CN106366941A - Processing technology of shoe polish - Google Patents
Processing technology of shoe polish Download PDFInfo
- Publication number
- CN106366941A CN106366941A CN201610737227.3A CN201610737227A CN106366941A CN 106366941 A CN106366941 A CN 106366941A CN 201610737227 A CN201610737227 A CN 201610737227A CN 106366941 A CN106366941 A CN 106366941A
- Authority
- CN
- China
- Prior art keywords
- fiber
- liquid
- mass percent
- shoe polish
- black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a processing technology of shoe polish. The processing technology comprises the steps that 1, black dye is prepared into black liquid, wherein the preparation process of the black dye comprises the steps that ginkgo ketone is extracted from ginkgo leaves, waste materials obtained after extraction are dewatered to prepare dried waste materials, water is added into the dried waste materials, stirring is conducted, the waste materials are stirred to be uniform and then heated to be paste to obtain paste waste materials, and the black liquid is prepared by adding acid into the paste waste materials; 2, solid paraffin and beewax are mixed to be added into the black liquid to obtain colloidal liquid; 3, stearic acid and silicone oil are added into the colloidal liquid to prepare thick mixed liquid; 4, natural fibers are put into water to be subjected to ultrasonic treatment, heating and drying are conducted while ultrasonic treatment is conducted, the fibers obtained after treatment are added into glycerin, ultrasonic treatment is conducted again, and then a fiber and glycerin mixture obtained after treatment is added into the mixed liquid. The prepared shoe polish has a good cleaning effect on leather shoes.
Description
Technical field
The present invention relates to a kind of processing technique of shoe polish.
Background technology
Shoe polish is to embrocate in the protective agent of leather shoes and leather surface and glazing agent, has waterproof, guard, strengthens leather surface
Gloss, cleaning, the effect of attractive in appearance and additive color complementary color, daily life consumption is very big.Textural classification pressed by shoe polish, has solvent-borne type plaster
Body, emulsion type ointment body and liquid type, first two is traditional product, and liquid shoe polish is domestic at present popular new product.Liquid
Body shoe polish have do not wipe from bright, easy to carry, save time the features such as, the features such as embrocate easy, deep liked by consumer.With regard to liquid
The main body of shoe polish, there are reports and launch, and its primary raw material is wax emulsion and the mixing of wax emulsion and synthetic resin
Thing etc..But existing shoe polish need to be improved to the clean effect of leather shoes.
Content of the invention
For above-mentioned technical problem, the present invention has designed and developed a kind of good shoe polish of cleaning effect.
Present invention offer technical scheme below:
A kind of processing technique of shoe polish, comprising:
Black dyes is modulated into black liquor by step (1), and the preparation process of black dyes is: will extract from Folium Ginkgo
Bilobanone, the waste material after extracting is removed moisture, makes dry waste material, then the stirring that adds water in dry waste material, after stirring again
It is heated to paste, obtains paste waste material, add acid to be modulated into black liquor in paste waste material;
Step (2) adds hard paraffin and Cera Flava mixing to black liquor, is stirred and heated to merge, obtains glue
Liquid, wherein, mass percent in black liquor for the hard paraffin is 4~5%, percent mass in black liquor for the Cera Flava
Than for 4~5%;
Step (3) adds stearic acid and silicone oil in colloidal liquid, makes thick mixing liquid, and wherein, stearic acid exists
Mass percent in mixing liquid is 0.2~0.3%, and mass percent in mixing liquid for the silicone oil is 0.1~0.2%;
Natural fiber is placed in water by step (4), carries out supersound process, the time of supersound process is 1~2h, supersound process
Frequency be 50~70khz, also heated while supersound process, heating-up temperature be 100~120 DEG C, obtaining length is
Fiber after 100~120 μm of process, is dried, and the fiber after processing is added in glycerol, is then sonicated 15~20min, surpass
The frequency of sonication is 50~70khz, and the mass ratio of the fiber after process and glycerol is 3:1, afterwards by the fiber after processing and
The mixture of glycerol adds to mixing liquid, mass percent in mixing liquid for the fiber after process be 0.7~
0.9%, stir.
