CN106521765A - Manufacture method of fabrics blended by bamboo pulp fiber and tencel - Google Patents

Manufacture method of fabrics blended by bamboo pulp fiber and tencel Download PDF

Info

Publication number
CN106521765A
CN106521765A CN201610932356.8A CN201610932356A CN106521765A CN 106521765 A CN106521765 A CN 106521765A CN 201610932356 A CN201610932356 A CN 201610932356A CN 106521765 A CN106521765 A CN 106521765A
Authority
CN
China
Prior art keywords
bamboo pulp
pulp fiber
tencel
manufacture method
fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610932356.8A
Other languages
Chinese (zh)
Inventor
仝晓婷
陈红霞
陆鹏
丁可敬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Goldsun Textile Science and Technology Co Ltd
Original Assignee
Jiangsu Goldsun Textile Science and Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Goldsun Textile Science and Technology Co Ltd filed Critical Jiangsu Goldsun Textile Science and Technology Co Ltd
Priority to CN201610932356.8A priority Critical patent/CN106521765A/en
Publication of CN106521765A publication Critical patent/CN106521765A/en
Pending legal-status Critical Current

Abstract

The invention discloses a manufacture method of fabrics blended by bamboo pulp fiber and tencel, and the warp and weft yarn of the fabrics are blended yarns of the tencel and the bamboo pulp fiber. The warp and the weft yarn are made into finished products by warp arranging, sizing, drafting and denting, weft insertion weaving, pre-treating, soft fixing, once preshrinking, press polishing, and secondary preshrinking. <{EN2}>By controlling warp arranging tension force, sizing tension force and two preshrinking technology in the printing and dying process, washing shrinkage in warp direction is controlled; by adding a waxing apparatus in weft direction, fineness of the weft yarn is improved, thereby reducing jet tension in weft direction, and controlling the washing shrinkage in weft direction. <{EN3}>According to the manufacture method, the fabrics blended by bamboo pulp fiber and tencel are soft; the yarnlevelness is even; and the washing shrinkage meets a first grade standard.

