CN106366735A - Dumping grate for boiler - Google Patents
Dumping grate for boiler Download PDFInfo
- Publication number
- CN106366735A CN106366735A CN201610785681.6A CN201610785681A CN106366735A CN 106366735 A CN106366735 A CN 106366735A CN 201610785681 A CN201610785681 A CN 201610785681A CN 106366735 A CN106366735 A CN 106366735A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- weight portion
- protective paint
- fire grate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a dumping grate for a boiler. The surface of a metal grate body is coated with protective paint, and the protective paint is prepared by the follow steps: 1) sequentially adding 1-2 parts of tributyl phosphate, 0.5 part of calcium chloride, 1.6 parts of vinyl trimethoxy silane, 2.3 parts of malonic acid and 13 parts of EVA emulsion into 20 parts of deionized water, and uniformly stirring; 2) sequentially adding 2.6 parts of three (2, 3-dibromopropyl) isocyanuric acid esters, 0.8 part of lgepon T, 1.4 parts of coconut fatty acid diethanol amide, 1.8 parts of N-acyl amino acid salt and 1.5 sodium xylene sulfonate, and continuing to stirring until sufficiently and uniformly mixing is achieved to obtain the protective paint. According to the dumping grate for the boiler, the surface of the metal grate body is coated with the protective paint, so that long-term use of the grate can be guaranteed.
Description
Technical field
The present invention relates to a kind of boiler dumping-grate.
Background technology
Existing boiler dumping-grate, heat-resisting, wear-resisting, antirust, the corrosion-resistant, antioxygenic property of its metal fire grate main body
Have much room for improvement, the life-time service of impact fire grate.
Content of the invention
It is an object of the invention to provide a kind of boiler dumping-grate, its metal fire grate body surfaces is coated with protection
Paint, makes metal fire grate main body have excellent heat-resisting, wear-resisting, antirust, corrosion-resistant, antioxygenic property, thus ensureing that fire grate can be grown
Phase uses.
For achieving the above object, the technical scheme is that a kind of boiler dumping-grate of design, including metal furnaces
Row's main body, this metal fire grate body surfaces is covered with protective paint, and described protective paint is made by the steps:
1) by 1～2 parts by weight of phosphoric acid tributyl, 0.5 weight portion calcium chloride, 1.6 parts by weight of ethylene base trimethoxy silanes,
2.3 weight portion malonic acid, 13 weight portion eva emulsions put in 20 parts by weight of deionized water successively, stir；
2) put into 2.6 weight portion three (2,3- dibromopropyl) fulminuric acid esters more successively, 0.8 weight portion pancreas add drift t,
1.4 weight portion lauric acid amide of ethanol, 1.8 weight portion n- acyl amino hydrochlorates, 1.5 parts by weight of xylene sodium sulfonates, continue
Stirring, prepared protective paint uniform to being sufficiently mixed.
Preferably, boiler dumping-grate, including metal fire grate main body, this metal fire grate body surfaces is covered with protection
Paint, described protective paint is made by the steps:
1) by 1 parts by weight of phosphoric acid tributyl, 0.5 weight portion calcium chloride, 1.6 parts by weight of ethylene base trimethoxy silanes, 2.3
Weight portion malonic acid, 13 weight portion eva emulsions put in 20 parts by weight of deionized water successively, stir；
2) put into 2.6 weight portion three (2,3- dibromopropyl) fulminuric acid esters more successively, 0.8 weight portion pancreas add drift t,
1.4 weight portion lauric acid amide of ethanol, 1.8 weight portion n- acyl amino hydrochlorates, 1.5 parts by weight of xylene sodium sulfonates, continue
Stirring, prepared protective paint uniform to being sufficiently mixed.
Preferably, boiler dumping-grate, including metal fire grate main body, this metal fire grate body surfaces is covered with protection
Paint, described protective paint is made by the steps:
1) by 2 parts by weight of phosphoric acid tributyls, 0.5 weight portion calcium chloride, 1.6 parts by weight of ethylene base trimethoxy silanes, 2.3
Weight portion malonic acid, 13 weight portion eva emulsions put in 20 parts by weight of deionized water successively, stir；
2) put into 2.6 weight portion three (2,3- dibromopropyl) fulminuric acid esters more successively, 0.8 weight portion pancreas add drift t,
1.4 weight portion lauric acid amide of ethanol, 1.8 weight portion n- acyl amino hydrochlorates, 1.5 parts by weight of xylene sodium sulfonates, continue
Stirring, prepared protective paint uniform to being sufficiently mixed.