Preferably, in the processing technique of described shoe polish, in described step (2), hard paraffin is in black liquor
Mass percent is 4.5%, and mass percent in black liquor for the Cera Flava is 4.5%.
Preferably, in the processing technique of described shoe polish, in described step (3), matter in mixing liquid for the stearic acid
Amount percentage ratio is 0.2%, and mass percent in mixing liquid for the silicone oil is 0.1%.
Preferably, in the processing technique of described shoe polish, in described step (4), the length of the fiber after process is 100
~110 μm.
The preparation-obtained shoe polish of the present invention is good to the clean effect of leather shoes.
Specific embodiment
The present invention is described in further detail below, with make those skilled in the art with reference to specification word being capable of evidence
To implement.
The present invention provides a kind of processing technique of shoe polish, comprising:
Black dyes is modulated into black liquor by step (1), and the preparation process of black dyes is: will extract from Folium Ginkgo
Bilobanone, the waste material after extracting is removed moisture, makes dry waste material, then the stirring that adds water in dry waste material, after stirring again
It is heated to paste, obtains paste waste material, add acid to be modulated into black liquor in paste waste material;
Step (2) adds hard paraffin and Cera Flava mixing to black liquor, is stirred and heated to merge, obtains glue
Liquid, wherein, mass percent in black liquor for the hard paraffin is 4~5%, percent mass in black liquor for the Cera Flava
Than for 4~5%;
Step (3) adds stearic acid and silicone oil in colloidal liquid, makes thick mixing liquid, and wherein, stearic acid exists
Mass percent in mixing liquid is 0.2~0.3%, and mass percent in mixing liquid for the silicone oil is 0.1~0.2%;
Natural fiber is placed in water by step (4), carries out supersound process, the time of supersound process is 1~2h, supersound process
Frequency be 50~70khz, also heated while supersound process, heating-up temperature be 100~120 DEG C, obtaining length is
Fiber after 100~200 μm of process, is dried, and the fiber after processing is added in glycerol, is then sonicated 15~20min, surpass
The frequency of sonication is 50~70khz, and the mass ratio of the fiber after process and glycerol is 3:1, afterwards by the fiber after processing and
The mixture of glycerol adds to mixing liquid, mass percent in mixing liquid for the fiber after process be 0.7~
0.9%, stir.
The present invention prepares black dyes using extracting remaining waste material during bilobanone from Folium Ginkgo, and Color is good,
Color is firm;And also improve the utilization rate to waste product, energy-conserving and environment-protective.And during using waste material, be first by waste material
In moisture remove, make dry waste material, then add water in dry waste material, again make paste waste material.So be conducive to removing waste material
In impurity, the volatilizable composition being especially mixed in waste material can be removed as far as possible;In addition, being so also beneficial to improve black
The uniformity of color liquid, that is, ensure the viscosity uniformity of each several part in black liquor, thus ensureing the composition of final shoe polish
It is evenly distributed consistent.
The present invention with the addition of in shoe polish has the fiber that length is 100~200 μm.When wiping leather shoes using shoe polish, fine
Dimension composition plays the effect of wiping to the surface of leather shoes, thus improving the clean effect to leather shoes.Chi due to fibre composition
Leather shoes will not be damaged by very little only micron order.
In the present invention, the processing method of natural fiber is, carries out supersound process to natural fiber, and by accurately setting
The time of supersound process and the frequency of supersound process, come length and the diameter of the fiber after control process.Based on aforesaid operations bar
Part, uniformly, the length difference between fiber after process is away from ± 5 μm for the distribution of lengths of the fiber after process.And supersound process
The outer surface that the fiber after process can be made becomes coarse, makes the fiber after process relatively stable and is evenly dispersed in shoe polish
In bulk composition.
