CN107263645A - It is a kind of to lift the reinforcement process that wicker products uses characteristic - Google Patents
It is a kind of to lift the reinforcement process that wicker products uses characteristic Download PDFInfo
- Publication number
- CN107263645A CN107263645A CN201710342970.3A CN201710342970A CN107263645A CN 107263645 A CN107263645 A CN 107263645A CN 201710342970 A CN201710342970 A CN 201710342970A CN 107263645 A CN107263645 A CN 107263645A
- Authority
- CN
- China
- Prior art keywords
- wicker products
- pressure
- processing
- treatment tank
- modification liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The reinforcement process that wicker products uses characteristic is lifted the invention discloses a kind of, is comprised the following steps：（1）Vacuum exhaust processing,（2）Modification liquid processing,（3）Vacuum discharge opeing processing,（4）Isothermal holding,（5）Cooling treatment.The reasonable mating reaction that the present invention passes through each step, effectively realize the reinforcing improvement processing to purple willow product, the mechanical characteristics such as hardness, the modulus of elasticity of purple willow product after final process are significantly improved, and service life has obtained fine lifting, the great market competitiveness.
Description
Technical field
The invention belongs to wicker plaiting article processing technique field, and in particular to a kind of lifting wicker products uses the reinforcing work of characteristic
Skill.
Background technology
Funan County, is under the jurisdiction of Anhui Province's Fuyang City, area earlier is developed in category inland, on the Anhui Province northwestward, Huaihe River
Middle reaches joint portion north bank.Funan County have " famous-brand and high-quality special product county ", the title of " Natural resources reservoir ", be national grain-production great Xian, in
The unique agricultural in township, the whole nation of state's wicker plaiting article（Forestry）Recycling economy demonstration pilot project county, Funan is the township of national wicker plaiting article, wicker products
It is sold abroad.
Purple willow is one of conventional raw material in wicker plaiting article processing and manufacturing, when being processed to purple willow, its common technique stream
Cheng Shi：Peeling, cleaning, softening, braiding, drying, dyeing, storage are preserved.Wherein softening process is essential during purple willow weaves
A step, it is intended to improve the pliability of purple willow branch, be easy to shaping, but asking for the impaired performances such as branch hardness can be brought simultaneously
Topic, although in the natural drying efflorescence after, hardness etc. has certain recovery, but effect is weaker, and this problem can be made
Easily occur deformation, problems of crack in use into wicker plaiting article finished product, have impact on its use value, therefore need badly to this problem
It is improved.
The content of the invention
The purpose of the present invention is that there is provided a kind of reinforcing work for lifting wicker products using characteristic the problem of being directed to existing
Skill.
The present invention is achieved by the following technical solutions：
It is a kind of to lift the reinforcement process that wicker products uses characteristic, comprise the following steps：
（1）Vacuum exhaust is handled：
Wicker products after the completion of braiding is put into pressure treatment tank, vacuumize process, place are then carried out to pressure treatment tank
Manage standby after 40 ~ 45min；
（2）Modification liquid processing：
After being disposed to wicker products progress vacuum exhaust, the vavuum pump in pressure treatment tank is still kept to open, then to pressure
Injection modification liquid in power process tank, be totally submerged wicker products when modification liquid, full of pressurized tank after, close vavuum pump, and to pressure
Pressurized treatment is carried out in power process tank, pressure is increased into 1.5 ~ 2MPa, pressurize handles 25 ~ 30min；Described modification liquid is by as follows
The material composition of parts by weight：90 ~ 100 parts of Ludox, 5 ~ 8 parts of titanate coupling agents, 2 ~ 5 parts of hydroxy silicon oils, 1 ~ 3 part of traditional Chinese medicine extraction
Liquid；Described Chinese medicine extract is made up of the material of following parts by weight：6 ~ 10 parts of dried peppermint leaves, 3 ~ 6 parts of myrobalans, 1 ~ 3 part of reed rhizome, 2 ~
5 portions of fruit ofs Chinese magnoliavine, 4 ~ 7 portions of folium artemisiae argyis；
（3）Vacuum discharge opeing is handled：
Step（2）After the completion of processing, the pressure in pressure treatment tank is down to normal pressure, then again will be unnecessary in pressure treatment tank
Modification liquid, which is drawn, to be reclaimed, and then pressure treatment tank is carried out again after vacuumize process, 5 ~ 10min of processing, is excluded wicker products
It is standby after the modification liquid of excess surface；
（4）Isothermal holding：
Step（3）After the completion of processing, close vavuum pump and recover the pressure in pressure treatment tank to normal pressure, then by wicker products
Taking-up, which is put into thermostatic chamber, carries out isothermal holding, and it is to take out standby after 68 ~ 74 DEG C, 1 ~ 2h of isothermal holding to keep the temperature in thermostatic chamber
With；
（5）Cooling treatment：
By step（4）Wicker products after processing naturally cools to normal temperature after taking out.
