CN106365659A - 一种刚玉耐磨防腐浇注料 - Google Patents
一种刚玉耐磨防腐浇注料 Download PDFInfo
- Publication number
- CN106365659A CN106365659A CN201610785157.9A CN201610785157A CN106365659A CN 106365659 A CN106365659 A CN 106365659A CN 201610785157 A CN201610785157 A CN 201610785157A CN 106365659 A CN106365659 A CN 106365659A
- Authority
- CN
- China
- Prior art keywords
- resistant
- corrosion
- castable
- corundum
- particle diameter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种刚玉耐磨防腐浇注料,包括以下主要成分:矾土熟料、白刚玉、莫来石、红柱石、二氧化硅、碳化硅、氧化铝微粉和粘结剂。通过将不同粒径的各原料,按照一定的比例混合后,再加入特定标号的抗渗水泥作为粘结剂,不但保留了各原料的耐火、耐磨、防腐蚀方面的优点,同时还具有非常好的气密性和抗折强度,从而延长了耐火材料的使用时间,降低了生产能耗,提高了生产效率,促进了节能减排。
Description
技术领域
本发明涉及耐火材料技术领域,尤其涉及一种刚玉耐磨防腐浇注料。
背景技术
自流浇注料,是指低水泥、超低水泥或水泥耐火浇注料以其混合后的流动性为特征,具有这种流动性的耐火浇注料无需施加外力即可流动和脱气,且无明显偏析。由于自流浇注料具有良好的流动特性,近年来已引起人们的关注。
刚玉耐磨防腐浇注料适合于垃圾焚烧设备。用于高温炉在进料或出料区域均受到不同程度的磨擦,使耐火砖或浇注受到损坏,它的特点是,抗酸碱渣液,抗氧化、抗冲刷。
一些特殊情况下,对浇注料的耐磨,特别是碱腐蚀、金属和金属渣腐蚀情况下的耐磨防腐性能要求较高,故有必要研究一种刚玉耐磨防腐浇注料。
发明内容
基于背景技术存在的技术问题,本发明提出了一种刚玉耐磨防腐浇注料。
一种刚玉耐磨防腐浇注料,包括以下重量百分比的组分:
优选的,所述的结合剂为抗渗水泥。
进一步优选的,所述的结合剂为S6水泥。
优选的,所述的刚玉耐磨防腐浇注料,包括以下重量百分比的组分:
矾土是由三种铝的氢氧化物以不同的比率组成的胶体混合物。根据其用途将其分为冶金级、化工级、耐火级、研磨级、水泥级等。被用于制造耐火材料,这种矾土被称为耐火级矾土。而AL2O3/Fe2O3和AL2O3/Fe2O3比例适当的矾土熟料,用于熔氧化铝./Fe2O3和AL2O3/Fe2O3比例适当的矾土熟料,用于熔氧化铝.
矾土抗酸、碱性熔渣侵蚀的能力强,高温强度高,广泛应用于钢铁、有色等行业,但其抗急冷热能力差、高温体积稳定性不好,导致材料的变形和剥落,降低材料的使用寿命。目前国内基本采用加入人工合成莫来石的方法来克服其缺点,然而人工合成莫来石的价格高,限制了其使用。矾土在耐火材料和铝工业中有着广泛的用途。矾土最基本的用途是在生产铝的冶金部门,占矾土总消耗的85%。其余的矾土消耗可分为特种氧化铝和“其它”两大类。特种铝中矾土用于生产氮板化铝、锻烧氧化铝和活性氧化铝,占矾土总消耗盘的10%。“其它”类指直接用于像耐火材料、水泥和腐蚀剂工业等开采的矾土。就市场规模和价值而言,耐火矾土在这种非冶金市场最终用途中占有重要的地位。
白刚玉中三氧化二铝(AL2O3)含量在99%以上,并含有少量氧化铁、氧化硅等成分,呈白色。以工业氧化铝粉为原料,于电弧中经2000度以上高温熔炼后冷却制成,经粉碎整形,磁选去铁,筛分成多种粒度,其质地致密、硬度高,粒形成尖角状,适用于制造陶瓷、树脂固结磨具以及研磨、抛光、喷砂、精密铸造(精铸专用刚玉)等,还可用于制造高级耐火材料,代号“WA”于国际通用标准、国家标准一致,多数供出口,也有一定量供应国内用户。
