CN107974019A - A kind of additive for lifting acryl plates service life - Google Patents
A kind of additive for lifting acryl plates service life Download PDFInfo
- Publication number
- CN107974019A CN107974019A CN201711324360.7A CN201711324360A CN107974019A CN 107974019 A CN107974019 A CN 107974019A CN 201711324360 A CN201711324360 A CN 201711324360A CN 107974019 A CN107974019 A CN 107974019A
- Authority
- CN
- China
- Prior art keywords
- parts
- particle
- additive
- service life
- attapulgite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of additive for lifting acryl plates service life, by following material composition：Functional stuffing, silane coupling agent, neopelex, fatty alcohol polyoxyethylene ether, age resister, ultra-violet absorber, glycerine, water.A kind of special additive of the present invention, can effectively lift the characteristics such as the wear-resisting of acryl plates, corrosion resistant, intensity, antibacterial, hence it is evident that extend its service life, great popularizing value.
Description
Technical field
The invention belongs to acrylic working process technical field, and in particular to a kind of lifting acryl plates service life
Additive.
Background technology
Acrylic, chemical name are polymethyl methacrylate, its transparency is as glass.Acrylic has preferable
Chemical stability, easy dyeing, easy processing and grace appearance and extensively liked by people.Though existing acrylic has above-mentioned excellent
Point, but it does not have special functional quality, and it is easy to aging, the service life needs to be further improved, and have impact on it and preferably pushes away
Wide application.
The content of the invention
The purpose of the present invention is for it is existing the problem of, there is provided it is a kind of lifted acryl plates service life addition
Agent.
The present invention is achieved by the following technical solutions：
A kind of additive for lifting acryl plates service life, by the material composition of following parts by weight：
10 ~ 15 parts of functional stuffings, 7 ~ 10 parts of silane coupling agents, 3 ~ 5 parts of neopelexes, 4 ~ 6 parts of fatty alcohol polyoxy second
Alkene ether, 2 ~ 3 parts of age resisters, 0.5 ~ 1 part of ultra-violet absorber, 30 ~ 40 parts of glycerine, 180 ~ 200 parts of water.
Preferably, by the material composition of following parts by weight：
13 ~ 15 parts of functional stuffings, 9 ~ 10 parts of silane coupling agents, 4 ~ 5 parts of neopelexes, 5 ~ 6 parts of fatty alcohol polyoxy second
Alkene ether, 2.5 ~ 3 parts of age resisters, 0.8 ~ 1 part of ultra-violet absorber, 35 ~ 40 parts of glycerine, 190 ~ 200 parts of water.
Preferably, by the material composition of following parts by weight：
13 parts of functional stuffings, 9 parts of silane coupling agents, 4 parts of neopelexes, 5 parts of fatty alcohol polyoxyethylene ether, 2.5 parts
Age resister, 0.8 part of ultra-violet absorber, 35 parts of glycerine, 190 parts of water.
Further, the preparation method of the functional stuffing includes the following steps：
（1）Attapulgite is first put into 7 ~ 9min of immersion treatment in the hydrochloric acid solution that mass fraction is 8 ~ 10%, then takes out and puts
Enter 5 ~ 7min of immersion treatment into the sodium hydroxide solution that mass fraction is 10 ~ 12%, finally take out and use deionized water rinsing one time
It is spare afterwards；
（2）By step（1）Attapulgite after processing, which is put into calcining furnace, carries out calcination processing, is taken out after 50 ~ 60min standby
With；
（3）By step（2）Attapulgite after processing is put into immersion treatment in modification liquid A, during which persistently carries out at ultrasonic wave
Manage, filter out attapulgite after 30 ~ 40min rear spare；The modification liquid A by following parts by weight material composition：25 ~ 30 parts are received
Rice carbon pipe, 6 ~ 8 parts of magnesium stearates, 4 ~ 7 parts of calgons, 8 ~ 10 parts of polyethylene glycol, 340 ~ 360 parts of water；
（4）By step（3）Attapulgite after processing is put into immersion treatment in modification liquid B, after high-speed stirred handles 1 ~ 1.5h
Attapulgite is filtered out spare；The modification liquid B by following parts by weight material composition：3 ~ 4 parts of Chinese medical extracts, 10 ~ 13 parts
Water；
（5）By step（4）Attapulgite after processing, which is put into drying box, is dried processing, after the completion of take out be put into powder
Pulverization process is carried out in broken machine, and it is divided into three grades according to granular size, respectively particle A, particle B and particle C, institute
The particle diameter for stating particle A is 300 ~ 400nm, and the particle diameter of particle B is 1 ~ 15 μm, and the particle diameter of particle C is 60 ~ 80 μ
M, the particle A, particle B and particle C correspond to the weight ratio mixed：5~6:2~3:3~4.
