EVA 15份，磷酸三苯酯10份，硬脂酸0.5份。
比较例1
一种常规聚酰胺材料的制备，按重量份计，由以下组分制备而成：尼龙100份，氢氧化镁6份，KH270 5份，有机蒙脱土10份，玻纤35份，纳米氢氧化铝2份，EVA 15份，磷酸三苯酯10份，硬脂酸1.5份。
名称 拉伸强度MPa 环境条件
实施例1 325 常温常压
实施例2 235 常温常压
实施例3 195 常温常压
比较例1 185 常温常压
与现有技术相比，本发明的聚酰胺材料解决了常规聚酰胺材料拉伸强度差的缺点,提升了材料的性能，扩大了材料的应用范围。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。在没有更多限制的情况下，由语句“包括一个……”限定的要素，并不排除在包括所述要素的过程、方法、物品或者设备中还存在另外的相同要素。
以上所述仅是本申请的具体实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本申请原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本申请的保护范围。

Claims (2)

1.一种高强度的聚酰胺材料，其特征在于，由下述重量份的原料制备而成：石墨烯2-10份，PA40-100份，氢氧化镁4-6份，KH270 1-7份，有机蒙脱土10-30份，玻纤0-45份，纳米氢氧化铝2-18份，EVA 15-35份，磷酸三苯酯10-20份，硬脂酸0.5-2.5份。
2.根据权利要求1所述的具有高强度的聚酰胺材料，其特征在于，由下述重量份的原料制备而成：石墨烯10份，尼龙100份，氢氧化镁4份，KH2707份，有机蒙脱土10份，玻纤45份，纳米氢氧化铝8份，EVA 35份，磷酸三苯酯10份，硬脂酸2.5份。
CN201611090363.4A 2016-12-01 2016-12-01 一种高强度的聚酰胺材料 Pending CN106554617A (zh)