莫来石(或莫乃石)是一系列由铝硅酸盐组成的矿物统称,莫来石是AL2O3一SiO2系中唯一稳定的二元化合物,这一类矿物比较稀少。莫来石是一种优质的耐火原料,这一类矿物比较稀少。莫来石是铝硅酸盐在高温下生成的矿物,人工加热铝硅酸盐时会形成莫来石。天然的莫来石晶体为细长的针状且呈放射簇状。莫来石矿被用来生产高温耐火材料。在C/C复合材料中多作为热障涂层,应用广泛。莫来石AL2O3-Si02元系中常压下唯一稳定的二元固溶体,化学式为3AL2O3-2Si02天然的莫来石非常少,通常烧结法或电容法等人工合成。密度;3.16g/cm3莫式硬度;6-7耐火度:1800℃是稳定,1810℃分解为刚玉和液相。
红柱石化学组成为Al2[SiO4]O、晶体属正交(斜方)晶系的岛状结构硅酸盐矿物。英文名来自首先发现它的西班牙名城安达卢西亚(Andalucia)。与蓝晶石、夕线石成同质多象。通常呈柱状晶体,横断面接近四方形。有些红柱石在生长过程中俘获部分碳质和粘土矿物,在晶体内定向排列,在横断面上呈十字形,称空晶石。
集合体形态多呈放射状或粒状,呈放射状的,俗称菊花石。呈粉红色、玫瑰红色、红褐色或灰白色,玻璃光泽,柱面解理中等。摩斯硬度6.5~7.5,比重3.15~3.16。
红柱石常见于泥质岩和侵入体的接触带,是典型的接触热变质矿物。中国北京西山盛产放射状红柱石。世界其他著名产地有西班牙的安达卢西亚、奥地利的蒂罗尔州、巴西的米纳斯吉拉斯等。
红柱石加热至1300℃变为莫来石,是高级耐火材料,用途同蓝晶石。淡红色或绿色透明的晶体可作宝石。空晶石因在粉红、灰白的底色上衬托有黑十字,常被加工成工艺装饰品。
碳化硅(SiC)是用石英砂、石油焦(或煤焦)、木屑(生产绿色碳化硅时需要加食盐)等原料通过电阻炉高温冶炼而成。碳化硅在大自然也存在罕见的矿物,莫桑石。碳化硅又称碳硅石。在当代C、N、B等非氧化物高技术耐火原料中,碳化硅为应用最广泛、最经济的一种,可以称为金钢砂或耐火砂。
本发明中矾土熟料、白刚玉、莫来石、红柱石、氧化铝微粉、二氧化硅这些原料的主要化学成分均为二氧化硅、氧化铝,只是它们各自的化学结构各不相同,例如矾土中含有结晶水,莫来石是AL2O3一SiO2系中唯一稳定的二元化合物晶体;红柱石化学组成为Al2[SiO4]O、属正交(斜方)晶系,这些不同的原料由于其结构不同,耐火、耐磨、防腐蚀效果也各不相同。
本方案的有益之处在于:本发明中通过将不同粒径的各原料,按照一定的比例混合后,再加入特定标号的抗渗水泥作为粘结剂,不但保留了各原料的耐火、耐磨、防腐蚀方面的优点,同时还具有非常好的气密性和抗折强度,从而延长了耐火材料的使用时间,降低了生产能耗,提高了生产效率,促进了节能减排。
具体实施方式
实施例1:
一种刚玉耐磨防腐浇注料,包括以下重量百分比的组分:
所述的结合剂为S6水泥。
实施例2:
一种刚玉耐磨防腐浇注料,包括以下重量百分比的组分:
所述的结合剂为S6水泥。
实施例3:
一种刚玉耐磨防腐浇注料,包括以下重量百分比的组分:
所述的结合剂为S6水泥。
对实施例1-3进行检测:
检测项目 | 实施例1 | 实施例2 | 实施例3 |
显气孔率(%) | 2.8 | 2.8 | 2.9 |
密度(g/cm3) | 2.75 | 2.72 | 2.65 |
抗折强度(MPa) | 5.2 | 5.0 | 5.0 |
此检测数据只针对上述检测样品。
以上所述,仅为本发明较佳的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明揭露的技术范围内,根据本发明的技术方案及其发明构思加以等同替换或改变,都应涵盖在本发明的保护范围之内。
Claims (4)
1.一种刚玉耐磨防腐浇注料,其特征在于,包括以下重量百分比的组分:
矾土熟料 3mm <粒径≤5mm 20-30%
矾土熟料 5mm <粒径≤8mm 10-20%
白刚玉 1mm <粒径≤3mm 10-20%
莫来石 粒径≤1mm 10-20%
红柱石 200目 8-12%
碳化硅 320目 5-8%
氧化铝微粉 2-5%
二氧化硅 4-8%
结合剂 3-6%。
2.如权利要求1所述的刚玉耐磨防腐浇注料,其特征在于,所述的结合剂为抗渗水泥。
3.如权利要求1所述的刚玉耐磨防腐浇注料,其特征在于,所述的结合剂为S6水泥。
4.如权利要求1所述的刚玉耐磨防腐浇注料,其特征在于,所述的刚玉耐磨防腐浇注料,包括以下重量百分比的组分:
矾土熟料 3mm <粒径≤5mm 25%
矾土熟料 5mm <粒径≤8mm 15%
白刚玉 1mm <粒径≤3mm 15%
莫来石 粒径≤1mm 15%
红柱石 200目 10%
碳化硅 320目 6%
氧化铝微粉 4%
二氧化硅 5%
结合剂 5%。