CN106432954A - Flame-retardant oil-resistant anti-ageing thermoplastic elastomer cable material - Google Patents
Flame-retardant oil-resistant anti-ageing thermoplastic elastomer cable material Download PDFInfo
- Publication number
- CN106432954A CN106432954A CN201610847860.8A CN201610847860A CN106432954A CN 106432954 A CN106432954 A CN 106432954A CN 201610847860 A CN201610847860 A CN 201610847860A CN 106432954 A CN106432954 A CN 106432954A
- Authority
- CN
- China
- Prior art keywords
- parts
- flame
- powder
- cable material
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a flame-retardant oil-resistant anti-ageing thermoplastic elastomer cable material. The cable material is prepared from, by weight, 100 parts of polyvinyl chloride SG-3, 10-20 parts of butadiene-acrylonitrile rubber N26, 10-15 parts of polycarbonate, 10-15 parts of polyethylene glycol terephthalate-1,4-cyclohexanedimethanol terephthalate, 15-20 parts of silane coupling agent, 30-40 parts of bisphenol A diphosphate, 20-30 parts of calcium carbonate, 1-2 parts of calcium silicate, 30-50 parts of barium stearate, 10-15 parts of cresyl diphenyl phosphate, 3-4 parts of glycerol trioleate, 2-3 parts of cross-linking agent TAIC, 2-3 parts of stearic acid, 1-2 parts of N,N-m-phenylenedimaleimide, 5-8 parts of texanol, 0.5-1.0 part of PE wax, 1-2 parts of aluminum nitride, 1-2 parts of jade powder and 8-10 parts of modified filler. The flame-retardant oil-resistant anti-ageing thermoplastic elastomer cable material has the advantages of being retardant to flame, resistant to oil and ageing, resistant to acid and alkali, low in specific gravity and low in manufacturing cost.
Description
Technical field
The present invention relates to CABLE MATERIALS field and in particular to a kind of Flame-retardant oil-resistant aging-resistant thermoplastic elastomer cable material and its
Preparation method.
Background technology
With the fast development of global economy, and the enhancing of mankind's environmental consciousness, each field to the quality of electric wire and
How the requirement more and more higher of performance, because electric wire, cable aging and fire that cause also get more and more, reduce the generation of fire
Rate and occur fire when the death rate, low cigarette, Halogen, the developing direction that fire-retardant, environmental protection also becomes wires and cables industry.Wherein
The demand of halide-free low-smoke fireproof cable material is increasing, and the production of current halide-free low-smoke fireproof cable material is in polyolefin mostly
Substantial amounts of magnesium hydroxide or magnesium hydroxide is added to reach flame retardant effect in base material, however, the addition of a large amount of inorganic material, impact
The physical and mechanical properties of CABLE MATERIALS and process industrial art performance, softness, against weather be poor at normal temperatures for it, oil resistivity, resistance to
Cryogenic property is not fine.
Content of the invention
A kind of the invention aims to solve above-mentioned technical problem, the invention provides the ageing-resistant thermoplastic of Flame-Retardant and Oil-Resistant
Property elastomer cable material.
In order to realize above-mentioned technical purpose, reach above-mentioned technical requirements, the technical solution used in the present invention is:A kind of resistance
Combustion the ageing-resistant thermoplastic elastomer cable material of oil resistant it is characterised in that:It is prepared by the raw materials in:Polyvinyl chloride SG-
3100th, NBR N2610-20, Merlon 10-15, polyethylene terephthalate -1,4 cyclohexane dimethanol ester 10-
15th, silane coupler 15-20, tetraphenyl-(bisphenol-A) bisphosphate 30-40, calcium carbonate 20-30, calcium silicates 1-2, stearic acid
Barium 30-50, phosphate toluene diphenyl ester 10-15, glycerine glycerinate 3-4, crosslinking agent TAIC2-3, stearic acid, 2-3, N, N
A '-penylene BMI 1-2, alcohol ester 12 5-8, PE wax 0.5-1.0, aluminum nitride powder 1-2, jade powder 1-2, modification are filled out
Material 8-10.
Described Flame-retardant oil-resistant aging-resistant thermoplastic elastomer cable material is it is characterised in that component by following weight portion
Raw material is prepared:Polyvinyl chloride SG-3100, NBR N2615, Merlon 12, polyethylene terephthalate -1,4-
Cyclohexanedimethanoester ester 2, silane coupler 18, tetraphenyl-(bisphenol-A) bisphosphate 35, calcium carbonate 25, calcium silicates 2, tristearin
Sour barium 35, phosphate toluene diphenyl ester 12, glycerine glycerinate 3, crosslinking agent TAIC2, stearic acid, 2, N, a N '-penylene is double
Maleimide 1, alcohol ester 12, PE wax 0.8, aluminum nitride powder 1, jade powder 2, modified filler 9.
Described Flame-retardant oil-resistant aging-resistant thermoplastic elastomer cable material is it is characterised in that described modified filler is logical
Cross following method to be prepared:Attapulgite is calcined 3-4 hour at 540-580 DEG C, after taking-up, adds the hydroxide of 3-4%
Grind 1-2 hour in sodium solution, then, add the hydrochloric acid solution of 12-15%, regulation pH value is 4-5, is aged 10-15 hour, then
It is neutrality that hydro-oxidation sodium solution adjusts lapping liquid pH, filters, and dries and obtains filler powder, then adds phase in gained powder
When in the tea tree ethereal oil of powder weight 1-2%, the zinc oxide of 1-2%, the pentaerythrite of 1-2%, 2-3% nanometer jade powder, jointly grind
After mill 1-2 hour, add and be equivalent to the aminopropyl triethoxysilane of powder weight 2-3%, 4-5% Macrogol 6000,2-
3% morpholine, is uniformly dispersed with 11000-12000 rev/min of high speed, obtains final product.
