CN106366777A - Master control box of mining automatic water spraying dustfall device - Google Patents
Master control box of mining automatic water spraying dustfall device Download PDFInfo
- Publication number
- CN106366777A CN106366777A CN201610763043.4A CN201610763043A CN106366777A CN 106366777 A CN106366777 A CN 106366777A CN 201610763043 A CN201610763043 A CN 201610763043A CN 106366777 A CN106366777 A CN 106366777A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- weight
- protective paint
- parts
- metal shell
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a master control box of a mining automatic water spraying dustfall device. The surface of a metal shell of the master control box is coated with protective paint. The protective paint is prepared in the steps that firstly, 1-2 parts by weight of tetrabutyltin, 1.2 parts by weight of triethanolamine, 1.5 parts by weight of succinic acid alkyl ester sulfonates, 1.2 parts by weight of sodium silicate and 11 parts by weight of EVA emulsion are sequentially put into 25 parts by weight of deionized water and evenly stirred; secondly, 6 parts by weights of castor oil alkyd resin, 0.5 part by weight of sericite, 0.9 part by weight of fatty acid methyl ester sulfonate, 1.1 parts by weight of PAA and 0.4 part by weight of nickel nitrate are sequentially added and continuously stirred till the components are fully and evenly mixed, and the protective paint is prepared. The surface of the metal shell of the master control box of the mining automatic water spraying dustfall device is coated with the protective paint, and it can be guaranteed that the master control box of the mining automatic water spraying dustfall device is used for a long time.
Description
Technical field
The present invention relates to a kind of automatic sprinkling dust suppression device for mines Main Control Tank.
Background technology
Existing automatic sprinkling dust suppression device for mines Main Control Tank, the antirust, antistatic of its metal shell, corrosion-resistant, heat-resisting, anti-
Oxidation susceptibility has much room for improvement, the life-time service of impact automatic sprinkling dust suppression device for mines Main Control Tank.
Content of the invention
It is an object of the invention to provide a kind of automatic sprinkling dust suppression device for mines Main Control Tank, the coating of its metal housing surface
There is protective paint, making metal shell have excellent antirust, antistatic, corrosion-resistant, heat-resisting, antioxygenic property, thus ensureing mining
Automatic dust suppression device by water spray Main Control Tank energy life-time service.
For achieving the above object, the technical scheme is that a kind of automatic sprinkling dust suppression device for mines Main Control Tank of design,
Including metal shell, this metal housing surface is covered with protective paint, and described protective paint is made by the steps:
1) by 1~2 weight portion tetrabutyltin, 1.2 weight portion triethanolamine, 1.5 weight portion succinic acid alkyl ester sulfonate sodium,
1.2 weight portion sodium silicate, 11 weight portion eva emulsions put in 25 parts by weight of deionized water successively, stir;
2) 6 weight portion ricinoleyl alcohol acid resins, 0.5 weight portion sericite, 0.9 weight portion fatty acid methyl ester are put into again successively
Sulfonate, 1.1 weight parts of polymer hydramine, 0.4 weight portion nickel nitrate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Preferably, automatic sprinkling dust suppression device for mines Main Control Tank, including metal shell, this metal housing surface is covered with anti-
Vernix, described protective paint is made by the steps:
1) by 1 weight portion tetrabutyltin, 1.2 weight portion triethanolamine, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 1.2
Weight portion sodium silicate, 11 weight portion eva emulsions put in 25 parts by weight of deionized water successively, stir;
2) 6 weight portion ricinoleyl alcohol acid resins, 0.5 weight portion sericite, 0.9 weight portion fatty acid methyl ester are put into again successively
Sulfonate, 1.1 weight parts of polymer hydramine, 0.4 weight portion nickel nitrate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Preferably, automatic sprinkling dust suppression device for mines Main Control Tank, including metal shell, this metal housing surface is covered with anti-
Vernix, described protective paint is made by the steps:
1) by 2 weight portion tetrabutyltins, 1.2 weight portion triethanolamine, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 1.2