Further, step（2）Described in calcination processing when to control temperature in calcining furnace be 750 ~ 800 DEG C.
Further, step（3）Described in the frequency of ultrasonication be 100 ~ 105kHz.
Further, step（4）Described in the preparation method of Chinese medical extract be：By chinaberry, rhizoma menispermi, Radix Paeoniae Alba,
The coptis, illiciumverum are corresponding according to weight ratio 5:4:6:9:3 carry out co-grindings, are then mixed jointly with the clear water of 8 times of its gross mass
It is put into pot, heating boiling is filtered after boiling processing 1.5h, finally concentrates the filtrate to the 1/12 of original volume again.
Further, step（5）Described in drying process when to control temperature in drying box be 80 ~ 85 DEG C.
The present invention is prepared for a kind of additive, effectively improves the use quality of acryl plates, wherein that adds is anti-ageing
Agent enhances overall anti-aging property, and the ultra-violet absorber of addition enhances its anti-uv-ray, and with the addition of one
The special functional stuffing of kind, it is to be modified to form as matrix using attapulgite, has first carried out soda acid immersion treatment to it, has had
Effect eliminates its impurity component, has dredged channel design, has then carried out calcination processing, has further improved the ratio of attapulgite
Surface area and characterization of adsorption, have then carried out modification to attapulgite with modification liquid A again, have been grafted carbon nanotubes after processing
It is inserted in attapulgite, the adsorption capacity of attapulgite is further increased using the middle outage characterization of adsorption of carbon nanotubes,
Immersion treatment then is carried out to attapulgite with the modification liquid B with antibacterial characteristics, enhances the anti-microbial property of attapulgite, most
Crushing and classification processing has been carried out to its granular size afterwards, has improved the effect of filling well, the particle after classification processing disperses
Property is good, is not easy to reunite, enhances the mechanical qualities such as overall intensity, has more preferable filling effect.
The present invention has the following advantages compared with prior art：
A kind of special additive of the present invention, can effectively lift the characteristics such as the wear-resisting of acryl plates, corrosion resistant, intensity, antibacterial,
It has been obviously prolonged its service life, great popularizing value.
Embodiment
Embodiment 1
A kind of additive for lifting acryl plates service life, by the material composition of following parts by weight：
10 parts of functional stuffings, 7 parts of silane coupling agents, 3 parts of neopelexes, 4 parts of fatty alcohol polyoxyethylene ether, 2 parts it is anti-
Aging agent, 0.5 part of ultra-violet absorber, 30 parts of glycerine, 180 parts of water.
