CN106336837A - Heat resistant adhesive and preparation method thereof - Google Patents
Heat resistant adhesive and preparation method thereof Download PDFInfo
- Publication number
- CN106336837A CN106336837A CN201610704425.XA CN201610704425A CN106336837A CN 106336837 A CN106336837 A CN 106336837A CN 201610704425 A CN201610704425 A CN 201610704425A CN 106336837 A CN106336837 A CN 106336837A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- resin
- weight
- resisting adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a heat resistant adhesive and a preparation method thereof, and belongs to the chemical technical field. The heat resistant adhesive is made from the following raw materials in parts by weight: 4-10 parts of terpene resin, 3-9 parts of triethanolamine, 2-8 parts of glycidyl phenyl ether, 3-9 parts of phenolic resin, 6-12 parts of methyl acetate, 3-9 parts of polysulfone resin, 4-10 parts of hydroxy propyl distarch phosphate, 1-5 parts of asbestos powder, 1-5 parts of N-methyl pyrrolidone, 4-10 parts of quartz sand, 5-10 parts of Triisopropanolamine, 6-12 parts of an antioxidant and 6-12 parts of a crosslinking agent. The heat resistant adhesive has good high temperature resistance, at high temperatures can be normally used, and has the advantages of very good cohesiveness, good bonding effect, simple preparation, low cost and good performance.
Description
Technical field
The present invention relates to a kind of heat-resisting adhesive and preparation method thereof, belong to chemical technology field.
Background technology
Adhesive, refers to the technology that homogeneity or heterogeneous body surface adhesive link together, and has stress distribution even
Continuous, lightweight, the low feature of technological temperature.Glued joint and be particularly well-suited to unlike material, different-thickness, ultra-thin specification and complex component
Connection.Splicing RECENT DEVELOPMENTS is the fastest, and application industry is extremely wide.The sorting technique of adhesive is a lot, can be divided into heat by application process
Curable type, heat molten type, room temperature curing type, pressure sensitive etc.;It is divided into structural type, non-configuration or special gelatin by application;Connecing form can
It is divided into water-soluble, emulsion type, solvent-borne type and various solid-state version etc.;Traditional adhesive production cost is high, and using effect is bad.
Content of the invention
The purpose of the present invention is to make up the deficiencies in the prior art, provides a kind of heat-resisting adhesive and preparation method thereof.This
The adhesive of invention has good resistance to elevated temperatures, can normally use at high temperature, have good caking property simultaneously, glues
Knot effect is good, and prepares simple, with low cost, function admirable.
The technical scheme is that a kind of heat-resisting adhesive, by following parts by weight
Raw material make: 4~10 parts of terpene resin, 3~9 parts of triethanolamine, 2~8 parts of expoxy propane phenyl ether, phenolic resin 3~9
Part, 6~12 parts of methyl acetate, 3~9 parts of polysulfone resin, 4~10 parts of hydroxypropyl PASELLI EASYGEL, 1~5 part of flake asbestos, n- first
1~5 part of base ketopyrrolidine, 4~10 parts of quartz sand, 5~10 parts of triisopropanolamine, 6~12 parts of antioxidant and cross-linking agent 6~12
Part.
On the basis of technique scheme, the present invention can also do following improvement.
Further, it is made up of the raw material of following parts by weight: 7 parts of terpene resin, 6 parts of triethanolamine, expoxy propane phenyl
5 parts of ether, 6 parts of phenolic resin, 9 parts of methyl acetate, 6 parts of polysulfone resin, 7 parts of hydroxypropyl PASELLI EASYGEL, 3 parts of flake asbestos, n-
3 parts of methyl pyrrolidone, 7 parts of quartz sand, 8 parts of triisopropanolamine, 9 parts of antioxidant and 9 parts of cross-linking agent.
Further, described antioxidant is vitamin e oil, and described cross-linking agent is Biformyl.
A kind of preparation method of heat-resisting adhesive, comprises the steps:
(1) weigh the raw material of following parts by weight: 4~10 parts of terpene resin, 3~9 parts of triethanolamine, expoxy propane phenyl
2~8 parts of ether, 3~9 parts of phenolic resin, 6~12 parts of methyl acetate, 3~9 parts of polysulfone resin, hydroxypropyl PASELLI EASYGEL 4~
10 parts, 1~5 part of flake asbestos, 1~5 part of n- methyl pyrrolidone, 4~10 parts of quartz sand and 5~10 parts of triisopropanolamine, add
In reactor, progressively heat up, and be slowly stirred, start timing when temperature rises to 90~96 DEG C, be incubated 40~50 minutes, simultaneously
At the uniform velocity stirred, until it reaches reaction end;
(2) it is continuously heating to 100 DEG C, add the cross-linking agent of the antioxidant that parts by weight are 6~12 parts and 6~12 parts,
After stirring, obtain final product described heat-resisting adhesive.
On the basis of technique scheme, the present invention can also do following improvement.