Weight portion sodium silicate, 11 weight portion eva emulsions put in 25 parts by weight of deionized water successively, stir;
2) 6 weight portion ricinoleyl alcohol acid resins, 0.5 weight portion sericite, 0.9 weight portion fatty acid methyl ester are put into again successively
Sulfonate, 1.1 weight parts of polymer hydramine, 0.4 weight portion nickel nitrate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Preferably, automatic sprinkling dust suppression device for mines Main Control Tank, including metal shell, this metal housing surface is covered with anti-
Vernix, described protective paint is made by the steps:
1) by 1.2 weight portion tetrabutyltins, 1.2 weight portion triethanolamine, 1.5 weight portion succinic acid alkyl ester sulfonate sodium,
1.2 weight portion sodium silicate, 11 weight portion eva emulsions put in 25 parts by weight of deionized water successively, stir;
2) 6 weight portion ricinoleyl alcohol acid resins, 0.5 weight portion sericite, 0.9 weight portion fatty acid methyl ester are put into again successively
Sulfonate, 1.1 weight parts of polymer hydramine, 0.4 weight portion nickel nitrate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Advantages of the present invention and having the beneficial effects that: a kind of automatic sprinkling dust suppression device for mines Main Control Tank, its metal are provided
Surface of shell is coated with protective paint, makes metal shell have excellent antirust, antistatic, corrosion-resistant, heat-resisting, antioxygenic property,
Thus ensureing automatic sprinkling dust suppression device for mines Main Control Tank energy life-time service.
The performance of " protective paint " and purposes are determined by its component and proportioning, and the different component meeting in " protective paint "
Influence each other, component and its proportioning can determine the final performance of " protective paint ", such as fruit component and its proportioning be not mutually coordinated, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, when serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " protection
The optimal component of paint " and proportioning so that multiple component combine, mutually coordinated and produce positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Automatic sprinkling dust suppression device for mines Main Control Tank, including metal shell, this metal housing surface is covered with protective paint, institute
State protective paint to be made by the steps:
1) by 1~2 weight portion tetrabutyltin, 1.2 weight portion triethanolamine, 1.5 weight portion succinic acid alkyl ester sulfonate sodium,
1.2 weight portion sodium silicate, 11 weight portion eva emulsions put in 25 parts by weight of deionized water successively, stir;
2) 6 weight portion ricinoleyl alcohol acid resins, 0.5 weight portion sericite, 0.9 weight portion fatty acid methyl ester are put into again successively
Sulfonate, 1.1 weight parts of polymer hydramine, 0.4 weight portion nickel nitrate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Embodiment 2
Automatic sprinkling dust suppression device for mines Main Control Tank, including metal shell, this metal housing surface is covered with protective paint, institute
State protective paint to be made by the steps:
1) by 1 weight portion tetrabutyltin, 1.2 weight portion triethanolamine, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 1.2
Weight portion sodium silicate, 11 weight portion eva emulsions put in 25 parts by weight of deionized water successively, stir;
2) 6 weight portion ricinoleyl alcohol acid resins, 0.5 weight portion sericite, 0.9 weight portion fatty acid methyl ester are put into again successively
Sulfonate, 1.1 weight parts of polymer hydramine, 0.4 weight portion nickel nitrate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Embodiment 3
Automatic sprinkling dust suppression device for mines Main Control Tank, including metal shell, this metal housing surface is covered with protective paint, institute
State protective paint to be made by the steps:
1) by 2 weight portion tetrabutyltins, 1.2 weight portion triethanolamine, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 1.2
Weight portion sodium silicate, 11 weight portion eva emulsions put in 25 parts by weight of deionized water successively, stir;
2) 6 weight portion ricinoleyl alcohol acid resins, 0.5 weight portion sericite, 0.9 weight portion fatty acid methyl ester are put into again successively
