CN106147460A - A kind of heat insulating coatings - Google Patents
A kind of heat insulating coatings Download PDFInfo
- Publication number
- CN106147460A CN106147460A CN201610866269.7A CN201610866269A CN106147460A CN 106147460 A CN106147460 A CN 106147460A CN 201610866269 A CN201610866269 A CN 201610866269A CN 106147460 A CN106147460 A CN 106147460A
- Authority
- CN
- China
- Prior art keywords
- heat insulating
- insulating coatings
- sepiolite
- agent
- dispersant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of heat insulating coatings, this coating includes following component: water, acrylate copolymer emulsion, propane diols, sepiolite, nano ceramics cenosphere, yittrium oxide, titanium dioxide, crushed crude pearlite, mica powder, talcum powder, hydroxyethyl cellulose, lignin, anti-settling agent, advection agent, dispersant, defoamer.This coating has excellent heat preservation and insulation, and overcome the shortcomings such as tradition heat insulating coatings impact resistance is weak, be dried contraction greatly, adhesive strength is low, decorative effect is poor, it is the compound heat insulating coatings of a kind of function admirable, have broad application prospects.
Description
Technical field
The invention belongs to paint field, be specifically related to a kind of heat insulating coatings.
Background technology
The energy is premise and the basis of human society survival and development, and wherein, building energy conservation is the weight of China's energy conservation
One of point, and exterior-wall heat insulation has become the major product of building energy conservation, thermal insulation coatings, can after compound with the enclosure body of building
Make building reach insulation and heat insulation purpose, be material conventional during building energy conservation is implemented.
At present, the conduct such as sepiolite, crushed crude pearlite commonly used by the coating being used as finish coat in skin heat insulation system
Insulation additive is prepared, and film forming matter commonly uses ordinary emulsion, and when the external environment temperature difference becomes big, the film of finish coat can occur
Cracking, in turn results in the cracking of heat-insulation layer, thus affects the service life of the whole heat insulation system of skin, therefore, and research and development
Go out the compound heat insulation coating that can solve drawbacks described above, there is deep realistic meaning.
Content of the invention
In view of this, it is an object of the invention to provide a kind of heat insulating coatings.
For reaching above-mentioned purpose, the present invention provides following technical scheme:
A kind of heat insulating coatings, each component materials and mass fraction thereof be: water 15~20%;Acrylate copolymer emulsion 25
~35%;Propane diols 2~3%;Sepiolite 3.2~4.5%;Nano ceramics cenosphere 7~9%;Yittrium oxide 6~8%;Titanium white
Powder 2~4%;Crushed crude pearlite 2~4%;Mica powder 3~5%;Talcum powder 2.5~3.5%;Hydroxyethyl cellulose 1~1.5%;Wood
Quality 9~10%;Anti-settling agent 0.23~0.4%;Advection agent 0.1~0.25%;Dispersant 0.3~0.5%;Defoamer 0.2~
0.4%.
Further, each component materials and mass fraction thereof are: water 19%;Acrylate copolymer emulsion 32%;Propane diols
2.5%;Sepiolite 4%;Nano ceramics cenosphere 8.3%;Yittrium oxide 6.8%;Titanium dioxide 3.2%;Crushed crude pearlite 3%;Cloud
Female powder 4.2%;Talcum powder 3%;Hydroxyethyl cellulose 1.3%;Lignin 9.5%;Anti-settling agent 0.32%;Advection agent 0.2%;Point
Powder 0.4%;Defoamer 0.3%.
Further, described sepiolite is lithium ion modified meerschaum.
Further, described titanium dioxide is the one in rutile-type or anatase titanium dioxide.
Further, described anti-settling agent is montmorillonite.
Further, described advection agent is terminal groups modification organosilicon.
Further, described dispersant be lithium magnesium silicate, one or more in OP-5035 or OP-8146.
Further, described defoamer is the mixture of broken bubble polymer and polysiloxane solution.
The beneficial effects of the present invention is: the present invention provides a kind of heat insulating coatings, this coating has excellent heat insulation
Heat-insulating property, wherein, the nano ceramics cenosphere of interpolation and yittrium oxide are the nanoscale reflective insulation that reflectivity is high, thermal resistance is big
Material, makes this coating can form, at body surface, the three-dimensional network hollow-core construction being linked together by microballon, can effectively suppress too
Positive and ultrared radiant heat and conduction heat, in conjunction with the heat-proof quality of sepiolite, utilize reflective insulation and heat insulation two kinds of barrier
The synergy of heat-insulation and heat-preservation mechanism, improves its heat preservation and insulation, further meanwhile, by optimizing the interpolation of other components
Amount, overcome that tradition heat insulating coatings impact resistance is weak, be dried shrink big, adhesive strength is low, decorative effect is poor lacks
Point so that it is become the compound heat insulating coatings of function admirable, have broad application prospects.
Detailed description of the invention
The preferred embodiments of the present invention will be described in detail below.