Further, the parts by weight of the described raw material of step (1) are: 7 parts of terpene resin, 6 parts of triethanolamine, expoxy propane benzene
5 parts of base ether, 6 parts of phenolic resin, 9 parts of methyl acetate, 6 parts of polysulfone resin, 7 parts of hydroxypropyl PASELLI EASYGEL, 3 parts of flake asbestos,
3 parts of n- methyl pyrrolidone, 7 parts of quartz sand, 8 parts of triisopropanolamine.
Further, the parts by weight of the described antioxidant of step (2) are 9 parts, and the parts by weight of described cross-linking agent are 9 parts.
Further, described antioxidant is vitamin e oil, and described cross-linking agent is Biformyl.
The invention has the beneficial effects as follows:
(1) adhesive of the present invention has good resistance to elevated temperatures, can normally use at high temperature, has very simultaneously
Good caking property, bond effect is good.
(2) present invention prepare simple, with low cost, function admirable, suitable large-scale production.
Specific embodiment
Below in conjunction with specific embodiment, the principle of the present invention and feature are described, example is served only for explaining this
Bright, it is not intended to limit the scope of the present invention.
Embodiment 1:
The heat-resisting adhesive of the present embodiment, is made up of the raw material of following weight: terpene resin 4kg, triethanolamine 9kg,
Expoxy propane phenyl ether 2kg, phenolic resin 9kg, methyl acetate 6kg, polysulfone resin 9kg, hydroxypropyl PASELLI EASYGEL 4kg,
Flake asbestos 5kg, n- methyl pyrrolidone 1kg, quartz sand 10kg, triisopropanolamine 5kg, vitamin e oil 12kg and Biformyl
6kg.
The preparation method of the heat-resisting adhesive of the present embodiment, comprises the steps:
(1) weigh the raw material of following weight: terpene resin 4kg, triethanolamine 9kg, expoxy propane phenyl ether 2kg, phenolic aldehyde
Resin 9kg, methyl acetate 6kg, polysulfone resin 9kg, hydroxypropyl PASELLI EASYGEL 4kg, flake asbestos 5kg, n- crassitude
Ketone 1kg, quartz sand 10kg, triisopropanolamine 5kg, add in reactor, progressively heat up, and be slowly stirred, treat that temperature rises to 90
DEG C when start timing, be incubated 50 minutes, at the uniform velocity stirred, until it reaches reaction end simultaneously;
(2) it is continuously heating to 100 DEG C, add the vitamin e oil of 12kg and the Biformyl of 6kg, after stirring, obtain final product institute
State heat-resisting adhesive.
Embodiment 2:
The heat-resisting adhesive of the present embodiment, is made up of the raw material of following weight: terpene resin 7kg, triethanolamine 6kg,
Expoxy propane phenyl ether 5kg, phenolic resin 6kg, methyl acetate 9kg, polysulfone resin 6kg, hydroxypropyl PASELLI EASYGEL 7kg,
Flake asbestos 3kg, n- methyl pyrrolidone 3kg, quartz sand 7kg, triisopropanolamine 8kg, vitamin e oil 9kg and Biformyl 9kg.
The preparation method of the heat-resisting adhesive of the present embodiment, comprises the steps:
(1) weigh the raw material of following weight: terpene resin 7kg, triethanolamine 6kg, expoxy propane phenyl ether 5kg, phenolic aldehyde
Resin 6kg, methyl acetate 9kg, polysulfone resin 6kg, hydroxypropyl PASELLI EASYGEL 7kg, flake asbestos 3kg, n- crassitude
Ketone 3kg, quartz sand 7kg, triisopropanolamine 8kg, add in reactor, progressively heat up, and be slowly stirred, treat that temperature rises to 93 DEG C
When start timing, be incubated 45 minutes, at the uniform velocity stirred, until it reaches reaction end simultaneously;
(2) it is continuously heating to 100 DEG C, add the vitamin e oil of 9kg and the Biformyl of 9kg, after stirring, obtain final product institute
State heat-resisting adhesive.
Embodiment 3:
The heat-resisting adhesive of the present embodiment, is made up of the raw material of following weight: terpene resin 10kg, triethanolamine 3kg,
Expoxy propane phenyl ether 8kg, phenolic resin 3kg, methyl acetate 12kg, polysulfone resin 3kg, hydroxypropyl PASELLI EASYGEL
10kg, flake asbestos 1kg, n- methyl pyrrolidone 5kg, quartz sand 4kg, triisopropanolamine 10kg, vitamin e oil 6kg and second two
Aldehyde 12kg.
