CN108858612A - A kind of colouring method of the wicker for braiding - Google Patents
A kind of colouring method of the wicker for braiding Download PDFInfo
- Publication number
- CN108858612A CN108858612A CN201810899592.3A CN201810899592A CN108858612A CN 108858612 A CN108858612 A CN 108858612A CN 201810899592 A CN201810899592 A CN 201810899592A CN 108858612 A CN108858612 A CN 108858612A
- Authority
- CN
- China
- Prior art keywords
- wicker
- parts
- colouring method
- coloring agent
- dye
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of colouring methods of wicker for braiding, belong to wicker working process technical field, include the following steps：（1）Wicker pretreatment；（2）Exploding technology；（3）Just dye；（4）Low-temperature treatment；（5）Chase after dye.Wicker even dyeing, the exquisiteness of colouring method dye system through the invention, bright, coloring agent adhesive ability is strong, and performance is stablized, and colouring method is scientific and reasonable, incremental, ensure that the efficiency of dyeing, great market popularization value.
Description
Technical field
The invention belongs to wicker working process technical fields, and in particular to a kind of colouring method of the wicker for braiding.
Background technique
Wicker plaiting article is one of folks of china traditional handicraft product.People are intended only as common daily utility in ancient times, directly
Decades just gradually rise after to 20th century, also the project for becoming selected areas of China foreign exchange earning gradually.The whole nation has three big
Wicker plaiting article production base, Hubei, Shandong, Anhui（In addition Henan also abounds with wicker plaiting article）.Wicker soft pliable, thickness are well-balanced, color is high
It is refined, by novel design, natural, handsome in appearance, Portable durable the practical art product of various honesties can be woven into.Its product
Including：Crate（Packet）, meal basket, food basket（Circle, ellipse）, bamboo strainer, needlework shallow basket made of wicker or thin bamboo strips, kang mat, reed matting etc.
With the continuous improvement of people's living standards, it is higher and higher to the cosmetic requirements of craftwork, daily necessity, in addition to production
Other than technique, raw material color influences product to be also extremely crucial, the wicker of existing wicker colouring method dye system, coloring agent
It is poor with wicker combination degree, it will fall off over time, the phenomenon that colour fading, seriously affect the quality of wicker products.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of colouring method of wicker for braiding is provided.Pass through
Wicker even dyeing, the exquisiteness of colouring method dye system of the invention, bright, coloring agent adhesive ability is strong, and performance is stablized, and
And colouring method is scientific and reasonable, and it is incremental, it ensure that the efficiency of dyeing, great market popularization value.
The present invention is achieved by the following technical solutions：
A kind of colouring method of the wicker for braiding, includes the following steps：
（1）Wicker pretreatment：
A. 20 ~ 30 parts of river silt of long-term feeding lotus root are taken, are placed in agitator tank, are then 1 according to weight ratio by light-coloured vinegar and tap water:
30 ~ 40 are collectively disposed in agitator tank, after 20 ~ 30min of stir process, filter to get filtrate；
B. wicker will be removed the peel and be placed in the filtrate that operation a is obtained and impregnated, the temperature control in filtrate is 35 ~ 39 DEG C, is impregnated
It takes out, polishes after 1 ~ 2h, go flash removed spare；
（2）Exploding technology：By step（1）In pretreated wicker be placed in continous way screw rod and dodge in quick-fried machine, time of exploding technology
Number is 2 ~ 3 times；
（3）Just dye：Coloring agent is coated uniformly on wicker surface, after the completion of coating at once by wicker be placed in infra-red drying room into
Row drying, until coloring agent is completely dried；
（4）Low-temperature treatment：In step（3）Just one layer of sterile water is sprayed on the wicker surface after dye, is then immediately placed in -10 ~ -6 DEG C
It is placed in environment, after placing 4 ~ 5h, takes out wicker and be processed by shot blasting；
（5）Chase after dye：Coloring agent is coated in step（4）Wicker, is placed in by the wicker surface after middle polishing treatment after the completion of coating
Infra-red drying is dried in room, and drying to surface moisture content is 4 ~ 5%, then coats one layer of fixer on wicker surface, then will
Wicker, which is placed in uv curing machine, carries out curing process.