Weigh each component raw material by formula rate, the component raw material weighing stirs in high-speed mixer, then
Through banbury banburying, twin-screw extrusion under 115-145 DEG C of temperature range, flour milling earnestly granulates, cyclopneumatic separator feeding, vibration
Sieve screening and then packaging, that is, be obtained CABLE MATERIALS finished product.
This Flame-retardant oil-resistant aging-resistant thermoplastic elastomer cable material has the characteristics that fire-retardant, oil resistant, ageing-resistant, acid and alkali-resistance, and compares
Weight is relatively low, cheap.
Specific embodiment
Flame-retardant oil-resistant aging-resistant thermoplastic elastomer cable material, by following weight(kg)Raw material make:
Polyvinyl chloride SG-3100, NBR N2615, Merlon 12, polyethylene terephthalate -1,4- hexamethylene two
Methyl alcohol ester 2, silane coupler 18, tetraphenyl-(bisphenol-A) bisphosphate 35, calcium carbonate 25, calcium silicates 2, barium stearate 35, phosphorus
Sour toluene diphenyl ester 12, glycerine glycerinate 3, crosslinking agent TAIC2, stearic acid, 2, N, a N '-penylene BMI
1st, alcohol ester 12, PE wax 0.8, aluminum nitride powder 1, jade powder 2, modified filler 9,
Wherein, modified filler is to be prepared by following method:
Attapulgite is calcined 3-4 hour at 540-580 DEG C, after taking-up, adds and in the sodium hydroxide solution of 3-4%, grind 1-2
Hour, then, add the hydrochloric acid solution of 12-15%, regulation pH value is 4-5, is aged 10-15 hour, and repeated hydrogenation sodium hydroxide solution is adjusted
Section lapping liquid pH is neutrality, filters, and dries and obtains filler powder, then adds in gained powder and is equivalent to powder weight 1-2%
Tea tree ethereal oil, the zinc oxide of 1-2%, the pentaerythrite of 1-2%, 2-3% nanometer jade powder, after co-ground 1-2 hour, then plus
Enter to be equivalent to the aminopropyl triethoxysilane of powder weight 2-3%, 4-5% Macrogol 6000, the morpholine of 2-3%, with 11000-
12000 revs/min of high speed is uniformly dispersed, and obtains final product.
The preparation method of finished cable material:
Weigh each component raw material by formula rate, the component raw material weighing stirs in high-speed mixer, then in 115-
Through banbury banburying, twin-screw extrusion under 145 DEG C of temperature range, flour milling earnestly granulates, cyclopneumatic separator feeding, Vibration Screen
Divide and then pack, that is, CABLE MATERIALS finished product is obtained.Above-described embodiment is only used for that the present invention will be described, and not constituting will to right
Ask the restriction of scope, it may occur to persons skilled in the art that other alternative means, all within the scope of the invention as claimed.
Claims (3)
1. a kind of Flame-retardant oil-resistant aging-resistant thermoplastic elastomer cable material it is characterised in that:It is prepared by the raw materials in:
Polyvinyl chloride SG-3 100, NBR N26 10-20, Merlon 10-15, polyethylene terephthalate -1,4- hexamethylene
Alkane diformazan alcohol ester 10-15, silane coupler 15-20, tetraphenyl-(bisphenol-A) bisphosphate 30-40, calcium carbonate 20-30,
Calcium silicates 1-2, barium stearate 30-50, phosphate toluene diphenyl ester 10-15, glycerine glycerinate 3-4, crosslinking agent TAIC2-
3rd, stearic acid 2-3, N, a N '-penylene BMI 1-2, alcohol ester 12 5-8, PE wax 0.5-1.0, aluminum nitride powder 1-2, jade
Stone flour 1-2, modified filler 8-10.
2. Flame-retardant oil-resistant aging-resistant thermoplastic elastomer cable material according to claim 1 is it is characterised in that by following heavy
The component raw material of amount part is prepared:Polyvinyl chloride SG-3 100, NBR N26 15, Merlon 12, poly terephthalic acid
Glycol ester -1,4 cyclohexane dimethanol ester 2, silane coupler 18, tetraphenyl-(bisphenol-A) bisphosphate 35, carbonic acid
Calcium 25, calcium silicates 2, barium stearate 35, phosphate toluene diphenyl ester 12, glycerine glycerinate 3, crosslinking agent TAIC 2, tristearin
Acid, 2, N, a N '-penylene BMI 1, alcohol ester 12, PE wax 0.8, aluminum nitride powder 1, jade powder 2, modified filler 9.
3. Flame-retardant oil-resistant aging-resistant thermoplastic elastomer cable material according to claim 1 and 2 is it is characterised in that described
Modified filler be to be prepared by following method:Attapulgite is calcined 3-4 hour at 540-580 DEG C, after taking-up, plus
Enter grinding 1-2 hour in the sodium hydroxide solution of 3-4%, then, add the hydrochloric acid solution of 12-15%, regulation pH value is 4-5, old
Change 10-15 hour, it is neutrality that repeated hydrogenation sodium hydroxide solution adjusts lapping liquid pH, filters, and dries and obtains filler powder, then to institute
Add in powder and be equivalent to the tea tree ethereal oil of powder weight 1-2%, the zinc oxide of 1-2%, the pentaerythrite of 1-2%, 2-3% nanometer
Jade powder, after co-ground 1-2 hour, add be equivalent to the aminopropyl triethoxysilane of powder weight 2-3%, 4-5% gathers
Ethylene glycol 6000, the morpholine of 2-3%, are uniformly dispersed with 11000-12000 rev/min of high speed, obtain final product.