CN106349951A - Shoe polish preparation method - Google Patents
Shoe polish preparation method Download PDFInfo
- Publication number
- CN106349951A CN106349951A CN201610737283.7A CN201610737283A CN106349951A CN 106349951 A CN106349951 A CN 106349951A CN 201610737283 A CN201610737283 A CN 201610737283A CN 106349951 A CN106349951 A CN 106349951A
- Authority
- CN
- China
- Prior art keywords
- mass percent
- liquid
- shoe polish
- preparation
- black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a shoe polish preparation method. The shoe polish preparation method includes steps: (1) making black dye into black liquid; (2) mixing solid paraffin and beewax, adding into the black liquid, and stirring and heating to fuse, so that colloidal liquid is obtained, wherein the mass percent of the solid paraffin in the black liquid is 4-5%, and the mass percent of the beewax in the black liquid is 4-5%; (3) adding stearic acid and silicone oil into the colloidal liquid to obtain thick mixed liquid, wherein the mass percent of the stearic acid in the mixed liquid is 0.2-0.3%, and the mass percent of the silicon oil in the mixed liquid is 0.1-0.2%; (4) subjecting natural fibers to ultrasonic treatment to obtain treated fibers being 100-200micron in length, adding the treated fibers into the mixed liquid, and well stirring. Shoe polish prepared according to the method is great in leather shoe cleaning effect.
Description
Technical field
The present invention relates to a kind of preparation method of shoe polish.
Background technology
Shoe polish is to embrocate in the protective agent of leather shoes and leather surface and glazing agent, has waterproof, guard, strengthens leather surface
Gloss, cleaning, the effect of attractive in appearance and additive color complementary color, daily life consumption is very big.Textural classification pressed by shoe polish, has solvent-borne type plaster
Body, emulsion type ointment body and liquid type, first two is traditional product, and liquid shoe polish is domestic at present popular new product.Liquid
Body shoe polish have do not wipe from bright, easy to carry, save time the features such as, the features such as embrocate easy, deep liked by consumer.With regard to liquid
The main body of shoe polish, there are reports and launch, and its primary raw material is wax emulsion and the mixing of wax emulsion and synthetic resin
Thing etc..But existing shoe polish need to be improved to the clean effect of leather shoes.
Content of the invention
For above-mentioned technical problem, the present invention has designed and developed a kind of good shoe polish of cleaning effect.
Present invention offer technical scheme below:
A kind of preparation method of shoe polish, comprising:
Black dyes is modulated into black liquor by step (1)；
Step (2) adds hard paraffin and Cera Flava mixing to black liquor, is stirred and heated to merge, obtains glue
Liquid, wherein, mass percent in black liquor for the hard paraffin is 4～5%, percent mass in black liquor for the Cera Flava
Than for 4～5%；
Step (3) adds stearic acid and silicone oil in colloidal liquid, makes thick mixing liquid, and wherein, stearic acid exists
Mass percent in mixing liquid is 0.2～0.3%, and mass percent in mixing liquid for the silicone oil is 0.1～0.2%；
Natural fiber is carried out supersound process by step (4), obtains the fiber after the process that length is 100～200 μm, will locate
Fiber after reason adds to mixing liquid, and mass percent in mixing liquid for the fiber after process is 0.7～0.9%,
Stir.
Preferably, in the preparation method of described shoe polish, in described step (2), hard paraffin is in black liquor
Mass percent is 4.5%, and mass percent in black liquor for the Cera Flava is 4.5%.
Preferably, in the preparation method of described shoe polish, in described step (3), matter in mixing liquid for the stearic acid
Amount percentage ratio is 0.2%, and mass percent in mixing liquid for the silicone oil is 0.1%.
Preferably, in the preparation method of described shoe polish, in described step (4), the length of the fiber after process is 100
～120 μm.
The preparation-obtained shoe polish of the present invention is good to the clean effect of leather shoes.
Specific embodiment
The present invention is described in further detail below, with make those skilled in the art with reference to specification word being capable of evidence
To implement.
The present invention provides a kind of preparation method of shoe polish, comprising:
Black dyes is modulated into black liquor by step (1)；
Step (2) adds hard paraffin and Cera Flava mixing to black liquor, is stirred and heated to merge, obtains glue
Liquid, wherein, mass percent in black liquor for the hard paraffin is 4～5%, percent mass in black liquor for the Cera Flava
Than for 4～5%；
Step (3) adds stearic acid and silicone oil in colloidal liquid, makes thick mixing liquid, and wherein, stearic acid exists
Mass percent in mixing liquid is 0.2～0.3%, and mass percent in mixing liquid for the silicone oil is 0.1～0.2%；
Natural fiber is carried out supersound process by step (4), obtains the fiber after the process that length is 100～200 μm, will locate
Fiber after reason adds to mixing liquid, and mass percent in mixing liquid for the fiber after process is 0.7～0.9%,
Stir.
The present invention with the addition of in shoe polish has the fiber that length is 100～200 μm.When wiping leather shoes using shoe polish, fine
Dimension composition plays the effect of wiping to the surface of leather shoes, thus improving the clean effect to leather shoes.Chi due to fibre composition
Leather shoes will not be damaged by very little only micron order.
Preferably, in the preparation method of described shoe polish, in described step (2), hard paraffin is in black liquor
Mass percent is 4.5%, and mass percent in black liquor for the Cera Flava is 4.5%.
Preferably, in the preparation method of described shoe polish, in described step (3), matter in mixing liquid for the stearic acid
Amount percentage ratio is 0.2%, and mass percent in mixing liquid for the silicone oil is 0.1%.
Preferably, in the preparation method of described shoe polish, in described step (4), the length of the fiber after process is 100
～120 μm.
Although embodiment of the present invention is disclosed as above, it is not restricted to listed in description and embodiment
With, it can be applied to various suitable the field of the invention completely, for those skilled in the art, can be easily
Realize other modification, therefore under the general concept being limited without departing substantially from claim and equivalency range, the present invention does not limit
In specific details.
Claims (4)
1. a kind of preparation method of shoe polish is it is characterised in that include:
Black dyes is modulated into black liquor by step (1)；
Step (2) adds hard paraffin and Cera Flava mixing to black liquor, is stirred and heated to merge, obtains Colloidal fluid
Body, wherein, mass percent in black liquor for the hard paraffin is 4～5%, mass percent in black liquor for the Cera Flava
For 4～5%；
Step (3) adds stearic acid and silicone oil in colloidal liquid, makes thick mixing liquid, and wherein, stearic acid is in mixing
Mass percent in liquid is 0.2～0.3%, and mass percent in mixing liquid for the silicone oil is 0.1～0.2%；
Natural fiber is carried out supersound process by step (4), obtains the fiber after the process that length is 100～200 μm, after processing
Fiber add to mixing liquid, mass percent in mixing liquid for the fiber after process be 0.7～0.9%, stirring
Uniformly.
2. the preparation method of shoe polish as claimed in claim 1 is it is characterised in that in described step (2), hard paraffin is in black
Mass percent in liquid is 4.5%, and mass percent in black liquor for the Cera Flava is 4.5%.
3. the preparation method of shoe polish as claimed in claim 1 is it is characterised in that in described step (3), stearic acid is in mixed liquor
Mass percent in body is 0.2%, and mass percent in mixing liquid for the silicone oil is 0.1%.
4. the preparation method of shoe polish as claimed in claim 1 is it is characterised in that in described step (4), the fiber after process
Length is 100～120 μm.