Further, step（1）Described in vacuumize process when control vacuum be 0.09MPa.
Further, step（2）Described in Ludox in the mass fraction of silica be 19 ~ 20%, particle size is
5~15nm。
Further, step（2）Described in the preparation method of Chinese medicine extract be by dried peppermint leaf, myrobalan, reed rhizome, the five tastes
Son, folium artemisiae argyi are mixed jointly, in the clear water for being then added to 5 ~ 8 times of its gross mass, and heating boiling is boiled and filtered after 50 ~ 55min of processing, finally
Chinese medicine extract is produced behind concentrate the filtrate to original volume 1/10.
Further, step（3）Described in vacuumize process when control vacuum be 0.07MPa.
Further, step（4）Described in isothermal holding when control relative humidity in thermostatic chamber to be 30 ~ 40%.
Handling process rarely effectively for recoveries such as wicker products intensity, is by the wicker plaiting article system after braiding mostly at present
Product are put into self-recovery under natural conditions, and its effect is not satisfactory.Present invention selection carries out strong after the completion of wicker softening braiding
Change is handled, and to improve the performance of wicker plaiting article finished product, the wherein semi-finished product of wicker plaiting article first carry out vacuum exhaust processing, eliminate wicker
Composition of air in tissue, is easy to the immersion of successive modified liquid to handle, then by modification liquid pressure injection to Qi by way of supercharging
The inside of withy bar, it is ensured that modification liquid contains Ludox, titanium to the uniformity of purple willow branch tissue treatment everywhere in modification liquid
The nanometer silicon dioxide particle of acid esters coupling agent, hydroxy silicon oil and Chinese medicine extract, wherein Ludox can penetrate into lumen and
In cell membrane, its tissue characteristics is improved, and then improves the performances such as its intensity, in order to further lift filling effect, is added again
Titanate coupling agent and hydroxy silicon oil are added, titanate coupling agent used can improve the spy on nanometer silicon dioxide particle surface
Property, can promote its with cellulose etc. composition occur chemical bond and, strengthen its bonding strength, and then enhance filling effect, and
When wicker softens, the hydrogen bond considerable damage between cellulose and hemicellulose chain equimolecular, pliability gets a promotion, and intensive treatment
Then need to this progress reverse process, the hydroxy silicon oil of addition can be lifted between intermolecular hydrogen bond formation, connection, enhancing tissue
Crosslinking degree, the Chinese medicine extract of addition has good mildew and insect proof characteristic, extends the service life of product, carries out afterwards
The stable effect for enhancing above-mentioned modification of isothermal holding, be indispensable step process.
The present invention has advantages below compared with prior art：
The present invention effectively realizes the reinforcing improvement processing to purple willow product, final place by the reasonable mating reaction of each step
The mechanical characteristics such as hardness, the modulus of elasticity of purple willow product after reason are significantly improved, and service life has obtained fine lifting,
The great market competitiveness.
