CN106437083A - High-temperature-resistant flame-retardant solid wood floor - Google Patents
High-temperature-resistant flame-retardant solid wood floor Download PDFInfo
- Publication number
- CN106437083A CN106437083A CN201611035083.3A CN201611035083A CN106437083A CN 106437083 A CN106437083 A CN 106437083A CN 201611035083 A CN201611035083 A CN 201611035083A CN 106437083 A CN106437083 A CN 106437083A
- Authority
- CN
- China
- Prior art keywords
- layer
- parts
- steel tank
- temperature
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-temperature-resistant flame-retardant solid wood floor. The high-temperature-resistant flame-retardant solid wood floor comprises a flame-retardant painting layer, a wear-resistant painting layer, a decorating layer, a base material layer and a steel tank. The wear-resistant painting layer and the flame-retardant painting layer cover the upper surface of the decorating layer from bottom to top in sequence, and a glass fabric layer, the base material layer and the steel tank are laid on the lower surface of the decorating layer from top to bottom in sequence; the base material comprises a solid wood surface layer, a core layer and a reinforcing plate from top to bottom in sequence, wherein the positions of the solid wood surface layer, the core layer and the steel tank are overlapped with one another, the reinforcing plate, the core layer and the steel tank are arranged in an interlaced mode, and one end of the reinforcing plate protrudes and forms a protruding block between the core layer and the steel tank; the steel tank is of a hollow structure and is filled with a damp-proof layer; and the glass fabric layer is of a two-layer structure and comprises an upper glass fabric and a lower glass fabric, and the upper glass fabric and the lower glass fabric are overlapped with each other. According to the high-temperature-resistant flame-retardant solid wood floor, the service life of the floor is prolonged, industrial production is promoted, environmental friendliness is achieved, and safety is improved.
Description
Technical field
The present invention relates to technical field of floor, particularly relates to a kind of heat-resistant fireproof solid wooden floor board.
Background technology
In recent years, with the economic steady and stabilized growth of China, decoration design for residence is persistently overheating, is that timber floor is provided
Good market environment, creates the huge market demand, and timber floor is a kind of conventional floor decorative material, with other ground
Ornament materials carpet, stone material, ceramic tile are compared, and timber floor has nature, texture attractive in appearance, light weight and be easily worked, good heat preservation performance,
Can adjust indoor temperature, humidity, flexible the features such as relax impact, a kind of sensation for going back to nature is given people, is therefore suffered from
People like；With the improvement of people's living standards, on the basis of timber floor, people more and more pursue solid wooden floor board
Quality, solid wooden floor board of the prior art exist variable, not wear-resisting, cost is expensive and be difficult to prevent fires, moistureproof, be difficult peace in quality
Dress and aberration unsightly the problems such as.
Content of the invention
The technical problem to be solved is the shortcoming for overcoming prior art, provides a kind of heat-resistant fireproof solid wood ground
Plate, improves the utilization rate on floor, reduces learies, environmental protection, and the life for meeting modern people is required.