Further, the preparation method of the functional stuffing includes the following steps：
（1）Attapulgite is first put into immersion treatment 7min in the hydrochloric acid solution that mass fraction is 8%, then takes out and is put into
Immersion treatment 5min in the sodium hydroxide solution that mass fraction is 10%, finally takes out with spare after deionized water rinsing one time；
（2）By step（1）Attapulgite after processing, which is put into calcining furnace, carries out calcination processing, is taken out after 50min spare；
（3）By step（2）Attapulgite after processing is put into immersion treatment in modification liquid A, during which persistently carries out at ultrasonic wave
Manage, filter out attapulgite after 30min rear spare；The modification liquid A by following parts by weight material composition：25 parts of nano-sized carbons
Pipe, 6 parts of magnesium stearates, 4 parts of calgons, 8 parts of polyethylene glycol, 340 parts of water；
（4）By step（3）Attapulgite after processing is put into immersion treatment in modification liquid B, will be recessed after high-speed stirred processing 1h
Convex rod soil filters out spare；The modification liquid B by following parts by weight material composition：3 parts of Chinese medical extracts, 10 parts of water；
（5）By step（4）Attapulgite after processing, which is put into drying box, is dried processing, after the completion of take out be put into powder
Pulverization process is carried out in broken machine, and it is divided into three grades according to granular size, respectively particle A, particle B and particle C, institute
The particle diameter for stating particle A is 300 ~ 400nm, and the particle diameter of particle B is 1 ~ 15 μm, and the particle diameter of particle C is 60 ~ 80 μ
M, the particle A, particle B and particle C correspond to the weight ratio mixed：5:2:3.
Further, step（2）Described in calcination processing when to control temperature in calcining furnace be 750 DEG C.
Further, step（3）Described in the frequency of ultrasonication be 100kHz.
Further, step（4）Described in the preparation method of Chinese medical extract be：By chinaberry, rhizoma menispermi, Radix Paeoniae Alba,
The coptis, illiciumverum are corresponding according to weight ratio 5:4:6:9:3 carry out co-grindings, are then mixed jointly with the clear water of 8 times of its gross mass
It is put into pot, heating boiling is filtered after boiling processing 1.5h, finally concentrates the filtrate to the 1/12 of original volume again.
Further, step（5）Described in drying process when to control temperature in drying box be 80 DEG C.
Embodiment 2
A kind of additive for lifting acryl plates service life, by the material composition of following parts by weight：
13 parts of functional stuffings, 9 parts of silane coupling agents, 4 parts of neopelexes, 5 parts of fatty alcohol polyoxyethylene ether, 2.5 parts
Age resister, 0.8 part of ultra-violet absorber, 35 parts of glycerine, 190 parts of water.
Further, the preparation method of the functional stuffing includes the following steps：
（1）Attapulgite is first put into immersion treatment 8min in the hydrochloric acid solution that mass fraction is 9%, then takes out and is put into
Immersion treatment 6min in the sodium hydroxide solution that mass fraction is 11%, finally takes out with spare after deionized water rinsing one time；
（2）By step（1）Attapulgite after processing, which is put into calcining furnace, carries out calcination processing, is taken out after 55min spare；
（3）By step（2）Attapulgite after processing is put into immersion treatment in modification liquid A, during which persistently carries out at ultrasonic wave
Manage, filter out attapulgite after 35min rear spare；The modification liquid A by following parts by weight material composition：28 parts of nano-sized carbons
Pipe, 7 parts of magnesium stearates, 6 parts of calgons, 9 parts of polyethylene glycol, 350 parts of water；
（4）By step（3）Attapulgite after processing is put into immersion treatment in modification liquid B, will after high-speed stirred processing 1.2h
Attapulgite filters out spare；The modification liquid B by following parts by weight material composition：3.5 parts of Chinese medical extracts, 12 parts of water；
（5）By step（4）Attapulgite after processing, which is put into drying box, is dried processing, after the completion of take out be put into powder
Pulverization process is carried out in broken machine, and it is divided into three grades according to granular size, respectively particle A, particle B and particle C, institute
The particle diameter for stating particle A is 300 ~ 400nm, and the particle diameter of particle B is 1 ~ 15 μm, and the particle diameter of particle C is 60 ~ 80 μ
M, the particle A, particle B and particle C correspond to the weight ratio mixed：5.5:2.5:3.6.
Further, step（2）Described in calcination processing when to control temperature in calcining furnace be 780 DEG C.
Further, step（3）Described in the frequency of ultrasonication be 103kHz.