Preferably, boiler dumping-grate, including metal fire grate main body, this metal fire grate body surfaces is covered with protection
Paint, described protective paint is made by the steps:
1) by 1.2 parts by weight of phosphoric acid tributyls, 0.5 weight portion calcium chloride, 1.6 parts by weight of ethylene base trimethoxy silanes,
2.3 weight portion malonic acid, 13 weight portion eva emulsions put in 20 parts by weight of deionized water successively, stir；
2) put into 2.6 weight portion three (2,3- dibromopropyl) fulminuric acid esters more successively, 0.8 weight portion pancreas add drift t,
1.4 weight portion lauric acid amide of ethanol, 1.8 weight portion n- acyl amino hydrochlorates, 1.5 parts by weight of xylene sodium sulfonates, continue
Stirring, prepared protective paint uniform to being sufficiently mixed.
Advantages of the present invention and having the beneficial effects that: a kind of boiler dumping-grate, its metal fire grate body table are provided
Face is coated with protective paint, makes metal fire grate main body have excellent heat-resisting, wear-resisting, antirust, corrosion-resistant, antioxygenic property, thus
Ensure fire grate energy life-time service.
The performance of " protective paint " and purposes are determined by its component and proportioning, and the different component meeting in " protective paint "
Influence each other, component and its proportioning can determine the final performance of " protective paint ", such as fruit component and its proportioning be not mutually coordinated, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, when serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " protection
The optimal component of paint " and proportioning so that multiple component combine, mutually coordinated and produce positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Boiler dumping-grate, including metal fire grate main body, this metal fire grate body surfaces is covered with protective paint, described
Protective paint is made by the steps:
1) by 1～2 parts by weight of phosphoric acid tributyl, 0.5 weight portion calcium chloride, 1.6 parts by weight of ethylene base trimethoxy silanes,
2.3 weight portion malonic acid, 13 weight portion eva emulsions put in 20 parts by weight of deionized water successively, stir；
2) put into 2.6 weight portion three (2,3- dibromopropyl) fulminuric acid esters more successively, 0.8 weight portion pancreas add drift t,
1.4 weight portion lauric acid amide of ethanol, 1.8 weight portion n- acyl amino hydrochlorates, 1.5 parts by weight of xylene sodium sulfonates, continue
Stirring, prepared protective paint uniform to being sufficiently mixed.
Embodiment 2
Boiler dumping-grate, including metal fire grate main body, this metal fire grate body surfaces is covered with protective paint, described
Protective paint is made by the steps:
1) by 1 parts by weight of phosphoric acid tributyl, 0.5 weight portion calcium chloride, 1.6 parts by weight of ethylene base trimethoxy silanes, 2.3
Weight portion malonic acid, 13 weight portion eva emulsions put in 20 parts by weight of deionized water successively, stir；
2) put into 2.6 weight portion three (2,3- dibromopropyl) fulminuric acid esters more successively, 0.8 weight portion pancreas add drift t,
1.4 weight portion lauric acid amide of ethanol, 1.8 weight portion n- acyl amino hydrochlorates, 1.5 parts by weight of xylene sodium sulfonates, continue
Stirring, prepared protective paint uniform to being sufficiently mixed.
Embodiment 3
Boiler dumping-grate, including metal fire grate main body, this metal fire grate body surfaces is covered with protective paint, described
Protective paint is made by the steps:
1) by 2 parts by weight of phosphoric acid tributyls, 0.5 weight portion calcium chloride, 1.6 parts by weight of ethylene base trimethoxy silanes, 2.3
Weight portion malonic acid, 13 weight portion eva emulsions put in 20 parts by weight of deionized water successively, stir；
2) put into 2.6 weight portion three (2,3- dibromopropyl) fulminuric acid esters more successively, 0.8 weight portion pancreas add drift t,
1.4 weight portion lauric acid amide of ethanol, 1.8 weight portion n- acyl amino hydrochlorates, 1.5 parts by weight of xylene sodium sulfonates, continue
Stirring, prepared protective paint uniform to being sufficiently mixed.