A kind of heat-resistant fireproof solid wooden floor board, including flame retardant oil enamelled coating, wearproof paint layer, decorative layer, substrate layer and steel
Groove, the upper surface of decorative layer is coated with wearproof paint layer and flame retardant oil enamelled coating from bottom to top successively, and the lower surface of decorative layer is from upper
And under be equipped with glass layer of cloth, substrate layer and steel tank successively；
Substrate layer includes solid wood surface layer, sandwich layer and reinforcing plate, the position phase of solid wood surface layer, sandwich layer and steel tank from top to bottom successively
Mutually overlap, reinforcing plate is crisscross arranged between sandwich layer and steel tank, strengthen plate one end stretch out formed between sandwich layer and steel tank convex
Block；
Steel tank is hollow structure, is wherein filled with damp-proof layer；Glass layer of cloth includes, for double-layer structure, the upper glass-fiber-fabric for overlapping up and down
With lower glass-fiber-fabric；
Flame retardant oil enamelled coating raw materials by weight portion is calculated as：Epoxy resin：14-19 part, ATO powder:28-32 part, ethanol：9-12
Part, dispersant：4-9 part, graphite powder：10-15 part, thickening agent：9-11 part, alcohol-soluble acrylate：31-33 part is ultraviolet
Light absorbers：5-10 part, waterglass：15-18 part, antioxidant：6-8 part, fire retardant:25-30 part；
Alcohol-soluble acrylate is made up of following composition by mass percentage：Ethanol：30-40%, azodiisobutyronitrile：
20-25%, methyl methacrylate：10-15%, butyl acrylate：10-15%, butyl methacrylate：10-15%, above each group
/ and be 100%；
Dispersant is DP-518, and it is UV-O that thickening agent is AT-70, UV absorbent, and antioxidant is diphenylamines or dihydroquinoline
In one kind, fire retardant is the one kind in aluminium hydroxide or magnesium hydroxide；
The preparation method of flame retardant oil enamelled coating is carried out according to the following steps：
（One）Epoxy resin, ethanol, dispersant and ATO powder are added the temperature for controlling dispersion cylinder in dispersion cylinder in 40-45
DEG C, high-speed stirred is uniform, and it is 38-42min that mixing speed is 420-450r/min, mixing time；
（Two）Again to step（One）Middle addition graphite powder, thickening agent and waterglass, high-speed stirred 45-50min, mixing speed is
660-700r/min, controls the temperature of dispersion cylinder at 80-85 DEG C；
（Three）Again to step（Two）In sequentially add alcohol-soluble acrylate, UV absorbent, antioxidant and fire-retardant
Agent stirs at normal temperatures and obtains high-temperature coatings, is then coated with wearproof paint layer surface, and under room temperature, dry solidification is
Can to flame retardant oil enamelled coating.
Aforesaid heat-resistant fireproof solid wooden floor board, flame retardant oil enamelled coating raw materials by weight portion is calculated as：Epoxy resin：14 parts,
ATO powder:28 parts, ethanol：9 parts, dispersant：4 parts, graphite powder：10 parts, thickening agent：9 parts, alcohol-soluble acrylate：31
Part, UV absorbent：5 parts, waterglass：15 parts, antioxidant：6 parts, fire retardant:25 parts；
Alcohol-soluble acrylate is made up of following composition by mass percentage：Ethanol：35%, azodiisobutyronitrile：22%,
Methyl methacrylate：13%th, butyl acrylate：15%, butyl methacrylate：15%, that above each group is divided and be 100%；
Dispersant is DP-518, and it is UV-O that thickening agent is AT-70, described UV absorbent, and antioxidant is diphenylamines or two
Hydrogen quinoline, fire retardant is aluminium hydroxide；
The preparation method of flame retardant oil enamelled coating is carried out according to the following steps：
（One）Epoxy resin, ethanol, dispersant and ATO powder are added the temperature for controlling dispersion cylinder in dispersion cylinder at 43 DEG C,
High-speed stirred is uniform, and it is 40min that mixing speed is 430r/min, mixing time；
（Two）Again to step（One）Middle addition graphite powder, thickening agent and waterglass, high-speed stirred 48min, mixing speed is
680r/min, controls the temperature of dispersion cylinder at 81 DEG C；
（Three）Again to step（Two）In sequentially add alcohol-soluble acrylate, UV absorbent, antioxidant and fire-retardant
Agent stirs at normal temperatures and obtains high-temperature coatings, is then coated with wearproof paint layer surface, and under room temperature, dry solidification is
Can to flame retardant oil enamelled coating.
