CN106467849A - A kind of compositionss of magnesium alloy rolling and processing lubricant - Google Patents

A kind of compositionss of magnesium alloy rolling and processing lubricant Download PDF

Info

Publication number
CN106467849A
CN106467849A CN201610840978.8A CN201610840978A CN106467849A CN 106467849 A CN106467849 A CN 106467849A CN 201610840978 A CN201610840978 A CN 201610840978A CN 106467849 A CN106467849 A CN 106467849A
Authority
CN
China
Prior art keywords
compositionss
magnesium alloy
processing lubricant
alloy rolling
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610840978.8A
Other languages
Chinese (zh)
Inventor
黄福川
黄显昆
潘发存
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi University
Original Assignee
Guangxi University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi University filed Critical Guangxi University
Priority to CN201610840978.8A priority Critical patent/CN106467849A/en
Publication of CN106467849A publication Critical patent/CN106467849A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of compositionss of magnesium alloy rolling and processing lubricant it is characterised in that：Using oil based on No. 22 total loss system oil, coordinate multiple compound additives, including：Antioxidant, metal deactivator, oiliness improver, friction improver, extreme pressure agent, antiwear additive, antirust agent, anti-foaming agent, oxidation and corrosion inhibitor, anti emulsifier, urge cryogen.The compositionss of the present invention have good extruding and carry wear resistence, reduce coefficient of friction, improve slide coefficient, and good cooling, diffusibility, detergent-dispersant performance, rust-preventing characteristic, oxidation stability, anti-foaming property, resistance to emulsion, cleaning and abrasive dust adhesion caking reduce.

Description

A kind of compositionss of magnesium alloy rolling and processing lubricant
Technical field
The invention belongs to metal working lubricant field, particularly to a kind of combination of magnesium alloy rolling and processing lubricant Thing.
Background technology
Magnesium alloy is the alloy adding other elements composition with magnesium for base.It is characterized in：Little (the 1.8g/cm3 magnesium alloy of density Left and right), specific strength is high, good heat dissipation bigger than elastic modelling quantity, and absorb shock resistance is good, and the load-carrying ability that withstands shocks is bigger than aluminium alloy, resistance to organic The corrosive nature of thing and alkali is good.Main alloy element has aluminum, zinc, manganese, cerium, thorium and a small amount of zirconium or cadmium etc..At present using the widest Be magnalium, next to that magnesium-manganese alloy and magnesium zinc zircaloy.It is mainly used in the works such as Aeronautics and Astronautics, transport, chemical industry, rocket Industry department.It is the metal the lightest in practical metal, high intensity, high rigidity.
Machinery manufacturing industry just develops towards high accuracy, high speed with high-power, digitized direction now.Therefore to machinery The requirement of the material of part, machining accuracy and workmanship also more and more higher.And be used for improve machinery part surface quality and Improve the hydraulic pressure processing technique of its physics, mechanical performance, be widely applied.In hydraulic pressure processing, existed using hydraulic tool Under normal temperature state, pressure is applied to component surface, make matallic surface layer produce plastic deformation, revise component surface microcosmic and put down Whole degree, to improve surface smoothness.At the same time it can also change the metallographic structure of component surface, form favourable residual stress Distribution, thus improving the mechanical performance of parts and using service life.Rolling processing process cannot be only used for finishing and strengthening Outer ring, endoporus and plane, and it is also applied to finishing and strengthening screw thread, gear curved surface and various types of special surface etc..
It is the frictional force in order to reduce roller and workpiece using lubricant in rolling technology, thus reducing institute in rolling process The power consuming, improves the service life of roller and the surface smoothness of parts, and during rolling, lubrication firmly must supply abundance, no Can interruption, in good time cooling processed part, reduce the generation of thermal stress effects.Therefore, rolling technology lubricant must have Good extruding is had to carry wear resistence, reduce coefficient of friction, improve slide coefficient, good cooling, diffusibility, peace and quiet dispersion Property, rust-preventing characteristic, oxidation stability, anti-foaming property, resistance to emulsion and cleaning.Good manufacturability that it has (weldability and Cold formability) it is adaptable to common engineering structure and standard machinery parts.
Content of the invention
The technical problem to be solved in the present invention is that offer is a kind of to be had good extruding carrying wear resistence, reduces friction system Number, improve slide coefficient, good cooling, diffusibility, detergent-dispersant performance, rust-preventing characteristic, oxidation stability, anti-foaming property, anti-breast The compositionss of the magnesium alloy rolling and processing lubricant of the property changed and cleaning.
The present invention adopts the following technical scheme that solution above-mentioned technical problem：
A kind of compositionss of magnesium alloy rolling and processing lubricant, using oil based on No. 22 total loss system oil, join Close multiple compound additives, the one-tenth of its respective mass percent is grouped into：
Component Mass percentage content
Base oil Surplus
Antioxidant 0.05%～0.3%
Metal deactivator 0.1%～0.3%
Oiliness improver 3%～6%
Friction improver 1%～2%
Extreme pressure agent 4%～6%
Antiwear additive 3%～5%
Antirust agent 0.06%～0.3%
Anti-foaming agent 10～50ppm
Oxidation and corrosion inhibitor 0.5%～1%
Anti emulsifier 0.05%～0.2%
Urge cryogen 1%～2%
Each constituent mass percentage ratio summation is 100% above.
Antioxidant is the DBPC 2,6 ditertiary butyl p cresol T502A of mass ratio 50% and 50% N- phenyl-alpha-naphthylamine T531 answers Close.
Oiliness improver is sulfuration cottonseed oil T404；Metal deactivator is the complexing agent T532 of derivant containing benzotriazole.
Friction improver is zinc stearate.
Extreme pressure agent is chlorinated paraffin T301.
Antiwear additive is sulfide isobutene T321.
Antirust agent is the barium dinonyl napthalene sulphonate T705A of mass ratio 50% and 50% alkenyl succinic acid ester T706A answers Close.
Anti-foaming agent is methyl-silicone oil T901.
Oxidation and corrosion inhibitor is dialkyldithiocarbamacompositions sulfuration oxygen molybdenum MoPTC；Anti emulsifier is Mohilad-404 second Diol ester；Cryogen is urged to be polyisobutylene T603C.
The beneficial effects of the present invention is：The present composition has good extruding to be carried wear resistence, reduces friction system Number, improve slide coefficient, good cooling, diffusibility, detergent-dispersant performance, rust-preventing characteristic, oxidation stability, anti-foaming property, anti-breast The property changed and cleaning；Reduce abrasive dust adhesion caking；The good manufacturability having：Weldability and cold formability are it is adaptable to one As engineering structure and standard machinery parts.
Specific embodiment
Embodiment 1：
Following component is in harmonious proportion by mass percentage and forms：
Each constituent mass percentage ratio summation is equal to 100% above.
Embodiment 2：
Following component is in harmonious proportion by mass percentage and forms：
Each constituent mass percentage ratio summation is equal to 100% above.
Embodiment 3：
Following component is in harmonious proportion by mass percentage and forms：
Each constituent mass percentage ratio summation is equal to 100% above.
Embodiment 1 product typical technology index：
Project Index
40 DEG C of kinematic viscosity mm2/s 23.6
Flash-point (opening)/DEG C 181
Pour point/DEG C -16
Viscosity index (VI) 95
Corrosion experiment (copper sheet, 100 DEG C, 3h)/level 1
54 DEG C of demulsification number (4.-37-3), min 11
Oxidation stability (Rotary Oxygen elasticity, 150 DEG C), min 310
Tetra-ball machine test Pb/N 688
Sintering load PD/N 5050
Terraced nurse agrees/N 303
FZG, level 13
Mechanical admixture, % No
Moisture, % Vestige
Coefficient of friction 0.04
Water soluble acid or alkali No

