CN106381037A - Finishing-free texture paint and preparation method thereof - Google Patents
Finishing-free texture paint and preparation method thereof Download PDFInfo
- Publication number
- CN106381037A CN106381037A CN201610781362.8A CN201610781362A CN106381037A CN 106381037 A CN106381037 A CN 106381037A CN 201610781362 A CN201610781362 A CN 201610781362A CN 106381037 A CN106381037 A CN 106381037A
- Authority
- CN
- China
- Prior art keywords
- water
- dispersion
- preparation
- finishing
- speed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of paint application, specifically to finishing-free texture paint and a preparation method thereof. The finishing-free texture paint is composed of the following ingredients: water, cellulose, bentonite, a pH regulator, an antimicrobial mildew-inhibitor, a dispersant, a wetting agent, an antifoaming agent, titanium dioxide, heavy calcium, a super-hydrophilic emulsion, a coalescing agent, an alkali-swelling thickener, a PU thickener, an antifreezing agent and quartz sand. Through specially-modified super-hydrophilic emulsion, the texture paint main-material with stains on the surface is easy to wash with water under the precondition of no finishing coat, and also has excellent stain resistance. Meanwhile, due to the internal hydrophobic structure, the texture paint main-material has excellent water resistance and low permeable rate under the precondition of no finishing coat. Thus, it is ensured that the main-material structure is not easy to damage by water.
Description
Technical field
The present invention relates to coating applied technical field is and in particular to one kind exempts from cover texture coating and preparation method thereof.
Background technology
Compare and lithotome finishing material, had into the true mineral varnish that acrylic acid ester emulsion is formulated with various coloured silk sand
This is low, security performance is high, health environment-friendly the features such as, just gradually substitute exterior wall lithotome facing, become external wall decorative material
Main flow.
The texture coating also most of proportion occupying coating application visual field progressively, but traditional texture coating is applied in main material
After work, need, using finish paint, main material is carried out with overlay treatment, the anti-pollution characteristic of guarantee coating and water resistance etc., operation fiber crops
Tired, technological process is complicated.
Content of the invention
For effectively solving the problems referred to above, the present invention provides one kind to exempt from cover texture coating and preparation method thereof.
The concrete scheme of the present invention is:One kind exempts from cover texture coating, is made up of the composition of following weight ratio:
A kind of preparation method exempting from cover texture coating, above-mentioned exempts from cover texture coating, methods described bag for preparing
Include following steps:
(1) cellulose and bentonite are carried out being dispersed at a high speed in water and be uniformly dispersed;
Described mixing speed is 200-300r/min, a length of 15-20min during stirring;
(2) low speed dispersion, sequentially adds PH regulator, biocide mildewcide, dispersant, wetting agent and defoamer;
Described low speed rate of dispersion is 50-70r/min, a length of 20min during dispersion stirring;
(3) it is slowly added to titanium dioxide and triple superphosphate, at a high speed dispersion 30min;
The speed of dispersion stirring is 150-170r/min at a high speed;
(4) add super hydrophilic emulsion and coalescents, be uniformly dispersed;
Scattered mixing speed is 20-30r/min, and maintains and terminate to preparation;
(5) alkali swollen thickener and PU thickening agent are mixed homogeneously with water and antifreezing agent respectively, be then slowly added to successively;
(6) stir paint, add quartz sand mix homogeneously;
(7) packing subpackage.
Beneficial effects of the present invention are:Special modified super hydrophilic emulsion is so that texture coating main material is in not brushing finish paint
On the premise of have main material surface blot easily be washed clean ability under water, have excellent contaminated resistance;With
When its inner hydrophobic structure make it have excellent resistance to water and low permeability rate on the premise of not brushing finish paint it is ensured that main
Material structure is difficult by water destruct.
Biocide mildewcide can ensure that main material is difficult by mycete and algal spoilage on the premise of not brushing finish paint.
Specific embodiment
In order that the objects, technical solutions and advantages of the present invention become more apparent, with reference to embodiments, to the present invention
It is explained in further detail.It should be appreciated that specific embodiment described herein is used only for explaining the present invention, it is not used to
Limit the present invention.
On the contrary, the present invention covers any replacement done in the spirit and scope of the present invention being defined by the claims, repaiies
Change, equivalent method and scheme.Further, in order that the public has a better understanding to the present invention, thin to the present invention below
In section description, detailed describe some specific detail sections.Part without these details for a person skilled in the art
Description can also understand the present invention completely.