Sulfonate, 1.1 weight parts of polymer hydramine, 0.4 weight portion nickel nitrate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Embodiment 4
Automatic sprinkling dust suppression device for mines Main Control Tank, including metal shell, this metal housing surface is covered with protective paint, institute
State protective paint to be made by the steps:
1) by 1.2 weight portion tetrabutyltins, 1.2 weight portion triethanolamine, 1.5 weight portion succinic acid alkyl ester sulfonate sodium,
1.2 weight portion sodium silicate, 11 weight portion eva emulsions put in 25 parts by weight of deionized water successively, stir;
2) 6 weight portion ricinoleyl alcohol acid resins, 0.5 weight portion sericite, 0.9 weight portion fatty acid methyl ester are put into again successively
Sulfonate, 1.1 weight parts of polymer hydramine, 0.4 weight portion nickel nitrate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
The automatic sprinkling dust suppression device for mines Main Control Tank of the various embodiments described above, its metal housing surface is coated with protective paint,
Metal shell is made to have excellent antirust, antistatic, corrosion-resistant, heat-resisting, antioxygenic property, thus ensureing mining Self-watering fall
Dirt device Main Control Tank energy life-time service.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. a kind of automatic sprinkling dust suppression device for mines Main Control Tank is it is characterised in that include metal shell, this metal housing surface
It is covered with protective paint, described protective paint is made by the steps:
1) by 1~2 weight portion tetrabutyltin, 1.2 weight portion triethanolamine, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 1.2
Weight portion sodium silicate, 11 weight portion eva emulsions put in 25 parts by weight of deionized water successively, stir;
2) 6 weight portion ricinoleyl alcohol acid resins, 0.5 weight portion sericite, 0.9 weight portion fatty acid methyl ester sulfonic acid are put into again successively
Salt, 1.1 weight parts of polymer hydramine, 0.4 weight portion nickel nitrate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
2. automatic sprinkling dust suppression device for mines Main Control Tank according to claim 1 it is characterised in that include metal shell,
This metal housing surface is covered with protective paint, and described protective paint is made by the steps:
1) by 1 weight portion tetrabutyltin, 1.2 weight portion triethanolamine, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 1.2 weight
Part sodium silicate, 11 weight portion eva emulsions put in 25 parts by weight of deionized water successively, stir;
2) 6 weight portion ricinoleyl alcohol acid resins, 0.5 weight portion sericite, 0.9 weight portion fatty acid methyl ester sulfonic acid are put into again successively
Salt, 1.1 weight parts of polymer hydramine, 0.4 weight portion nickel nitrate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
3. automatic sprinkling dust suppression device for mines Main Control Tank according to claim 1 it is characterised in that include metal shell,
This metal housing surface is covered with protective paint, and described protective paint is made by the steps:
1) by 2 weight portion tetrabutyltins, 1.2 weight portion triethanolamine, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 1.2 weight
Part sodium silicate, 11 weight portion eva emulsions put in 25 parts by weight of deionized water successively, stir;
2) 6 weight portion ricinoleyl alcohol acid resins, 0.5 weight portion sericite, 0.9 weight portion fatty acid methyl ester sulfonic acid are put into again successively
Salt, 1.1 weight parts of polymer hydramine, 0.4 weight portion nickel nitrate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
4. automatic sprinkling dust suppression device for mines Main Control Tank according to claim 1 it is characterised in that include metal shell,
This metal housing surface is covered with protective paint, and described protective paint is made by the steps:
1) by 1.2 weight portion tetrabutyltins, 1.2 weight portion triethanolamine, 1.5 weight portion succinic acid alkyl ester sulfonate sodium, 1.2 weights
Amount part sodium silicate, 11 weight portion eva emulsions put in 25 parts by weight of deionized water successively, stir;
2) 6 weight portion ricinoleyl alcohol acid resins, 0.5 weight portion sericite, 0.9 weight portion fatty acid methyl ester sulfonic acid are put into again successively
Salt, 1.1 weight parts of polymer hydramine, 0.4 weight portion nickel nitrate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.