CN106483732A - 一种高红外反射电致变色玻璃及其制备方法 - Google Patents
一种高红外反射电致变色玻璃及其制备方法 Download PDFInfo
- Publication number
- CN106483732A CN106483732A CN201611168288.9A CN201611168288A CN106483732A CN 106483732 A CN106483732 A CN 106483732A CN 201611168288 A CN201611168288 A CN 201611168288A CN 106483732 A CN106483732 A CN 106483732A
- Authority
- CN
- China
- Prior art keywords
- layer
- substrate
- glass
- infrared reflection
- gas
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高红外反射电致变色玻璃及其制备方法,其技术方案要点是：包括第一玻璃基板和第二玻璃基板，所述第一玻璃基板和第二玻璃基板间设有电解质层，所述第一玻璃基板包括第一基板和依次设于所述第一基板和电解质层间的ITO层和WO3层。本发明的一种高红外反射电致变色玻璃，采用主动节能与被动节能相复合，产品全波段透过率可调，具有高红外反射效果。
Description
【技术领域】
本发明涉及一种镀膜玻璃，具体涉及一种高红外反射电致变色玻璃及其制备方法。
【背景技术】
镀膜玻璃具有节能减排及装饰幕墙的双重功效，推出市场后，深受人们喜爱，Low-E玻璃也叫做低辐射镀膜玻璃，传统的LOW-E玻璃，装上墙后可见光及红外的透过率及反射率均固定，无法再改变，被称之为被动节能；而目前电致变色玻璃，虽然能主动节能，但其对红外的反射不论是着色成还是褪色态都不明显。
【发明内容】
本发明的一种高红外反射电致变色玻璃，采用主动节能与被动节能相复合，产品全波段透过率可调，具有高红外反射效果。
本发明另一目的是提供一种高红外反射电致变色玻璃的制备方法。
本发明是通过以下技术方案实现的：
一种高红外反射电致变色玻璃，包括第一玻璃基板和第二玻璃基板，所述第一玻璃基板和第二玻璃基板间设有电解质层，所述第一玻璃基板包括第一基板和依次设于所述第一基板和电解质层间的ITO层和WO3层。
优选的，第二玻璃基板包括第二基板和依次设于所述第二基板和电解质层间的ITO层、AZO层、Ag层和NiO层。
优选的，所述ITO层膜厚120～135nm，方阻<15欧。
优选的，所述WO3层膜厚500～600nm。
优选的，所述电解质层电导率>10-6μs/cm。
优选的，所述NiO层膜厚50～100nm。
优选的，所述Ag层膜厚8～12nm。
优选的，所述AZO层膜厚300～400nm。
优选的，所述第一基板和第二基板均为厚度4～8mm的浮法玻璃。
一种制备高红外反射电致变色玻璃的方法，包括以下步骤：
1、磁控溅射第一ITO层，用交流电源、Ar气作为保护气体，磁控溅射氧化铟锡靶In2O3：SnO2＝90：10(wt％)，用Ar气流量800SCCM；
2、磁控溅射WO3层，用交流电源、Ar气、O2气作为保护气体，磁控溅射钨靶，氩氧流量比为400～425SCCM:600～630SCCM；
3、制备电解质层，将PVB、锂盐、助剂按重量比60～70：10～20：10～30挤出流延制成，其中锂盐为高氯酸锂、钽酸锂等的混合物，其它助剂为注塑剂、抗氧化剂、紫外吸光剂、稳定剂；
4、磁控溅射NiO层，用交流电源、Ar气、O2气作为保护气体，磁控溅射钨镍靶W：Ni＝8：92(wt％)，氩氧流量比为380～400SCCM:600～625SCCM；
5、磁控溅射Ag层，直流电源溅射，用Ar气作为保护气体，气体流量500～550SCCM；
6、制备AZO层，铝掺杂的氧化锌层；