Embodiment 4
Boiler dumping-grate, including metal fire grate main body, this metal fire grate body surfaces is covered with protective paint, described
Protective paint is made by the steps:
1) by 1.2 parts by weight of phosphoric acid tributyls, 0.5 weight portion calcium chloride, 1.6 parts by weight of ethylene base trimethoxy silanes,
2.3 weight portion malonic acid, 13 weight portion eva emulsions put in 20 parts by weight of deionized water successively, stir；
2) put into 2.6 weight portion three (2,3- dibromopropyl) fulminuric acid esters more successively, 0.8 weight portion pancreas add drift t,
1.4 weight portion lauric acid amide of ethanol, 1.8 weight portion n- acyl amino hydrochlorates, 1.5 parts by weight of xylene sodium sulfonates, continue
Stirring, prepared protective paint uniform to being sufficiently mixed.
The boiler dumping-grate of the various embodiments described above, its metal fire grate body surfaces is coated with protective paint, makes metal
Fire grate main body has excellent heat-resisting, wear-resisting, antirust, corrosion-resistant, antioxygenic property, thus ensureing fire grate energy life-time service.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. boiler dumping-grate is it is characterised in that include metal fire grate main body, this metal fire grate body surfaces is covered with anti-
Vernix, described protective paint is made by the steps:
1) by 1～2 parts by weight of phosphoric acid tributyl, 0.5 weight portion calcium chloride, 1.6 parts by weight of ethylene base trimethoxy silanes, 2.3
Weight portion malonic acid, 13 weight portion eva emulsions put in 20 parts by weight of deionized water successively, stir；
2) 2.6 weight portion three (2,3- dibromopropyl) fulminuric acid esters are put into again successively, 0.8 weight portion pancreas adds drift t, 1.4 weights
Amount part lauric acid amide of ethanol, 1.8 weight portion n- acyl amino hydrochlorates, 1.5 parts by weight of xylene sodium sulfonates, continue stirring,
Uniform, the prepared protective paint to being sufficiently mixed.
2. boiler dumping-grate according to claim 1 is it is characterised in that include metal fire grate main body, this metal
Fire grate body surfaces are covered with protective paint, and described protective paint is made by the steps:
1) by 1 parts by weight of phosphoric acid tributyl, 0.5 weight portion calcium chloride, 1.6 parts by weight of ethylene base trimethoxy silanes, 2.3 weight
Part malonic acid, 13 weight portion eva emulsions put in 20 parts by weight of deionized water successively, stir；
2) 2.6 weight portion three (2,3- dibromopropyl) fulminuric acid esters are put into again successively, 0.8 weight portion pancreas adds drift t, 1.4 weights
Amount part lauric acid amide of ethanol, 1.8 weight portion n- acyl amino hydrochlorates, 1.5 parts by weight of xylene sodium sulfonates, continue stirring,
Uniform, the prepared protective paint to being sufficiently mixed.
3. boiler dumping-grate according to claim 1 is it is characterised in that include metal fire grate main body, this metal
Fire grate body surfaces are covered with protective paint, and described protective paint is made by the steps:
1) by 2 parts by weight of phosphoric acid tributyls, 0.5 weight portion calcium chloride, 1.6 parts by weight of ethylene base trimethoxy silanes, 2.3 weight
Part malonic acid, 13 weight portion eva emulsions put in 20 parts by weight of deionized water successively, stir；
2) 2.6 weight portion three (2,3- dibromopropyl) fulminuric acid esters are put into again successively, 0.8 weight portion pancreas adds drift t, 1.4 weights
Amount part lauric acid amide of ethanol, 1.8 weight portion n- acyl amino hydrochlorates, 1.5 parts by weight of xylene sodium sulfonates, continue stirring,
Uniform, the prepared protective paint to being sufficiently mixed.
4. boiler dumping-grate according to claim 1 is it is characterised in that include metal fire grate main body, this metal
Fire grate body surfaces are covered with protective paint, and described protective paint is made by the steps:
1) by 1.2 parts by weight of phosphoric acid tributyls, 0.5 weight portion calcium chloride, 1.6 parts by weight of ethylene base trimethoxy silanes, 2.3 weights
Amount part malonic acid, 13 weight portion eva emulsions put in 20 parts by weight of deionized water successively, stir；
2) 2.6 weight portion three (2,3- dibromopropyl) fulminuric acid esters are put into again successively, 0.8 weight portion pancreas adds drift t, 1.4 weights
Amount part lauric acid amide of ethanol, 1.8 weight portion n- acyl amino hydrochlorates, 1.5 parts by weight of xylene sodium sulfonates, continue stirring,
Uniform, the prepared protective paint to being sufficiently mixed.