CN106349827A - Iron hoop for packaging barrel - Google Patents
Iron hoop for packaging barrel Download PDFInfo
- Publication number
- CN106349827A CN106349827A CN201610778145.3A CN201610778145A CN106349827A CN 106349827 A CN106349827 A CN 106349827A CN 201610778145 A CN201610778145 A CN 201610778145A CN 106349827 A CN106349827 A CN 106349827A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- weight
- iron hoop
- parts
- protective paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an iron hoop for a packaging barrel. The surface of an iron hoop main body is coated with protective paint, and the protective paint is prepared by the following steps: 1) putting 1 to 2 parts by weight of aluminum stearate, 2.6 parts by weight of cyclohexanone, 2.3 parts by weight of polyoxyethylene polyoxypropylene ether carboxylate of fatty alcohol, 1.8 parts by weight of methyl cellulose and 8 parts by weight of E-51 epoxy resin sequentially into 22 parts by weight of deionized water and stirring uniformly; 2) putting 14 parts by weight of styrene-acrylic emulsion, 0.5 part by weight of zinc naphthenate, 2.3 parts by weight of sorbitan fatty acid ester, 1.2 parts by weight of sodium hydroxide and 0.5 part by weight of barium petroleum sulfonate sequentially, and continuously stirring until the materials are mixed completely and uniformly to prepare the protective paint. According to the iron hoop provided by the invention, the surface of the iron hoop main body is coated with the protective paint, so long-term use of the iron hoop for the packaging barrel can be guaranteed.
Description
Technical field
The present invention relates to a kind of pail pack iron hoop.
Background technology
Existing pail pack iron hoop, the antioxidation of its iron hoop main body, antirust, decay resistance have much room for improvement, impact packaging
The life-time service of bucket iron hoop.
Content of the invention
It is an object of the invention to provide a kind of pail pack iron hoop, its iron hoop body surfaces is coated with protective paint, makes ferrum
Hoop main body has excellent antioxidation, antirust, decay resistance, thus protective packing bucket iron hoop energy life-time service.
For achieving the above object, the technical scheme is that a kind of pail pack iron hoop of design, including iron hoop main body, should
Iron hoop body surfaces are covered with protective paint, and described protective paint is made by the steps:
1) by 1～2 weight portion aluminium stearate, 2.6 weight portion Ketohexamethylene, 2.3 weight portion aliphatic alcohol polyethenoxy polyoxies third
Alkene ether, 1.8 weight portion methylcellulose, 8 weight portion e-51 epoxy resin put in 22 parts by weight of deionized water successively, and stirring is all
Even；
2) 14 weight portion styrene-acrylic emulsions, 0.5 weight portion zinc naphthenate, 2.3 weight portion Sorbitan alcohol esters are put into again successively
Fat acid esters, 1.2 parts by weight of sodium hydroxide, 0.5 weight portion barium mahogany sulfonate, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.
Preferably, pail pack iron hoop, including iron hoop main body, this iron hoop body surfaces is covered with protective paint, described protection
Paint is made by the steps:
1) by 1 weight portion aluminium stearate, 2.6 weight portion Ketohexamethylene, 2.3 weight portion aliphatic alcohol polyethenoxy polyoxypropylenes
Ether, 1.8 weight portion methylcellulose, 8 weight portion e-51 epoxy resin put in 22 parts by weight of deionized water successively, and stirring is all
Even；
2) 14 weight portion styrene-acrylic emulsions, 0.5 weight portion zinc naphthenate, 2.3 weight portion Sorbitan alcohol esters are put into again successively
Fat acid esters, 1.2 parts by weight of sodium hydroxide, 0.5 weight portion barium mahogany sulfonate, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.
Preferably, pail pack iron hoop, including iron hoop main body, this iron hoop body surfaces is covered with protective paint, described protection
Paint is made by the steps:
1) by 2 weight portion aluminium stearate, 2.6 weight portion Ketohexamethylene, 2.3 weight portion aliphatic alcohol polyethenoxy polyoxypropylenes
Ether, 1.8 weight portion methylcellulose, 8 weight portion e-51 epoxy resin put in 22 parts by weight of deionized water successively, and stirring is all
Even；
2) 14 weight portion styrene-acrylic emulsions, 0.5 weight portion zinc naphthenate, 2.3 weight portion Sorbitan alcohol esters are put into again successively
Fat acid esters, 1.2 parts by weight of sodium hydroxide, 0.5 weight portion barium mahogany sulfonate, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.