Claims (9)

1. a kind of compositionss of magnesium alloy rolling and processing lubricant it is characterised in that：Using No. 22 total loss system oil conducts Base oil, coordinates multiple compound additives, and the one-tenth of its respective mass percent is grouped into：
Component Mass percentage content Base oil Surplus Antioxidant 0.05%～0.3% Metal deactivator 0.1%～0.3% Oiliness improver 3%～6% Friction improver 1%～2% Extreme pressure agent 4%～6% Antiwear additive 3%～5% Antirust agent 0.06%～0.3% Anti-foaming agent 10～50ppm Oxidation and corrosion inhibitor 0.5%～1% Anti emulsifier 0.05%～0.2% Urge cryogen 1%～2%
Each constituent mass percentage ratio summation is 100% above.
2. as claimed in claim 1 a kind of compositionss of magnesium alloy rolling and processing lubricant it is characterised in that antioxidant is matter Amount is combined than 50% DBPC 2,6 ditertiary butyl p cresol T502A and 50% N- phenyl-alpha-naphthylamine T531.
3. as claimed in claim 1 a kind of compositionss of magnesium alloy rolling and processing lubricant it is characterised in that oiliness improver is sulfur Change Oleum Gossypii semen T404；Metal deactivator is the complexing agent T532 of derivant containing benzotriazole.
4. as claimed in claim 1 a kind of compositionss of magnesium alloy rolling and processing lubricant it is characterised in that friction improver It is zinc stearate.
5. as claimed in claim 1 a kind of compositionss of magnesium alloy rolling and processing lubricant it is characterised in that extreme pressure agent is chlorine Fossil waxes T301.
6. as claimed in claim 1 a kind of compositionss of magnesium alloy steel rolling and processing lubricant it is characterised in that antiwear additive is Sulfide isobutene T321.
7. as claimed in claim 1 a kind of compositionss of magnesium alloy rolling and processing lubricant it is characterised in that antirust agent is matter Amount is combined than 50% barium dinonyl napthalene sulphonate T705A and 50% alkenyl succinic acid ester T706A.
8. as claimed in claim 1 a kind of compositionss of magnesium alloy rolling and processing lubricant it is characterised in that anti-foaming agent is first Base silicone oil T901.
9. as claimed in claim 1 a kind of compositionss of magnesium alloy rolling and processing lubricant it is characterised in that oxidation and corrosion inhibitor It is dialkyldithiocarbamacompositions sulfuration oxygen molybdenum MoPTC；Anti emulsifier is Mohilad-404 glycol ester；Cryogen is urged to be poly- Isobutene. T603C.
CN201610840978.8A 2016-09-21 2016-09-21 A kind of compositionss of magnesium alloy rolling and processing lubricant Pending CN106467849A (en)