Further, the step（1）The total weight parts of middle light-coloured vinegar and tap water are 4 ~ 5 times of river silt.
Further, the step（3）The coating of middle coloring agent with a thickness of 0.53 ~ 0.57mm.
Further, the step（3）Or step（5）In infrared wavelength be 35 ~ 45 μm.
Further, the step（5）The coating of middle coloring agent with a thickness of 0.38 ~ 0.42mm.
Further, the step（5）Middle fixer is made of following parts by weight of component：4 ~ 5 parts of nano zine oxide is received
Rice 6 ~ 8 parts of silica, 2 ~ 3 parts of thulium sulfate, 2 ~ 3 parts of cerous nitrate, 10 ~ 14 parts of tara gum, 12 ~ 16 parts of cassia gum, poly- second two
8 ~ 12 parts of alcohol, 18 ~ 20 parts of sterile water.
Further, the step（5）The coating of middle fixer with a thickness of 0.12 ~ 0.14mm.
Further, the step（5）The wavelength of ultra-violet curing is 300 ~ 310nm.
The present invention provides a kind of colouring methods of wicker for braiding, pre-process first to wicker, specially
The river silt for taking long-term feeding lotus root, is added light-coloured vinegar and water is stirred, a large amount of microorganism is contained in filtrate obtained, to wicker table
Face is decomposed and is softened, and the uniformity for improving surface is conducive to, and establishes excellent basis for subsequent dyeing processing.Then will
Wicker after pretreatment carries out exploding technology, during processing, it may occur that the degradation of the cellulose, lignin on wicker surface
And softening of lignin etc., weaken the bonding effect between cellulose, unexpected pressure release, wicker superficial cell instantaneous expansion is externally done
Function, so that the structure of cellulose is destroyed, superficial cell is dissociated into single fibrocyte, can effectively promote wicker to dye
The absorption of toner improves the functioning efficiency of coloring agent.And then coloring agent is coated in the wicker surface after exploding technology,
Coloring agent can quickly infect wicker, and coloring agent generates dizzy dye in order to prevent, and wicker is placed in infra-red drying at once after the completion of coating
Interior is dried, and infrared ray has transmission effect, and the intersection of coloring agent and wicker can be made to heat up, and promotes coloring agent
Directed movement guarantees that even dyeing is fine and smooth.Just when dye, coloring agent coating with a thickness of 0.53 ~ 0.57mm, it is thicker, mainly
In order to which subsequent low-temperature treatment is prepared, one layer of sterile water just is sprayed on the surface of wicker after dye, is then immediately placed in low temperature ring
In border, the moisture on surface immediately can condense into ice crystal, then be processed by shot blasting, the fiber on wicker surface and floating for coloring agent
Color can be removed with ice crystal, keep wicker surface more smooth, fine and smooth.It subsequently carries out chasing after dye, chases after and set wicker after contaminating
It in infra-red drying room, is on the one hand dried, the phenomenon for preventing coloring agent trickling uneven, still further aspect is control coloring agent
Movement, reinforce dyeing effect, finally coat one layer of fixer on surface, nano zine oxide, nanometer two are added in fixer
Silica, thulium sulfate, cerous nitrate, tara gum etc. mutually act synergistically, and form huge molecular network on wicker surface,
Promote wicker surface even closer, enhances the overall performance of wicker, in addition, this fixer transparency is very high, it not only will not shadow
The function and effect for ringing coloring agent, can also make dyeing effect vivider, carry out ultra-violet curing after coating fixer, promote to fix
Liquid is combined closely with wicker.
The present invention has the following advantages that compared with prior art：
Wicker even dyeing, the exquisiteness of colouring method dye system through the invention, bright, coloring agent adhesive ability is strong, property
It can stablize, and colouring method is scientific and reasonable, it is incremental, it ensure that the efficiency of dyeing, great market popularization value.