Aforesaid heat-resistant fireproof solid wooden floor board, flame retardant oil enamelled coating raw materials by weight portion is calculated as：Epoxy resin：19 parts,
ATO powder:32 parts, ethanol：12 parts, dispersant：9 parts, graphite powder：15 parts, thickening agent：11 parts, alcohol-soluble acrylate：
33 parts, UV absorbent：10 parts, waterglass：18 parts, antioxidant：8 parts, fire retardant:30 parts；
Alcohol-soluble acrylate is made up of following composition by mass percentage：Ethanol：40%, azodiisobutyronitrile：20%,
Methyl methacrylate：13%th, butyl acrylate：15%, butyl methacrylate：12%, that above each group is divided and be 100%；
Dispersant is DP-518, and it is UV-O that thickening agent is AT-70, UV absorbent, and antioxidant is that dihydroquinoline, fire retardant is
Magnesium hydroxide；
The preparation method of flame retardant oil enamelled coating is carried out according to the following steps：
（One）Epoxy resin, ethanol, dispersant and ATO powder are added the temperature for controlling dispersion cylinder in dispersion cylinder at 43 DEG C,
High-speed stirred is uniform, and it is 40min that mixing speed is 430r/min, mixing time；
（Two）Again to step（One）Middle addition graphite powder, thickening agent and waterglass, high-speed stirred 48min, mixing speed is
680r/min, controls the temperature of dispersion cylinder at 81 DEG C；
（Three）Again to step（Two）In sequentially add alcohol-soluble acrylate, UV absorbent, antioxidant and fire-retardant
Agent stirs at normal temperatures and obtains high-temperature coatings, is then coated with wearproof paint layer surface, and under room temperature, dry solidification is
Can to flame retardant oil enamelled coating.
Aforesaid heat-resistant fireproof solid wooden floor board, heat-resistant fireproof solid wooden floor board, overlap between solid wood surface layer and sandwich layer
Fixing, sealing wax layer is coated with overlapping.
Aforesaid heat-resistant fireproof solid wooden floor board, the lower surface for strengthening plate opens up fluted, and the upper surface of steel tank is provided with prominent
Go out portion and protuberance and the fit depressions for strengthening plate lower surface.
Aforesaid heat-resistant fireproof solid wooden floor board, the damp-proof layer of filling is moistureproof silicone rubber, and the material of moistureproof silicone rubber is
Polysiloxanes high molecular polymer.
Aforesaid heat-resistant fireproof solid wooden floor board, the material of the sandwich layer in substrate layer is solid wood sandwich layer.
Aforesaid heat-resistant fireproof solid wooden floor board, the upper glass-fiber-fabric in glass layer of cloth be impregnated of thermostable phenolic resin
Glass-fiber-fabric, lower glass-fiber-fabric is the glass-fiber-fabric impregnated of the alcohol-soluble phenolic resin for adding fire retardant.
Using technical scheme beneficial effect it is：The lower surface for strengthening plate in the present invention is connected with steel tank, plus
Consolidate the hollow structure between reinforcing plate and ground, is filled with moistureproof silicone rubber in steel tank, steel tank has stronger seal so that
Silicone rubber not easy to leak, effectively strengthens floor because of the cracking damage that ground is moist or infiltration causes, and moistureproof silicone rubber is poly-
Siloxanes high molecular polymer, the relatively low and protection that be conducive to environment of the cost of material；
Glass layer of cloth in the present invention is double-layer structure, and upper glass layer of cloth is impregnated of the glass-fiber-fabric of thermostable phenolic resin, lower glass
Fine layer of cloth is the glass-fiber-fabric of the alcohol-soluble phenolic resin for adding fire retardant, and glass layer of cloth is arranged between substrate layer and decorative layer,
The heat-resisting quantity of solid wooden floor board and good anti-flammability is improve, extends the service life of solid wooden floor board；
Without unit equipment or parts such as extra increase locks in the present invention, projection is formed by the iterative structure of itself and facilitate group
Assembly and disassembly are unloaded, it is to avoid the phenomenon such as relax, come off, and enhance solid wooden floor board overall steadiness when mounted, it is ensured that using normal；
The present invention is when the flame retardant oil enamelled coating on the floor is prepared, and method and step is simple, and raw material environmental protection is conducive to the guarantor to environment
Shield, and improve utilization rate and the safety on floor.