The present invention is also heated while supersound process, and heating-up temperature is 100~120 DEG C, through surpassing for a long time
Sonication and heating, can make the fiber after process form the form of curling, rather than rectilinear form.So contribute to promoting
So that the fiber after process is more stably dispersed in the bulk composition of shoe polish, and be difficult to settle from the bulk composition of shoe polish or divide
From.
After drying, then by the fiber after processing add to glycerol, then carry out the supersound process of short time.Due to place
Fiber surface after reason is in more coarse state, the fiber surface after glycerol can be promoted when ultrasonic to adhere to process, surely
The fixed fiber surface combining after treatment;Afterwards the fiber after processing and the mixture of glycerol are directly added to mixing liquid
In, make shoe polish, now, the outer surface due to the fiber after processing has wrapped up one layer of glycerol, easily with mixing liquid in its
His composition is mixed into an entirety, so that the shoe polish made is more stable, dispersibility is more preferable.
Preferably, in the processing technique of described shoe polish, in described step (2), hard paraffin is in black liquor
Mass percent is 4.5%, and mass percent in black liquor for the Cera Flava is 4.5%.
Preferably, in the processing technique of described shoe polish, in described step (3), matter in mixing liquid for the stearic acid
Amount percentage ratio is 0.2%, and mass percent in mixing liquid for the silicone oil is 0.1%.
Preferably, in the processing technique of described shoe polish, in described step (4), the length of the fiber after process is 100
~110 μm.
Although embodiment of the present invention is disclosed as above, it is not restricted to listed in description and embodiment
With, it can be applied to various suitable the field of the invention completely, for those skilled in the art, can be easily
Realize other modification, therefore under the general concept being limited without departing substantially from claim and equivalency range, the present invention does not limit
In specific details.
Claims (4)
1. a kind of processing technique of shoe polish is it is characterised in that include:
Black dyes is modulated into black liquor by step (1), and the preparation process of black dyes is: will extract Semen Ginkgo from Folium Ginkgo
Ketone, the waste material after extracting is removed moisture, makes dry waste material, then the stirring that adds water in dry waste material, heats after stirring again
To paste, obtain paste waste material, add acid to be modulated into black liquor in paste waste material;
Step (2) adds hard paraffin and Cera Flava mixing to black liquor, is stirred and heated to merge, obtains Colloidal fluid
Body, wherein, mass percent in black liquor for the hard paraffin is 4~5%, mass percent in black liquor for the Cera Flava
For 4~5%;
Step (3) adds stearic acid and silicone oil in colloidal liquid, makes thick mixing liquid, and wherein, stearic acid is in mixing
Mass percent in liquid is 0.2~0.3%, and mass percent in mixing liquid for the silicone oil is 0.1~0.2%;
Natural fiber is placed in water by step (4), carries out supersound process, the time of supersound process is 1~2h, the frequency of supersound process
Rate be 50~70khz, also heated while supersound process, heating-up temperature be 100~120 DEG C, obtain length be 100~
Fiber after 120 μm of process, is dried, and the fiber after processing is added in glycerol, is then sonicated 15~20min, ultrasonic place
The frequency of reason is 50~70khz, and the fiber after process is 3:1 with the mass ratio of glycerol, afterwards by the fiber after processing and glycerol
Mixture add to mixing liquid, mass percent in mixing liquid for the fiber after process be 0.7~0.9%, stir
Mix uniformly.
2. the processing technique of shoe polish as claimed in claim 1 is it is characterised in that in described step (2), hard paraffin is in black
Mass percent in liquid is 4.5%, and mass percent in black liquor for the Cera Flava is 4.5%.
3. the processing technique of shoe polish as claimed in claim 1 is it is characterised in that in described step (3), stearic acid is in mixed liquor
Mass percent in body is 0.2%, and mass percent in mixing liquid for the silicone oil is 0.1%.
4. the processing technique of shoe polish as claimed in claim 1 is it is characterised in that in described step (4), the fiber after process
Length is 100~110 μm.