Preferably, pail pack iron hoop, including iron hoop main body, this iron hoop body surfaces is covered with protective paint, described protection
Paint is made by the steps:
1) by 1.2 weight portion aluminium stearate, 2.6 weight portion Ketohexamethylene, 2.3 weight portion aliphatic alcohol polyethenoxy polyoxypropylenes
Ether, 1.8 weight portion methylcellulose, 8 weight portion e-51 epoxy resin put in 22 parts by weight of deionized water successively, and stirring is all
Even；
2) 14 weight portion styrene-acrylic emulsions, 0.5 weight portion zinc naphthenate, 2.3 weight portion Sorbitan alcohol esters are put into again successively
Fat acid esters, 1.2 parts by weight of sodium hydroxide, 0.5 weight portion barium mahogany sulfonate, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.
Advantages of the present invention and having the beneficial effects that: provide a kind of pail pack iron hoop, its iron hoop body surfaces is coated with
Protective paint, makes iron hoop main body have excellent antioxidation, antirust, decay resistance, thus protective packing bucket can be long-term with iron hoop
Use.
The performance of " protective paint " and purposes are determined by its component and proportioning, and the different component meeting in " protective paint "
Influence each other, component and its proportioning can determine the final performance of " protective paint ", such as fruit component and its proportioning be not mutually coordinated, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, when serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " protection
The optimal component of paint " and proportioning so that multiple component combine, mutually coordinated and produce positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Pail pack iron hoop, including iron hoop main body, this iron hoop body surfaces is covered with protective paint, and described protective paint passes through such as
Lower step preparation:
1) by 1～2 weight portion aluminium stearate, 2.6 weight portion Ketohexamethylene, 2.3 weight portion aliphatic alcohol polyethenoxy polyoxies third
Alkene ether, 1.8 weight portion methylcellulose, 8 weight portion e-51 epoxy resin put in 22 parts by weight of deionized water successively, and stirring is all
Even；
2) 14 weight portion styrene-acrylic emulsions, 0.5 weight portion zinc naphthenate, 2.3 weight portion Sorbitan alcohol esters are put into again successively
Fat acid esters, 1.2 parts by weight of sodium hydroxide, 0.5 weight portion barium mahogany sulfonate, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.
Embodiment 2
Pail pack iron hoop, including iron hoop main body, this iron hoop body surfaces is covered with protective paint, and described protective paint passes through such as
Lower step preparation:
1) by 1 weight portion aluminium stearate, 2.6 weight portion Ketohexamethylene, 2.3 weight portion aliphatic alcohol polyethenoxy polyoxypropylenes
Ether, 1.8 weight portion methylcellulose, 8 weight portion e-51 epoxy resin put in 22 parts by weight of deionized water successively, and stirring is all
Even；
2) 14 weight portion styrene-acrylic emulsions, 0.5 weight portion zinc naphthenate, 2.3 weight portion Sorbitan alcohol esters are put into again successively
Fat acid esters, 1.2 parts by weight of sodium hydroxide, 0.5 weight portion barium mahogany sulfonate, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.
Embodiment 3
Pail pack iron hoop, including iron hoop main body, this iron hoop body surfaces is covered with protective paint, and described protective paint passes through such as
Lower step preparation:
1) by 2 weight portion aluminium stearate, 2.6 weight portion Ketohexamethylene, 2.3 weight portion aliphatic alcohol polyethenoxy polyoxypropylenes
Ether, 1.8 weight portion methylcellulose, 8 weight portion e-51 epoxy resin put in 22 parts by weight of deionized water successively, and stirring is all
Even；
2) 14 weight portion styrene-acrylic emulsions, 0.5 weight portion zinc naphthenate, 2.3 weight portion Sorbitan alcohol esters are put into again successively
Fat acid esters, 1.2 parts by weight of sodium hydroxide, 0.5 weight portion barium mahogany sulfonate, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.