Specific embodiment
Embodiment 1
A kind of colouring method of the wicker for braiding, includes the following steps：
（1）Wicker pretreatment：
A. 20 parts of river silt of long-term feeding lotus root are taken, are placed in agitator tank, are then 1 according to weight ratio by light-coloured vinegar and tap water:30 is total
With being placed in agitator tank, after stir process 20min, filter to get filtrate；
B. wicker will be removed the peel and be placed in the filtrate that operation a is obtained and impregnated, the temperature control in filtrate is 35 DEG C, impregnates 1h
After take out, polish, go flash removed spare；
（2）Exploding technology：By step（1）In pretreated wicker be placed in continous way screw rod and dodge in quick-fried machine, time of exploding technology
Number is 2 times；
（3）Just dye：Coloring agent is coated uniformly on wicker surface, after the completion of coating at once by wicker be placed in infra-red drying room into
Row drying, until coloring agent is completely dried；
（4）Low-temperature treatment：In step（3）Just one layer of sterile water is sprayed on the wicker surface after dye, is then immediately placed in -10 DEG C of environment
In placed, place 4h after, take out wicker be processed by shot blasting；
（5）Chase after dye：Coloring agent is coated in step（4）Wicker, is placed in by the wicker surface after middle polishing treatment after the completion of coating
Infra-red drying is dried in room, and dry to surface moisture content is 4%, then coats one layer of fixer on wicker surface, then by willow
Item, which is placed in uv curing machine, carries out curing process.
Further, the step（1）The total weight parts of middle light-coloured vinegar and tap water are 4 times of river silt.
Further, the step（3）The coating of middle coloring agent with a thickness of 0.53mm.
Further, the step（3）Or step（5）In infrared wavelength be 35 μm.
Further, the step（5）The coating of middle coloring agent with a thickness of 0.38mm.
Further, the step（5）Middle fixer is made of following parts by weight of component：Nano zine oxide 4 part, nanometer
6 parts of silica, 2 parts of thulium sulfate, 2 parts of cerous nitrate, 10 parts of tara gum, 12 parts of cassia gum, 8 parts of polyethylene glycol, sterile water 18
Part.
Further, the step（5）The coating of middle fixer with a thickness of 0.12mm.
Further, the step（5）The wavelength of ultra-violet curing is 300nm.
Embodiment 2
A kind of colouring method of the wicker for braiding, includes the following steps：
（1）Wicker pretreatment：
A. 25 parts of river silt of long-term feeding lotus root are taken, are placed in agitator tank, are then 1 according to weight ratio by light-coloured vinegar and tap water:35 is total
With being placed in agitator tank, after stir process 25min, filter to get filtrate；
B. wicker will be removed the peel and be placed in the filtrate that operation a is obtained and impregnated, the temperature control in filtrate is 37 DEG C, is impregnated
It takes out, polishes after 1.5h, go flash removed spare；
（2）Exploding technology：By step（1）In pretreated wicker be placed in continous way screw rod and dodge in quick-fried machine, time of exploding technology
Number is 2 times；
（3）Just dye：Coloring agent is coated uniformly on wicker surface, after the completion of coating at once by wicker be placed in infra-red drying room into
Row drying, until coloring agent is completely dried；
（4）Low-temperature treatment：In step（3）Just one layer of sterile water is sprayed on the wicker surface after dye, is then immediately placed in -8 DEG C of environment
In placed, place 4.5h after, take out wicker be processed by shot blasting；
（5）Chase after dye：Coloring agent is coated in step（4）Wicker, is placed in by the wicker surface after middle polishing treatment after the completion of coating
Infra-red drying is dried in room, and drying to surface moisture content is 4.5%, then coats one layer of fixer on wicker surface, then will
Wicker, which is placed in uv curing machine, carries out curing process.
Further, the step（1）The total weight parts of middle light-coloured vinegar and tap water are 4.5 times of river silt.
Further, the step（3）The coating of middle coloring agent with a thickness of 0.55mm.
Further, the step（3）Or step（5）In infrared wavelength be 40 μm.