Description of the drawings
Fig. 1 is the structural representation of the present invention；
Wherein：1- flame retardant oil enamelled coating, 2- wearproof paint layer, 3- decorative layer, 4- substrate layer, 5- damp-proof layer, 6- solid wood surface layer, 7- core
Layer, 8- strengthens plate, 9- steel tank, 10- glass layer of cloth.
Specific embodiment
Embodiment 1
The present embodiment provides a kind of heat-resistant fireproof solid wooden floor board, including flame retardant oil enamelled coating 1, wearproof paint layer 2, decorative layer 3, base
Material layer 4 and steel tank 9, the upper surface of decorative layer 3 is coated with wearproof paint layer 2 and flame retardant oil enamelled coating 1 from bottom to top successively, decoration
The lower surface of layer 3 is equipped with glass layer of cloth 10, substrate layer 4 and steel tank 9 from top to bottom successively；
Substrate layer 4 includes solid wood surface layer 6, sandwich layer 7 and reinforcing plate 8 from top to bottom successively, and the material of sandwich layer 7 is solid wood, solid wood
The position of surface layer 6, sandwich layer 7 and steel tank 9 overlaps, and is crisscross arranged between reinforcing plate 8 and sandwich layer 7 and steel tank 9, strengthens plate 8
Formation projection between sandwich layer 7 and steel tank 9 is stretched out in one end；
Steel tank 9 is hollow structure, is wherein filled with damp-proof layer 5, and the material of the damp-proof layer 5 of filling is moistureproof silicone rubber, moistureproof silicon
Rubber is polysiloxanes high molecular polymer；Glass layer of cloth 10 includes the upper glass-fiber-fabric for overlapping up and down with lower glass for double-layer structure
Cloth, the upper glass-fiber-fabric in glass layer of cloth 10 is the glass-fiber-fabric impregnated of thermostable phenolic resin, lower glass-fiber-fabric be impregnated of interpolation
The glass-fiber-fabric of the alcohol-soluble phenolic resin of fire retardant；Between solid wood surface layer 6 and sandwich layer 7, overlapping is fixed, and is coated with overlapping
Sealing wax layer；The lower surface of reinforcing plate 8 opens up fluted, and the upper surface of steel tank 9 is provided with protuberance and protuberance and reinforcing 8 following table of plate
The fit depressions in face；
1 raw materials by weight portion of flame retardant oil enamelled coating is calculated as：Epoxy resin：14 parts, ATO powder:28 parts, ethanol：9 parts, dispersant：
4 parts, graphite powder：10 parts, thickening agent：9 parts, alcohol-soluble acrylate：31 parts, UV absorbent：5 parts, waterglass：15
Part, antioxidant：6 parts, fire retardant:25 parts；
Alcohol-soluble acrylate is made up of following composition by mass percentage：Ethanol：35%, azodiisobutyronitrile：22%,
Methyl methacrylate：13%th, butyl acrylate：15%, butyl methacrylate：15%, that above each group is divided and be 100%；
Dispersant is DP-518, and it is UV-O that thickening agent is AT-70, UV absorbent, and antioxidant is diphenylamines or dihydroquinoline
In one kind, fire retardant is the one kind in aluminium hydroxide or magnesium hydroxide；
The preparation method of above-mentioned flame retardant oil enamelled coating 1 is carried out according to the following steps：
（One）Epoxy resin, ethanol, dispersant and ATO powder are added the temperature for controlling dispersion cylinder in dispersion cylinder at 40 DEG C,
High-speed stirred is uniform, and it is 38min that mixing speed is 420r/min, mixing time；
（Two）Again to step（One）Middle addition graphite powder, thickening agent and waterglass, high-speed stirred 45min, mixing speed is
660r/min, controls the temperature of dispersion cylinder at 80 DEG C；
（Three）Again to step（Two）In sequentially add alcohol-soluble acrylate, UV absorbent, antioxidant and fire-retardant
Agent stirs at normal temperatures and obtains high-temperature coatings, is then coated with wearproof paint layer surface, and under room temperature, dry solidification is
Can to flame retardant oil enamelled coating.