Embodiment 1
A kind of heat insulating coatings, component contained by it and each composition mass percent are as follows:
Water 15%;Acrylate copolymer emulsion 25%;Propane diols 2%;Lithium ion modified meerschaum 3.2%;Nano ceramics is empty
Heart microballon 7%;Yittrium oxide 6%;Rutile type titanium white 2%;Crushed crude pearlite 2%;Mica powder 3%;Talcum powder 2.5%;Hydroxyl second
Base cellulose 1%;Lignin 9%;Montmorillonite 0.23%;Terminal groups modification organosilicon 0.1%;Lithium magnesium silicate 0.3%;Broken bubble polymerization
The mixture 0.2% of thing and polysiloxane solution.
Embodiment 2
A kind of heat insulating coatings, component contained by it and each composition mass percent are as follows:
Water 16%;Acrylate copolymer emulsion 28%;Propane diols 2.5%;Lithium ion modified meerschaum 3.5%;Nano ceramics
Cenosphere 7.5%;Yittrium oxide 7%;Rutile type titanium white 3%;Crushed crude pearlite 3%;Mica powder 4%;Talcum powder 3%;Hydroxyl
Ethyl cellulose 1.25%;Lignin 9.5%;Montmorillonite 0.3%;Terminal groups modification organosilicon 0.15%;OP-5035 0.4%;
Broken bubble polymer and the mixture 0.3% of polysiloxane solution.
Embodiment 3
A kind of heat insulating coatings, component contained by it and each composition mass percent are as follows:
Water 18%;Acrylate copolymer emulsion 32%;Propane diols 2.5%;Lithium ion modified meerschaum 4%;Nano ceramics is empty
Heart microballon 8%;Yittrium oxide 7.5%;Anatase thpe white powder 3%;Crushed crude pearlite 3%;Mica powder 4%;Talcum powder 3%;Ethoxy
Cellulose 1.25%;Lignin 9.5%;Montmorillonite 0.35%;Terminal groups modification organosilicon 0.2%;OP-8146 0.4%;Broken bubble
The mixture 0.3% of polymer and polysiloxane solution.
Embodiment 4
A kind of heat insulating coatings, component contained by it and each composition mass percent are as follows:
Water 20%;Acrylate copolymer emulsion 35%;Propane diols 3%;Lithium ion modified meerschaum 4.5%;Nano ceramics is empty
Heart microballon 9%;Yittrium oxide 8%;Anatase thpe white powder 4%;Crushed crude pearlite 4%;Mica powder 5%;Talcum powder 3.5%;Ethoxy
Cellulose 1.5%;Lignin 10%;Montmorillonite 0.4%;Terminal groups modification organosilicon 0.25%;OP-5035 is mixed with lithium magnesium silicate
Compound 0.5%;Broken bubble polymer and the mixture 0.4% of polysiloxane solution.
Finally illustrate, preferred embodiment above only in order to technical scheme being described and unrestricted, although logical
Cross above preferred embodiment to be described in detail the present invention, it is to be understood by those skilled in the art that can be
In form and various change is made to it, without departing from claims of the present invention limited range in details.
Claims (8)
1. a heat insulating coatings, it is characterised in that each component materials and mass fraction thereof be: water 15~20%;Acrylic acid
Copolymer emulsion 25~35%;Propane diols 2~3%;Sepiolite 3.2~4.5%;Nano ceramics cenosphere 7~9%;Yittrium oxide 6
~8%;Titanium dioxide 2~4%;Crushed crude pearlite 2~4%;Mica powder 3~5%;Talcum powder 2.5~3.5%;Hydroxyethyl cellulose 1
~1.5%;Lignin 9~10%;Anti-settling agent 0.23~0.4%;Advection agent 0.1~0.25%;Dispersant 0.3~0.5%;Disappear
Infusion 0.2~0.4%.
2. heat insulating coatings as claimed in claim 1 a kind of, it is characterised in that each component materials and mass fraction thereof be:
Water 19%;Acrylate copolymer emulsion 32%;Propane diols 2.5%;Sepiolite 4%;Nano ceramics cenosphere 8.3%;Yittrium oxide
6.8%;Titanium dioxide 3.2%;Crushed crude pearlite 3%;Mica powder 4.2%;Talcum powder 3%;Hydroxyethyl cellulose 1.3%;Lignin
9.5%;Anti-settling agent 0.32%;Advection agent 0.2%;Dispersant 0.4%;Defoamer 0.3%.
3. a kind of heat insulating coatings as claimed in claim 1, it is characterised in that described sepiolite is the modified Hai Pao of lithium ion
Stone.
4. a kind of heat insulating coatings as claimed in claim 1, it is characterised in that described titanium dioxide is rutile-type or sharp titanium
One in type.
5. a kind of heat insulating coatings as claimed in claim 1, it is characterised in that described anti-settling agent is montmorillonite.
6. a kind of heat insulating coatings as claimed in claim 1, it is characterised in that described advection agent is that terminal groups modification is organic
Silicon.
7. a kind of heat insulating coatings as claimed in claim 1, it is characterised in that described dispersant is lithium magnesium silicate, OP-
One or more in 5035 or OP-8146.
8. one heat insulating coatings as claimed in claim 1, it is characterised in that described defoamer is for broken bubble polymer and gathers
The mixture of siloxane solution.