7、磁控溅射第二ITO层，用交流电源、Ar气作为保护气体，磁控溅射氧化铟锡靶In2O3：SnO2＝90：10(wt％)，用Ar气流量800SCCM；
8、合片，由第一基板11、第一ITO层12和WO3层13组成第一玻璃基板1，由第二基板21、第二ITO层22、AZO层23、Ag层24、NiO层25组成第二玻璃基板2，第一玻璃基板1、电解质层3与第二玻璃基板2通过高压釜进行合片，制备得高红外反射电致变色玻璃。
一种装配有所述双色防透明扩散板支架的电视机。
与现有技术相比，本发明具有如下优点：
1、本发明的高红外反射电致变色玻璃，氧化铟锡膜层具有透明导电功能，且抗化学性能稳定，可有效对红外进行反射同时，可起到保护功能膜层的作用，具有LOW-E玻璃高红外反射的被动节能效果；
2、本发明的高红外反射电致变色玻璃，具有电致变色的主动节能效果，对红外线反射率达到80％以上；
3、本发明的高红外反射电致变色玻璃，可与智能家居互联，通过控制电路实现智能控制；
4、本发明的高红外反射电致变色玻璃制备方法，功能膜层依次沉积在玻璃基片上，膜层具有耐候性和耐腐蚀性能优秀、辐射率低、表面电阻小、均匀性好、结合力强的优点。
【附图说明】
图1是本发明结构示意图。
【具体实施方式】
如附图1所示的一种高红外反射电致变色玻璃，包括第一玻璃基板1和第二玻璃基板2，所述第一玻璃基板1和第二玻璃基板2间设有电解质层3，所述第一玻璃基板1包括第一基板11和依次设于所述第一基板11和电解质层3间的ITO层12和WO3层13。本发明的玻璃单元由两块不同的玻璃基板及电解质层复合而成，每边的玻璃基板均由多个膜层构成，其中第一玻璃基板上复合有ITO层和WO3层，以实现被动节能的效果。
第二玻璃基板2包括第二基板21和依次设于所述第二基板21和电解质层3间的第二ITO层22、AZO层23、Ag层24和NiO层25。第二玻璃基板上复合有第二ITO层、AZO层、Ag层和NiO层，结合电解质层以实现电致变色的主动节能效果。
所述第一ITO层12膜厚120～135nm，方阻<15欧。交流电源磁控溅射氧化铟锡靶In2O3：SnO2＝90：10(wt％)，制备第一ITO层膜，用Ar气作为溅射气体，气体流量800SCCM，膜厚120～135nm，优选为125nm，1m＝109nm。
所述WO3层13膜厚500～600nm。交流电源磁控溅射钨靶，用Ar气、O2作为溅射气体，气体流量控制在400～425SCCM:600～630SCCM，膜厚500-600nm，优选为550nm。
所述电解质层3电导率>10-6μs/cm。电解质层由PVB-Li构成，金属锂以离子态存在，将PVB、锂盐(高氯酸锂、钽酸锂等)、助剂(注塑剂、抗氧化剂、紫外吸光剂、稳定剂)按重量比60～70：10～20：10～30挤出流延制得导电PVB，其电导率>10-6μs/cm。
所述NiO层25膜厚50～100nm。采用交流电源磁控溅射钨镍靶W：Ni＝8:92，用Ar气、O2作为溅射气体，气体流量控制在380～400SCCM:600～625SCCM，膜厚50-100nm，优选为100nm。
所述Ag层24膜厚8～12nm。直流电源溅射，用Ar作为溅射气体气体流量500～550SCCM，膜厚8～12nm，优选为8nm。
所述AZO层23膜厚300～400nm。采用铝掺杂的氧化锌层，作为保护层，可进一步降低辐射率。
所述第一基板11和第二基板12均为厚度4～8mm的浮法玻璃。优选的第一基板和第二基板均选择6mm的浮法玻。
一种制备高红外反射电致变色玻璃的方法，包括以下步骤：
1)、磁控溅射第一ITO层12，用交流电源、Ar气作为保护气体，磁控溅射氧化铟锡靶In2O3：SnO2＝90：10(wt％)，用Ar气流量800SCCM；
2)、磁控溅射WO3层13，用交流电源、Ar气、O2气作为保护气体，磁控溅射钨靶，氩氧流量比为400～425SCCM:600～630SCCM；
3)、制备电解质层3，将PVB、锂盐、其它助剂按重量比60～70：10～20：10～30挤出流延制成；