Embodiment 2
The present embodiment provides a kind of heat-resistant fireproof solid wooden floor board, including flame retardant oil enamelled coating 1, wearproof paint layer 2, decorative layer 3, base
Material layer 4 and steel tank 9, the upper surface of decorative layer 3 is coated with wearproof paint layer 2 and flame retardant oil enamelled coating 1 from bottom to top successively, decoration
The lower surface of layer 3 is equipped with glass layer of cloth 10, substrate layer 4 and steel tank 9 from top to bottom successively；
Substrate layer 4 includes solid wood surface layer 6, sandwich layer 7 and reinforcing plate 8 from top to bottom successively, and the material of sandwich layer 7 is solid wood, solid wood
The position of surface layer 6, sandwich layer 7 and steel tank 9 overlaps, and is crisscross arranged between reinforcing plate 8 and sandwich layer 7 and steel tank 9, strengthens plate 8
Formation projection between sandwich layer 7 and steel tank 9 is stretched out in one end；
Steel tank 9 is hollow structure, is wherein filled with damp-proof layer 5, and the material of the damp-proof layer 5 of filling is moistureproof silicone rubber, moistureproof silicon
Rubber is polysiloxanes high molecular polymer；Glass layer of cloth 10 includes the upper glass-fiber-fabric for overlapping up and down with lower glass for double-layer structure
Cloth, the upper glass-fiber-fabric in glass layer of cloth 10 is the glass-fiber-fabric impregnated of thermostable phenolic resin, lower glass-fiber-fabric be impregnated of interpolation
The glass-fiber-fabric of the alcohol-soluble phenolic resin of fire retardant；Between solid wood surface layer 6 and sandwich layer 7, overlapping is fixed, and is coated with overlapping
Sealing wax layer；The lower surface of reinforcing plate 8 opens up fluted, and the upper surface of steel tank 9 is provided with protuberance and protuberance and reinforcing 8 following table of plate
The fit depressions in face；
1 raw materials by weight portion of flame retardant oil enamelled coating is calculated as：Epoxy resin：19 parts, ATO powder:32 parts, ethanol：12 parts, dispersion
Agent：9 parts, graphite powder：15 parts, thickening agent：11 parts, alcohol-soluble acrylate：33 parts, UV absorbent：10 parts, water glass
Glass：18 parts, antioxidant：8 parts, fire retardant:30 parts；
Alcohol-soluble acrylate is made up of following composition by mass percentage：Ethanol：40%, azodiisobutyronitrile：20%,
Methyl methacrylate：13%th, butyl acrylate：15%, butyl methacrylate：12%, that above each group is divided and be 100%；
Dispersant is DP-518, and it is UV-O that thickening agent is AT-70, UV absorbent, and antioxidant is diphenylamines or dihydroquinoline
In one kind, fire retardant is the one kind in aluminium hydroxide or magnesium hydroxide；
The preparation method of above-mentioned flame retardant oil enamelled coating 1 is carried out according to the following steps：
（One）Epoxy resin, ethanol, dispersant and ATO powder are added the temperature for controlling dispersion cylinder in dispersion cylinder at 45 DEG C,
High-speed stirred is uniform, and it is 42min that mixing speed is 450r/min, mixing time；
（Two）Again to step（One）Middle addition graphite powder, thickening agent and waterglass, high-speed stirred 50min, mixing speed is
700r/min, controls the temperature of dispersion cylinder at 85 DEG C；
（Three）Again to step（Two）In sequentially add alcohol-soluble acrylate, UV absorbent, antioxidant and fire-retardant
Agent stirs at normal temperatures and obtains high-temperature coatings, is then coated with wearproof paint layer surface, and under room temperature, dry solidification is
Can to flame retardant oil enamelled coating.
In addition to the implementation, the present invention can also have other embodiment.All employing equivalents or equivalent transformation shape
The technical scheme for becoming, all falls within the protection domain of application claims.
