CN106221349A - A kind of plywood putty high from dryness and preparation method thereof - Google Patents
A kind of plywood putty high from dryness and preparation method thereof Download PDFInfo
- Publication number
- CN106221349A CN106221349A CN201610578448.0A CN201610578448A CN106221349A CN 106221349 A CN106221349 A CN 106221349A CN 201610578448 A CN201610578448 A CN 201610578448A CN 106221349 A CN106221349 A CN 106221349A
- Authority
- CN
- China
- Prior art keywords
- parts
- putty
- plywood
- dryness
- emulsifying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of plywood putty high from dryness and preparation method thereof, relate to plywood putty production technical field, be made up of following components raw material by weight, water 20～30 parts, silica flour 2～4 parts, bauxite 1～3 parts, GM 1 resin 2～3 parts 10～20 parts, thickening agent 5～7 parts, hydroxylmethyl cellulose 3～5 parts, petroleum coke powder 1～3 parts, urea-formaldehyde glue 5～10 parts, defoamer 2～4 parts and pigment 2～3 parts.Comprise the following steps, whole for solid material pulverizing are processed, then all of raw material is sufficiently mixed and carries out emulsifying, emulsifying temperature during emulsifying 80 DEG C, emulsification stirring speed 2500r/min, emulsification times 20min.Viscosity of the present invention is high, fine and smooth, and the uniformity is high, and rate of drying is fast, and after molding, hardness is high, it is not easy to come off.
Description
Technical field:
The present invention relates to plywood putty production technical field, a kind of plywood putty high from dryness and system thereof
Preparation Method.
Background technology:
Plywood is to be peeled into veneer by juggle or become veneer by flitch slicing, then stick with glue three layers of agent gluing or
The board-like material of multilamellar, generally uses odd-level veneer, and make the orthogonal gluing of machine direction of adjacent layer veneer form.Glued
Plate after hot-forming it is generally required to putty comes the hole on padding gum plywood, gap, the fault location such as come unglued, in prior art
Powder of lacquer putty for use on formula fairly simple, be typically all and be formed by directly mixing by viscose, stone powder and pigment etc., viscosity is not enough,
Easily come off after filling up, and intensity is substantially low than the position do not filled up after filling up after-hardening, need after filling up to put for a long time
Putting and could be dried, rate of drying is slow.
Summary of the invention:
The technical problem to be solved is to provide a kind of viscosity high, and rate of drying is fast, and after molding, hardness is high, no
Hold caducous plywood putty high from dryness and preparation method thereof.
Solve the technical problem that used following technical scheme:
A kind of plywood putty high from dryness, it is characterised in that: it is made up of following components raw material by weight,
A kind of preparation method of the plywood putty high from dryness, it is characterised in that: comprise the following steps, by solid material
All pulverizing processes, and is then sufficiently mixed by all of raw material and carries out emulsifying, and emulsifying temperature during emulsifying 80 DEG C, emulsifying is stirred
Mix speed 2500r/min, emulsification times 20min.
Described defoamer includes by weight, wood triethanolamine 2～6 parts, triisopropanolamine 1～3 parts, ethylene glycol 3～7
Part.
Described thickening agent is wollastonite, apatite and corn starch, and both ratios are 111.
After powder of lacquer putty for use in the present invention is floating, there is higher slickness, can preferably repair the defect of plywood, viscous
Property foot, intensity is high, and rate of drying is fast, it is not easy to drop.The defoamer of the present invention not only has efficient froth breaking effect, improves all
Evenness, and play putty rapid draing and strengthen the dried intensity of putty and the purpose of hardness, the thickening agent in the present invention simultaneously
Putty bonding and intensity itself can also be strengthened, be i.e. encounter hard object also will not be broken rotten.The making side of the present invention
Method makes by pulverizing, emulsifying and under specific temperature, time, and powder of lacquer putty for use on fineness, the uniformity are high, is conducive to improving product
Performance.
The invention has the beneficial effects as follows: viscosity of the present invention is high, fine and smooth, the uniformity is high, and rate of drying is fast, hardness after molding
High, it is not easy to come off.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below knot
Close instantiation, the present invention is expanded on further.
A kind of plywood putty high from dryness, is made up of following components raw material by weight,
The preparation method of a kind of plywood putty high from dryness, comprises the following steps, at whole for solid material pulverizing
Reason, is then sufficiently mixed all of raw material and carries out emulsifying, emulsifying temperature during emulsifying 80 DEG C, emulsification stirring speed
2500r/min, emulsification times 20min.
Defoamer includes by weight, wood triethanolamine 2～6 parts, triisopropanolamine 1～3 parts, ethylene glycol 3～7 parts.
Thickening agent is wollastonite, apatite and corn starch, and both ratios are 111.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry
Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become
Change and improvement both falls within scope of the claimed invention.Claimed scope by appending claims and
Equivalent defines.
Claims (4)
1. one kind from the high plywood putty of dryness, it is characterised in that: it is made up of following components raw material by weight,
The preparation method of a kind of plywood putty high from dryness the most according to claim 1, it is characterised in that: include with
Whole for solid material pulverizing are processed, are then sufficiently mixed by all of raw material and carry out emulsifying by lower step, breast during emulsifying
Change temperature 80 DEG C, emulsification stirring speed 2500r/min, emulsification times 20min.
A kind of plywood putty high from dryness the most according to claim 1, it is characterised in that: described defoamer is by weight
Amount part includes, wood triethanolamine 2～6 parts, triisopropanolamine 1～3 parts, ethylene glycol 3～7 parts.
A kind of plywood putty high from dryness the most according to claim 1, it is characterised in that: described thickening agent is silicon
Lime stone, apatite and corn starch, both ratios are 111.