CN103667617A - 一种提高1Cr12Ni3Mo2VN透平叶片冲击韧性的热处理工艺 - Google Patents

一种提高1Cr12Ni3Mo2VN透平叶片冲击韧性的热处理工艺 Download PDF

Info

Publication number
CN103667617A
CN103667617A CN201310677997.XA CN201310677997A CN103667617A CN 103667617 A CN103667617 A CN 103667617A CN 201310677997 A CN201310677997 A CN 201310677997A CN 103667617 A CN103667617 A CN 103667617A
Authority
CN
China
Prior art keywords
heat treatment
treatment process
turbine blade
thermal treatment
quenching
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310677997.XA
Other languages
English (en)
Other versions
CN103667617B (zh
Inventor
刘新权
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi Turbine Blade Co Ltd
Original Assignee
Wuxi Turbine Blade Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Turbine Blade Co Ltd filed Critical Wuxi Turbine Blade Co Ltd
Priority to CN201310677997.XA priority Critical patent/CN103667617B/zh
Publication of CN103667617A publication Critical patent/CN103667617A/zh
Application granted granted Critical
Publication of CN103667617B publication Critical patent/CN103667617B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种提高1Cr12Ni3Mo2VN透平叶片冲击韧性的热处理工艺，其能有效解决1Cr12Ni3Mo2VN透平叶片在热处理过程中由于碳化物偏聚而引起的回火脆性。其特征在于：在对1Cr12Ni3Mo2VN材料叶片钢进行常规淬火热处理之前，先对1Cr12Ni3Mo2VN材料叶片钢进行预备热处理。

Description

一种提高1Cr12Ni3Mo2VN透平叶片冲击韧性的热处理工艺
技术领域
本发明涉及透平叶片的热处理工艺领域，具体为一种提高1Cr12Ni3Mo2VN透平叶片冲击韧性的热处理工艺。
背景技术
叶片钢的脆化是生产与使用过程中常遇到的问题，由于叶片钢脆化产生原因的复杂性，因此叶片钢脆化一直是透平叶片研究的热点。1Cr12Ni3Mo2VN耐热钢是我国新引进的钢种，已广泛用于制造超超临界火电机组的末级长叶片。1Cr12Ni3Mo2VN叶片钢冲击韧性一般都较好，通常KV8≥100J，但是在实际生产过程中按正常热处理工艺处理后叶片钢的冲击韧性KV8只能达到20～35J，脆化严重，重复热处理后冲击韧性也未有改善。
发明内容
针对上述问题，本发明提供了一种提高1Cr12Ni3Mo2VN透平叶片冲击韧性的热处理工艺，其能有效解决1Cr12Ni3Mo2VN透平叶片在热处理过程中由于碳化物偏聚而引起的回火脆性。
其技术方案是这样的，其特征在于：在对1Cr12Ni3Mo2VN材料叶片钢进行常规淬火热处理之前，先对所述1Cr12Ni3Mo2VN材料叶片钢进行预备热处理。
其进一步特征在于：
所述预备热处理温度比所述1Cr12Ni3Mo2VN材料叶片钢常规淬火温度高30℃～80℃；所述预备热处理的保温时间为1.5小时～3小时；
所述预备热处理的冷却方法为空冷、风冷或油冷中的任一种；
所述1Cr12Ni3Mo2VN材料叶片钢常规淬火温度为1000℃～1020℃，，常规淬火保温时间为90分钟～150分钟。
本发明热处理工艺的有益效果在于：由于该叶片钢材料常规的淬火温度较低，大颗粒碳化物很难在热处理过程中进一步组织均匀化，因此在锻后晶界连续析出大颗粒碳化物，并且常规较低的淬火无法消除，本发明方法在常规热处理之前先对叶片钢材料进行预备热处理，可以使叶片钢材料在热处理之前组织更均匀化，从而提高1Cr12Ni3Mo2VN透平叶片冲击韧性。
具体实施方式
实施例一：
（1）将1Cr12Ni3Mo2VN材料叶片按照工艺方案均匀地放到通用的淬火料筐中，再将所述淬火料筐放入热处理淬火炉内；
（2）预备热处理：加热温度为为1050℃，保温1.5小时，空冷； 
（3）常规淬火热处理：淬火温度1020℃，保温90分钟，油冷；
采用以上工艺重复热处理后，冲击韧性提高，见表1。 
表1：
Figure 543911DEST_PATH_IMAGE001
实施例二：
（1）将叶片按照工艺方案均匀放到通用的淬火料筐中，再将所述淬火料筐放入热处理淬火炉内； 
（2）预备热处理：加热温度1100℃，保温2小时，风冷； 
（3）常规淬火热处理：淬火温度1020℃，保温120分钟，油冷；
采用以上工艺重复热处理后，冲击韧性提高，见表2。 
 
       表2：
Figure 523368DEST_PATH_IMAGE002
实施例三：
（1）将叶片按照工艺方案均匀放到通用的淬火料筐中，再将所述淬火料筐放入热处理淬火炉内； 
（2）预备热处理：加热温度1030℃，保温3小时，空冷； 
（3）常规淬火热处理：淬火温度1020℃，保温150分钟，油冷。
采用以上工艺重复热处理后，冲击韧性提高，见表3。
 
    表3：
Figure 303106DEST_PATH_IMAGE003
实施例四：
（1）将叶片按照工艺方案均匀放到通用的淬火料筐中，再将所述淬火料筐放入热处理淬火炉内； 
（2）预备热处理：加热温度1065℃，保温2.25小时，油冷； 
（3）常规淬火热处理：淬火温度1020℃，保温120分钟，油冷。
采用以上工艺重复热处理后，冲击韧性提高，见表4。
表4：
   
Figure 259167DEST_PATH_IMAGE004

Claims (4)

1.一种提高1Cr12Ni3Mo2VN透平叶片冲击韧性的热处理工艺，其特征在于：在对1Cr12Ni3Mo2VN材料叶片钢进行常规淬火热处理之前，先对所述1Cr12Ni3Mo2VN材料叶片钢进行预备热处理。
2.根据权利要求1所述的一种提高1Cr12Ni3Mo2VN透平叶片冲击韧性的热处理工艺，其特征在于：所述预备热处理温度比所述1Cr12Ni3Mo2VN材料叶片钢常规淬火温度高30℃～80℃；所述预备热处理的保温时间为1.5小时～3小时。
3.根据权利要求2所述的一种提高1Cr12Ni3Mo2VN透平叶片冲击韧性的热处理工艺，其特征在于：所述预备热处理的冷却方法为空冷、风冷或油冷中的任一种。
4.根据权利要求3所述的一种提高1Cr12Ni3Mo2VN透平叶片冲击韧性的热处理工艺，其特征在于：所述1Cr12Ni3Mo2VN材料叶片钢常规淬火温度为1000℃～1020℃，，常规淬火保温时间为90分钟～150分钟。
CN201310677997.XA 2013-12-13 2013-12-13 一种提高1Cr12Ni3Mo2VN透平叶片冲击韧性的热处理工艺 Active CN103667617B (zh)