Description

A kind of manufacture method of bamboo pulp fiber and tencel blended fabric
Technical field
The invention belongs to household textiles technical field, and in particular to the manufacture of a kind of bamboo pulp fiber and tencel blended fabric Method.
Background technology
Summer environment temperature is high, high humidity, and bed necessaries are often easiest to breed bacteria, and there is bamboo pulp fiber excellent moisture absorption to put Wet performance, pro-skin are soft, bacteriostasis and health-care, be highly suitable for summer bed necessaries fabric, but bamboo pulp fiber product has fiber moisture absorption Expansion is big, causes fabric washing shrinkage big, it is difficult to washing shrinkage is controlled, and bed necessaries fabric requires that Grade A washing shrinkage is+2-4%. CN105483904A discloses a kind of tencel/bamboo pulp fibre blending shell-fabric dyeing and finishing processing method, and the invention provides a kind of tencel/bamboo Pulp fibres blended yarn weaved fabric dyeing and finishing processing method, wherein in order to control fabric washing shrinkage, the caustic soda opposite of 80-90g/L used in text Material carries out mercerising, and the method can preferably control the washing shrinkage of tencel bamboo pulp fiber fabric, but regenerated cellulose fabric organizine light After technique, feel is easily hardened, and sense of touch pro-skin comfort property is deteriorated.Meet bed for how to provide a kind of more preferable method production Product fabric quality requires and retains the fabric of tencel and bamboo pulp fiber good characteristic, will be highly desirable to.
The content of the invention
The technical problem of solution:The present invention is not enough for prior art, there is provided a kind of bamboo pulp fiber and tencel blended fabric Manufacture method, the fabric has soft sense of touch, and bar is dry uniform, and washing shrinkage can reach Grade A standard.
Technical scheme:In order to realize above-mentioned beneficial effect, the present invention is employed the following technical solutions:
The manufacture method of a kind of bamboo pulp fiber and tencel blended fabric, the longitude and latitude yarn of the fabric are tencel and bamboo pulp fiber Mixed yarn, longitude and latitude yarn sequentially passes through warping → sizing → denting of gaiting → wefting insertion weaving → pre-treatment → softness sizing → once The operation of preshrunk → press polish → secondary preshrunk makes finished product.
Further, in the mixed yarn of the tencel and bamboo pulp fiber, the mass percent of bamboo pulp fiber is 30-70%, bamboo The specification of pulp fibres is 1.33dtex*38mm;Tencel raw material is half cross-linking type tencel, and specification is 1.33dtex*38mm.
Further, the tencel and the yarn count of the mixed yarn of bamboo pulp fiber are 40S-60S.
Further, the fabric tissue of the bamboo pulp fiber tencel blended fabric is five pieces of Warp Satin tissues, warp thread Denting mode enters/reed for 2, and it is 140 pieces/inch -200 pieces/inch that Jing is close.
Further, the weft accumulator quantity for adopting in wefting insertion weaving process for three, between guide eyelit and weft accumulator Increase is provided with waxing attachment.
Further, for low melting point solid wax, fusing point is 30-40 DEG C to the wax that the waxing attachment is adopted.
Further, in wefting insertion weaving process, loom temple adopts rubber rollers.
Further, in shrinking processes pressure-bearing roller pressure be 8-10KG, speed 30-40m/min, temperature 40-50 ℃。
Further, in secondary shrinking processes pressure-bearing roller pressure be 5-7KG, speed 50-60m/min, temperature 40-50 ℃。
Beneficial effect:The bamboo pulp fiber and tencel blended fabric of the present invention, bamboo pulp fiber have excellent humidity absorption and release Can be smooth elegant with natural bacteriostatic effect, tencel, pro-skin is soft, and two kinds of Fiber Materials have complementary advantages, and fabric warp-wise is by control Preshrinking process twice in tension in Warping, sizing tension and dyeing process, reaches the washing shrinkage of control warp-wise, broadwise by increasing on Wax apparatus improve the fineness of weft yarn so as to reduce broadwise jet tension force, reach the washing shrinkage of control broadwise.Fabric warp thread passes through The transformation of denting mode and pneumatic picking, improves the exquisiteness and uniformity of cloth cover, so as to finally give with excellent moisture absorption Moisture releasing performance, pro-skin are submissive, the pendant that hangs down is elegant, and fabric good stability of the dimension, cloth cover exquisiteness are bright and clean, the high bamboo pulp fiber of class sense Tencel fabric.
Description of the drawings
Fig. 1 is the fabric structure figure of the present invention, wherein, longitudinal direction represents warp thread, laterally represents weft yarn, and ■ represents Jing groups Knit a little, represents latitude interlacing point.
Specific embodiment