Further, the step（5）The coating of middle coloring agent with a thickness of 0.4mm.
Further, the step（5）Middle fixer is made of following parts by weight of component：4.5 parts of nano zine oxide is received
Rice 7 parts of silica, 2.5 parts of thulium sulfate, 2.5 parts of cerous nitrate, 12 parts of tara gum, 14 parts of cassia gum, 10 parts of polyethylene glycol, nothing
19 parts of bacterium water.
Further, the step（5）The coating of middle fixer with a thickness of 0.13mm.
Further, the step（5）The wavelength of ultra-violet curing is 305nm.
Embodiment 3
A kind of colouring method of the wicker for braiding, includes the following steps：
（1）Wicker pretreatment：
A. 30 parts of river silt of long-term feeding lotus root are taken, are placed in agitator tank, are then 1 according to weight ratio by light-coloured vinegar and tap water:40 is total
With being placed in agitator tank, after stir process 30min, filter to get filtrate；
B. wicker will be removed the peel and be placed in the filtrate that operation a is obtained and impregnated, the temperature control in filtrate is 39 DEG C, impregnates 2h
After take out, polish, go flash removed spare；
（2）Exploding technology：By step（1）In pretreated wicker be placed in continous way screw rod and dodge in quick-fried machine, time of exploding technology
Number is 3 times；
（3）Just dye：Coloring agent is coated uniformly on wicker surface, after the completion of coating at once by wicker be placed in infra-red drying room into
Row drying, until coloring agent is completely dried；
（4）Low-temperature treatment：In step（3）Just one layer of sterile water is sprayed on the wicker surface after dye, is then immediately placed in -6 DEG C of environment
In placed, place 5h after, take out wicker be processed by shot blasting；
（5）Chase after dye：Coloring agent is coated in step（4）Wicker, is placed in by the wicker surface after middle polishing treatment after the completion of coating
Infra-red drying is dried in room, and dry to surface moisture content is 5%, then coats one layer of fixer on wicker surface, then by willow
Item, which is placed in uv curing machine, carries out curing process.
Further, the step（1）The total weight parts of middle light-coloured vinegar and tap water are 5 times of river silt.
Further, the step（3）The coating of middle coloring agent with a thickness of 0.57mm.
Further, the step（3）Or step（5）In infrared wavelength be 45 μm.
Further, the step（5）The coating of middle coloring agent with a thickness of 0.42mm.
Further, the step（5）Middle fixer is made of following parts by weight of component：Nano zine oxide 5 part, nanometer
8 parts of silica, 3 parts of thulium sulfate, 3 parts of cerous nitrate, 14 parts of tara gum, 16 parts of cassia gum, 12 parts of polyethylene glycol, sterile water 20
Part.
Further, the step（5）The coating of middle fixer with a thickness of 0.14mm.
Further, the step（5）The wavelength of ultra-violet curing is 310nm.
Comparative example 1
This comparative example 1 compared with Example 2, saves step（1）The pretreated whole operation of wicker, method step in addition to this
It is rapid all the same.
Comparative example 2
This comparative example 2 compared with Example 2, saves step（2）The whole operation of exploding technology, method and step in addition to this
It is all the same.
Comparative example 3
This comparative example 3 compared with Example 2, saves step（4）The whole operation of low-temperature treatment, method and step in addition to this
It is all the same.
Comparative example 4
This comparative example 4 compared with Example 2, saves step（3）Just dye and step（4）The whole operation of low-temperature treatment, is removed
Furthermore method and step is all the same.
Control group
Existing conventional wicker colouring method.