4)、磁控溅射NiO层25，用交流电源、Ar气、O2气作为保护气体，磁控溅射钨镍靶W：Ni＝8：92(wt％)，氩氧流量比为380～400SCCM:600～625SCCM；
5)、磁控溅射Ag层24，直流电源溅射，用Ar气作为保护气体，气体流量500～550SCCM；
6)、制备AZO层23，铝掺杂的氧化锌层；
7)、磁控溅射第二ITO层12，用交流电源、Ar气作为保护气体，磁控溅射氧化铟锡靶In2O3：SnO2＝90：10(wt％)，用Ar气流量800SCCM；
8)、合片，由第一基板11、第一ITO层12和WO3层13组成第一玻璃基板1，由第二基板21、第二ITO层22、AZO层23、Ag层24、NiO层25组成第二玻璃基板2，第一玻璃基板1、电解质层3与第二玻璃基板2通过高压釜进行合片，制备得高红外反射电致变色玻璃。功能膜层依次沉积在玻璃基片上，膜层具有耐候性和耐腐蚀性能优秀、辐射率低、表面电阻小、均匀性好、结合力强的优点。
Claims (10)
1.一种高红外反射电致变色玻璃，其特征在于：包括第一玻璃基板(1)和第二玻璃基板(2)，所述第一玻璃基板(1)和第二玻璃基板(2)间设有电解质层(3)，所述第一玻璃基板(1)包括第一基板(11)和依次设于所述第一基板(11)和电解质层(3)间的第一ITO层(12)和WO3层(13)。
2.根据权利要求1所述的一种高红外反射电致变色玻璃，其特征在于：第二玻璃基板(2)包括第二基板(21)和依次设于所述第二基板(21)和电解质层(3)间的第二ITO层(22)、AZO层(23)、Ag层(24)和NiO层(25)。
3.根据权利要求1所述的一种高红外反射电致变色玻璃，其特征在于：所述第一ITO层(12)膜厚120～135nm，方阻<15欧。
4.根据权利要求1所述的一种高红外反射电致变色玻璃，其特征在于：所述WO3层(13)膜厚500～600nm。
5.根据权利要求1所述的一种高红外反射电致变色玻璃，其特征在于：所述电解质层(3)电导率>10-6μs/cm。
6.根据权利要求2所述的一种高红外反射电致变色玻璃，其特征在于：所述NiO层(25)膜厚50～100nm。
7.根据权利要求2所述的一种高红外反射电致变色玻璃，其特征在于：所述Ag层(24)膜厚8～12nm。
8.根据权利要求2所述的一种高红外反射电致变色玻璃，其特征在于：所述AZO层(23)膜厚300～400nm。
9.根据权利要求2所述的一种高红外反射电致变色玻璃，其特征在于：所述第一基板(11)和第二基板(12)均为厚度4～8mm的浮法玻璃。
10.一种制备高红外反射电致变色玻璃的方法，其特征在于包括以下步骤：
1)、磁控溅射第一ITO层(12)，用交流电源、Ar气作为保护气体，磁控溅射氧化铟锡靶In2O3：SnO2＝90：10(wt％)，用Ar气流量800SCCM；
2)、磁控溅射WO3层(13)，用交流电源、Ar气、O2气作为保护气体，磁控溅射钨靶，氩氧流量比为400～425SCCM:600～630SCCM；
3)、制备电解质层(3)，将PVB、锂盐、助剂按重量比60～70：10～20：10～30挤出流延制成；
4)、磁控溅射NiO层(25)，用交流电源、Ar气、O2气作为保护气体，磁控溅射钨镍靶W：Ni＝8：92(wt％)，氩氧流量比为380～400SCCM:600～625SCCM；
5)、磁控溅射Ag层(24)，直流电源溅射，用Ar气作为保护气体，气体流量500～550SCCM；
6)、制备AZO层(23)，铝掺杂的氧化锌层；
7)、磁控溅射第二ITO层(22)，用交流电源、Ar气作为保护气体，磁控溅射氧化铟锡靶In2O3：SnO2＝90：10(wt％)，用Ar气流量800SCCM；
8)、合片，由第一基板(11)、第一ITO层(12)和WO3层(13)组成第一玻璃基板(1)，由第二基板(21)、第二ITO层(22)、AZO层(23)、Ag层(24)、NiO层(25)组成第二玻璃基板(2)，第一玻璃基板(1)、电解质层(3)与第二玻璃基板(2)通过高压釜进行合片，制备得高红外反射电致变色玻璃。