Invention is described in further detail below by specific embodiment.It will be apparent, however, to one skilled in the art, that The following example is merely to illustrate the present invention, and should not be taken as limiting the scope of the invention.Unreceipted particular technique in embodiment Or condition person, (for example write with reference to Shen Lan duckweeds according to the technology or condition described by document in the art《Fabric construction with set Meter》, 2005) or according to product description China Textiles Press carried out.
The present invention provides a kind of manufacture method of bamboo pulp fiber tencel blended fabric, and longitude and latitude yarn sequentially passes through warping → sizing The operation of → denting of gaiting → wefting insertion weaving → pre-treatment → softness sizing → preshrunk → press polish → secondary preshrunk is made into Product.
The longitude and latitude yarn of the fabric is the mixed yarn yarn of tencel and bamboo pulp fiber, and yarn is using match network compact spinning side Formula, yarn count are 40S-60S;Wherein the shared mass percent in mixed yarn of bamboo pulp fiber is 30%-70%, bamboo pulp fiber Specification is 1.33dtex*38mm, and tencel raw material is half cross-linking type tencel, and specification is 1.33dtex*38mm.
Fabric tissue flies through face satin weave using five piece three, fabric made by the tissue, soft, reflecting feel It is good.Fabric warp-wise density is 140 pieces/inch -200 pieces/inch, and fabric denting mode enters/reed for 2, and mode of gaiting is to fly the method for wearing.
Loom speed 450-500m/min in weaving, 290-310 ° of opening time, wefting insertion are weaved and adopt three weft accumulators, three Weft accumulator three cylinder yarn cyclical-transformations of correspondence provide weft yarn, avoid same cylinder yarn well because the dry problem of bar is in fabric broadwise collection Middle embodiment, can make the cloth cover broadwise uniformity more preferable;Increase waxing attachment between guide eyelit and weft accumulator, on for eutectic Point solid wax, its fusing point is 30-40 DEG C, yarn can be caused yam surface filoplume can be made docile before being subject to jet air pressure, dropped Frictional force of the low-flow to yarn, so as to reduce the tension force that weft yams are subject to, improves broadwise washing shrinkage.In weaving process it is Solve the problems, such as temple mark, make fabric appearance more satin, using rubber rollers, such yarn will not because coronule produce filoplume and Fine and closely woven problem, cloth cover are more uniform.
Fabric singe using two just two it is counter singe, roll desizing enzyme fire extinguishing, after 3-4 hours of banking up wash.
Cold dome amount of caustic soda 13-15g/L, dioxygen water consumption 14-16g/L, stabilizer 8-10g/L, bleeding agent 5-7g/L, car Fast 50-60m/min.
Evaporate after stamp, evaporate speed 40-50m/min, temperature 100-103 DEG C.
Fabric using preshrinking process twice, first time preshrinking process is:Preshrunk pressure-bearing roller pressure be 8-10KG, speed 30- 40m/min, temperature 40-50 DEG C make fabric fully shrink elimination warp-wise internal stress along warp-wise, reduce the contact pressure of filling yarn Power, carries out press polish after preshrunk, the purpose of press polish is the poised state of Jing weft yarns recovery after reservation first time preshrunk.Carry out after press polish Secondary preshrunk, second preshrinking process be:Preshrunk pressure-bearing roller pressure is 5-7KG, speed 50-60m/min, temperature 40-50 DEG C, the The purpose of secondary preshrunk is that, for the feel for obtaining softness, and the internal stress further eliminated between filling yarn and yarn makes fabric Space structure is balanced, and reduces warp-wise washing shrinkage.
Embodiment one
Fabric warp thread is that 40S matches network compact spinning bamboo pulp fiber tencel blended fabric, and wherein bamboo pulp fiber is shared in the yarn Mass percent be 50%, weft yarn be 40S match network compact spinning bamboo pulp fiber tencel blended fabric, wherein bamboo pulp fiber is in yarn In shared mass percent be 50%, fabric specification is 40S*40S/140*80, and five piece three is flown through face satin weave.Wherein mix In spinning, the specification of bamboo pulp fiber raw material used is 1.33dtex*38mm, and tencel fiber specification is 1.33dtex*38mm
The fabric warping adopts Benniger warping machine, and wherein warping speed is 450m/min, using zonal control yarn Tension force, make piece yarn tension uniformity.
The fabric sizing starches starching using converted starch, and the rate of sizing is 15%, and sizing speed is 45m/min, and yarn stretches It is long to control 1%.
Fabric denting mode enters/reed for 2, and mode of gaiting is to fly the method for wearing.
Loom speed 500m/min in weaving, 290 ° of opening time, wefting insertion weaving using three weft accumulators, and in guide eyelit and Increase waxing attachment between weft accumulator, on wax be low melting point solid wax, its fusing point be 30-40 DEG C.
Fabric singe using two just two it is counter singe, roll desizing enzyme fire extinguishing, after 3-4 hours of banking up wash.