Embodiment
Embodiment 1
It is a kind of to lift the reinforcement process that wicker products uses characteristic, comprise the following steps：
（1）Vacuum exhaust is handled：
Wicker products after the completion of braiding is put into pressure treatment tank, vacuumize process, place are then carried out to pressure treatment tank
Manage standby after 40min；
（2）Modification liquid processing：
After being disposed to wicker products progress vacuum exhaust, the vavuum pump in pressure treatment tank is still kept to open, then to pressure
Injection modification liquid in power process tank, be totally submerged wicker products when modification liquid, full of pressurized tank after, close vavuum pump, and to pressure
Pressurized treatment is carried out in power process tank, pressure is increased into 1.5MPa, pressurize processing 25min；Described modification liquid is by following weight
The material composition of part：90 parts of Ludox, 5 parts of titanate coupling agents, 2 parts of hydroxy silicon oils, 1 part of Chinese medicine extract；Described Chinese medicine
Extract solution is made up of the material of following parts by weight：6 portions of dried peppermint leaves, 3 portions of myrobalans, 1 portion of reed rhizome, 2 portions of fruit ofs Chinese magnoliavine, 4 portions of folium artemisiae argyis；
（3）Vacuum discharge opeing is handled：
Step（2）After the completion of processing, the pressure in pressure treatment tank is down to normal pressure, then again will be unnecessary in pressure treatment tank
Modification liquid, which is drawn, to be reclaimed, and then pressure treatment tank is carried out again after vacuumize process, processing 5min, is excluded wicker products surface
It is standby after unnecessary modification liquid；
（4）Isothermal holding：
Step（3）After the completion of processing, close vavuum pump and recover the pressure in pressure treatment tank to normal pressure, then by wicker products
Taking-up, which is put into thermostatic chamber, carries out isothermal holding, and it is to take out standby after 68 DEG C, isothermal holding 1h to keep the temperature in thermostatic chamber；
（5）Cooling treatment：
By step（4）Wicker products after processing naturally cools to normal temperature after taking out.
Further, step（1）Described in vacuumize process when control vacuum be 0.09MPa.
Further, step（2）Described in Ludox in silica mass fraction be 19%, particle size be 5 ~
15nm。
Further, step（2）Described in the preparation method of Chinese medicine extract be by dried peppermint leaf, myrobalan, reed rhizome, the five tastes
Son, folium artemisiae argyi are mixed jointly, in the clear water for being then added to 5 times of its gross mass, and heating boiling is filtered after boiling processing 50min, finally will filter
Liquid produces Chinese medicine extract after being concentrated into the 1/10 of original volume.
Further, step（3）Described in vacuumize process when control vacuum be 0.07MPa.
Further, step（4）Described in isothermal holding when control relative humidity in thermostatic chamber to be 30 ~ 40%.
Embodiment 2
It is a kind of to lift the reinforcement process that wicker products uses characteristic, comprise the following steps：
（1）Vacuum exhaust is handled：
Wicker products after the completion of braiding is put into pressure treatment tank, vacuumize process, place are then carried out to pressure treatment tank
Manage standby after 43min；
（2）Modification liquid processing：
After being disposed to wicker products progress vacuum exhaust, the vavuum pump in pressure treatment tank is still kept to open, then to pressure
Injection modification liquid in power process tank, be totally submerged wicker products when modification liquid, full of pressurized tank after, close vavuum pump, and to pressure
Pressurized treatment is carried out in power process tank, pressure is increased into 1.8MPa, pressurize processing 28min；Described modification liquid is by following weight
The material composition of part：95 parts of Ludox, 7 parts of titanate coupling agents, 4 parts of hydroxy silicon oils, 2 parts of Chinese medicine extracts；Described Chinese medicine
Extract solution is made up of the material of following parts by weight：8 portions of dried peppermint leaves, 5 portions of myrobalans, 2 portions of reed rhizomes, 4 portions of fruit ofs Chinese magnoliavine, 5 portions of folium artemisiae argyis；
（3）Vacuum discharge opeing is handled：
Step（2）After the completion of processing, the pressure in pressure treatment tank is down to normal pressure, then again will be unnecessary in pressure treatment tank
Modification liquid, which is drawn, to be reclaimed, and then pressure treatment tank is carried out again after vacuumize process, processing 8min, is excluded wicker products surface
It is standby after unnecessary modification liquid；
（4）Isothermal holding：
Step（3）After the completion of processing, close vavuum pump and recover the pressure in pressure treatment tank to normal pressure, then by wicker products
Taking-up, which is put into thermostatic chamber, carries out isothermal holding, and it is to take out standby after 72 DEG C, isothermal holding 1.5h to keep the temperature in thermostatic chamber；
（5）Cooling treatment：
By step（4）Wicker products after processing naturally cools to normal temperature after taking out.
Further, step（1）Described in vacuumize process when control vacuum be 0.09MPa.