Below by way of specific embodiment, the present invention is further explained;The embodiment of the present invention provides one kind to exempt from cover
Texture coating, should be made up of the composition of following weight ratio:
Described cellulose is that hydroxyethyl cellulose, methylcellulose, carboxymethyl cellulose, ethyl cellulose or hydroxypropyl are fine
One or more therein of dimension element;
Biocide mildewcide therein be relatively conventional in coating application in prior art there is fungus and mildew resistance function,
Can be for example n-octyl Kazon, but be not limited to only n-octyl Kazon;
Described PH regulator is AMP95;Described antifreezing agent is alcohols antifreezing agent;
Described dispersant is low molecule wax class dispersant;
Described defoamer is mineral oil antifoam agent;Described coalescents are 2,2,4- trimethyl -1,3- pentanediol list isobutyl
Acid esters;Described wetting agent is conventional wetting agent in existing coating products technical field.
Described quartz sand is the quartz sand of 40-50 mesh.
Described super hydrophilic emulsion include nano titanic oxide sol, polyvinyl alcohol, Polyethylene Glycol, modified polyacrylate and
Water, applies above-mentioned raw material to pass through modification method for preparing, obtains super hydrophilic emulsion;
Concrete preparation process is as follows, by nano titanic oxide sol, polyvinyl alcohol, Polyethylene Glycol, modified polyacrylate
And nano cupric oxide granule is according to weight portion 4:3:15:1:2 proportions obtain mixture, are then added in water, are stirring
Mix in machine and be stirred, the weight ratio being just met for mixture with water is 1:2.5;Mixing speed is 400-600r/min,
Simultaneously need to temperature-pressure, described be heated up to 300-350 DEG C, under conditions of 2-3 atmospheric pressure, be stirred 30 minutes, real
Now complete modified preparation;The size of wherein said nano cupric oxide granule is 200-250nm, realizes in modified preparation process,
The mixing homogeneity of balance different components, realizes in modifying process simultaneously, raising activity of being heated, the molecule structure to other materials
Become to realize impact, reach the preparation effect of optimum;The super hydrophilic emulsion crossing special modification is not so that texture coating main material is being brushed
Have on the premise of finish paint main material surface blot easily be washed clean ability under water, have excellent stain resistance
Energy.
A kind of preparation method exempting from cover texture coating, above-mentioned exempts from cover texture coating, methods described bag for preparing
Include following steps:
(1) cellulose and bentonite are carried out being dispersed at a high speed in water and be uniformly dispersed;
Described mixing speed is 200-300r/min, a length of 15-20min during stirring;
(2) low speed dispersion, sequentially adds PH regulator, biocide mildewcide, dispersant, wetting agent and defoamer;
Described low speed rate of dispersion is 50-70r/min, a length of 20min during dispersion stirring;
(3) it is slowly added to titanium dioxide and triple superphosphate, at a high speed dispersion 30min;
The speed of dispersion stirring is 150-170r/min at a high speed;
(4) add super hydrophilic emulsion and coalescents, be uniformly dispersed;
Scattered mixing speed is 20-30r/min, and maintains and terminate to preparation;
(5) alkali swollen thickener and PU thickening agent are mixed homogeneously with water and antifreezing agent respectively, be then slowly added to successively;
(6) stir paint, add quartz sand mix homogeneously;
(7) packing subpackage.
Claims (2)
1. a kind of exempt from cover texture coating it is characterised in that being made up of the composition of following weight ratio:
2. a kind of preparation method exempting from cover texture coating, exempts from cover texture coating for preparing described in the claims 1,
It is characterized in that, methods described comprises the steps:
(1) cellulose and bentonite are carried out being dispersed at a high speed in water and be uniformly dispersed;
Described mixing speed is 200-300r/min, a length of 15-20min during stirring;
(2) low speed dispersion, sequentially adds PH regulator, biocide mildewcide, dispersant, wetting agent and defoamer;
Described low speed rate of dispersion is 50-70r/min, a length of 20min during dispersion stirring;
(3) it is slowly added to titanium dioxide and triple superphosphate, at a high speed dispersion 30min;
The speed of dispersion stirring is 150-170r/min at a high speed;
(4) add super hydrophilic emulsion and coalescents, be uniformly dispersed;
Scattered mixing speed is 20-30r/min, and maintains and terminate to preparation;
(5) alkali swollen thickener and PU thickening agent are mixed homogeneously with water and antifreezing agent respectively, be then slowly added to successively;
(6) stir paint, add quartz sand mix homogeneously;
(7) packing subpackage.