Further, step（4）Described in the preparation method of Chinese medical extract be：By chinaberry, rhizoma menispermi, Radix Paeoniae Alba,
The coptis, illiciumverum are corresponding according to weight ratio 5:4:6:9:3 carry out co-grindings, are then mixed jointly with the clear water of 8 times of its gross mass
It is put into pot, heating boiling is filtered after boiling processing 1.5h, finally concentrates the filtrate to the 1/12 of original volume again.
Further, step（5）Described in drying process when to control temperature in drying box be 82 DEG C.
Embodiment 3
A kind of additive for lifting acryl plates service life, by the material composition of following parts by weight：
15 parts of functional stuffings, 10 parts of silane coupling agents, 5 parts of neopelexes, 6 parts of fatty alcohol polyoxyethylene ether, 3 parts it is anti-
Aging agent, 1 part of ultra-violet absorber, 40 parts of glycerine, 200 parts of water.
Further, the preparation method of the functional stuffing includes the following steps：
（1）Attapulgite is first put into immersion treatment 9min in the hydrochloric acid solution that mass fraction is 10%, then takes out and is put into
Immersion treatment 7min in the sodium hydroxide solution that mass fraction is 12%, finally takes out with spare after deionized water rinsing one time；
（2）By step（1）Attapulgite after processing, which is put into calcining furnace, carries out calcination processing, is taken out after 60min spare；
（3）By step（2）Attapulgite after processing is put into immersion treatment in modification liquid A, during which persistently carries out at ultrasonic wave
Manage, filter out attapulgite after 40min rear spare；The modification liquid A by following parts by weight material composition：30 parts of nano-sized carbons
Pipe, 8 parts of magnesium stearates, 7 parts of calgons, 10 parts of polyethylene glycol, 360 parts of water；
（4）By step（3）Attapulgite after processing is put into immersion treatment in modification liquid B, will after high-speed stirred processing 1.5h
Attapulgite filters out spare；The modification liquid B by following parts by weight material composition：4 parts of Chinese medical extracts, 13 parts of water；
（5）By step（4）Attapulgite after processing, which is put into drying box, is dried processing, after the completion of take out be put into powder
Pulverization process is carried out in broken machine, and it is divided into three grades according to granular size, respectively particle A, particle B and particle C, institute
The particle diameter for stating particle A is 300 ~ 400nm, and the particle diameter of particle B is 1 ~ 15 μm, and the particle diameter of particle C is 60 ~ 80 μ
M, the particle A, particle B and particle C correspond to the weight ratio mixed：6:3:4.
Further, step（2）Described in calcination processing when to control temperature in calcining furnace be 800 DEG C.
Further, step（3）Described in the frequency of ultrasonication be 105kHz.
Further, step（4）Described in the preparation method of Chinese medical extract be：By chinaberry, rhizoma menispermi, Radix Paeoniae Alba,
The coptis, illiciumverum are corresponding according to weight ratio 5:4:6:9:3 carry out co-grindings, are then mixed jointly with the clear water of 8 times of its gross mass
It is put into pot, heating boiling is filtered after boiling processing 1.5h, finally concentrates the filtrate to the 1/12 of original volume again.
Further, step（5）Described in drying process when to control temperature in drying box be 85 DEG C.
Additive of the present invention effectively improves the integrated quality of acryl plates, impart its well it is wear-resisting, antibacterial is special
Property, its impact strength, tensile strength are improved more than 30%, service life extends 25% or so, has and promotes well
Use value.
Claims (8)
1. a kind of additive for lifting acryl plates service life, it is characterised in that by the material composition of following parts by weight：
10 ~ 15 parts of functional stuffings, 7 ~ 10 parts of silane coupling agents, 3 ~ 5 parts of neopelexes, 4 ~ 6 parts of fatty alcohol polyoxy second
Alkene ether, 2 ~ 3 parts of age resisters, 0.5 ~ 1 part of ultra-violet absorber, 30 ~ 40 parts of glycerine, 180 ~ 200 parts of water.