Further, step（2）Described in Ludox in silica mass fraction be 19.6%, particle size is 5
~15nm。
Further, step（2）Described in the preparation method of Chinese medicine extract be by dried peppermint leaf, myrobalan, reed rhizome, the five tastes
Son, folium artemisiae argyi are mixed jointly, in the clear water for being then added to 7 times of its gross mass, and heating boiling is filtered after boiling processing 52min, finally will filter
Liquid produces Chinese medicine extract after being concentrated into the 1/10 of original volume.
Further, step（3）Described in vacuumize process when control vacuum be 0.07MPa.
Further, step（4）Described in isothermal holding when control relative humidity in thermostatic chamber to be 30 ~ 40%.
Embodiment 3
It is a kind of to lift the reinforcement process that wicker products uses characteristic, comprise the following steps：
（1）Vacuum exhaust is handled：
Wicker products after the completion of braiding is put into pressure treatment tank, vacuumize process, place are then carried out to pressure treatment tank
Manage standby after 45min；
（2）Modification liquid processing：
After being disposed to wicker products progress vacuum exhaust, the vavuum pump in pressure treatment tank is still kept to open, then to pressure
Injection modification liquid in power process tank, be totally submerged wicker products when modification liquid, full of pressurized tank after, close vavuum pump, and to pressure
Pressurized treatment is carried out in power process tank, pressure is increased into 2MPa, pressurize processing 30min；Described modification liquid is by following parts by weight
Material composition：100 parts of Ludox, 8 parts of titanate coupling agents, 5 parts of hydroxy silicon oils, 3 parts of Chinese medicine extracts；Described Chinese medicine is carried
Liquid is taken to be made up of the material of following parts by weight：10 portions of dried peppermint leaves, 6 portions of myrobalans, 3 portions of reed rhizomes, 5 portions of fruit ofs Chinese magnoliavine, 7 portions of folium artemisiae argyis；
（3）Vacuum discharge opeing is handled：
Step（2）After the completion of processing, the pressure in pressure treatment tank is down to normal pressure, then again will be unnecessary in pressure treatment tank
Modification liquid, which is drawn, to be reclaimed, and then pressure treatment tank is carried out again after vacuumize process, processing 10min, is excluded wicker products table
It is standby after the unnecessary modification liquid in face；
（4）Isothermal holding：
Step（3）After the completion of processing, close vavuum pump and recover the pressure in pressure treatment tank to normal pressure, then by wicker products
Taking-up, which is put into thermostatic chamber, carries out isothermal holding, and it is to take out standby after 74 DEG C, isothermal holding 2h to keep the temperature in thermostatic chamber；
（5）Cooling treatment：
By step（4）Wicker products after processing naturally cools to normal temperature after taking out.
Further, step（1）Described in vacuumize process when control vacuum be 0.09MPa.
Further, step（2）Described in Ludox in silica mass fraction be 20%, particle size be 5 ~
15nm。
Further, step（2）Described in the preparation method of Chinese medicine extract be by dried peppermint leaf, myrobalan, reed rhizome, the five tastes
Son, folium artemisiae argyi are mixed jointly, in the clear water for being then added to 8 times of its gross mass, and heating boiling is filtered after boiling processing 55min, finally will filter
Liquid produces Chinese medicine extract after being concentrated into the 1/10 of original volume.
Further, step（3）Described in vacuumize process when control vacuum be 0.07MPa.
Further, step（4）Described in isothermal holding when control relative humidity in thermostatic chamber to be 30 ~ 40%.
Comparative example 1
This comparative example 1 compared with Example 2, in step（2）During modification liquid processing, the titanate esters coupling in modification liquid is saved
Agent and hydroxy silicon oil composition, method and step all same in addition.
Comparative example 2
This comparative example 2 compared with Example 2, saves step（4）Isothermal holding, method and step all same in addition.
Comparative example 3
This comparative example 3 compared with Example 2, in step（2）During modification liquid processing, the titanate esters coupling in modification liquid is saved
Agent and hydroxy silicon oil composition, while also saving step（4）Isothermal holding, method and step all same in addition.