Claims (8)
1. a kind of heat-resistant fireproof solid wooden floor board, including flame retardant oil enamelled coating（1）, wearproof paint layer（2）, decorative layer（3）, substrate layer
（4）And steel tank（9）, it is characterised in that：The decorative layer（3）Upper surface be coated with wearproof paint layer from bottom to top successively
（2）And flame retardant oil enamelled coating（1）, the decorative layer（3）Lower surface be equipped with glass layer of cloth from top to bottom successively（10）, substrate layer
（4）And steel tank（9）；
The substrate layer（4）Include solid wood surface layer from top to bottom successively（6）, sandwich layer（7）And reinforcing plate（8）, the solid wood surface
Layer（6）, sandwich layer（7）And steel tank（9）Position overlap, the reinforcing plate（8）With sandwich layer（7）And steel tank（9）Between interlock
Arrange, the reinforcing plate（8）One end stretch out and sandwich layer（7）With steel tank（9）Between formed projection；
The steel tank（9）For hollow structure, damp-proof layer is wherein filled with（5）；The glass layer of cloth（10）Include for double-layer structure
The upper glass-fiber-fabric for overlapping up and down and lower glass-fiber-fabric；
The flame retardant oil enamelled coating（1）Raw materials by weight portion is calculated as：Epoxy resin：14-19 part, ATO powder:28-32 part, second
Alcohol：9-12 part, dispersant：4-9 part, graphite powder：10-15 part, thickening agent：9-11 part, alcohol-soluble acrylate：31-33
Part, UV absorbent：5-10 part, waterglass：15-18 part, antioxidant：6-8 part, fire retardant:25-30 part；
The alcohol-soluble acrylate is made up of following composition by mass percentage：Ethanol：30-40%, two isobutyl of azo
Nitrile：20-25%, methyl methacrylate：10-15%, butyl acrylate：10-15%, butyl methacrylate：10-15%, above
That each group is divided and be 100%；
Described dispersant is DP-518, and described thickening agent is AT-70, and described UV absorbent is UV-O, described
Antioxidant is diphenylamines or the one kind in dihydroquinoline, and described fire retardant is aluminium hydroxide or the one kind in magnesium hydroxide；
The flame retardant oil enamelled coating（1）Preparation method carry out according to the following steps：
（One）Epoxy resin, ethanol, dispersant and ATO powder are added the temperature for controlling dispersion cylinder in dispersion cylinder in 40-45
DEG C, high-speed stirred is uniform, and it is 38-42min that mixing speed is 420-450r/min, mixing time；
（Two）Again to step（One）Middle addition graphite powder, thickening agent and waterglass, high-speed stirred 45-50min, mixing speed is
660-700r/min, controls the temperature of dispersion cylinder at 80-85 DEG C；
（Three）Again to step（Two）In sequentially add alcohol-soluble acrylate, UV absorbent, antioxidant and fire-retardant
Agent stirs at normal temperatures and obtains high-temperature coatings, is then coated with wearproof paint layer surface, and under room temperature, dry solidification is
Can to flame retardant oil enamelled coating.
2. heat-resistant fireproof solid wooden floor board according to claim 1, it is characterised in that：The flame retardant oil enamelled coating（1）Raw material
It is calculated by weight as：Epoxy resin：14 parts, ATO powder:28 parts, ethanol：9 parts, dispersant：4 parts, graphite powder：10 parts, increase
Thick dose：9 parts, alcohol-soluble acrylate：31 parts, UV absorbent：5 parts, waterglass：15 parts, antioxidant：6 parts, fire-retardant
Agent:25 parts；
The alcohol-soluble acrylate is made up of following composition by mass percentage：Ethanol：35%, azodiisobutyronitrile：
22%, methyl methacrylate：13%th, butyl acrylate：15%, butyl methacrylate：15%, that above each group is divided and be
100%；
Described dispersant is DP-518, and described thickening agent is AT-70, and described UV absorbent is UV-O, described
Antioxidant is diphenylamines or dihydroquinoline, and described fire retardant is aluminium hydroxide；
The flame retardant oil enamelled coating（1）Preparation method carry out according to the following steps：
（One）Epoxy resin, ethanol, dispersant and ATO powder are added the temperature for controlling dispersion cylinder in dispersion cylinder at 43 DEG C,
High-speed stirred is uniform, and it is 40min that mixing speed is 430r/min, mixing time；
（Two）Again to step（One）Middle addition graphite powder, thickening agent and waterglass, high-speed stirred 48min, mixing speed is
680r/min, controls the temperature of dispersion cylinder at 81 DEG C；
（Three）Again to step（Two）In sequentially add alcohol-soluble acrylate, UV absorbent, antioxidant and fire-retardant
Agent stirs at normal temperatures and obtains high-temperature coatings, is then coated with wearproof paint layer surface, and under room temperature, dry solidification is
Can to flame retardant oil enamelled coating.