Embodiment 4
Pail pack iron hoop, including iron hoop main body, this iron hoop body surfaces is covered with protective paint, and described protective paint passes through such as
Lower step preparation:
1) by 1.2 weight portion aluminium stearate, 2.6 weight portion Ketohexamethylene, 2.3 weight portion aliphatic alcohol polyethenoxy polyoxypropylenes
Ether, 1.8 weight portion methylcellulose, 8 weight portion e-51 epoxy resin put in 22 parts by weight of deionized water successively, and stirring is all
Even；
2) 14 weight portion styrene-acrylic emulsions, 0.5 weight portion zinc naphthenate, 2.3 weight portion Sorbitan alcohol esters are put into again successively
Fat acid esters, 1.2 parts by weight of sodium hydroxide, 0.5 weight portion barium mahogany sulfonate, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.
The pail pack iron hoop of the various embodiments described above, its iron hoop body surfaces is coated with protective paint, so that iron hoop main body is had
Excellent antioxidation, antirust, decay resistance, thus protective packing bucket iron hoop energy life-time service.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. it is characterised in that including iron hoop main body, this iron hoop body surfaces is covered with protective paint to a kind of pail pack iron hoop, institute
State protective paint to be made by the steps:
1) by 1～2 weight portion aluminium stearate, 2.6 weight portion Ketohexamethylene, 2.3 weight portion Fatty alcohol polyoxyethylene polyoxypropylene ether,
1.8 weight portion methylcellulose, 8 weight portion e-51 epoxy resin put in 22 parts by weight of deionized water successively, stir；
2) 14 weight portion styrene-acrylic emulsions, 0.5 weight portion zinc naphthenate, 2.3 weight portion sorbitan fatty acid are put into again successively
Ester, 1.2 parts by weight of sodium hydroxide, 0.5 weight portion barium mahogany sulfonate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
2. pail pack iron hoop according to claim 1 is it is characterised in that include iron hoop main body, this iron hoop body surfaces
It is covered with protective paint, described protective paint is made by the steps:
1) by 1 weight portion aluminium stearate, 2.6 weight portion Ketohexamethylene, 2.3 weight portion Fatty alcohol polyoxyethylene polyoxypropylene ether, 1.8
Weight portion methylcellulose, 8 weight portion e-51 epoxy resin put in 22 parts by weight of deionized water successively, stir；
2) 14 weight portion styrene-acrylic emulsions, 0.5 weight portion zinc naphthenate, 2.3 weight portion sorbitan fatty acid are put into again successively
Ester, 1.2 parts by weight of sodium hydroxide, 0.5 weight portion barium mahogany sulfonate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
3. pail pack iron hoop according to claim 1 is it is characterised in that include iron hoop main body, this iron hoop body surfaces
It is covered with protective paint, described protective paint is made by the steps:
1) by 2 weight portion aluminium stearate, 2.6 weight portion Ketohexamethylene, 2.3 weight portion Fatty alcohol polyoxyethylene polyoxypropylene ether, 1.8
Weight portion methylcellulose, 8 weight portion e-51 epoxy resin put in 22 parts by weight of deionized water successively, stir；
2) 14 weight portion styrene-acrylic emulsions, 0.5 weight portion zinc naphthenate, 2.3 weight portion sorbitan fatty acid are put into again successively
Ester, 1.2 parts by weight of sodium hydroxide, 0.5 weight portion barium mahogany sulfonate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
4. pail pack iron hoop according to claim 1 is it is characterised in that include iron hoop main body, this iron hoop body surfaces
It is covered with protective paint, described protective paint is made by the steps:
1) by 1.2 weight portion aluminium stearate, 2.6 weight portion Ketohexamethylene, 2.3 weight portion Fatty alcohol polyoxyethylene polyoxypropylene ether,
1.8 weight portion methylcellulose, 8 weight portion e-51 epoxy resin put in 22 parts by weight of deionized water successively, stir；
2) 14 weight portion styrene-acrylic emulsions, 0.5 weight portion zinc naphthenate, 2.3 weight portion sorbitan fatty acid are put into again successively
Ester, 1.2 parts by weight of sodium hydroxide, 0.5 weight portion barium mahogany sulfonate, continue stirring, uniform to being sufficiently mixed, prepared protective paint.