In order to contrast effect of the present invention, from the purple willow branch with a collection of harvesting, after the processing of identical softening process,
Carried out respectively with the method described in above-described embodiment 2, comparative example 1, comparative example 2, comparative example 3 at reinforcing again
Reason, then carries out performance detection, for finer contrast treatment effect, from nanometer pressure to the purple willow branch after intensive treatment
Trace measuring technology is tested the characteristic in purple willow wood cell parietal layer face, and specific data are as shown in table 1 below：
Table 1
| Modulus of elasticity（GPa） | Hardness（GPa） | |
| Embodiment 2 | 19.16 | 0.56 |
| Comparative example 1 | 17.08 | 0.47 |
| Comparative example 2 | 18.45 | 0.52 |
| Comparative example 3 | 16.23 | 0.42 |
Note：Performance test described in upper table 1 is the test carried out to the wood cell wall at purple willow branch central tissue.
Processing method of the present invention can effectively lift the intensive treatment effect to purple willow branch it can be seen from upper table 1, change
Enter it and use characteristic, and can be by overall service life extension more than 25%.
Claims (6)
1. a kind of lift the reinforcement process that wicker products uses characteristic, it is characterised in that comprises the following steps：
（1）Vacuum exhaust is handled：
Wicker products after the completion of braiding is put into pressure treatment tank, vacuumize process, place are then carried out to pressure treatment tank
Manage standby after 40 ~ 45min；
（2）Modification liquid processing：
After being disposed to wicker products progress vacuum exhaust, the vavuum pump in pressure treatment tank is still kept to open, then to pressure
Injection modification liquid in power process tank, be totally submerged wicker products when modification liquid, full of pressurized tank after, close vavuum pump, and to pressure
Pressurized treatment is carried out in power process tank, pressure is increased into 1.5 ~ 2MPa, pressurize handles 25 ~ 30min；Described modification liquid is by as follows
The material composition of parts by weight：90 ~ 100 parts of Ludox, 5 ~ 8 parts of titanate coupling agents, 2 ~ 5 parts of hydroxy silicon oils, 1 ~ 3 part of traditional Chinese medicine extraction
Liquid；Described Chinese medicine extract is made up of the material of following parts by weight：6 ~ 10 parts of dried peppermint leaves, 3 ~ 6 parts of myrobalans, 1 ~ 3 part of reed rhizome, 2 ~
5 portions of fruit ofs Chinese magnoliavine, 4 ~ 7 portions of folium artemisiae argyis；
（3）Vacuum discharge opeing is handled：
Step（2）After the completion of processing, the pressure in pressure treatment tank is down to normal pressure, then again will be unnecessary in pressure treatment tank
Modification liquid, which is drawn, to be reclaimed, and then pressure treatment tank is carried out again after vacuumize process, 5 ~ 10min of processing, is excluded wicker products
It is standby after the modification liquid of excess surface；
（4）Isothermal holding：
Step（3）After the completion of processing, close vavuum pump and recover the pressure in pressure treatment tank to normal pressure, then by wicker products
Taking-up, which is put into thermostatic chamber, carries out isothermal holding, and it is to take out standby after 68 ~ 74 DEG C, 1 ~ 2h of isothermal holding to keep the temperature in thermostatic chamber
With；
（5）Cooling treatment：
By step（4）Wicker products after processing naturally cools to normal temperature after taking out.
2. a kind of reinforcement process for lifting wicker products using characteristic according to claim 1, it is characterised in that step
（1）Described in vacuumize process when control vacuum be 0.09MPa.
3. a kind of reinforcement process for lifting wicker products using characteristic according to claim 1, it is characterised in that step
（2）Described in Ludox in silica mass fraction be 19 ~ 20%, particle size be 5 ~ 15nm.
4. a kind of reinforcement process for lifting wicker products using characteristic according to claim 1, it is characterised in that step
（2）Described in the preparation method of Chinese medicine extract be to mix dried peppermint leaf, myrobalan, reed rhizome, the fruit of Chinese magnoliavine, folium artemisiae argyi jointly, then add
Enter into the clear water of 5 ~ 8 times of its gross mass, heating boiling is boiled and filtered after 50 ~ 55min of processing, finally concentrates the filtrate to original volume
Chinese medicine extract is produced after 1/10.
5. a kind of reinforcement process for lifting wicker products using characteristic according to claim 1, it is characterised in that step
（3）Described in vacuumize process when control vacuum be 0.07MPa.
6. a kind of reinforcement process for lifting wicker products using characteristic according to claim 1, it is characterised in that step
（4）Described in isothermal holding when control relative humidity in thermostatic chamber to be 30 ~ 40%.