CN106380075A - 一种钢包镁碳砖用涂料及其使用方法 - Google Patents
一种钢包镁碳砖用涂料及其使用方法 Download PDFInfo
- Publication number
- CN106380075A CN106380075A CN201610737696.5A CN201610737696A CN106380075A CN 106380075 A CN106380075 A CN 106380075A CN 201610737696 A CN201610737696 A CN 201610737696A CN 106380075 A CN106380075 A CN 106380075A
- Authority
- CN
- China
- Prior art keywords
- coating
- carbon brick
- magnesia carbon
- powder
- ladle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种钢包镁碳砖用涂料,原料的重量百分比为:粘土熟料粉20‑30%;粘土生料粉10‑15%;硼玻璃粉8‑15%;硅微粉5%,碳化硅细粉5%;固体水玻璃5%,广西白泥15‑25%;钠长石粉25‑30%,黄糊精2%,以上所有原料的重量百分比之和为100%。本发明的涂料在烘烤时随着温度的升高,逐渐溶化为玻璃态,粘附在镁碳砖表面,隔绝了镁碳砖和空气的接触,减少了氧化的可能性。
Description
技术领域
本发明涉及一种钢包镁碳砖用涂料及其使用方法。
背景技术
由于钢材质量的要求越来越高,钢包冶炼要求也越来越苛刻,对钢包使用的镁碳砖要求也越来越高,目前,钢包镁碳砖在烘烤及使用过程中,由于升温后镁碳砖表面一般都会形成一层10-30mm的脱碳氧化层,该氧化层会大大缩短钢包的使用寿命,降低钢材的质量。
发明内容
针对上述问题,本发明提供了一种钢包镁碳砖用涂料,涂在镁碳砖的表面料,来阻挡外界的氧气和镁碳砖中的碳接触,达到减少氧化层的目的,同时提高炉龄。
本发明采用的技术方案是:
一种钢包镁碳砖用涂料,原料的重量百分比为:粘土熟料粉20-30%;粘土生料粉10-15%;硼玻璃粉8-15%;硅微粉5%,碳化硅细粉5%;固体水玻璃5%,广西白泥15-25%;钠长石粉25-30%,黄糊精2%,以上所有原料的重量百分比之和为100%。
同时,本发明还提供了一种钢包镁碳砖用涂料的使用方法,包括以下步骤:
(1)将钢包镁碳砖用涂料放入搅拌机中,并加入水进行搅拌5-15分钟,得到钢包镁碳砖用涂料的混合物;
(2)搅拌后,将钢包镁碳砖用涂料的混合物直接刷或者涂抹在砌筑好的钢包镁碳砖的表面上。
本发明的涂料在烘烤时随着温度的升高,逐渐溶化为玻璃态,粘附在镁碳砖表面,隔绝了镁碳砖和空气的接触,减少了氧化的可能性。
具体实施方式
下面通过具体的实施例对本发明做进一步的详细描述。
实施例1
一种钢包镁碳砖用涂料,原料的重量百分比为:粘土熟料粉20-25%;粘土生料粉10-12%;硼玻璃粉8-12%;硅微粉5%,碳化硅细粉5%;固体水玻璃5%,广西白泥15-20%;钠长石粉25-27%,黄糊精2%,以上所有原料的重量百分比之和为100%。
实施例2
一种钢包镁碳砖用涂料,原料的重量百分比为:粘土熟料粉25-30%;粘土生料粉12-15%;硼玻璃粉12-15%;硅微粉5%,碳化硅细粉5%;固体水玻璃5%,广西白泥20-25%;钠长石粉27-30%,黄糊精2%,以上所有原料的重量百分比之和为100%。
实施例3
一种钢包镁碳砖用涂料的使用方法,包括以下步骤:
(1)将钢包镁碳砖用涂料放入搅拌机中,并加入水进行搅拌5-15分钟,得到钢包镁碳砖用涂料的混合物;
(2)搅拌后,将钢包镁碳砖用涂料的混合物直接撒在砌筑好的钢包镁碳砖的表面上。
优选的,步骤(1)中,加入的水的重量为钢包镁碳砖用涂料的10-20%。
Claims (2)
1.一种钢包镁碳砖用涂料,其特征在于,原料的重量百分比为:粘土熟料粉20-30%;粘土生料粉10-15%;硼玻璃粉8-15%;硅微粉5%,碳化硅细粉5%;固体水玻璃5%,广西白泥15-25%;钠长石粉25-30%,黄糊精2%,以上所有原料的重量百分比之和为100%。
2.一种钢包镁碳砖用涂料的使用方法,其特征在于,包括以下步骤:
(1)将钢包镁碳砖用涂料放入搅拌机中,并加入水进行搅拌5-15分钟,得到钢包镁碳砖用涂料的混合物;
(2)搅拌后,将钢包镁碳砖用涂料的混合物直接刷或者涂抹在砌筑好的钢包镁碳砖的表面上。