The preparation method of the heat-resisting adhesive of the present embodiment, comprises the steps:
(1) weigh the raw material of following weight: terpene resin 10kg, triethanolamine 3kg, expoxy propane phenyl ether 8kg, phenolic aldehyde
Resin 3kg, methyl acetate 12kg, polysulfone resin 3kg, hydroxypropyl PASELLI EASYGEL 10kg, flake asbestos 1kg, n- methylpyrrole
Alkanone 5kg, quartz sand 4kg, triisopropanolamine 10kg, add in reactor, progressively heat up, and be slowly stirred, treat that temperature rises to
Start timing when 96 DEG C, be incubated 40 minutes, at the uniform velocity stirred, until it reaches reaction end simultaneously;
(2) it is continuously heating to 100 DEG C, add the vitamin e oil of 6kg and the Biformyl of 12kg, after stirring, obtain final product institute
State heat-resisting adhesive.
Comparative example
Take the adhesive of certain producer domestic, it includes the raw material of following weight: terpene resin 10kg, triethanolamine 3kg, ring
Ethylene Oxide phenyl ether 8kg, phenolic resin 3kg, methyl acetate 12kg, polysulfone resin 3kg, hydroxypropyl PASELLI EASYGEL 10kg,
Flake asbestos 1kg, resistant to elevated temperatures adhesive contrasts with embodiment 1-3 gained, viscous material phase same material fine powder 200kg.Right
More as shown in table 1 than result.
Table 1 prior art and the comparing result of the method for the present invention
As can be seen here, the adhesive of the present invention has good resistance to elevated temperatures, can normally use at high temperature, simultaneously
There is good caking property, bond effect is good.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all spirit in the present invention and
Within principle, any modification, equivalent substitution and improvement made etc., should be included within the scope of the present invention.
Claims (7)
1. a kind of heat-resisting adhesive is it is characterised in that be made up of the raw material of following parts by weight: 4~10 parts of terpene resin, three
3~9 parts of ethanolamine, 2~8 parts of expoxy propane phenyl ether, 3~9 parts of phenolic resin, 6~12 parts of methyl acetate, polysulfone resin 3~9
Part, 4~10 parts of hydroxypropyl PASELLI EASYGEL, 1~5 part of flake asbestos, 1~5 part of n- methyl pyrrolidone, 4~10 parts of quartz sand,
5~10 parts of triisopropanolamine, 6~12 parts of antioxidant and 6~12 parts of cross-linking agent.
2. a kind of heat-resisting adhesive according to claim 1 is it is characterised in that raw material system by following parts by weight
Become: 7 parts of terpene resin, 6 parts of triethanolamine, 5 parts of expoxy propane phenyl ether, 6 parts of phenolic resin, 9 parts of methyl acetate, polysulfone resin
6 parts, 7 parts of hydroxypropyl PASELLI EASYGEL, 3 parts of flake asbestos, 3 parts of n- methyl pyrrolidone, 7 parts of quartz sand, triisopropanolamine 8
Part, 9 parts of antioxidant and 9 parts of cross-linking agent.
3. a kind of heat-resisting adhesive according to claim 1 and 2 is it is characterised in that described antioxidant is vitamin e
Oil, described cross-linking agent is Biformyl.
4. a kind of preparation method of heat-resisting adhesive is it is characterised in that comprise the steps:
(1) weigh the raw material of following parts by weight: 4~10 parts of terpene resin, 3~9 parts of triethanolamine, expoxy propane phenyl ether 2
~8 parts, 3~9 parts of phenolic resin, 6~12 parts of methyl acetate, 3~9 parts of polysulfone resin, hydroxypropyl PASELLI EASYGEL 4~10
Part, 1~5 part of flake asbestos, 1~5 part of n- methyl pyrrolidone, 4~10 parts of quartz sand and 5~10 parts of triisopropanolamine, add anti-
Answer in kettle, progressively heat up, and be slowly stirred, start timing when temperature rises to 90~96 DEG C, be incubated 40~50 minutes, enter simultaneously
Row at the uniform velocity stirs, until it reaches reaction end;
(2) it is continuously heating to 100 DEG C, add the cross-linking agent of the antioxidant that parts by weight are 6~12 parts and 6~12 parts, stirring
After uniformly, obtain final product described heat-resisting adhesive.
5. a kind of preparation method of heat-resisting adhesive according to claim 4 is it is characterised in that step (1) is described former
The parts by weight of material are: 7 parts of terpene resin, 6 parts of triethanolamine, 5 parts of expoxy propane phenyl ether, 6 parts of phenolic resin, methyl acetate
9 parts, 6 parts of polysulfone resin, 7 parts of hydroxypropyl PASELLI EASYGEL, 3 parts of flake asbestos, 3 parts of n- methyl pyrrolidone, 7 parts of quartz sand,
8 parts of triisopropanolamine.
6. a kind of preparation method of heat-resisting adhesive according to claim 4 is it is characterised in that step (2) is described anti-
The parts by weight of oxidant are 9 parts, and the parts by weight of described cross-linking agent are 9 parts.
7. a kind of heat-resisting adhesive according to any one of claim 4-6 is it is characterised in that described antioxidant is dimension
Raw element e oil, described cross-linking agent is Biformyl.