2. a kind of additive for lifting acryl plates service life according to claim 1, it is characterised in that by as follows
The material composition of parts by weight：
13 ~ 15 parts of functional stuffings, 9 ~ 10 parts of silane coupling agents, 4 ~ 5 parts of neopelexes, 5 ~ 6 parts of fatty alcohol polyoxy second
Alkene ether, 2.5 ~ 3 parts of age resisters, 0.8 ~ 1 part of ultra-violet absorber, 35 ~ 40 parts of glycerine, 190 ~ 200 parts of water.
3. a kind of additive for lifting acryl plates service life according to claim 1, it is characterised in that by as follows
The material composition of parts by weight：
13 parts of functional stuffings, 9 parts of silane coupling agents, 4 parts of neopelexes, 5 parts of fatty alcohol polyoxyethylene ether, 2.5 parts
Age resister, 0.8 part of ultra-violet absorber, 35 parts of glycerine, 190 parts of water.
4. a kind of additive of lifting acryl plates service life according to claim 1 ~ 3 any one, its feature
It is, the preparation method of the functional stuffing includes the following steps：
（1）Attapulgite is first put into 7 ~ 9min of immersion treatment in the hydrochloric acid solution that mass fraction is 8 ~ 10%, then takes out and puts
Enter 5 ~ 7min of immersion treatment into the sodium hydroxide solution that mass fraction is 10 ~ 12%, finally take out and use deionized water rinsing one time
It is spare afterwards；
（2）By step（1）Attapulgite after processing, which is put into calcining furnace, carries out calcination processing, is taken out after 50 ~ 60min standby
With；
（3）By step（2）Attapulgite after processing is put into immersion treatment in modification liquid A, during which persistently carries out at ultrasonic wave
Manage, filter out attapulgite after 30 ~ 40min rear spare；The modification liquid A by following parts by weight material composition：25 ~ 30 parts are received
Rice carbon pipe, 6 ~ 8 parts of magnesium stearates, 4 ~ 7 parts of calgons, 8 ~ 10 parts of polyethylene glycol, 340 ~ 360 parts of water；
（4）By step（3）Attapulgite after processing is put into immersion treatment in modification liquid B, after high-speed stirred handles 1 ~ 1.5h
Attapulgite is filtered out spare；The modification liquid B by following parts by weight material composition：3 ~ 4 parts of Chinese medical extracts, 10 ~ 13 parts
Water；
（5）By step（4）Attapulgite after processing, which is put into drying box, is dried processing, after the completion of take out be put into powder
Pulverization process is carried out in broken machine, and it is divided into three grades according to granular size, respectively particle A, particle B and particle C, institute
The particle diameter for stating particle A is 300 ~ 400nm, and the particle diameter of particle B is 1 ~ 15 μm, and the particle diameter of particle C is 60 ~ 80 μ
M, the particle A, particle B and particle C correspond to the weight ratio mixed：5~6:2~3:3~4.
A kind of 5. additive for lifting acryl plates service life according to claim 4, it is characterised in that step
（2）Described in calcination processing when to control temperature in calcining furnace be 750 ~ 800 DEG C.
A kind of 6. additive for lifting acryl plates service life according to claim 4, it is characterised in that step
（3）Described in the frequency of ultrasonication be 100 ~ 105kHz.
A kind of 7. additive for lifting acryl plates service life according to claim 4, it is characterised in that step
（4）Described in the preparation method of Chinese medical extract be：Chinaberry, rhizoma menispermi, Radix Paeoniae Alba, the coptis, illiciumverum is corresponding according to weight
Than 5:4:6:9:3 carry out co-grindings, are then put into common mix of the clear water of 8 times of its gross mass in pot, heat boiling and boil place
Filtered after reason 1.5h, finally concentrate the filtrate to the 1/12 of original volume again.
A kind of 8. additive for lifting acryl plates service life according to claim 4, it is characterised in that step
（5）Described in drying process when to control temperature in drying box be 80 ~ 85 DEG C.