In order to compare effect of the present invention, choose with a collection of size, the almost consistent wicker of thickness as experimental subjects, then
Respectively with embodiment 2, comparative example 1, comparative example 2, comparative example 3, comparative example 4, control group dyeing side
Method dyes wicker, and performance is measured after dyeing, and does ASSOCIATE STATISTICS record；
Specific experiment correlation data is as shown in table 1 below：
Table 1
Note：Adhesive force described in upper table 1 is referring to GB/T 4893.4-85《Furniture surface adhesive force cross-cut measuring method》To survey
It is fixed；The mass change is to carry out UV irradiation aging process to each group dyeing treated timber, specifically by birch wood
Plate is put into UV ageing oven, and the temperature in control cabinet is 50 DEG C, ultraviolet wavelength 250nm, irradiation intensity 38W/m2, spoke
A length of 150h when penetrating, the decline that its weight is weighed after drying after taking-up is rinsed one time with deionized water after the completion to normality change
Rate, to characterize the anti-aging fixed effect of coloring.
Wicker even dyeing, the exquisiteness of colouring method dye system it can be seen from upper table 1 through the invention, bright,
Coloring agent adhesive ability is strong, and performance is stablized, and colouring method is scientific and reasonable, incremental, ensure that the efficiency of dyeing, great
Market popularization value.
Claims (8)
1. a kind of colouring method of the wicker for braiding, which is characterized in that include the following steps：
（1）Wicker pretreatment：
A. 20 ~ 30 parts of river silt of long-term feeding lotus root are taken, are placed in agitator tank, are then 1 according to weight ratio by light-coloured vinegar and tap water:
30 ~ 40 are collectively disposed in agitator tank, after 20 ~ 30min of stir process, filter to get filtrate；
B. wicker will be removed the peel and be placed in the filtrate that operation a is obtained and impregnated, the temperature control in filtrate is 35 ~ 39 DEG C, is impregnated
It takes out, polishes after 1 ~ 2h, go flash removed spare；
（2）Exploding technology：By step（1）In pretreated wicker be placed in continous way screw rod and dodge in quick-fried machine, time of exploding technology
Number is 2 ~ 3 times；
（3）Just dye：Coloring agent is coated uniformly on wicker surface, after the completion of coating at once by wicker be placed in infra-red drying room into
Row drying, until coloring agent is completely dried；
（4）Low-temperature treatment：In step（3）Just one layer of sterile water is sprayed on the wicker surface after dye, is then immediately placed in -10 ~ -6 DEG C
It is placed in environment, after placing 4 ~ 5h, takes out wicker and be processed by shot blasting；
（5）Chase after dye：Coloring agent is coated in step（4）Wicker, is placed in by the wicker surface after middle polishing treatment after the completion of coating
Infra-red drying is dried in room, and drying to surface moisture content is 4 ~ 5%, then coats one layer of fixer on wicker surface, then will
Wicker, which is placed in uv curing machine, carries out curing process.
2. a kind of colouring method of the wicker for braiding according to claim 1, which is characterized in that the step（1）In
The total weight parts of light-coloured vinegar and tap water are 4 ~ 5 times of river silt.
3. a kind of colouring method of the wicker for braiding according to claim 1, which is characterized in that the step（3）In
Coloring agent coating with a thickness of 0.53 ~ 0.57mm.
4. a kind of colouring method of the wicker for braiding according to claim 1, which is characterized in that the step（3）Or
Step（5）In infrared wavelength be 35 ~ 45 μm.
5. a kind of colouring method of the wicker for braiding according to claim 1, which is characterized in that the step（5）In
Coloring agent coating with a thickness of 0.38 ~ 0.42mm.
6. a kind of colouring method of the wicker for braiding according to claim 1, which is characterized in that the step（5）In
Fixer is made of following parts by weight of component：4 ~ 5 parts of nano zine oxide, 6 ~ 8 parts of nano silica, 2 ~ 3 parts of thulium sulfate, nitre
2 ~ 3 parts of sour cerium, 10 ~ 14 parts of tara gum, 12 ~ 16 parts of cassia gum, 8 ~ 12 parts of polyethylene glycol, 18 ~ 20 parts of sterile water.
7. a kind of colouring method of the wicker for braiding according to claim 1, which is characterized in that the step（5）In
Fixer coating with a thickness of 0.12 ~ 0.14mm.
8. a kind of colouring method of the wicker for braiding according to claim 1, which is characterized in that the step（5）It is purple
Outer cured wavelength is 300 ~ 310nm.