Cold dome amount of caustic soda 15g/L, dioxygen water consumption 16g/L, stabilizer 10g/L, bleeding agent 7g/L, speed 60m/min.
Evaporate after stamp, evaporate speed 50m/min, 103 DEG C of temperature.
Fabric using preshrinking process twice, wherein first time preshrinking process is:Preshrunk pressure-bearing roller pressure be 10KG, speed 30m/min, temperature 50 C carry out press polish after preshrunk, secondary preshrunk is carried out after press polish, and second preshrinking process is:Preshrunk pressure-bearing Roller pressure is 7KG, speed 50m/min, temperature 50 C.
Embodiment two
Fabric warp thread is that 60S matches network compact spinning bamboo pulp fiber tencel blended fabric, and wherein bamboo pulp fiber is shared in the yarn Mass percent be 30%, weft yarn be 60S match network compact spinning bamboo pulp fiber tencel blended fabric, wherein bamboo pulp fiber is in yarn In shared mass percent be 30%, fabric specification is 60S*60S/182*120, and five piece three is flown through face satin weave.Wherein In mixed yarn, the specification of bamboo pulp fiber raw material used is 1.33dtex*38mm, and tencel fiber specification is 1.33dtex*38mm
The fabric warping adopts Benniger warping machine, and wherein warping speed is 400m/min, using zonal control yarn Tension force, make piece yarn tension uniformity.
The fabric sizing starches starching using converted starch, and the rate of sizing is 12%, and sizing speed is 40m/min, and yarn stretches It is long to control 0.6%.
Fabric denting mode enters/reed for 2, and mode of gaiting is to fly the method for wearing.
Loom speed 450m/min in weaving, 310 ° of opening time, wefting insertion weaving using three weft accumulators, and in guide eyelit and Increase waxing attachment between weft accumulator, on wax be low melting point solid wax, its fusing point be 30-40 DEG C.
Fabric singe using two just two it is counter singe, roll desizing enzyme fire extinguishing, after 3-4 hours of banking up wash.
Cold dome amount of caustic soda 13g/L, dioxygen water consumption 14g/L, stabilizer 8g/L, bleeding agent 5g/L, speed 50m/min.
Evaporate after stamp, evaporate speed 40m/min, 100 DEG C of temperature.
Fabric using preshrinking process twice, wherein first time preshrinking process is:Preshrunk pressure-bearing roller pressure be 8KG, speed 40m/min, 40 DEG C of temperature carry out press polish after preshrunk, secondary preshrunk is carried out after press polish, and second preshrinking process is:Preshrunk pressure-bearing Roller pressure is 5KG, speed 60m/min, 40 DEG C of temperature.
Embodiment three
Fabric warp thread is that 40S matches network compact spinning bamboo pulp fiber tencel blended fabric, and wherein bamboo pulp fiber is shared in the yarn Mass percent be 70%, weft yarn be 40S match network compact spinning bamboo pulp fiber tencel blended fabric, wherein bamboo pulp fiber is in yarn In shared mass percent be 70%, fabric specification is 40S*40S/144*85, and five piece three is flown through face satin weave.Wherein mix In spinning, the specification of bamboo pulp fiber raw material used is 1.33dtex*38mm, and tencel fiber specification is 1.33dtex*38mm
The fabric warping adopts Benniger warping machine, and wherein warping speed is 450m/min, using zonal control yarn Tension force, make piece yarn tension uniformity.
The fabric sizing starches starching using converted starch, and the rate of sizing is 15%, and sizing speed is 45m/min, and yarn stretches It is long to control 1%.
Fabric denting mode enters/reed for 2, and mode of gaiting is to fly the method for wearing.
Loom speed 500m/min in weaving, 290 ° of opening time, wefting insertion weaving using three weft accumulators, and in guide eyelit and Increase waxing attachment between weft accumulator, on wax be low melting point solid wax, its fusing point be 30-40 DEG C.
Fabric singe using two just two it is counter singe, roll desizing enzyme fire extinguishing, after 3-4 hours of banking up wash.
Cold dome amount of caustic soda 15g/L, dioxygen water consumption 16g/L, stabilizer 10g/L, bleeding agent 7g/L, speed 60m/min.
Evaporate after stamp, evaporate speed 50m/min, 103 DEG C of temperature.
Fabric using preshrinking process twice, wherein first time preshrinking process is:Preshrunk pressure-bearing roller pressure be 10KG, speed 30m/min, temperature 50 C carry out press polish after preshrunk, secondary preshrunk is carried out after press polish, and second preshrinking process is:Preshrunk pressure-bearing Roller pressure is 7KG, speed 50m/min, temperature 50 C.
Reference examples 1:Difference with embodiment 1 is not adopt waxing attachment.
Reference examples 2:Difference with embodiment 1 is only with a weft accumulator.
Reference examples 3:Difference with embodiment 1 is not adopt secondary shrinking processes.
Fabric obtained by above-described embodiment is carried out into performance test, it is as a result as follows:
As seen from the above table, there is softness with tencel blended fabric using the bamboo pulp fiber obtained by manufacture method of the invention Sense of touch, bar are dry uniform, and washing shrinkage can reach Grade A standard.

