CN106521383A - 一种经重复钎焊的gh4169合金锻件的热处理工艺 - Google Patents

一种经重复钎焊的gh4169合金锻件的热处理工艺 Download PDF

Info

Publication number
CN106521383A
CN106521383A CN201611069277.5A CN201611069277A CN106521383A CN 106521383 A CN106521383 A CN 106521383A CN 201611069277 A CN201611069277 A CN 201611069277A CN 106521383 A CN106521383 A CN 106521383A
Authority
CN
China
Prior art keywords
brazing
repetitive
processing technology
alloy forged
heat processing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201611069277.5A
Other languages
English (en)
Other versions
CN106521383B (zh
Inventor
佗劲红
邰清安
吴会萍
周浩浩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AECC Shenyang Liming Aero Engine Co Ltd
Original Assignee
Shenyang Liming Aero Engine Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenyang Liming Aero Engine Group Co Ltd filed Critical Shenyang Liming Aero Engine Group Co Ltd
Priority to CN201611069277.5A priority Critical patent/CN106521383B/zh
Publication of CN106521383A publication Critical patent/CN106521383A/zh
Application granted granted Critical
Publication of CN106521383B publication Critical patent/CN106521383B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种热处理工艺，具体涉及一种经重复钎焊的GH4169合金锻件的热处理工艺。本发明的技术方案如下：一种经重复钎焊的GH4169合金锻件的热处理工艺，包括如下步骤：1)真空钎焊；2)中间热处理；3)标准时效。本发明提供的经重复钎焊的GH4169合金锻件的热处理工艺，解决经重复钎焊的GH4169合金锻件的缺口敏感问题。

Description

一种经重复钎焊的GH4169合金锻件的热处理工艺
技术领域
本发明涉及一种热处理工艺，具体涉及一种经重复钎焊的GH4169合金锻件的热处理工艺。
背景技术
GH4169合金在我国的应用较为广泛，特别是航空工业上的应用，如GH4169合金制造的鼓筒轴、涡轮盘等。目前国内没有专用的GH4169合金锻件钎焊后热处理的验收技术条件，考虑到材料的加工过程及性能，通常时效热处理安排在钎焊后的组件上进行，而组件热处理制度的编制依据来源于材料标准。GH4169材料标准的技术条件规定时效制度为700℃～800℃，保温8h，以50±10℃/h速率炉冷至600℃～700℃，保温8h，空冷。GH4169合金锻件经固溶处理后，按现有工艺(即真空钎焊+标准时效工艺)，经真空钎焊和时效处理后力学性能检查时，发现一些锻件存在缺口持久性能不合格。经分析，主要原因是试验件经过真空钎焊后试样组织中δ相含量较少，晶界上几乎无δ相析出，造成缺口持久敏感。
发明内容
本发明提供一种经重复钎焊的GH4169合金锻件的热处理工艺，解决经重复钎焊的GH4169合金锻件的缺口敏感问题。
本发明的技术方案如下：一种经重复钎焊的GH4169合金锻件的热处理工艺，包括如下步骤：
1)真空钎焊
将经过固溶处理的GH4169合金锻件放入真空钎焊炉中，进行真空钎焊；
2)中间热处理
a)将经过二次真空钎焊处理后的GH4169合金锻件放入空气炉中，加热至800℃～900℃，保温4h，空冷；
b)将经过三次真空钎焊处理后的GH4169合金锻件放入空气炉中，加热至900℃～960℃，保温0.5h，快冷；
3)标准时效
将经过中间热处理后的GH4169合金锻件放入空气炉中，进行标准时效处理。
本发明的有益效果为：本发明采用真空钎焊+中间热处理+标准时效的热处理工艺，可以解决现有的GH4169合金焊接组件时效后缺口持久不合格问题，提高经重复钎焊的GH4169合金锻件的合格率，为后续建立零件及组合件检验标准提供依据。
具体实施方式
一种经重复钎焊的GH4169合金锻件的热处理工艺，包括如下步骤：
1)真空钎焊
将经过固溶处理的GH4169合金锻件放入真空钎焊炉中，进行真空钎焊；
2)中间热处理
a)将经过二次真空钎焊处理后的GH4169合金锻件放入空气炉中，加热至850℃，保温4h，空冷；
b)将经过三次真空钎焊处理后的GH4169合金锻件放入空气炉中，加热至950℃，保温0.5h，快冷；
3)标准时效
将经过中间热处理后的GH4169合金锻件放入空气炉中，进行标准时效处理。

Claims (1)

1.一种经重复钎焊的GH4169合金锻件的热处理工艺，其特征在于，包括如下步骤：
1)真空钎焊
将经过固溶处理的GH4169合金锻件放入真空钎焊炉中，进行真空钎焊；
2)中间热处理
a)将经过二次真空钎焊处理后的GH4169合金锻件放入空气炉中，加热至800℃～900℃，保温4h，空冷；
b)将经过三次真空钎焊处理后的GH4169合金锻件放入空气炉中，加热至900℃～960℃，保温0.5h，快冷；
3)标准时效
将经过中间热处理后的GH4169合金锻件放入空气炉中，进行标准时效处理。
CN201611069277.5A 2016-11-29 2016-11-29 一种经重复钎焊的gh4169合金锻件的热处理工艺 Active CN106521383B (zh)