CN106433273A - Rattan-woven artware putty and preparation method thereof - Google Patents
Rattan-woven artware putty and preparation method thereof Download PDFInfo
- Publication number
- CN106433273A CN106433273A CN201610783712.4A CN201610783712A CN106433273A CN 106433273 A CN106433273 A CN 106433273A CN 201610783712 A CN201610783712 A CN 201610783712A CN 106433273 A CN106433273 A CN 106433273A
- Authority
- CN
- China
- Prior art keywords
- parts
- putty
- rattan
- preparation
- emulsification
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a rattan-woven artware putty and a preparation method thereof, and relates to the technical field of putty production. The rattan-woven artware putty is prepared from, by weight, 20-30 parts of water, 10-20 parts of modified organopolysiloxane, 6-10 parts of a thickener, 5-6 parts of talcum powder, 3-5 parts of hydroxymethyl fibers, 1-3 parts of petroleum coke powder, 5-10 parts of urea-formaldehyde glue, 6-8 parts of triisopropanolamine, 2-4 parts of an antifoaming agent, 2-4 parts of aluminum powder and 2-3 parts of a pigment. The preparation method comprises the following steps: completely milling solid raw materials, fully mixing all the raw materials, and emulsifying all the raw materials at 70 DEG C under a stirring speed of 3000 r/min for 20 min. The putty has the advantages of high viscosity, fineness, high uniformity, fast drying speed, high hardness after formation, and difficulty in shedding.
Description
Technical field：
The present invention relates to putty production technical field, specifically a kind of rattan plaited handicraft putty and preparation method thereof.
Background technology：
Typically can carry out some special process to rattan before rattan weaving handicraft, generally comprise softening, strengthen
Toughness, peeling etc. are processed, rattan plaited handicraft come sometimes for putty on knitting forming later stage surface hole on fill process product,
Gap, the fault location such as come unglued, and powder of lacquer putty for use on formula of the prior art is fairly simple, typically all passes through viscose, stone flour and face
Material etc. is formed by directly mixing, and viscosity is not enough, and the effect of waterproof is poor, easily comes off after filling up, and strong after filling up after-hardening
Degree substantially, slow drying speed lower than the position do not filled up.
Content of the invention：
The technical problem to be solved is to provide a kind of viscosity high, and rate of drying is fast, and after shaping, hardness is high, no
Hold caducous rattan plaited handicraft putty and preparation method thereof.
The technical problem solving is adopted following technical scheme：
A kind of rattan plaited handicraft putty it is characterised in that：It is made up of following components raw material by weight,
A kind of preparation method of rattan plaited handicraft putty, comprises the following steps, and whole for solid material abrasive dusts is processed, then
All of raw material is sufficiently mixed and carries out emulsification treatment, 70 DEG C of emulsifying temperature during emulsification, emulsification stirring speed 3000r/min,
Emulsification times 20min.
Described defoamer includes by weight, 2～4 parts of wooden triethanolamine and 3～7 parts of ethylene glycol.
Described thickener is wollastonite, gypsum and cornstarch, and both ratios are 111.
There is after powder of lacquer putty for use in the present invention is floating higher slickness, can preferable renovation technique product defect, glue
Property foot, intensity is high, rate of drying fast it is not easy to drop.The defoamer of the present invention not only has efficient froth breaking effect, improves all
Evenness, and play the purpose that intensity and hardness after putty is dried are strengthened in putty rapid draing simultaneously, the thickener in the present invention
Can also strengthen putty bonding and the intensity of itself, be encounter hard object also will not be broken rotten.The making side of the present invention
Method is passed through abrasive dust, emulsification and is made under specific temperature, time, and putty powder fineness, the uniformity are high, is conducive to improving product
Performance.
The invention has the beneficial effects as follows：Viscosity of the present invention is high, fine and smooth, and the uniformity is high, and rate of drying is fast, hardness after shaping
Height is it is not easy to come off.
Specific embodiment：
In order that technological means, creation characteristic, reached purpose and effect that the present invention realizes are easy to understand, tie below
Close instantiation, the present invention is expanded on further.
A kind of rattan plaited handicraft putty, is made up of following components raw material by weight,
A kind of preparation method of rattan plaited handicraft putty, comprises the following steps, and whole for solid material abrasive dusts is processed, then
All of raw material is sufficiently mixed and carries out emulsification treatment, 70 DEG C of emulsifying temperature during emulsification, emulsification stirring speed 3000r/min,
Emulsification times 20min.
Defoamer includes by weight, 2～4 parts of wooden triethanolamine and 3～7 parts of ethylene glycol.
Thickener is wollastonite, gypsum and cornstarch, and both ratios are 111.
General principle and principal character and the advantages of the present invention of the present invention have been shown and described above.The technology of the industry
, it should be appreciated that the present invention is not restricted to the described embodiments, the simply explanation described in above-described embodiment and specification is originally for personnel
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these changes
Change and improvement both falls within scope of the claimed invention.Claimed scope by appending claims and its
Equivalent thereof.
Claims (4)
1. a kind of rattan plaited handicraft putty it is characterised in that：It is made up of following components raw material by weight,
2. a kind of rattan plaited handicraft putty according to claim 1 preparation method it is characterised in that：Walk including following
Suddenly, whole for solid material abrasive dusts are processed, then all of raw material is sufficiently mixed and carries out emulsification treatment, emulsification temperature during emulsification
70 DEG C of degree, emulsification stirring speed 3000r/min, emulsification times 20min.
3. a kind of rattan plaited handicraft putty according to claim 1 it is characterised in that：Described defoamer wraps by weight
Include, 2～4 parts of wooden triethanolamine and 3～7 parts of ethylene glycol.
4. a kind of rattan plaited handicraft putty according to claim 1 it is characterised in that：Described thickener be wollastonite,
Gypsum and cornstarch, both ratios are 111.