Claims (9)

1. the manufacture method of a kind of bamboo pulp fiber and tencel blended fabric, it is characterised in that:The longitude and latitude yarn of the fabric is tencel With the mixed yarn of bamboo pulp fiber, longitude and latitude yarn sequentially passes through warping → sizing → denting of gaiting → wefting insertion weaving → pre-treatment → softness The operation of sizing → preshrunk → press polish → secondary preshrunk makes finished product.
2. the manufacture method of bamboo pulp fiber according to claim 1 and tencel blended fabric, it is characterised in that:The tencel Mass percent with bamboo pulp fiber in the mixed yarn of bamboo pulp fiber is 30-70%, and the specification of bamboo pulp fiber is 1.33dtex* 38mm;Tencel raw material is half cross-linking type tencel, and specification is 1.33dtex*38mm.
3. the manufacture method of bamboo pulp fiber according to claim 1 and tencel blended fabric, it is characterised in that:The tencel Yarn count with the mixed yarn of bamboo pulp fiber is 40S-60S.
4. the manufacture method of bamboo pulp fiber according to claim 1 and tencel blended fabric, it is characterised in that:The bamboo pulp The fabric tissue of fiber tencel blended fabric is that five pieces of Warp Satins are organized, and the denting mode of warp thread enters/reed for 2, and it is 140 that Jing is close Pieces/inch -200 pieces/inch.
5. the manufacture method of bamboo pulp fiber according to claim 1 and tencel blended fabric, it is characterised in that:Knit in wefting insertion For three, the increase between guide eyelit and weft accumulator is provided with waxing attachment to the weft accumulator quantity adopted in making operation.
6. the manufacture method of bamboo pulp fiber according to claim 5 and tencel blended fabric, it is characterised in that:The waxing The wax that device is adopted is low melting point solid wax, and fusing point is 30-40 DEG C.
7. the manufacture method of bamboo pulp fiber according to claim 1 and tencel blended fabric, it is characterised in that:Knit in wefting insertion In making operation, loom temple adopts rubber rollers.
8. the manufacture method of bamboo pulp fiber according to claim 1 and tencel blended fabric, it is characterised in that:Once pre- In contracting operation pressure-bearing roller pressure be 8-10KG, speed 30-40m/min, temperature 40-50 DEG C.
9. the manufacture method of bamboo pulp fiber according to claim 1 and tencel blended fabric, it is characterised in that:Secondary pre- In contracting operation pressure-bearing roller pressure be 5-7KG, speed 50-60m/min, temperature 40-50 DEG C.
CN201610932356.8A 2016-10-25 2016-10-25 Manufacture method of fabrics blended by bamboo pulp fiber and tencel Pending CN106521765A (en)