3. heat-resistant fireproof solid wooden floor board according to claim 1, it is characterised in that：The flame retardant oil enamelled coating（1）Raw material
It is calculated by weight as：Epoxy resin：19 parts, ATO powder:32 parts, ethanol：12 parts, dispersant：9 parts, graphite powder：15 parts, increase
Thick dose：11 parts, alcohol-soluble acrylate：33 parts, UV absorbent：10 parts, waterglass：18 parts, antioxidant：8 parts, resistance
Combustion agent:30 parts；
The alcohol-soluble acrylate is made up of following composition by mass percentage：Ethanol：40%, azodiisobutyronitrile：
20%, methyl methacrylate：13%th, butyl acrylate：15%, butyl methacrylate：12%, that above each group is divided and be
100%；
Described dispersant is DP-518, and described thickening agent is AT-70, and described UV absorbent is UV-O, described
Antioxidant is dihydroquinoline, and described fire retardant is magnesium hydroxide；
The flame retardant oil enamelled coating（1）Preparation method carry out according to the following steps：
（One）Epoxy resin, ethanol, dispersant and ATO powder are added the temperature for controlling dispersion cylinder in dispersion cylinder at 43 DEG C,
High-speed stirred is uniform, and it is 40min that mixing speed is 430r/min, mixing time；
（Two）Again to step（One）Middle addition graphite powder, thickening agent and waterglass, high-speed stirred 48min, mixing speed is
680r/min, controls the temperature of dispersion cylinder at 81 DEG C；
（Three）Again to step（Two）In sequentially add alcohol-soluble acrylate, UV absorbent, antioxidant and fire-retardant
Agent stirs at normal temperatures and obtains high-temperature coatings, is then coated with wearproof paint layer surface, and under room temperature, dry solidification is
Can to flame retardant oil enamelled coating.
4. heat-resistant fireproof solid wooden floor board according to claim 1, it is characterised in that：The solid wood surface layer（6）And core
Layer（7）Between overlapping fix, be coated with sealing wax layer at the overlapping.
5. heat-resistant fireproof solid wooden floor board according to claim 1, it is characterised in that：The reinforcing plate（8）Lower surface
Open up fluted, the steel tank（9）Upper surface be provided with protuberance and the protuberance and reinforcing plate（8）The groove phase of lower surface
Coordinate.
6. heat-resistant fireproof solid wooden floor board according to claim 1, it is characterised in that：The damp-proof layer of the filling（5）'s
Material is moistureproof silicone rubber, and the protection against the tide silicone rubber is polysiloxanes high molecular polymer.
7. heat-resistant fireproof solid wooden floor board according to claim 1, it is characterised in that：The sandwich layer（7）Material be real
Wood.
8. heat-resistant fireproof solid wooden floor board according to claim 1, it is characterised in that：The glass layer of cloth（10）In upper
Glass-fiber-fabric is the glass-fiber-fabric impregnated of thermostable phenolic resin, and lower glass-fiber-fabric is the alcohol-soluble phenolic aldehyde tree impregnated of interpolation fire retardant
The glass-fiber-fabric of fat.